CN105567094A - Automobile grinding fine wax formulation - Google Patents
Automobile grinding fine wax formulation Download PDFInfo
- Publication number
- CN105567094A CN105567094A CN201610073160.8A CN201610073160A CN105567094A CN 105567094 A CN105567094 A CN 105567094A CN 201610073160 A CN201610073160 A CN 201610073160A CN 105567094 A CN105567094 A CN 105567094A
- Authority
- CN
- China
- Prior art keywords
- parts
- wax
- automobile
- grinding
- fine wax
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to an automobile grinding fine wax formulation. Automobile fine wax is prepared by mixing, by weight, 2-6 parts of suspending agent, 150-200 parts of clear water, 15-50 parts of kerosene, 10-50 parts of white mineral oil, 5-50 parts of polyethylene wax liquid, 2-40 parts of palm wax liquid, 10-60 parts of butyl ether, 10-50 parts of lighter fuel, 2-30 parts of dichloromethane, 10-100 parts of cerium oxide and 15-150 parts of aluminum oxide. The PH value of the formed mixture fine wax liquid ranges from 7.8 to 8.2. The automobile grinding fine wax formulation has the advantages that a fine wax product formed through the formulation can be used for surface grinding and polishing of products or automobile parts made of glass fiber reinforced plastics or glass fiber materials. The material ingredients of grinding wax are optimally matched, so that the surface grinding time of the products is greatly shortened, the grinding efficiency is greatly improved, the surface light and color effect of the ground products is good, and manpower and time are greatly saved.
Description
Technical field
The present invention relates to car wax formula technique, particularly relate to a kind of automobile and to polish thin wax formula.
Background technology
Car wax belongs to traditional automobile finish maintenance thing, is with natural wax or synthetic wax for main component, and it plays by making surfacing in the gap that infiltrates through lacquer painting the effect increasing luminance brightness.Orthodox car waxing is based on glazing protection; now along with the development of car detailing industry, automobile waxing is endowed new intension, i.e. the appearance of lapping wax and increasingly extensive application; if wax played by a car, can reach good brightness effect has just needed thicker wax layer.
Car wax can be divided into solid wax and liquid wax two kinds by physical condition difference, waterproof wax, high temperature-proof wax, anti-electrostatic wax and antiultraviolet wax can be divided into multiple, be divided into polishing wax and polishing lapping wax two kinds by its function difference by its effect difference.Existing different car wax has different features; such as; the peculiar function of new car protection wax is containing a large amount of high molecular polymer; as Warcraft new car wax adopts nano molecular technology; superhard wax shell; coordinate new car to adopt nano-high molecule technology to form hard protective layer at lacquer painting without change trace feature, distinctive chemical molecular structure is not containing any polishing material.Diamond wax has the noble quality of diamond; distinctive hard, the smooth and graceful protective membrane of palm wax can be formed after using; Aero Glass is produced after using lacquer painting; super brightness; silkiness feel, special expelling water lets out dirt ability, containing uv-resistant composition; be not afraid of solar exposure, anti-washing, and can retain for a long time.Most distinguished hard wax is not afraid of and is washed silk ribbon, superhard protection, sturdy and durable, really anti-scratch, superpower waterproof, the infiltration of rainwater and acid rain can be blocked completely, it is lasting to protect, and gloss is dazzling brilliant, the sustainable several months long.Crystal wax is multiple polymers synthesis, not containing paraffin component, is equipped with the unique formula of lasting resin spirit, lacquer painting can be made to form permanence protective membrane, strengthen its face and thoroughly feel, and decontamination, waterproof, acid rain resistant burn into are antistatic.Colored wax is developed for the car paint brightening effect of different colours, has cultivation color effects, and can modify the aberration of local touch-up paint generation or fade.Uv-resistant wax is high molecular polymerization fat formula, has uv-resistant composition, acid rain preventing, anti-oxidant, corrosion-resistant.Waterproof wax is complete rapidly, extreme water-sprinkling effect, and ultra-long time protection car paint, top waterproof resin, air reaction type is filled a prescription, and can block rainwater acid-rain corrosion completely, and generation is difficult impayable luster effect.Brightening wax is made up of multiple high molecular polymer, natural plant formula, strong dirt-removing, easily removes hair cut, prevents lacquer painting from turning white, sends out variable color dirty.Multiple color vernix polishing wax integrates removes Micro scratching and glazing, can remove the shadow scratch of bodywork surface fast, wipe line, piebald, remove zone of oxidation and the dumb light look of old paint film, make aging, fade, the lacquer painting of loss of gloss recovers original color and luster and smooth finish.Clean sand wax can prevent that automobile finish from fading, dirt, removes shadow scratch, wipes line, piebald, remove zone of oxidation and the dumb light look of old paint film.
But; general protectiveness car wax is mixed by compositions such as wax, silicon, greases; belong to oily matter; it can form one deck oil film at lacquer painting and distribute gloss; but because the bonding force of oil film and lacquer painting is poor, guard time is shorter, this wax is usually because the factors such as rainy or flushing run off; sometimes be even attached on windshield, and form grease.In addition, the water droplet remaining in car table, generally in hemispherical, can produce lensing, and focusing sunlight is so that lacquer painting of burning.High-grade beauty treatment wax price is high, because this kind of car wax is except having general protective wax function, it is also containing the permeate agent that a kind of activity is very strong, can make car wax rapid permeability in enamelled coating, the molecular structure that it is special, can and lacquer painting between produce firmly bonding force, the lacquer painting after waxing seems one integrated mass, and effect is rather good.
This case it is important to note that, if some component of present automobile select carbon fiber, glass fibre manufacture, to the polishing operation more complicated on its surface, waxy stone polishing is first adopted successively in the construction of component table buffed surface place, middle wax polishing, thin wax polishing, the effects on surface treatment time is long, and working efficiency is not high, inadequate energy-conserving and environment-protective.
Therefore, for above aspect, need effectively to innovate prior art, provide a kind of material composition to polishing wax to be optimized the formula of collocation.
Summary of the invention
For above defect, the invention provides a kind of automobile being optimized collocation to the material composition of polishing wax to polish thin wax formula, the product surface time of polishing is shortened greatly, and grinding efficiency improves greatly, the product surface photochromic effect polished is good, greatly saves manpower and time.
For achieving the above object, the present invention is by the following technical solutions:
A kind of automobile is polished thin wax formula, is made up of the material mixing of the following parts by weight chosen:
Suspension agent 2-6 part;
Clear water 150-200 part;
Kerosene 15-50 part;
White mineral oil 10-50 part;
Polyethylene wax liquid 5-50 part;
Palm wax liquid 2-40 part;
Butyl ether 10-60 part;
White spirit 10-50 part;
Methylene dichloride 2-30 part;
Cerium oxide 10-100 part;
Aluminum oxide 15-150 part.
The pH value of the thin wax liquid of above formed mixture is 7.8-8.2.
The polish beneficial effect of thin wax formula of automobile of the present invention is:
(1) the thin wax product that this formula is formed can be used for the surface finish polishing of product or the automobile component produced carbon fiber, glass fiber material;
(2) by being optimized collocation to the material composition of polishing wax, the disposable polishing of surface finish process can be carried out to the product of employing carbon fiber, glass fibre manufacture or part, the product surface time of polishing is shortened greatly, grinding efficiency improves greatly, the product surface photochromic effect polished is good, greatly saves manpower and time.
Embodiment
Automobile described in the embodiment of the present invention is polished thin wax formula, is made up of the material mixing of the following parts by weight chosen:
Suspension agent 2-6 part;
Clear water 150-200 part;
Kerosene 15-50 part;
White mineral oil 10-50 part;
Polyethylene wax liquid 5-50 part;
Palm wax liquid 2-40 part;
Butyl ether 10-60 part;
White spirit 10-50 part;
Methylene dichloride 2-30 part;
Cerium oxide 10-100 part;
Aluminum oxide 15-150 part;
The pH value of the thin wax liquid formed is between 7.8-8.2.
Above embodiment is the one of the present invention's more preferably embodiment, and the usual change that those skilled in the art carry out within the scope of the technical program and replacing should be included in protection scope of the present invention.
Claims (2)
1. automobile is polished a thin wax formula, it is characterized in that, is made up of the material mixing of the following parts by weight chosen:
Suspension agent 2-6 part;
Clear water 150-200 part;
Kerosene 15-50 part;
White mineral oil 10-50 part;
Polyethylene wax liquid 5-50 part;
Palm wax liquid 2-40 part;
Butyl ether 10-60 part;
White spirit 10-50 part;
Methylene dichloride 2-30 part;
Cerium oxide 10-100 part;
Aluminum oxide 15-150 part.
2. automobile according to claim 1 is polished thin wax formula, it is characterized in that: the pH value of the thin wax liquid of above formed mixture is 7.8-8.2.