CN107325733A - 一种建筑防潮涂料 - Google Patents

一种建筑防潮涂料 Download PDF

Info

Publication number
CN107325733A
CN107325733A CN201710656831.8A CN201710656831A CN107325733A CN 107325733 A CN107325733 A CN 107325733A CN 201710656831 A CN201710656831 A CN 201710656831A CN 107325733 A CN107325733 A CN 107325733A
Authority
CN
China
Prior art keywords
parts
emulsion
powder
building
titanium dioxide
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201710656831.8A
Other languages
English (en)
Inventor
姚丽玉
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ANHUI ZHENXIN PAINT Co Ltd
Original Assignee
ANHUI ZHENXIN PAINT Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ANHUI ZHENXIN PAINT Co Ltd filed Critical ANHUI ZHENXIN PAINT Co Ltd
Priority to CN201710656831.8A priority Critical patent/CN107325733A/zh
Publication of CN107325733A publication Critical patent/CN107325733A/zh
Pending legal-status Critical Current

Abstract

本发明提供一种建筑防潮涂料，组分重量百分比如下，六偏磷酸钠3～5份，氯丁橡胶8～14份、银浆粉9～12份、云母粉3～5份、助剂10～12份、胶水15～30份、聚醋酸乙烯胶结剂1～3份纳米石墨烯粉末10‑25份、纳米二氧化硅10‑30份、纳米二氧化铁10‑20份、乳液5‑10份、颜料5‑8份。所述助剂为丁二醇、硫酸钙、氧化锌的混合物。该涂料施工简单，成本低廉，不用熟化，无气化污染的建筑防潮涂料；具有优异的防潮性能和抗高低温效果，能承受强酸碱盐的各种腐蚀和高湿度的环境，并具有独特的柔性和附着力强的特性，适用于在建筑工程领域普遍推广与应用。

Description

一种建筑防潮涂料
技术领域
本发明属于化工涂料领域，具体涉及一种建筑防潮涂料。
背景技术
涂料又称油漆。指涂布于物体表面在一定的条件下能形成薄膜而起保护、装潢或其他特殊功能(绝缘、防锈、防霉、耐热等)的一类液体或固体材料。因早期的涂料大多以植物油为主要原料，故又称作油漆。现在合成树脂已大部分或全部取代了植物油，故称为涂料。建筑防水涂料是在常温下呈无固定形状的粘稠液态高分子合成材料。经涂布后，通过溶剂的挥发或水分的蒸发或反应固化后在基层面上形成坚韧的防水膜的材料的总称。
目前，国内广泛使用的涂料种类繁多，而用于建筑物表面，如屋顶、外墙等仍然使用三油二毡防水材料，施工时费时费工，而且使用范围受到了很大的局限。特别是这种方法五反光降温性能，每到夏天由于三油二毡得吸热作用，使得顶楼或者冷库、粮库的温度升高，要保持温度适宜，耗能较大。
发明内容
本发明的目的是针对上述现有技术中的不足，提供一种施工简单，成本低廉，不用熟化，无气化污染的建筑防水涂料。
为实现上述目的，本发明解决其技术问题所采用的技术方案是：
一种建筑防潮涂料，其特征在于，由以下质量份数的原料组成：六偏磷酸钠3～5份，氯丁橡胶8～14份、银浆粉9～12份、云母粉3～5份、助剂10～12份、胶水15～30份、聚醋酸乙烯胶结剂1～3份纳米石墨烯粉末10-25份、纳米二氧化硅10-30份、纳米二氧化铁10-20份、乳液5-10份、颜料5-8份。
本发明所述的一种建筑防潮涂料，由以下质量份数的原料组成：六偏磷酸钠4份，氯丁橡胶9份、银浆粉10份、云母粉4份、助剂11份、胶水18份、聚醋酸乙烯胶结剂2份、纳米石墨烯粉末18份、纳米二氧化硅15份、纳米二氧化铁15份、乳液8份、颜料6份。
进一步的，所述助剂为丁二醇、硫酸钙、氧化锌的混合物。
进一步的，所述颜料由以下质量百分比的原料组成：20％金红石型钛白粉、30％板钛矿型钛白粉、30％锐钛矿型钛白粉和20％立德粉的混合物。
进一步的，所述的乳液由以下质量百分比的原料组成：50％醋酸乙烯均聚物乳液、20％纯丙烯酸共聚物乳液、30％丙酸乙烯聚合物乳液。
有益效果：本发明提供一种施工简单，成本低廉，不用熟化，无气化污染的建筑防潮涂料。该涂料具有优异的防潮性能和抗高低温效果，能承受强酸碱盐的各种腐蚀和高湿度的环境，并具有独特的柔性和附着力强的特性，适用于在建筑工程领域普遍推广与应用。
具体实施方式
下面结合具体实施例来进一步描述本发明，以下实施例仅是本发明的最佳实施例，并不对本发明的范围构成任何限制。本领域技术人员应该理解的是，在不偏离本发明的精神和范围下可以对本发明技术方案的细节和形式进行修改或替换，但这些修改和替换均落入本发明的保护范围内。
实施例1
一种建筑防潮涂料，由以下质量份数的原料组成：六偏磷酸钠4份，氯丁橡胶9份、银浆粉10份、云母粉4份、助剂11份、胶水18份、聚醋酸乙烯胶结剂2份、纳米石墨烯粉末18份、纳米二氧化硅15份、纳米二氧化铁15份、乳液8份、颜料6份。
进一步的，所述助剂为丁二醇、硫酸钙、氧化锌的混合物。
进一步的，所述颜料由以下质量百分比的原料组成：20％金红石型钛白粉、30％板钛矿型钛白粉、30％锐钛矿型钛白粉和20％立德粉的混合物。
进一步的，所述的乳液由以下质量百分比的原料组成：50％醋酸乙烯均聚物乳液、20％纯丙烯酸共聚物乳液、30％丙酸乙烯聚合物乳液。
实施例2
一种建筑防潮涂料，由以下质量份数的原料组成：六偏磷酸钠3份，氯丁橡胶8份、银浆9份、云母粉3份、助剂10份、胶水15份、聚醋酸乙烯胶结剂1份纳米石墨烯粉末10份、纳米二氧化硅10份、纳米二氧化铁10份、乳液5份、颜料5份。
进一步的，所述助剂为丁二醇、硫酸钙、氧化锌的混合物。
进一步的，所述颜料由以下质量百分比的原料组成：20％金红石型钛白粉、30％板钛矿型钛白粉、30％锐钛矿型钛白粉和20％立德粉的混合物。
进一步的，所述的乳液由以下质量百分比的原料组成：50％醋酸乙烯均聚物乳液、20％纯丙烯酸共聚物乳液、30％丙酸乙烯聚合物乳液。
实施例3
一种建筑防潮涂料，由以下质量份数的原料组成：六偏磷酸钠5份，氯丁橡胶14份、银浆粉12份、云母粉5份、助剂12份、胶水30份、聚醋酸乙烯胶结剂3份纳米石墨烯粉末25份、纳米二氧化硅30份、纳米二氧化铁20份、乳液10份、颜料8份。
进一步的，所述助剂为丁二醇、硫酸钙、氧化锌的混合物。
进一步的，所述颜料由以下质量百分比的原料组成：20％金红石型钛白粉、30％板钛矿型钛白粉、30％锐钛矿型钛白粉和20％立德粉的混合物。
进一步的，所述的乳液由以下质量百分比的原料组成：50％醋酸乙烯均聚物乳液、20％纯丙烯酸共聚物乳液、30％丙酸乙烯聚合物乳液。

Claims (5)

1.一种建筑防潮涂料，其特征在于，由以下质量份数的原料组成：六偏磷酸钠3～5份，氯丁橡胶8～14份、银浆粉9～12份、云母粉3～5份、助剂10～12份、胶水15～30份、聚醋酸乙烯胶结剂1～3份纳米石墨烯粉末10-25份、纳米二氧化硅10-30份、纳米二氧化铁10-20份、乳液5-10份、颜料5-8份。
2.根据权利要求1所述的一种建筑防潮涂料，其特征在于，由以下质量份数的原料组成：六偏磷酸钠4份，氯丁橡胶9份、银浆粉10份、云母粉4份、助剂11份、胶水18份、聚醋酸乙烯胶结剂2份、纳米石墨烯粉末18份、纳米二氧化硅15份、纳米二氧化铁15份、乳液8份、颜料6份。
3.根据权利要求1所述的一种建筑防潮涂料，其特征在于,所述助剂为丁二醇、硫酸钙、氧化锌的混合物。
4.根据权利要求1所述的一种建筑防潮涂料，其特征在于，所述颜料由以下质量百分比的原料组成：20％金红石型钛白粉、30％板钛矿型钛白粉、30％锐钛矿型钛白粉和20％立德粉的混合物。
5.根据权利要求1所述的一种建筑防潮涂料，其特征在于，所述的乳液由以下质量百分比的原料组成：50％醋酸乙烯均聚物乳液、20％纯丙烯酸共聚物乳液、30％丙酸乙烯聚合物乳液。
CN201710656831.8A 2017-08-03 2017-08-03 一种建筑防潮涂料 Pending CN107325733A (zh)