CN105238265A - 一种有机硅耐热底漆 - Google Patents

一种有机硅耐热底漆 Download PDF

Info

Publication number
CN105238265A
CN105238265A CN201510812169.1A CN201510812169A CN105238265A CN 105238265 A CN105238265 A CN 105238265A CN 201510812169 A CN201510812169 A CN 201510812169A CN 105238265 A CN105238265 A CN 105238265A
Authority
CN
China
Prior art keywords
parts
powder
organosilicon
heat
polysiloxane
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510812169.1A
Other languages
English (en)
Inventor
于涛
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Tianjin Meishibang Paint and Chemicals Co Ltd
Original Assignee
Tianjin Meishibang Paint and Chemicals Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Tianjin Meishibang Paint and Chemicals Co Ltd filed Critical Tianjin Meishibang Paint and Chemicals Co Ltd
Priority to CN201510812169.1A priority Critical patent/CN105238265A/zh
Publication of CN105238265A publication Critical patent/CN105238265A/zh
Pending legal-status Critical Current

Abstract

本发明提供了一种有机硅耐热底漆，包括如下重量份数的原料，环氧改性有机硅树脂30～60份、聚有机硅氧烷树脂30～60份、有机硅-丙烯酸乳液20～40份、乙酸叔丁酯15～35份、云母粉3～6份、滑石粉3～6份、重钙粉3～6份、有机膨润土3～6份、沉淀硫酸钡3～6份、成膜助剂13～16份、聚硅氧烷-聚醚共聚物13～16份、硝酸盐13～16份、金红石钛白粉15～30份。本发明具有较强的附着力，优良的防腐能力、耐热性能好，且减少裂皮的现象，具有一定的防腐性能。

Description

一种有机硅耐热底漆
技术领域
本发明属于涂料技术领域，尤其是涉及一种有机硅耐热底漆。
背景技术
涂料广泛应用在国民经济各个部门，涂刷在物体表面对各种材料起保护和装饰作用。涂料在基体材料表面形成的固体膜状物称为涂层。涂层起到覆盖基体材料和隔离介质的作用。单一一种涂料组成的涂层一般很少被采用，因为单一品种涂料不可能满足所有的要求。有的附着力好而耐候性或耐腐蚀性能差，有的耐腐蚀性能好，但与钢铁表面附着力很差，如某些高分子聚合物形成的涂层，由于附着力不良，涂膜下的金属仍然会锈蚀，使用后，不久涂层会大面积剥落，所以多采用复合涂层——底层、中间层和面层构成，对应的涂料就有涂料底漆、中间漆和面漆之分。
有机硅密封剂是用于建筑行业的结构玻璃和耐候密封应用的重要产品。有机硅密封剂的耐久性部分地是由于其使得可以保证使用20年或更长时间的弹性体特性。然而，耐久的密封剂基质还必须维持与用来建造建筑的各种建筑材料的粘附性。在一些情况下，需要用底层涂饰剂对表面进行准备或处理以提供密封剂的粘附促进组分可与之反应的反应性表面。现有涂料其隔热性能都欠佳。
发明内容
有鉴于此，本发明旨在提出一种有机硅耐热底漆，以克服现有技术中的不足。
为达到上述目的，本发明的技术方案是这样实现的：
一种有机硅耐热底漆，包括如下重量份数的原料，环氧改性有机硅树脂30～60份、聚有机硅氧烷树脂30～60份、有机硅-丙烯酸乳液20～40份、乙酸叔丁酯15～35份、云母粉3～6份、滑石粉3～6份、重钙粉3～6份、有机膨润土3～6份、沉淀硫酸钡3～6份、成膜助剂13～16份、聚硅氧烷-聚醚共聚物13～16份、硝酸盐13～16份、金红石钛白粉15～30份。
优选的，包括如下重量份数的原料，环氧改性有机硅树脂45份、聚有机硅氧烷树脂40份、有机硅-丙烯酸乳液30份、乙酸叔丁酯25份、云母粉4份、滑石粉4份、重钙粉4份、有机膨润土4份、沉淀硫酸钡4份、成膜助剂14份、聚硅氧烷-聚醚共聚物14份、硝酸盐14份、金红石钛白粉26份。
相对于现有技术，本发明具有以下优势：本发明底漆中含有的有机膨润土可使涂料具有防沉效果，能够有效改善涂料的触变性、流变性等涂刷性；硫酸钡具有较好的耐候性、耐酸碱、耐盐雾性和耐高温性；在各组分的作用下，具有较强的附着力，优良的防腐能力、耐热性能好，且减少裂皮的现象，具有一定的防腐性能。
具体实施方式
需要说明的是，在不冲突的情况下，本发明中的实施例及实施例中的特征可以相互组合。
下面结合实施例来详细说明本发明。
实施例一
一种有机硅耐热底漆，包括如下重量份数的原料，环氧改性有机硅树脂45份、聚有机硅氧烷树脂40份、有机硅-丙烯酸乳液30份、乙酸叔丁酯25份、云母粉4份、滑石粉4份、重钙粉4份、有机膨润土4份、沉淀硫酸钡4份、成膜助剂14份、聚硅氧烷-聚醚共聚物14份、硝酸盐14份、金红石钛白粉26份。
实施例二
一种有机硅耐热底漆，包括如下重量份数的原料，环氧改性有机硅树脂35份、聚有机硅氧烷树脂32份、有机硅-丙烯酸乳液25份、乙酸叔丁酯18份、云母粉3份、滑石粉3份、重钙粉4份、有机膨润土4份、沉淀硫酸钡4份、成膜助剂13份、聚硅氧烷-聚醚共聚物14份、硝酸盐14份、金红石钛白粉16份。
实施例三
一种有机硅耐热底漆，包括如下重量份数的原料，环氧改性有机硅树脂55份、聚有机硅氧烷树脂55份、有机硅-丙烯酸乳液35份、乙酸叔丁酯30份、云母粉5份、滑石粉5份、重钙粉5份、有机膨润土6份、沉淀硫酸钡6份、成膜助剂15份、聚硅氧烷-聚醚共聚物16份、硝酸盐16份、金红石钛白粉28份。
以上所述仅为本发明的较佳实施例而已，并不用以限制本发明，凡在本发明的精神和原则之内，所作的任何修改、等同替换、改进等，均应包含在本发明的保护范围之内。

Claims (2)

1.一种有机硅耐热底漆，其特征在于：包括如下重量份数的原料，环氧改性有机硅树脂30～60份、聚有机硅氧烷树脂30～60份、有机硅-丙烯酸乳液20～40份、乙酸叔丁酯15～35份、云母粉3～6份、滑石粉3～6份、重钙粉3～6份、有机膨润土3～6份、沉淀硫酸钡3～6份、成膜助剂13～16份、聚硅氧烷-聚醚共聚物13～16份、硝酸盐13～16份、金红石钛白粉15～30份。
2.根据权利要求1所述的有机硅耐热底漆，其特征在于：包括如下重量份数的原料，环氧改性有机硅树脂45份、聚有机硅氧烷树脂40份、有机硅-丙烯酸乳液30份、乙酸叔丁酯25份、云母粉4份、滑石粉4份、重钙粉4份、有机膨润土4份、沉淀硫酸钡4份、成膜助剂14份、聚硅氧烷-聚醚共聚物14份、硝酸盐14份、金红石钛白粉26份。
CN201510812169.1A 2015-11-20 2015-11-20 一种有机硅耐热底漆 Pending CN105238265A (zh)