CN107312261A - A kind of polyvinyl chloride cable sheathing compound for automotive wire bundle - Google Patents
A kind of polyvinyl chloride cable sheathing compound for automotive wire bundle Download PDFInfo
- Publication number
- CN107312261A CN107312261A CN201710468156.6A CN201710468156A CN107312261A CN 107312261 A CN107312261 A CN 107312261A CN 201710468156 A CN201710468156 A CN 201710468156A CN 107312261 A CN107312261 A CN 107312261A
- Authority
- CN
- China
- Prior art keywords
- parts
- polyvinyl chloride
- wire bundle
- antiseptic
- automotive wire
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of polyvinyl chloride cable sheathing compound for automotive wire bundle, its raw material includes by weight:50 90 parts of polyvinyl chloride, 10 20 parts of polytrifluorochloroethylene, 10 20 parts of ethylene-vinyl acetate copolymer, 30 40 parts of inserts, 12 parts of diethylenetriamines, 24 parts of cumyl peroxide, 12 parts of p-phenylenediamine, 25 parts of plasticizer, 0.1 0.4 parts of lanthana, 0.2 0.6 parts of cerium oxide, 13 parts of antioxidant 1076,12 parts of antioxidant 1010,15 25 parts of antiseptic.Polyvinyl chloride cable sheathing compound proposed by the present invention for automotive wire bundle, not only anti-microbial property is fabulous, and can effectively strengthen scratch-resistant and tear resistance, safety and environmental protection.
Description
Technical field
The present invention relates to cable cover(ing) technical field, more particularly to a kind of polyvinyl chloride cable sheath for automotive wire bundle
Material.
Background technology
Automotive wire bundle is the network principal of automobile circuit, and automobile circuit is also just not present without wire harness.Wire harness refers to by copper
After the contact terminal of material punching is crimped with electric wire, outside plastic compression insulator or added metal housing etc. again, with line
Tie in the component pricked and form connection circuit, and it is different with normal domestic use electric wire.Normal domestic use electric wire is copper single stamen electricity
Line, there is certain degree of hardness.And automobile electric wire is all copper many stamen flexible cords, some flexible cords are thin such as hair, several or even tens soft coppers
Line is wrapped in polyvinyl chloride insulation pipe, softness without easily snapping off, but at present polyvinyl chloride insulation pipe to there is antibiotic property poor, it is resistance to
Scraping can not meet the technical problem of demand with resistance to tearing, it would be highly desirable to solve.
The content of the invention
The technical problem existed based on background technology, the present invention proposes a kind of polyvinyl chloride cable for automotive wire bundle
Protective cover material, not only anti-microbial property is fabulous, and can effectively strengthen scratch-resistant and tear resistance, safety and environmental protection.
A kind of polyvinyl chloride cable sheathing compound for automotive wire bundle proposed by the present invention, its raw material includes by weight:
50-90 parts of polyvinyl chloride, 10-20 parts of polytrifluorochloroethylene, 10-20 parts of ethylene-vinyl acetate copolymer, 30-40 parts of inserts,
1-2 parts of diethylenetriamines, 2-4 parts of cumyl peroxide, 1-2 parts of p-phenylenediamine, 2-5 parts of plasticizer, lanthana 0.1-0.4
Part, 0.2-0.6 parts of cerium oxide, 1-3 parts of antioxidant 1076,1-2 parts of antioxidant 1010,15-25 parts of antiseptic.
Preferably, antiseptic is prepared using following technique:By atoleine, copper nitrate, sorbester p17 stirring, nitrogen protection
Under, heat up, stir, centrifugation, sediment washing spontaneously dries, add calcium carbonate, hydroxy silicon oil mixed grinding, adds at room temperature
MTES, crosslinking agent TAC, ascorbic acid continue to grind, and add cetyl trimethylammonium bromide, polyacrylamide
Amine, dimethyl dimercapto 2-ethyl hexyl ethanoate tin, sodium lignin sulfonate continue to grind, and dry, pulverize and obtain antiseptic.
Preferably, antiseptic is prepared using following technique:By atoleine, copper nitrate, sorbester p17 stirring 5-12min, stir
Speed is mixed for 3000-3400r/min, under nitrogen protection, 450-480 DEG C is warming up to, 10-20min is stirred, centrifugation, sediment is washed
Wash, spontaneously dry at room temperature, add calcium carbonate, hydroxy silicon oil mixed grinding 10-20min, add MTES, hand over
Join agent TAC, ascorbic acid to continue to grind 10-18min, add cetyl trimethylammonium bromide, polyacrylamide, dimethyl two
Octyltin Mercaptide, sodium lignin sulfonate continue to grind 20-50min, dry, pulverize and obtain antiseptic.
Preferably, antiseptic is prepared using following technique:By weight by 100 parts of atoleines, 20-40 parts of copper nitrates,
1-2 parts of sorbester p17s stir 5-12min, and mixing speed is 3000-3400r/min, under nitrogen protection, is warming up to 450-480 DEG C, stirs
10-20min is mixed, is centrifuged, sediment petroleum ether, water, absolute ethyl alcohol washing successively spontaneously dries, add 50-80 parts of carbon at room temperature
Sour calcium, 4-10 parts of hydroxy silicon oil mixed grinding 10-20min, add 0.5-1 parts of MTESs, 1-2 parts of crosslinking agents
TAC, 3-5 parts of ascorbic acid continue to grind 10-18min, add 1-2 parts of cetyl trimethylammonium bromides, 3-5 parts of polyacrylamides
Amine, 1-2 parts of dimethyl dimercapto 2-ethyl hexyl ethanoate tin, 1-2 parts of sodium lignin sulfonates continue to grind 20-50min, dry, pulverize
Obtain antiseptic.
Preferably, inserts includes by weight:10-18 parts of graphene, 3-10 parts of nano kaoline, hollow glass microballoon
5-15 parts.
Preferably, plasticizer includes by weight:1-3 parts of haloflex wax, 1-2 parts of microcrystalline wax.
The present invention is acted synergistically as major ingredient using polyvinyl chloride, polytrifluorochloroethylene, ethylene-vinyl acetate copolymer,
Ethylene-vinyl acetate copolymer has good filler pardon and cross linkable, above-mentioned major ingredient and antiseptic mating reaction, no
Only anti-microbial property is fabulous, and can effectively strengthen scratch-resistant and tear resistance, safety and environmental protection;In antiseptic, using copper nitrate as
Raw material, after being handled by solvent of atoleine with reducing agent, then through petroleum ether, water, absolute ethyl alcohol washing, forms Nanometer Copper, grain
Footpath is evenly distributed, not oxidizable in air, under the cooperation of hydroxy silicon oil, can be stably dispersed in calcium carbonate, and filling capacity is good,
Dispersiveness in major ingredient is good with compatibility, makes not only anti-microbial property of the invention fabulous, and can effectively strengthen scratch-resistant to tear with resistance to
Fragility energy;Antiseptic is compounded with graphene, nano kaoline, hollow glass microballoon, and filling capacity is fabulous, in haloflex
Under wax, the cooperation of microcrystalline wax, on the premise of hardness is met, toughness is fabulous, protects cable to be not susceptible to folding when being impacted
Curved phenomenon, is adapted to batch production.
Embodiment
Below, technical scheme is described in detail by specific embodiment.
Embodiment 1
A kind of polyvinyl chloride cable sheathing compound for automotive wire bundle proposed by the present invention, its raw material includes by weight:
50 parts of polyvinyl chloride, 20 parts of polytrifluorochloroethylene, 10 parts of ethylene-vinyl acetate copolymer, 40 parts of inserts, diethylenetriamines
1 part, 4 parts of cumyl peroxide, 1 part of p-phenylenediamine, 5 parts of plasticizer, 0.1 part of lanthana, 0.6 part of cerium oxide, antioxidant
1076 1 parts, 2 parts of antioxidant 1010,15 parts of antiseptic.
Embodiment 2
A kind of polyvinyl chloride cable sheathing compound for automotive wire bundle proposed by the present invention, its raw material includes by weight:
90 parts of polyvinyl chloride, 10 parts of polytrifluorochloroethylene, 20 parts of ethylene-vinyl acetate copolymer, 30 parts of inserts, diethylenetriamines
2 parts, 2 parts of cumyl peroxide, 2 parts of p-phenylenediamine, 2 parts of plasticizer, 0.4 part of lanthana, 0.2 part of cerium oxide, antioxidant
1076 3 parts, 1 part of antioxidant 1010,25 parts of antiseptic.
Inserts includes by weight:10 parts of graphene, 10 parts of nano kaoline, 5 parts of hollow glass microballoon.Plasticizer is pressed
Parts by weight include:3 parts of haloflex wax, 1 part of microcrystalline wax.
Antiseptic is prepared using following technique:By atoleine, copper nitrate, sorbester p17 stirring, under nitrogen protection, heating,
Stirring, centrifugation, sediment washing spontaneously dries, adds calcium carbonate, hydroxy silicon oil mixed grinding, adds the second of methyl three at room temperature
TMOS, crosslinking agent TAC, ascorbic acid continue to grind, and add cetyl trimethylammonium bromide, polyacrylamide, diformazan
Base dimercapto 2-ethyl hexyl ethanoate tin, sodium lignin sulfonate continue to grind, and dry, pulverize and obtain antiseptic.
Embodiment 3
A kind of polyvinyl chloride cable sheathing compound for automotive wire bundle proposed by the present invention, its raw material includes by weight:
60 parts of polyvinyl chloride, 18 parts of polytrifluorochloroethylene, 14 parts of ethylene-vinyl acetate copolymer, 37 parts of inserts, diethylenetriamines
1.2 parts, 3.5 parts of cumyl peroxide, 1.2 parts of p-phenylenediamine, 4 parts of plasticizer, 0.2 part of lanthana, 0.5 part of cerium oxide resists
1,076 1.5 parts of oxygen agent, 1.6 parts of antioxidant 1010,18 parts of antiseptic.
Inserts includes by weight:18 parts of graphene, 3 parts of nano kaoline, 15 parts of hollow glass microballoon.Plasticizer is pressed
Parts by weight include:1 part of haloflex wax, 2 parts of microcrystalline wax.
Antiseptic is prepared using following technique:By atoleine, copper nitrate, sorbester p17 stirring 8min, mixing speed is
3200r/min, under nitrogen protection, is warming up to 460 DEG C, stirs 15min, and centrifugation, sediment washing is spontaneously dried at room temperature, plus
Enter calcium carbonate, hydroxy silicon oil mixed grinding 15min, add MTES, crosslinking agent TAC, ascorbic acid and continue to grind
14min is ground, cetyl trimethylammonium bromide, polyacrylamide, dimethyl dimercapto 2-ethyl hexyl ethanoate tin, sulfomethylated lignin is added
Sour sodium continues to grind 35min, dry, pulverize and obtains antiseptic.
Embodiment 4
A kind of polyvinyl chloride cable sheathing compound for automotive wire bundle proposed by the present invention, its raw material includes by weight:
80 parts of polyvinyl chloride, 12 parts of polytrifluorochloroethylene, 16 parts of ethylene-vinyl acetate copolymer, 33 parts of inserts, diethylenetriamines
1.6 parts, 2.5 parts of cumyl peroxide, 1.8 parts of p-phenylenediamine, 3 parts of plasticizer, 0.3 part of lanthana, 0.3 part of cerium oxide resists
1,076 2.5 parts of oxygen agent, 1.2 parts of antioxidant 1010,22 parts of antiseptic.
Inserts includes by weight:12 parts of graphene, 8 parts of nano kaoline, 8 parts of hollow glass microballoon.Plasticizer is pressed
Parts by weight include:2.5 parts of haloflex wax, 1.2 parts of microcrystalline wax.
Antiseptic is prepared using following technique:100 parts of atoleines, 20 parts of copper nitrates, 2 parts of sorbester p17s are stirred by weight
Mix 5min, mixing speed is 3400r/min, under nitrogen protection, is warming up to 450 DEG C, stir 20min, centrifugation, sediment stone successively
Oily ether, water, absolute ethyl alcohol washing, spontaneously dry, add 50 parts of calcium carbonate, 10 parts of hydroxy silicon oil mixed grinding 10min at room temperature,
Add 1 part of MTES, 1 part of crosslinking agent TAC, 5 parts of ascorbic acid to continue to grind 10min, add 2 parts of cetyls
Trimethylammonium bromide, 3 parts of polyacrylamides, 2 parts of dimethyl dimercapto 2-ethyl hexyl ethanoate tin, 1 part of sodium lignin sulfonate continue to grind
50min is ground, dry, pulverize and obtain antiseptic.
Embodiment 5
A kind of polyvinyl chloride cable sheathing compound for automotive wire bundle proposed by the present invention, its raw material includes by weight:
70 parts of polyvinyl chloride, 15 parts of polytrifluorochloroethylene, 15 parts of ethylene-vinyl acetate copolymer, 35 parts of inserts, diethylenetriamines
1.4 parts, 3 parts of cumyl peroxide, 1.5 parts of p-phenylenediamine, 3.5 parts of plasticizer, 0.25 part of lanthana, 0.4 part of cerium oxide resists
1,076 2 parts of oxygen agent, 1.4 parts of antioxidant 1010,20 parts of antiseptic.
Inserts includes by weight:16 parts of graphene, 4 parts of nano kaoline, 12 parts of hollow glass microballoon.Plasticizer is pressed
Parts by weight include:1.5 parts of haloflex wax, 1.8 parts of microcrystalline wax.
Antiseptic is prepared using following technique:100 parts of atoleines, 40 parts of copper nitrates, 1 part of sorbester p17 are stirred by weight
12min is mixed, mixing speed is 3000r/min, under nitrogen protection, is warming up to 480 DEG C, stirs 10min, centrifuges, sediment is successively
Petroleum ether, water, absolute ethyl alcohol washing, spontaneously dry, add 80 parts of calcium carbonate, 4 parts of hydroxy silicon oil mixed grindings at room temperature
20min, adds 0.5 part of MTES, 2 parts of crosslinking agent TAC, 3 parts of ascorbic acid and continues to grind 18min, add 1 part
Cetyl trimethylammonium bromide, 5 parts of polyacrylamides, 1 part of dimethyl dimercapto 2-ethyl hexyl ethanoate tin, 2 parts of lignin sulfonic acids
Sodium continues to grind 20min, dry, pulverize and obtains antiseptic.
The foregoing is only a preferred embodiment of the present invention, but protection scope of the present invention be not limited thereto,
Any one skilled in the art the invention discloses technical scope in, technique according to the invention scheme and its
Inventive concept is subject to equivalent substitution or change, should all be included within the scope of the present invention.
Claims (6)
1. a kind of polyvinyl chloride cable sheathing compound for automotive wire bundle, it is characterised in that its raw material includes by weight:Polychlorostyrene
50-90 parts of ethene, 10-20 parts of polytrifluorochloroethylene, 10-20 parts of ethylene-vinyl acetate copolymer, 30-40 parts of inserts, two is sub-
1-2 parts of ethyl triamine, 2-4 parts of cumyl peroxide, 1-2 parts of p-phenylenediamine, 2-5 parts of plasticizer, 0.1-0.4 parts of lanthana,
0.2-0.6 parts of cerium oxide, 1-3 parts of antioxidant 1076,1-2 parts of antioxidant 1010,15-25 parts of antiseptic.
2. it is used for the polyvinyl chloride cable sheathing compound of automotive wire bundle according to claim 1, it is characterised in that antiseptic is used
It is prepared by following technique:By atoleine, copper nitrate, sorbester p17 stirring, under nitrogen protection, heat up, stir, centrifugation, sediment is washed
Wash, spontaneously dry at room temperature, add calcium carbonate, hydroxy silicon oil mixed grinding, add MTES, crosslinking agent TAC,
Ascorbic acid continues to grind, and adds cetyl trimethylammonium bromide, polyacrylamide, dimethyl dimercapto 2-ethyl hexyl ethanoate
Tin, sodium lignin sulfonate continue to grind, and dry, pulverize and obtain antiseptic.
3. the polyvinyl chloride cable sheathing compound according to claim 1 or claim 2 for automotive wire bundle, it is characterised in that antiseptic
Prepared using following technique:By atoleine, copper nitrate, sorbester p17 stirring 5-12min, mixing speed is 3000-3400r/
Min, under nitrogen protection, is warming up to 450-480 DEG C, stirs 10-20min, and centrifugation, sediment washing is spontaneously dried at room temperature, plus
Enter calcium carbonate, hydroxy silicon oil mixed grinding 10-20min, add MTES, crosslinking agent TAC, ascorbic acid and continue
10-18min is ground, cetyl trimethylammonium bromide, polyacrylamide, dimethyl dimercapto 2-ethyl hexyl ethanoate tin, wood is added
Quality sodium sulfonate continues to grind 20-50min, dry, pulverize and obtains antiseptic.
4. it is used for the polyvinyl chloride cable sheathing compound of automotive wire bundle according to claim any one of 1-3, it is characterised in that anti-
Microbial inoculum is prepared using following technique:100 parts of atoleines, 20-40 parts of copper nitrates, 1-2 parts of sorbester p17s are stirred into 5- by weight
12min, mixing speed is 3000-3400r/min, under nitrogen protection, is warming up to 450-480 DEG C, stirs 10-20min, centrifuges,
Sediment petroleum ether, water, absolute ethyl alcohol washing successively, spontaneously dries, adds 50-80 parts of calcium carbonate, 4-10 parts of hydroxyls at room temperature
Silicone oil mixed grinding 10-20min, adds 0.5-1 parts of MTESs, TAC, 3-5 parts of ascorbic acid of 1-2 parts of crosslinking agents
Continue to grind 10-18min, add 1-2 parts of cetyl trimethylammonium bromides, 3-5 parts of polyacrylamides, 1-2 parts of dimethyl two
Octyltin Mercaptide, 1-2 parts of sodium lignin sulfonates continue to grind 20-50min, dry, pulverize and obtain antiseptic.
5. it is used for the polyvinyl chloride cable sheathing compound of automotive wire bundle according to claim any one of 1-4, it is characterised in that fill out
Charge includes by weight:10-18 parts of graphene, 3-10 parts of nano kaoline, 5-15 parts of hollow glass microballoon.
6. it is used for the polyvinyl chloride cable sheathing compound of automotive wire bundle according to claim any one of 1-5, it is characterised in that increase
Modeling agent includes by weight:1-3 parts of haloflex wax, 1-2 parts of microcrystalline wax.