CN107312255A - A kind of electric wire for automobile - Google Patents
A kind of electric wire for automobile Download PDFInfo
- Publication number
- CN107312255A CN107312255A CN201710469640.0A CN201710469640A CN107312255A CN 107312255 A CN107312255 A CN 107312255A CN 201710469640 A CN201710469640 A CN 201710469640A CN 107312255 A CN107312255 A CN 107312255A
- Authority
- CN
- China
- Prior art keywords
- parts
- electric wire
- antiseptic
- weight
- automobile
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of electric wire for automobile, including cable core and the restrictive coating being coated on the outside of cable core, restrictive coating raw material includes by weight:150 170 parts of major ingredient, 20 26 parts of glass fibre, 10 20 parts of nanometer calcinated argil, 10 20 parts of expanded perlite, 59 parts of crosslinking agent, 24 parts of polyethylene glycol, 24 parts of chlorinated paraffin, 12 parts of yittrium oxide, 0.5 0.8 parts of praseodymium oxide, 24 parts of irgasfos 168,4,010 1.5 2.5 parts of antioxidant, 20 40 parts of antiseptic.Electric wire proposed by the present invention for automobile, not only anti-microbial property is fabulous, and can effectively strengthen scratch-resistant and tear resistance, safety and environmental protection.
Description
Technical field
The present invention relates to Power-line technology field, more particularly to a kind of electric wire for automobile.
Background technology
Usual automobile electric wire is, using chlorosulfonated polyethylene resin as base-material, to add with chlorosulfonated polyethylene CABLE MATERIALS production method
Plus plasticizer, stabilizer and processing aid, processed through special kneading device, although automobile electric wire production base can be met
This demand, but there is the problem of scraped finish performance is not good, resistance to tearing can not meet demand.Automotive line uses position due to it
Special, automobile in the process of running can not easy breed bacteria.In summary, the scratch resistance of chlorosulfonated polyethylene CABLE MATERIALS how is improved
Wipe and resistance to tearing energy, enhancing antibiotic property, it would be highly desirable to solve.
The content of the invention
The technical problem existed based on background technology, the present invention proposes a kind of electric wire for automobile, not only antibiotic property
Can be fabulous, and can effectively strengthen scratch-resistant and tear resistance, safety and environmental protection.
A kind of electric wire for automobile proposed by the present invention, including cable core and the restrictive coating being coated on the outside of cable core, sheath
Layer raw material includes by weight:150-170 parts of major ingredient, 20-26 parts of glass fibre, 10-20 parts of nanometer calcinated argil, expanded pearlite
10-20 parts of rock, 5-9 parts of crosslinking agent, 2-4 parts of polyethylene glycol, 2-4 parts of chlorinated paraffin, 1-2 parts of yittrium oxide, praseodymium oxide 0.5-0.8
Part, 2-4 parts of irgasfos 168,1.5-2.5 parts of antioxidant 4010,20-40 parts of antiseptic.
Preferably, major ingredient includes by weight in restrictive coating raw material:80-100 parts of chlorosulfonated polyethylene, polypropylene 20-40
Part, 25-35 parts of polystyrene.
Preferably, crosslinking agent includes by weight in restrictive coating raw material:2-4 parts of diethanol amine, benzoyl peroxide 1-2
Part, 2-3 parts of triethylamine.
Preferably, antiseptic is prepared using following technique:By microcrystalline wax, silver nitrate, Tween 80 stirring, nitrogen protection
Under, heat up, stir, centrifugation, sediment washing spontaneously dries, adds gas-phase silica, zinc stearate mixed grinding at room temperature,
Add n-octyl trimethoxy silane, organic zirconium crosslinker, ATBC to continue to grind, add cetyl trimethyl bromine
Change ammonium, polyacrylamide, dibutyl tin laurate, Cocoamidopropyl betaine to continue to grind, dry, pulverize and obtain antibacterial
Agent.
Preferably, antiseptic is prepared using following technique:By weight by 60-70 parts of microcrystalline waxes, 10-20 parts of nitric acid
Silver, 2-4 parts of Tween 80 stirrings, under nitrogen protection, heat up, stir, centrifugation, and sediment successively wash by petroleum ether, water, absolute ethyl alcohol
Wash, spontaneously dry at room temperature, add 70-90 parts of gas-phase silicas, 5-15 parts of zinc stearate mixed grindings, 1-2 parts of addition is just pungent
Base trimethoxy silane, 2-4 part organic zirconium crosslinker, 5-7 parts of ATBCs continue to grind, and add 2-4 parts of cetyls
Trimethylammonium bromide, 2-8 part polyacrylamide, 2-4 parts of dibutyl tin laurates, 2-4 parts of Cocoamidopropyl betaines continue
Grinding, dry, pulverize and obtain antiseptic.
Preferably, antiseptic is prepared using following technique:By weight by 60-70 parts of microcrystalline waxes, 10-20 parts of nitric acid
Silver, 2-4 parts of Tween 80 stirring 10-16min, mixing speed is 3300-3600r/min, under nitrogen protection, is warming up to 400-420
DEG C, 20-30min is stirred, centrifugation, sediment petroleum ether, water, absolute ethyl alcohol washing successively spontaneously dries, add 70- at room temperature
90 parts of gas-phase silicas, 5-15 parts of zinc stearate mixed grinding 20-30min, add 1-2 parts of n-octyl trimethoxy silanes, 2-4
Part organic zirconium crosslinker, 5-7 parts of ATBCs continue to grind 20-24min, add 2-4 parts of cetyl trimethyl brominations
Ammonium, 2-8 part polyacrylamide, 2-4 parts of dibutyl tin laurates, 2-4 parts of Cocoamidopropyl betaines continue to grind 40-
60min, dry, pulverize and obtain antiseptic.
The present invention is using chlorosulfonated polyethylene, polypropylene, polystyrene synergy as major ingredient, and polystyrene has good
Good filler pardon and cross linkable, above-mentioned major ingredient and antiseptic mating reaction, not only anti-microbial property is fabulous, and can be effective
Strengthen scratch-resistant and tear resistance, safety and environmental protection;In antiseptic, using silver nitrate as raw material, by solvent of microcrystalline wax with going back
After former agent processing, then through petroleum ether, water, absolute ethyl alcohol washing, Nano Silver is formed, particle diameter distribution is uniform, not oxidizable in air,
Under the cooperation of zinc stearate, can be stably dispersed in gas-phase silica, filling capacity is good, in major ingredient it is dispersed with it is compatible
Property it is good, making the present invention, not only anti-microbial property is fabulous, and can effectively strengthen scratch-resistant and resistance to tearing energy;Antiseptic and glass fibers
Dimension, nanometer calcinated argil, expanded perlite compounding, filling capacity are fabulous, under polyethylene glycol, the cooperation of chlorinated paraffin, full
On the premise of sufficient hardness, toughness is fabulous, protects cable to be not susceptible to bending phenomenon when being impacted, and is adapted to batch production.
Embodiment
Below, technical scheme is described in detail by specific embodiment.
Embodiment 1
A kind of electric wire for automobile proposed by the present invention, including cable core and the restrictive coating being coated on the outside of cable core, sheath
Layer raw material includes by weight:150 parts of major ingredient, 26 parts of glass fibre, 10 parts of nanometer calcinated argil, 20 parts of expanded perlite is handed over
Join 5 parts of agent, 4 parts of polyethylene glycol, 2 parts of chlorinated paraffin, 2 parts of yittrium oxide, 0.5 part of praseodymium oxide, 4 parts of irgasfos 168, antioxidant
4010 1.5 parts, 40 parts of antiseptic.
Embodiment 2
A kind of electric wire for automobile proposed by the present invention, including cable core and the restrictive coating being coated on the outside of cable core, sheath
Layer raw material includes by weight:170 parts of major ingredient, 20 parts of glass fibre, 20 parts of nanometer calcinated argil, 10 parts of expanded perlite is handed over
Join 9 parts of agent, 2 parts of polyethylene glycol, 4 parts of chlorinated paraffin, 1 part of yittrium oxide, 0.8 part of praseodymium oxide, 2 parts of irgasfos 168, antioxidant
4010 2.5 parts, 20 parts of antiseptic.
In restrictive coating raw material, major ingredient includes by weight:80 parts of chlorosulfonated polyethylene, 40 parts of polypropylene, polystyrene 25
Part;Crosslinking agent includes by weight:4 parts of diethanol amine, 1 part of benzoyl peroxide, 3 parts of triethylamine.
Antiseptic is prepared using following technique:By microcrystalline wax, silver nitrate, Tween 80 stirring, under nitrogen protection, heating,
Stirring, centrifugation, sediment washing spontaneously dries, adds gas-phase silica, zinc stearate mixed grinding, adds just pungent at room temperature
Base trimethoxy silane, organic zirconium crosslinker, ATBC continue to grind, and add cetyl trimethylammonium bromide, gather
Acrylamide, dibutyl tin laurate, Cocoamidopropyl betaine continue to grind, and dry, pulverize and obtain antiseptic.
Embodiment 3
A kind of electric wire for automobile proposed by the present invention, including cable core and the restrictive coating being coated on the outside of cable core, sheath
Layer raw material includes by weight:155 parts of major ingredient, 24 parts of glass fibre, 12 parts of nanometer calcinated argil, 17 parts of expanded perlite is handed over
6 parts of agent of connection, 3.5 parts of polyethylene glycol, 2.5 parts of chlorinated paraffin, 1.8 parts of yittrium oxide, 0.6 part of praseodymium oxide, 3.5 parts of irgasfos 168,
4,010 1.8 parts of antioxidant, 35 parts of antiseptic.
In restrictive coating raw material, major ingredient includes by weight:100 parts of chlorosulfonated polyethylene, 20 parts of polypropylene, polystyrene 35
Part;Crosslinking agent includes by weight:2 parts of diethanol amine, 2 parts of benzoyl peroxide, 2 parts of triethylamine.
Antiseptic is prepared using following technique:65 parts of microcrystalline waxes, 15 parts of silver nitrates, 3 parts of Tween 80s are stirred by weight
Mix, under nitrogen protection, heat up, stir, centrifugation, sediment petroleum ether, water, absolute ethyl alcohol washing successively is spontaneously dried at room temperature,
80 parts of gas-phase silicas, 10 parts of zinc stearate mixed grindings are added, 1.5 parts of n-octyl trimethoxy silanes, 3 parts of organic zirconiums are added
Crosslinking agent, 6 parts of ATBCs continue to grind, add 3 parts of cetyl trimethylammonium bromides, 5 parts of polyacrylamides, 3 part two
Dibutyl tin laurate, 3 parts of Cocoamidopropyl betaines continue to grind, and dry, pulverize and obtain antiseptic.
Embodiment 4
A kind of electric wire for automobile proposed by the present invention, including cable core and the restrictive coating being coated on the outside of cable core, sheath
Layer raw material includes by weight:165 parts of major ingredient, 22 parts of glass fibre, 18 parts of nanometer calcinated argil, 13 parts of expanded perlite is handed over
8 parts of agent of connection, 2.5 parts of polyethylene glycol, 3.5 parts of chlorinated paraffin, 1.2 parts of yittrium oxide, 0.7 part of praseodymium oxide, 2.5 parts of irgasfos 168,
4,010 2.2 parts of antioxidant, 25 parts of antiseptic.
In restrictive coating raw material, major ingredient includes by weight:85 parts of chlorosulfonated polyethylene, 35 parts of polypropylene, polystyrene 28
Part;Crosslinking agent includes by weight:3.5 parts of diethanol amine, 1.2 parts of benzoyl peroxide, 2.8 parts of triethylamine.
Antiseptic is prepared using following technique:60 parts of microcrystalline waxes, 20 parts of silver nitrates, 2 parts of Tween 80s are stirred by weight
16min is mixed, mixing speed is 3300r/min, under nitrogen protection, is warming up to 420 DEG C, stirs 20min, centrifuges, sediment is successively
Petroleum ether, water, absolute ethyl alcohol washing, spontaneously dry, add 90 parts of gas-phase silicas, 5 parts of zinc stearate mixed grindings at room temperature
30min, adds 1 part of n-octyl trimethoxy silane, 4 parts of organic zirconium crosslinkers, 5 parts of ATBCs and continues to grind 24min,
Add 2 parts of cetyl trimethylammonium bromides, 8 parts of polyacrylamides, 2 parts of dibutyl tin laurates, 4 parts of cocamidopropyl propyl amides
Glycine betaine continues to grind 40min, dry, pulverize and obtains antiseptic.
Embodiment 5
A kind of electric wire for automobile proposed by the present invention, including cable core and the restrictive coating being coated on the outside of cable core, sheath
Layer raw material includes by weight:160 parts of major ingredient, 23 parts of glass fibre, 15 parts of nanometer calcinated argil, 15 parts of expanded perlite is handed over
Join 7 parts of agent, 3 parts of polyethylene glycol, 3 parts of chlorinated paraffin, 1.5 parts of yittrium oxide, 0.65 part of praseodymium oxide, 3 parts of irgasfos 168, antioxidant
4010 2 parts, 30 parts of antiseptic.
In restrictive coating raw material, major ingredient includes by weight:95 parts of chlorosulfonated polyethylene, polipropene 25 part, polystyrene 32
Part;Crosslinking agent includes by weight:2.5 parts of diethanol amine, 1.8 parts of benzoyl peroxide, 2.2 parts of triethylamine.
Antiseptic is prepared using following technique:70 parts of microcrystalline waxes, 10 parts of silver nitrates, 4 parts of Tween 80s are stirred by weight
10min is mixed, mixing speed is 3600r/min, under nitrogen protection, is warming up to 400 DEG C, stirs 30min, centrifuges, sediment is successively
Petroleum ether, water, absolute ethyl alcohol washing, spontaneously dry, add 70 parts of gas-phase silicas, 15 parts of zinc stearate mixed grindings at room temperature
20min, adds 2 parts of n-octyl trimethoxy silanes, 2 parts of organic zirconium crosslinkers, 7 parts of ATBCs and continues to grind 20min,
Add 4 parts of cetyl trimethylammonium bromides, 2 parts of polyacrylamides, 4 parts of dibutyl tin laurates, 2 parts of cocamidopropyl propyl amides
Glycine betaine continues to grind 60min, dry, pulverize and obtains antiseptic.
The foregoing is only a preferred embodiment of the present invention, but protection scope of the present invention be not limited thereto,
Any one skilled in the art the invention discloses technical scope in, technique according to the invention scheme and its
Inventive concept is subject to equivalent substitution or change, should all be included within the scope of the present invention.
Claims (6)
1. a kind of electric wire for automobile, it is characterised in that including cable core and the restrictive coating being coated on the outside of cable core, restrictive coating is former
Material includes by weight:150-170 parts of major ingredient, 20-26 parts of glass fibre, 10-20 parts of nanometer calcinated argil, expanded perlite
10-20 parts, 5-9 parts of crosslinking agent, 2-4 parts of polyethylene glycol, 2-4 parts of chlorinated paraffin, 1-2 parts of yittrium oxide, 0.5-0.8 parts of praseodymium oxide,
2-4 parts of irgasfos 168,1.5-2.5 parts of antioxidant 4010,20-40 parts of antiseptic.
2. it is used for the electric wire of automobile according to claim 1, it is characterised in that major ingredient is wrapped by weight in restrictive coating raw material
Include:80-100 parts of chlorosulfonated polyethylene, 20-40 parts of polypropylene, 25-35 parts of polystyrene.
3. the electric wire according to claim 1 or claim 2 for automobile, it is characterised in that crosslinking agent is by weight in restrictive coating raw material
Part includes:2-4 parts of diethanol amine, 1-2 parts of benzoyl peroxide, 2-3 parts of triethylamine.
4. it is used for the electric wire of automobile according to claim any one of 1-3, it is characterised in that antiseptic uses following technique system
It is standby:By microcrystalline wax, silver nitrate, Tween 80 stirring, under nitrogen is protected, heat up, stir, centrifugation, sediment washing, at room temperature certainly
So dry, add gas-phase silica, zinc stearate mixed grinding, add n-octyl trimethoxy silane, organic zirconium crosslinker, lemon
Lemon acid tributyl continues to grind, and adds cetyl trimethylammonium bromide, polyacrylamide, dibutyl tin laurate, cocounut oil
Amido propyl betaine continues to grind, and dry, pulverize and obtains antiseptic.
5. it is used for the electric wire of automobile according to claim any one of 1-4, it is characterised in that antiseptic uses following technique system
It is standby:60-70 parts of microcrystalline waxes, 10-20 parts of silver nitrates, 2-4 parts of Tween 80s are stirred by weight, under nitrogen protection, heating is stirred
Mix, centrifuge, sediment petroleum ether, water, absolute ethyl alcohol washing successively spontaneously dries, add 70-90 parts of gas phase hard charcoals at room temperature
Black, 5-15 parts of zinc stearate mixed grinding, add 1-2 parts of n-octyl trimethoxy silanes, 2-4 parts of organic zirconium crosslinkers, 5-7 parts
ATBC continues to grind, and adds 2-4 parts of cetyl trimethylammonium bromides, 2-8 parts of polyacrylamides, 2-4 parts of February
Dilaurylate, 2-4 parts of Cocoamidopropyl betaines continue to grind, and dry, pulverize and obtain antiseptic.
6. it is used for the electric wire of automobile according to claim any one of 1-5, it is characterised in that antiseptic uses following technique system
It is standby:60-70 parts of microcrystalline waxes, 10-20 parts of silver nitrates, 2-4 parts of Tween 80s are stirred into 10-16min by weight, mixing speed is
3300-3600r/min, under nitrogen protection, is warming up to 400-420 DEG C, stirs 20-30min, centrifugation, sediment successively petroleum ether,
Water, absolute ethyl alcohol washing, spontaneously dry, add 70-90 parts of gas-phase silicas, 5-15 parts of zinc stearate mixed grindings at room temperature
20-30min, adds 1-2 parts of n-octyl trimethoxy silanes, 2-4 parts of organic zirconium crosslinkers, 5-7 parts of ATBCs and continues
20-24min is ground, 2-4 parts of cetyl trimethylammonium bromides, 2-8 parts of polyacrylamides, the 2-4 parts of fourths of tin dilaurate two are added
Ji Xi, 2-4 parts of Cocoamidopropyl betaines continue to grind 40-60min, dry, pulverize and obtain antiseptic.