CN107311603A - Purify antimicrobial form diatom ooze wall material - Google Patents
Purify antimicrobial form diatom ooze wall material Download PDFInfo
- Publication number
- CN107311603A CN107311603A CN201710534993.4A CN201710534993A CN107311603A CN 107311603 A CN107311603 A CN 107311603A CN 201710534993 A CN201710534993 A CN 201710534993A CN 107311603 A CN107311603 A CN 107311603A
- Authority
- CN
- China
- Prior art keywords
- wall material
- diatom ooze
- antimicrobial form
- parts
- ooze wall
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Antimicrobial form diatom ooze wall material is purified the present invention relates to one kind.The purification antimicrobial form diatom ooze wall material includes the component of following parts by weight:30~45 parts of calcium carbonate;5~15 parts of magnesium carbonate;3~12 parts of talcum powder;12~24 parts of diatomite;2~18 parts of bactericide containing zinc;0.1~1 part of hydroxypropyl methyl cellulose ether;0.1~1 part of hydroxypropyl starch ether;0.05~0.1 part of polyvinyl alcohol;1~2 part of bentonite;23~25 parts of calcium hydroxide;1~2 part of redispersable latex powder.The purification antimicrobial form diatom ooze wall material of the present invention can not only have certain inner wall decoration effect, the pernicious gases such as formaldehyde, benzene, ammonia in indoor air can also effectively be dispelled, purifying air improves human respiratory, beneficial health, and with being firmly bonded, produce it is simple, the features such as facilitate.
Description
Technical field
The present invention relates to construction engineering technical field, and in particular to one kind purification antimicrobial form diatom ooze wall material.
Background technology
With the development of the society, requirement of the people to finishing yet more and more higher, do not require nothing more than beautiful attractive in appearance, also require environmental protection
Health.After finishing, some peculiar smell are had indoors and the gas being detrimental to health is present, such as formaldehyde.Generally use
The method of windowing ventilation comes discharge of noxious gases and peculiar smell, or reduces indoor dirt using methods such as adsorbent, cultivation flowers and plants
Dye, but above-mentioned method can not be inherently eliminated pollution, and efficiency is low, and cost is high, and the operating time is longer.
Diatom ooze is as a kind of new environment friendly inorganic interior decoration wall material, and it has, and density is low, specific surface area is big, hole
Rate is high, adsorptive liquid ability is strong, chemical stability is high, fusing point is high, matter is soft, sound insulation, many excellent properties such as wear-resisting, heat-resisting,
Main function in coating is absorption and regulation humidity, can effectively adsorb the harmful substances such as formaldehyde, benzene, ammonia free in air,
And it can purify in air because of the peculiar smell of the generations such as pet, smoking, rubbish.
In conventional art, using nano titanium oxide as photochemical catalyst in most diatom ooze wall material, in illumination bar
Harmful substance under part including catalytic decomposition absorption, but titanium dioxide has that photocatalysis efficiency is low, only issued in ultraviolet light conditions
Photocatalysis is waved, the shortcomings of poor to the spectral response of visible ray, also poor to the adsorptivity of harmful substance, causes diatom ooze wall
Material purification air effect can not ensure, therefore most of such diatom ooze wall materials can only achieve partial adsorbates harmful substance, decompose
Harmful substance ability is weak, and antibacterial ability is also weaker, and automatic humidifying ability is undesirable, it is difficult to meets people and is adsorbed for persistent high efficiency
The active demand of the harmful substances such as decomposing formaldehyde.
The content of the invention
Based on this, a kind of adsorption-decomposition function harmful substance ability of present invention offer is strong, strong antibacterial, automatic humidifying, heatproof
The multi-functional purification antimicrobial form diatom ooze wall material such as fire prevention, environment friendly and pollution-free.
In order to realize the purpose of the present invention, the present invention uses following technical scheme:
One kind purification antimicrobial form diatom ooze wall material, includes the component of following parts by weight:
The purification antimicrobial form diatom ooze wall material of the present invention can not only have certain inner wall decoration effect, can also be effectively
Dispel the pernicious gases such as formaldehyde, benzene, ammonia in indoor air, purification air improves human respiratory, beneficial health, and
And with being firmly bonded, produce it is simple, the features such as facilitate.The wall material of the present invention is compared with traditional wall material, its production brushed
Product quality not chip off-falling not alice, not mouldy, bubble, not colour-fast, fire-retardant, and the same day brushes, and the same day is moved in without formaldehyde, VOC etc.
Noxious material, nonpoisonous and tasteless, service life is more than 20 years.
Wherein, diatom soil pores is more, specific surface area is high, and adsorptivity is strong, can play elimination peculiar smell, be harmful in adsorption cleaning room
The effect of gas.Calcium carbonate and magnesium carbonate play a part of binder materials, and the use of both materials can also ensure wall material
Later strength, reduces the usage amount of organic cementing material.Re-dispersible glue powder can improve mobility, improve workability, change
Kind cohesive force, extension open hour and enhancing water-retaining property, can make wall material have enough cohesive forces to ensure that upper wall is constructed, simultaneously
It ensure that adhesive strength of the slurry at initial stage on wall.On the basis of re-dispersible glue powder, then added with calcium hydroxide and
Polyvinyl alcohol, three coordinates jointly has deferred action to hydrated cementitious, helps to extend the operable time of mortar.Hydroxypropyl
Methyl cellulose ether can improve the water-retaining property of mixed slurry, and with the effect of thickening, can improve application property, and hydroxypropyl
Starch ether has cracking resistance effect, with cellulose ether collective effect, plays a part of thickening, thickening.
Nano-Zinc loses bacterium mass flow, admittedly with very strong sterilization and anti-microbial property, the cell membrane that can be destroyed in bacterium
Change virus protein, while exterminating bacterium, moreover it is possible to the harmful compound discharged in bacterium residuum is decomposed, due to Nano-Zinc
Physical property itself, oxidizable, made moist easy caking, and therefore, Nano-Zinc is protected added with iron oxide and calcium oxide, so that
Nano-Zinc can play its sterilization, antibacterial functions to greatest extent.Bentonite uses six alkyl trimethyl ammonium bromides, hexadecane bromide
Change the materials such as pyridine, hexadecyltrimethylammonium chloride to be modified, make it have except formaldehyde, except benzene, except purification functions such as ammonia,
Modified alta-mud combination diatomite, Nano-Zinc make the purification antimicrobial form diatom ooze wall material of the present invention have multiple sterilization, antibacterial
Effect and adsorption-decomposition function harmful substance ability are strong, the fire prevention of strong antibacterial, automatic humidifying, heatproof, many work(such as environment friendly and pollution-free
Energy.
In wherein some embodiments, include the component of following parts by weight:
In wherein some embodiments, include the component of following parts by weight:
In wherein some embodiments, the diatomite is the diatomite of 300~900 mesh.
In wherein some embodiments, the diatomaceous moisture content is less than 0.5%;The diatomaceous specific surface area is
40~65m2/g。
In wherein some embodiments, the particle size range of the Nano-Zinc is 10~50nm.
In wherein some embodiments, the bentonite is modified alta-mud.
In wherein some embodiments, the viscosity for stating modified alta-mud is 300~1800mPa.s.
In wherein some embodiments, six alkyl trimethyl ammonium bromides, hexadecane bromide are contained in the modified alta-mud
Change pyridine and hexadecyltrimethylammonium chloride.
In wherein some embodiments, in addition to appropriate pigment.
Embodiment
For the ease of understanding the present invention, the present invention will be described more fully below.But, the present invention can be with perhaps
More different form is realized, however it is not limited to embodiment described herein.On the contrary, the purpose for providing these embodiments is to make
Understanding to the disclosure is more thorough comprehensive.
Unless otherwise defined, all of technologies and scientific terms used here by the article is with belonging to technical field of the invention
The implication that technical staff is generally understood that is identical.Term used in the description of the invention herein is intended merely to description tool
The purpose of the embodiment of body, it is not intended that in the limitation present invention.
One kind purification antimicrobial form diatom ooze wall material, includes the component of following parts by weight:
In wherein some embodiments, include the component of following parts by weight:
In wherein some embodiments, include the component of following parts by weight:
In wherein some embodiments, the diatomite is the diatomite of 300~900 mesh.
In wherein some embodiments, the diatomaceous moisture content is less than 0.5%;The diatomaceous specific surface area is
40~65m2/g。
In wherein some embodiments, the particle size range of the Nano-Zinc is 10~50nm.
In wherein some embodiments, the bentonite is modified alta-mud.
In wherein some embodiments, the viscosity for stating modified alta-mud is 300~1800mPa.s.
In wherein some embodiments, six alkyl trimethyl ammonium bromides, hexadecane bromide are contained in the modified alta-mud
Change pyridine and hexadecyltrimethylammonium chloride.
The purification antimicrobial form diatom ooze wall material of the present invention can not only have certain inner wall decoration effect, can also be effectively
Dispel the pernicious gases such as formaldehyde, benzene, ammonia in indoor air, purification air improves human respiratory, beneficial health, and
And with being firmly bonded, produce it is simple, the features such as facilitate.The wall material of the present invention is compared with traditional wall material, its production brushed
Product quality not chip off-falling not alice, not mouldy, bubble, not colour-fast, fire-retardant, and the same day brushes, and the same day is moved in without formaldehyde, VOC etc.
Noxious material, nonpoisonous and tasteless, service life is more than 20 years.
Wherein, diatom soil pores is more, specific surface area is high, and adsorptivity is strong, can play elimination peculiar smell, be harmful in adsorption cleaning room
The effect of gas.Calcium carbonate and magnesium carbonate play a part of binder materials, and the use of both materials can also ensure wall material
Later strength, reduces the usage amount of organic cementing material.Re-dispersible glue powder can improve mobility, improve workability, change
Kind cohesive force, extension open hour and enhancing water-retaining property, can make wall material have enough cohesive forces to ensure that upper wall is constructed, simultaneously
It ensure that adhesive strength of the slurry at initial stage on wall.On the basis of re-dispersible glue powder, then added with calcium hydroxide and
Polyvinyl alcohol, three coordinates jointly has deferred action to hydrated cementitious, helps to extend the operable time of mortar.Hydroxypropyl
Methyl cellulose ether can improve the water-retaining property of mixed slurry, and with the effect of thickening, can improve application property, and hydroxypropyl
Starch ether has cracking resistance effect, with cellulose ether collective effect, plays a part of thickening, thickening.
Nano-Zinc loses bacterium mass flow, admittedly with very strong sterilization and anti-microbial property, the cell membrane that can be destroyed in bacterium
Change virus protein, while exterminating bacterium, moreover it is possible to the harmful compound discharged in bacterium residuum is decomposed, due to Nano-Zinc
Physical property itself, oxidizable, made moist easy caking, and therefore, Nano-Zinc is protected added with iron oxide and calcium oxide, so that
Nano-Zinc can play its sterilization, antibacterial functions to greatest extent.Bentonite uses six alkyl trimethyl ammonium bromides, hexadecane bromide
Change the materials such as pyridine, hexadecyltrimethylammonium chloride to be modified, make it have except formaldehyde, except benzene, except purification functions such as ammonia,
Modified alta-mud combination diatomite, Nano-Zinc make the purification antimicrobial form diatom ooze wall material of the present invention have multiple sterilization, antibacterial
Effect and adsorption-decomposition function harmful substance ability are strong, the fire prevention of strong antibacterial, automatic humidifying, heatproof, many work(such as environment friendly and pollution-free
Energy.
A kind of preparation method for purifying antimicrobial form diatom ooze wall material, comprises the following steps:
First calcium carbonate, magnesium carbonate are dissolved in water, are stirred in greenhouse to dissolving, then sequentially add into above-mentioned solution hydroxypropyl first
Base cellulose ether, hydroxypropyl starch ether, polyvinyl alcohol, redispersable latex powder, calcium hydroxide, stir, and then add silicon
Diatomaceous earth and bentonite, stir, then add bactericide containing zinc to above-mentioned solution, are eventually adding talcum powder, stir mediation viscosity,
The color needed further according to product, adds corresponding appropriate pigment.
The solution of the present invention will be further illustrated by several embodiments below.
Embodiment one:
Purification antimicrobial form diatom ooze wall material of the present invention, it includes the component of following parts by weight:
30 parts of calcium carbonate;5 parts of magnesium carbonate;3 parts of talcum powder;24 parts of diatomite;2 parts of bactericide containing zinc;Hydroxypropyl methyl is fine
Plain 0.1 part of the ether of dimension;0.1 part of hydroxypropyl starch ether;0.05 part of polyvinyl alcohol;1 part of bentonite;23 parts of calcium hydroxide;It is redispersible
1 part of latex powder;Appropriate pigment.
The method for preparing above-mentioned purification antimicrobial form diatom ooze wall material is:First calcium carbonate, magnesium carbonate are dissolved in water, are stirred in greenhouse
Mix to dissolving, then sequentially add into above-mentioned solution hydroxypropyl methyl cellulose ether, hydroxypropyl starch ether, polyvinyl alcohol, can be again
Dispersed latex powder, calcium hydroxide, stir, and then add diatomite and bentonite, stir, then are added to above-mentioned solution
Bactericide containing zinc, is eventually adding talcum powder, and stirring reconciles viscosity, the color needed further according to product, adds corresponding appropriate
Pigment.
Embodiment two:
Purification antimicrobial form diatom ooze wall material of the present invention, it includes the component of following parts by weight:
40 parts of calcium carbonate;10 parts of magnesium carbonate;8 parts of talcum powder;18 parts of diatomite;10 parts of bactericide containing zinc;Hydroxypropyl methyl
0.5 part of cellulose ether;0.5 part of hydroxypropyl starch ether;0.08 part of polyvinyl alcohol;1.5 parts of bentonite;24 parts of calcium hydroxide;Can be again
1.5 parts of dispersed latex powder;Appropriate pigment.
The method for preparing above-mentioned purification antimicrobial form diatom ooze wall material is:First calcium carbonate, magnesium carbonate are dissolved in water, are stirred in greenhouse
Mix to dissolving, then sequentially add into above-mentioned solution hydroxypropyl methyl cellulose ether, hydroxypropyl starch ether, polyvinyl alcohol, can be again
Dispersed latex powder, calcium hydroxide, stir, and then add diatomite and bentonite, stir, then are added to above-mentioned solution
Bactericide containing zinc, is eventually adding talcum powder, and stirring reconciles viscosity, the color needed further according to product, adds corresponding appropriate
Pigment.
Embodiment three:
Purification antimicrobial form diatom ooze wall material of the present invention, it includes the component of following parts by weight:
45 parts of calcium carbonate;15 parts of magnesium carbonate;12 parts of talcum powder;12 parts of diatomite;18 parts of bactericide containing zinc;Hydroxypropyl methyl
1 part of cellulose ether;1 part of hydroxypropyl starch ether;0.1 part of polyvinyl alcohol;2 parts of bentonite;25 parts of calcium hydroxide;Redispersable latex
2 parts of powder;Appropriate pigment.
The method for preparing above-mentioned purification antimicrobial form diatom ooze wall material is:First calcium carbonate, magnesium carbonate are dissolved in water, are stirred in greenhouse
Mix to dissolving, then sequentially add into above-mentioned solution hydroxypropyl methyl cellulose ether, hydroxypropyl starch ether, polyvinyl alcohol, can be again
Dispersed latex powder, calcium hydroxide, stir, and then add diatomite and bentonite, stir, then are added to above-mentioned solution
Bactericide containing zinc, is eventually adding talcum powder, and stirring reconciles viscosity, the color needed further according to product, adds corresponding appropriate
Pigment.
Example IV:
Purification antimicrobial form diatom ooze wall material of the present invention, it includes the component of following parts by weight:
38 parts of calcium carbonate;8 parts of magnesium carbonate;6 parts of talcum powder;20 parts of diatomite;15 parts of bactericide containing zinc;Hydroxypropyl methyl is fine
Plain 0.3 part of the ether of dimension;0.6 part of hydroxypropyl starch ether;0.06 part of polyvinyl alcohol;1.2 parts of bentonite;23 parts of calcium hydroxide;It can divide again
Dissipate 2 parts of latex powder.
The method for preparing above-mentioned purification antimicrobial form diatom ooze wall material is:First calcium carbonate, magnesium carbonate are dissolved in water, are stirred in greenhouse
Mix to dissolving, then sequentially add into above-mentioned solution hydroxypropyl methyl cellulose ether, hydroxypropyl starch ether, polyvinyl alcohol, can be again
Dispersed latex powder, calcium hydroxide, stir, and then add diatomite and bentonite, stir, then are added to above-mentioned solution
Bactericide containing zinc, is eventually adding talcum powder, stirring mediation viscosity.
Embodiment described above only expresses the several embodiments of the present invention, and it describes more specific and detailed, but simultaneously
Therefore the limitation to the scope of the claims of the present invention can not be interpreted as.It should be pointed out that for one of ordinary skill in the art
For, without departing from the inventive concept of the premise, various modifications and improvements can be made, these belong to the guarantor of the present invention
Protect scope.Therefore, the protection domain of patent of the present invention should be determined by the appended claims.
Claims (10)
1. one kind purification antimicrobial form diatom ooze wall material, it is characterised in that include the component of following parts by weight:
2. purification antimicrobial form diatom ooze wall material according to claim 1, it is characterised in that include the group of following parts by weight
Point:
3. purification antimicrobial form diatom ooze wall material according to claim 2, it is characterised in that include the group of following parts by weight
Point:
4. purification antimicrobial form diatom ooze wall material according to claim 3, it is characterised in that the diatomite is 300~900
Purpose diatomite.
5. purification antimicrobial form diatom ooze wall material according to claim 4, it is characterised in that the diatomaceous moisture content is small
In 0.5%;The diatomaceous specific surface area is 40~65m2/g。
6. purification antimicrobial form diatom ooze wall material according to claim 3, it is characterised in that the particle size range of the Nano-Zinc
For 10~50nm.
7. purification antimicrobial form diatom ooze wall material according to claim 3, it is characterised in that the bentonite is bentone
Soil.
8. purification antimicrobial form diatom ooze wall material according to claim 7, it is characterised in that the viscosity of the modified alta-mud
For 300~1800mPa.s.
9. purification antimicrobial form diatom ooze wall material according to claim 8, it is characterised in that contain in the modified alta-mud
Six alkyl trimethyl ammonium bromides, cetyl pyridinium bromide and hexadecyltrimethylammonium chloride.
10. the purification antimicrobial form diatom ooze wall material according to any one of claim 1 to 9, it is characterised in that also include
Appropriate pigment.