CN107311505B - A kind of composite material of modified industry inorganic powder and the inorganic powder containing modified industry - Google Patents
A kind of composite material of modified industry inorganic powder and the inorganic powder containing modified industry Download PDFInfo
- Publication number
- CN107311505B CN107311505B CN201710432380.XA CN201710432380A CN107311505B CN 107311505 B CN107311505 B CN 107311505B CN 201710432380 A CN201710432380 A CN 201710432380A CN 107311505 B CN107311505 B CN 107311505B
- Authority
- CN
- China
- Prior art keywords
- powder
- parts
- inorganic powder
- modified industry
- inorganic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses the composite material of a kind of modified industry inorganic powder and the inorganic powder containing modified industry, which includes following raw material: 100 parts of inorganic waste residue powder;3~40 parts of acrylate polymer emulsion or/and 1~10 part of redispersible latex powder;3~30 parts of polyether polyurethane.The alternative conventional filler of modified industry inorganic powder of the invention, has not only recycled waste material, reduces stacking cost of disposal, but also can bring certain economic benefit.Excellent, resistant to chemical etching, the resistance to microorganism of excellent in mechanical performance, the water resistances such as the toughness and impact resistance of the composite material of the inorganic powder containing modified industry of the invention, one-pass molding when manufacture, it is not required to steam pressure, maintenance, it can be widely used for being laid with highway pavement, pavement road surface, curb, bridge etc., and the composite material added with elastomeric polymer can be used for being laid with runway, athletic floor etc..
Description
Technical field
The present invention relates to the composite materials of a kind of modified industry inorganic powder and the inorganic powder containing modified industry, belong to composite material
Technical field.
Background technique
As modern industry is grown rapidly, each industrial enterprise can generate a large amount of waste residue in process of production, such as plating row
Industry can generate that plating slag, porcelain making industry can generate pitchers, Sulphuric acid or sulfurous acid industry can generate sulfate slag, and the discharge of waste residue
It measures growing day by day, not only needs to occupy a large amount of soils to stack, but also environment can be caused great harm.In fact, it only needs
Industrial residue is processed, useful raw material can be converted thereof into completely, not only can solve at waste residue routine
The existing problem of environmental pollution of reason, but also significant economic benefit can be brought.
Summary of the invention
The purpose of the present invention is to provide the composite materials of a kind of modified industry inorganic powder and the inorganic powder containing modified industry.
A kind of modified industry inorganic powder, the raw material comprising following mass parts:
100 parts of inorganic waste residue powder;
3~40 parts of acrylate polymer emulsion or/and 1~10 part of redispersible latex powder;
3~30 parts of polyether polyurethane.
The inorganic waste residue powder be tailings powder, sulfuric acid ground-slag, coal gangue powder, pitchers powder, chromium slag powder, titanium slag powder,
Ground-slag, red mud powder, waste stone dust, urban construction roach, cement is electroplated and abandons at least one of block powder.
The solid content of the acrylate polymer emulsion is 35%~55%.
The solid content of the polyether polyurethane is 10%~48%.
The preparation method of above-mentioned modified industry inorganic powder, comprising the following steps: by acrylate polymer emulsion or/and can be again
Dispersed latex powder, polyether polyurethane are uniformly mixed, and add inorganic waste residue powder, are sufficiently mixed uniformly, dry, are coated
Modified industrial inorganic powder.
A kind of composite material containing above-mentioned modified industry inorganic powder, the raw material comprising following mass parts:
100 parts of modified industry inorganic powder;0~3 part of fiber;0~1 part of methylcellulose;0~5 part of pigment;Active inorganic powder
20~60 parts of end;
Alternatively, 100 parts of modified industry inorganic powder;0~3 part of fiber;0~1 part of methylcellulose;0~5 part of pigment;Elasticity
3~60 parts of polymer;
Alternatively, 100 parts of modified industry inorganic powder;0~3 part of fiber;0~1 part of methylcellulose;0~5 part of pigment;Propylene
3~60 parts of acid polymer lotion;1~50 part of polyether-polyurethane.
The fiber is vinal.
The active inorganic powder is granulation electric furnace phosphoric slag powder, granulation water-quenched manganese slag powder, granulation water quenching steel-making slag powder, granulation
At least one of cinder powder, granulation granulated copper slag powder, granulation water quenching magnesium-reduced ground-slag, granulation nickel ground-slag, cement.
The specific surface area of the active inorganic powder is not less than 410m2/kg。
The elastomeric polymer is at least one of elastic printing paste, flexible foaming slurry.
The beneficial effects of the present invention are:
1) modified industry inorganic powder of the invention can substitute traditional filler, not only recycle waste material,
Stacking cost of disposal is reduced, but also certain economic benefit can be brought;
2) present invention is using acrylate polymer emulsion, redispersible latex powder, polyether polyurethane to poisonous and harmful
Industrial residue (such as chromium slag, plating slag) carry out coating modification and solve common landfill so that poisonous and harmful substance is difficult to ooze out
The problem of handling existing polluted underground water;
3) excellent in mechanical performance such as toughness and impact resistance of the composite material of the inorganic powder of the invention containing modified industry, resistance to
Water has excellent performance, is resistant to chemical etching, resistance to microorganism, and one-pass molding when manufacture is not required to steam pressure, maintenance, can be widely used for spreading
If highway pavement, pavement road surface, curb, bridge etc., and the composite material added with elastomeric polymer can be used for being laid with race
Road, athletic floor etc..
4) profile that the composite molding of the inorganic powder of the invention containing modified industry obtains can partially replace shaped plastics
Material, plaster profile and mental section.
Specific embodiment
A kind of modified industry inorganic powder, the raw material comprising following mass parts:
100 parts of inorganic waste residue powder;
3~40 parts of acrylate polymer emulsion or/and 1~10 part of redispersible latex powder;
3~30 parts of polyether polyurethane.
Preferably, the inorganic waste residue powder be tailings powder, sulfuric acid ground-slag, coal gangue powder, pitchers powder, chromium slag powder,
Titanium slag powder, plating ground-slag, red mud powder, waste stone dust, urban construction roach, cement abandon at least one of block powder.
Preferably, the solid content of the acrylate polymer emulsion is 35%~55%.
Preferably, the solid content of the polyether polyurethane is 10%~48%.
The preparation method of above-mentioned modified industry inorganic powder, comprising the following steps: by acrylate polymer emulsion or/and can be again
Dispersed latex powder, polyether polyurethane are uniformly mixed, and add inorganic waste residue powder, are sufficiently mixed uniformly, dry, are coated
Modified industrial inorganic powder.
A kind of composite material containing above-mentioned modified industry inorganic powder, the raw material comprising following mass parts:
100 parts of modified industry inorganic powder;0~3 part of fiber;0~1 part of methylcellulose;0~5 part of pigment;Active inorganic powder
20~60 parts of end;
Alternatively, 100 parts of modified industry inorganic powder;0~3 part of fiber;0~1 part of methylcellulose;0~5 part of pigment;Elasticity
3~60 parts of polymer;
Alternatively, 100 parts of modified industry inorganic powder;0~3 part of fiber;0~1 part of methylcellulose;0~5 part of pigment;Propylene
3~60 parts of acid polymer lotion;1~50 part of polyether-polyurethane.
Preferably, the fiber is vinal.
Preferably, the active inorganic powder is granulation electric furnace phosphoric slag powder, granulation water-quenched manganese slag powder, granulation water quenching steel slag
At least one of powder, granulation cinder powder, granulation granulated copper slag powder, granulation water quenching magnesium-reduced ground-slag, granulation nickel ground-slag, cement.
Preferably, the specific surface area of the active inorganic powder is not less than 410m2/kg。
Preferably, the elastomeric polymer is at least one of elastic printing paste, flexible foaming slurry.
The preparation method of the composite material of the above-mentioned inorganic powder containing modified industry the following steps are included:
Modified industry inorganic powder, fiber, methylcellulose, pigment and active inorganic powder are uniformly mixed, water is added to modulate
It at slurry, coats or is poured in mold, demoulded after dry solidification, obtain plate or profile;
Alternatively, modified industry inorganic powder, fiber, methylcellulose, pigment and elastomeric polymer are uniformly mixed, add water tune
Slurry is made, coat or is poured in mold, is demoulded after dry solidification, obtains plastic cement race track or athletic floor;
Alternatively, modified industry inorganic powder, fiber, methylcellulose, pigment, acrylate polymer emulsion and polyethers are birdsed of the same feather flock together
Urethane is uniformly mixed, and is added water to be modulated into paste, is molded into flexible bulk, plate, profile.
Preferably, the composite material of the above-mentioned inorganic powder containing modified industry be other than it can coat, be poured in die for molding,
It can also be with compression moulding.
The present invention will be further explained combined with specific embodiments below and explanation.
Embodiment 1:
A kind of modified industry inorganic powder, the raw material comprising following mass parts: sulfuric acid ground-slag: 100 parts;Acrylate copolymer cream
Liquid: 3 parts;Polyether polyurethane: 10 parts.
The preparation method of above-mentioned modified industry inorganic powder is the following steps are included: acrylate polymer emulsion, polyethers are birdsed of the same feather flock together
Urethane is uniformly mixed, and adds sulfuric acid ground-slag, is sufficiently mixed uniformly, dry, obtains the industrial inorganic powder of coating modification.
A kind of composite material of the inorganic powder containing modified industry, the raw material comprising following mass parts: above-mentioned modified industry is inorganic
Powder: 100 parts;Vinal: 1 part;Methylcellulose: 0.5 part;Pigment: 2 parts;Granulation water quenching steel-making slag powder: 30 parts.
The preparation method of the composite material of the above-mentioned inorganic powder containing modified industry is the following steps are included: inorganic by modified industry
Powder, vinal, methylcellulose, pigment and granulation water quenching steel-making slag powder are uniformly mixed, and are added water to be modulated into slurry, are poured in
It in mold, is demoulded after dry solidification, obtains plate.
Embodiment 2:
A kind of modified industry inorganic powder, the raw material comprising following mass parts: pitchers powder: 100 parts;Redispersible latex
Powder: 10 parts;Polyether polyurethane: 15 parts.
The preparation method of above-mentioned modified industry inorganic powder is the following steps are included: redispersible latex powder, polyethers are birdsed of the same feather flock together
Urethane is uniformly mixed, and adds pitchers powder, is sufficiently mixed uniformly, dry, obtains the industrial inorganic powder of coating modification.
A kind of composite material of the inorganic powder containing modified industry, the raw material comprising following mass parts: above-mentioned modified industry is inorganic
Powder: 100 parts;Vinal: 1.5 parts;Methylcellulose: 1 part;Granulation electric furnace phosphoric slag powder: 20 parts.
The preparation method of the composite material of the above-mentioned inorganic powder containing modified industry is the following steps are included: inorganic by modified industry
Powder, vinal, methylcellulose and granulation electric furnace phosphoric slag powder are uniformly mixed, and are added water to be modulated into slurry, are coated in mold
It is interior, it is demoulded after dry solidification, obtains plate.
Embodiment 3:
A kind of modified industry inorganic powder, the raw material comprising following mass parts: chromium slag powder: 100 parts;Acrylate copolymer cream
Liquid: 30 parts;Polyether polyurethane: 3 parts.
The preparation method of above-mentioned modified industry inorganic powder is the following steps are included: acrylate polymer emulsion, polyethers are birdsed of the same feather flock together
Urethane is uniformly mixed, and adds chromium slag powder, is sufficiently mixed uniformly, dry, obtains the industrial inorganic powder of coating modification.
A kind of composite material of the inorganic powder containing modified industry, the raw material comprising following mass parts: above-mentioned modified industry is inorganic
Powder: 100 parts;Vinal: 3 parts;Methylcellulose: 0.8 part;Pigment: 3 parts;Granulation nickel ground-slag: 40 parts.
The preparation method of the composite material of the above-mentioned inorganic powder containing modified industry is the following steps are included: inorganic by modified industry
Powder, vinal, methylcellulose, pigment and granulation nickel ground-slag are uniformly mixed, and are added water to be modulated into slurry, are poured in mold
It is interior, it is demoulded after dry solidification, obtains plate.
Embodiment 4:
A kind of modified industry inorganic powder, the raw material comprising following mass parts: titanium slag powder: 100 parts;Acrylate copolymer cream
Liquid: 40 parts;Polyether polyurethane: 20 parts.
The preparation method of above-mentioned modified industry inorganic powder is the following steps are included: acrylate polymer emulsion, polyethers are birdsed of the same feather flock together
Urethane is uniformly mixed, and adds titanium slag powder, is sufficiently mixed uniformly, dry, obtains the industrial inorganic powder of coating modification.
A kind of composite material of the inorganic powder containing modified industry, the raw material comprising following mass parts: above-mentioned modified industry is inorganic
Powder: 100 parts;Vinal: 2 parts;Methylcellulose: 0.5 part;Pigment: 2.5 parts;Elastic printing paste: 10 parts.
The preparation method of the composite material of the above-mentioned inorganic powder containing modified industry is the following steps are included: inorganic by modified industry
Powder, vinal, methylcellulose, pigment and elastic printing paste are uniformly mixed, and are added water to be modulated into slurry, are poured in mold
It is interior, it is demoulded after dry solidification, obtains athletic floor.
Embodiment 5:
A kind of modified industry inorganic powder, the raw material comprising following mass parts: plating ground-slag: 100 parts;Redispersible latex
Powder: 10 parts;Polyether polyurethane: 5 parts.
The preparation method of above-mentioned modified industry inorganic powder is the following steps are included: redispersibility latex powder, polyethers are birdsed of the same feather flock together ammonia
Ester is uniformly mixed, and adds plating ground-slag, is sufficiently mixed uniformly, dry, obtains the industrial inorganic powder of coating modification.
A kind of composite material of the inorganic powder containing modified industry, the raw material comprising following mass parts: above-mentioned modified industry is inorganic
Powder: 100 parts;Vinal: 1.5 parts;Methylcellulose: 1 part;Flexible foaming slurry: 15 parts.
The preparation method of the composite material of the above-mentioned inorganic powder containing modified industry is the following steps are included: inorganic by modified industry
Powder, vinal, methylcellulose and flexible foaming slurry are uniformly mixed, and are added water to be modulated into slurry, are coated or be poured in mould
It in tool, is demoulded after dry solidification, obtains athletic tracks.
Embodiment 6:
A kind of modified industry inorganic powder, the raw material comprising following mass parts: red mud powder: 100 parts;Redispersible latex
Powder: 5 parts;Polyether polyurethane: 30 parts.
The preparation method of above-mentioned modified industry inorganic powder is the following steps are included: redispersible latex powder, polyethers are birdsed of the same feather flock together
Urethane is uniformly mixed, and adds red mud powder, is sufficiently mixed uniformly, dry, obtains the industrial inorganic powder of coating modification.
A kind of composite material of the inorganic powder containing modified industry, the raw material comprising following mass parts: above-mentioned modified industry is inorganic
Powder: 100 parts;Vinal: 1 part;Methylcellulose: 0.5 part;Pigment: 5 parts;Acrylate polymer emulsion: 50 parts;It is poly-
Ether polyurethane: 10 parts.
The preparation method of the composite material of the above-mentioned inorganic powder containing modified industry is the following steps are included: inorganic by modified industry
Powder, vinal, methylcellulose, pigment, acrylate polymer emulsion and polyether-polyurethane are uniformly mixed, and water is added to modulate
At slurry, it is coated in mold, is demoulded after dry solidification, obtain profile.
Embodiment 7:
A kind of modified industry inorganic powder, the raw material comprising following mass parts: urban construction roach: 100 parts;Acrylate copolymer cream
Liquid: 10 parts;Redispersible latex powder: 1 part;Polyether polyurethane: 15 parts.
The preparation method of above-mentioned modified industry inorganic powder is the following steps are included: by acrylate polymer emulsion, redispersible
Property latex powder, polyether polyurethane be uniformly mixed, add urban construction roach, be sufficiently mixed uniformly, it is dry, obtain coating modification
Industrial inorganic powder.
A kind of composite material of the inorganic powder containing modified industry, the raw material comprising following mass parts: above-mentioned modified industry is inorganic
Powder: 100 parts;Vinal: 3 parts;Methylcellulose: 0.7 part;Pigment: 2 parts;Acrylate polymer emulsion: 15 parts;It is poly-
Ether polyurethane: 50 parts.
The preparation method of the composite material of the above-mentioned inorganic powder containing modified industry is the following steps are included: inorganic by modified industry
Powder, vinal, methylcellulose, pigment, acrylate polymer emulsion and polyether-polyurethane are uniformly mixed, and water is added to modulate
It at slurry, is poured in mold, is demoulded after dry solidification, obtain profile.
Test case:
The composite material of Examples 1 to 7 preparation is tested for the property, test result is as shown in table 1~3:
The performance test results of the composite material of 1 Examples 1 to 3 of table
The performance test results of the composite material of 2 embodiment 4~5 of table
The performance test results of the composite material of 3 embodiment 6~7 of table
The above embodiment is a preferred embodiment of the present invention, but embodiments of the present invention are not by above-described embodiment
Limitation, other any changes, modifications, substitutions, combinations, simplifications made without departing from the spirit and principles of the present invention,
It should be equivalent substitute mode, be included within the scope of the present invention.
Claims (8)
1. a kind of modified industry inorganic powder, it is characterised in that: the raw material comprising following mass parts:
100 parts of inorganic waste residue powder;
3~40 parts of acrylate polymer emulsion or/and 1~10 part of redispersible latex powder;
3~30 parts of polyether polyurethane;
The inorganic waste residue powder is tailings powder, sulfuric acid ground-slag, coal gangue powder, pitchers powder, chromium slag powder, titanium slag powder, plating
Ground-slag, red mud powder, waste stone dust, urban construction roach, cement abandon at least one of block powder;
The modified industry inorganic powder is prepared by the following method to obtain: by acrylate polymer emulsion or/and redispersible
Property latex powder, polyether polyurethane be uniformly mixed, add inorganic waste residue powder, be sufficiently mixed uniformly, it is dry.
2. modified industry inorganic powder according to claim 1, it is characterised in that: the acrylate polymer emulsion is consolidated
Content is 35%~55%.
3. modified industry inorganic powder according to claim 1, it is characterised in that: the solid content of the polyether polyurethane
It is 10%~48%.
4. a kind of composite material containing modified industry inorganic powder described in any one of claims 1 to 33, it is characterised in that: packet
Raw material containing following mass parts:
100 parts of modified industry inorganic powder;0~3 part of fiber;0~1 part of methylcellulose;0~5 part of pigment;Active inorganic powder 20
~60 parts;
Alternatively, 100 parts of modified industry inorganic powder;0~3 part of fiber;0~1 part of methylcellulose;0~5 part of pigment;Flexible polymer
3~60 parts of object;
Alternatively, 100 parts of modified industry inorganic powder;0~3 part of fiber;0~1 part of methylcellulose;0~5 part of pigment;Acrylic acid is poly-
Close 3~60 parts of object lotion;1~50 part of polyether-polyurethane.
5. the composite material of the inorganic powder according to claim 4 containing modified industry, it is characterised in that: the fiber is poly-
Alcohol fibers.
6. the composite material of the inorganic powder according to claim 4 containing modified industry, it is characterised in that: the active inorganic
Powder be granulation electric furnace phosphoric slag powder, granulation water-quenched manganese slag powder, granulation water quenching steel-making slag powder, granulation cinder powder, granulation granulated copper slag powder,
It is granulated at least one of water quenching magnesium-reduced ground-slag, granulation nickel ground-slag, cement.
7. the composite material of the inorganic powder according to claim 6 containing modified industry, it is characterised in that: the active inorganic
The specific surface area of powder is not less than 410m2/kg。
8. the composite material of the inorganic powder according to claim 4 containing modified industry, it is characterised in that: the flexible polymer
Object is at least one of elastic printing paste, flexible foaming slurry.