CN107311505A - A kind of composite of modified industry inorganic powder and the inorganic powder containing modified industry - Google Patents

A kind of composite of modified industry inorganic powder and the inorganic powder containing modified industry Download PDF

Info

Publication number
CN107311505A
CN107311505A CN201710432380.XA CN201710432380A CN107311505A CN 107311505 A CN107311505 A CN 107311505A CN 201710432380 A CN201710432380 A CN 201710432380A CN 107311505 A CN107311505 A CN 107311505A
Authority
CN
China
Prior art keywords
powder
inorganic powder
parts
modified industry
inorganic
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201710432380.XA
Other languages
Chinese (zh)
Other versions
CN107311505B (en
Inventor
石磊
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Guangdong Fumei material science and Technology Co., Ltd
Original Assignee
Guangdong Fumei Soft Porcelain Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Guangdong Fumei Soft Porcelain Co Ltd filed Critical Guangdong Fumei Soft Porcelain Co Ltd
Priority to CN201710432380.XA priority Critical patent/CN107311505B/en
Publication of CN107311505A publication Critical patent/CN107311505A/en
Application granted granted Critical
Publication of CN107311505B publication Critical patent/CN107311505B/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The invention discloses the composite of a kind of modified industry inorganic powder and the inorganic powder containing modified industry, the modified industry inorganic powder includes following raw material:Inorganic 100 parts of waste residue powder;1~10 part of 3~40 parts of acrylate polymer emulsion or/and redispersible latex powder;3~30 parts of polyether polyurethane.The alternative conventional filler of modified industry inorganic powder of the present invention, has not only recycled waste material, has reduced stacking cost of disposal, but also can bring certain economic benefit.Excellent in mechanical performance, the water resistances such as the toughness and impact resistance of the composite of the inorganic powder containing modified industry of the present invention are excellent, resistant to chemical etching, resistance to microorganism, one-shot forming during manufacture, it is not required to steam pressure, maintenance, laying highway pavement, pavement road surface, curb, bridge etc. are can be widely used for, and the composite added with elastomeric polymer can be used for laying runway, athletic floor etc..

Description

A kind of composite of modified industry inorganic powder and the inorganic powder containing modified industry
Technical field
The present invention relates to the composite of a kind of modified industry inorganic powder and the inorganic powder containing modified industry, belong to composite Technical field.
Background technology
With modern industry fast development, each industrial enterprise can produce substantial amounts of waste residue in process of production, such as plating row Industry can produce plating slag, porcelain making industry can produce pitchers, Sulphuric acid or sulfurous acid industry can produce sulfate slag, and the discharge of waste residue Amount is growing day by day, not only needs to take a large amount of soils to stack, but also greatly harm can be caused to environment.In fact, only need Industrial residue is processed, useful raw material can be converted thereof into completely, can not only solved at waste residue routine The existing problem of environmental pollution of reason, but also significant economic benefit can be brought.
The content of the invention
It is an object of the invention to provide the composite of a kind of modified industry inorganic powder and the inorganic powder containing modified industry.
A kind of modified industry inorganic powder, includes the raw material of following mass parts:
Inorganic 100 parts of waste residue powder;
1~10 part of 3~40 parts of acrylate polymer emulsion or/and redispersible latex powder;
3~30 parts of polyether polyurethane.
Described inorganic waste residue powder be tailings powder, sulfuric acid ground-slag, colliery powder, pitchers powder, chromium ground-slag, titanium slag powder, Plating ground-slag, red mud powder, waste stone dust, urban construction roach, cement abandon at least one of block powder.
The solid content of described acrylate polymer emulsion is 35%~55%.
The solid content of described polyether polyurethane is 10%~48%.
The preparation method of above-mentioned modified industry inorganic powder, comprises the following steps:By acrylate polymer emulsion or/and can be again Dispersed latex powder, polyether polyurethane are well mixed, and add inorganic waste residue powder, are sufficiently mixed uniformly, are dried, coated Modified industrial inorganic powder.
A kind of composite containing above-mentioned modified industry inorganic powder, includes the raw material of following mass parts:
100 parts of modified industry inorganic powder;0~3 part of fiber;0~1 part of methylcellulose;0~5 part of pigment;Active inorganic powder 20~60 parts of end;
Or, 100 parts of modified industry inorganic powder;0~3 part of fiber;0~1 part of methylcellulose;0~5 part of pigment;Elasticity 3~60 parts of polymer;
Or, 100 parts of modified industry inorganic powder;0~3 part of fiber;0~1 part of methylcellulose;0~5 part of pigment;Propylene 3~60 parts of acid polymer emulsion;1~50 part of polyether-polyurethane.
Described fiber is vinal.
Described active inorganic powder is granulation electric furnace phosphoric slag powder, granulation water-quenched manganese slag powder, granulation water quenching steel-making slag powder, granulation At least one of cinder powder, granulation granulated copper slag powder, granulation water quenching magnesium-reduced ground-slag, granulation nickel ground-slag, cement.
The specific surface area of described active inorganic powder is not less than 410m2/kg。
Described elastomeric polymer is at least one of elastic printing paste, flexible foaming slurry.
The beneficial effects of the invention are as follows:
1) modified industry inorganic powder of the invention can substitute traditional filler, not only recycle waste material, Stacking cost of disposal is reduced, but also certain economic benefit can be brought;
2) present invention uses acrylate polymer emulsion, redispersible latex powder, polyether polyurethane to poisonous and harmful Industrial residue (such as chromium slag, plating slag) carry out coating modification so that poisonous and harmful substance is difficult to ooze out, and solves common landfill The problem of handling the polluted underground water existed;
3) excellent in mechanical performance such as toughness and impact resistance of the composite of the inorganic powder containing modified industry of the invention, resistance to Water excellent performance, resistant to chemical etching, resistance to microorganism, one-shot forming during manufacture are not required to steam pressure, maintenance, can be widely used for paving If highway pavement, pavement road surface, curb, bridge etc., and the composite added with elastomeric polymer can be used for laying to run Road, athletic floor etc..
4) section bar that the composite shaping of the inorganic powder containing modified industry of the invention is obtained, can partly replace shaped plastics Material, plaster profile and shape.
Embodiment
A kind of modified industry inorganic powder, includes the raw material of following mass parts:
Inorganic 100 parts of waste residue powder;
1~10 part of 3~40 parts of acrylate polymer emulsion or/and redispersible latex powder;
3~30 parts of polyether polyurethane.
It is preferred that, described inorganic waste residue powder is tailings powder, sulfuric acid ground-slag, colliery powder, pitchers powder, chromium ground-slag, Titanium slag powder, plating ground-slag, red mud powder, waste stone dust, urban construction roach, cement abandon at least one of block powder.
It is preferred that, the solid content of described acrylate polymer emulsion is 35%~55%.
It is preferred that, the solid content of described polyether polyurethane is 10%~48%.
The preparation method of above-mentioned modified industry inorganic powder, comprises the following steps:By acrylate polymer emulsion or/and can be again Dispersed latex powder, polyether polyurethane are well mixed, and add inorganic waste residue powder, are sufficiently mixed uniformly, are dried, coated Modified industrial inorganic powder.
A kind of composite containing above-mentioned modified industry inorganic powder, includes the raw material of following mass parts:
100 parts of modified industry inorganic powder;0~3 part of fiber;0~1 part of methylcellulose;0~5 part of pigment;Active inorganic powder 20~60 parts of end;
Or, 100 parts of modified industry inorganic powder;0~3 part of fiber;0~1 part of methylcellulose;0~5 part of pigment;Elasticity 3~60 parts of polymer;
Or, 100 parts of modified industry inorganic powder;0~3 part of fiber;0~1 part of methylcellulose;0~5 part of pigment;Propylene 3~60 parts of acid polymer emulsion;1~50 part of polyether-polyurethane.
It is preferred that, described fiber is vinal.
It is preferred that, described active inorganic powder is granulation electric furnace phosphoric slag powder, granulation water-quenched manganese slag powder, granulation water quenching slag At least one of powder, granulation cinder powder, granulation granulated copper slag powder, granulation water quenching magnesium-reduced ground-slag, granulation nickel ground-slag, cement.
It is preferred that, the specific surface area of described active inorganic powder is not less than 410m2/kg。
It is preferred that, described elastomeric polymer is at least one of elastic printing paste, flexible foaming slurry.
The preparation method of the composite of the above-mentioned inorganic powder containing modified industry comprises the following steps:
Modified industry inorganic powder, fiber, methylcellulose, pigment and active inorganic powder are well mixed, add water modulation Into slurry, coat or be poured in mould, be stripped after dry solidification, obtain sheet material or section bar;
Or, modified industry inorganic powder, fiber, methylcellulose, pigment and elastomeric polymer are well mixed, add water tune Slurry is made, coats or is poured in mould, is stripped after dry solidification, obtains plastic cement race track or athletic floor;
Or, modified industry inorganic powder, fiber, methylcellulose, pigment, acrylate polymer emulsion and polyethers are birdsed of the same feather flock together Urethane is well mixed, and is added water and is modulated into paste, is molded into flexible bulk, sheet material, section bar.
It is preferred that, the composite of the above-mentioned inorganic powder containing modified industry in addition to it can coat, be poured in die for molding, Can also be compressing.
The present invention is made further explanation and description with reference to specific embodiment.
Embodiment 1:
A kind of modified industry inorganic powder, includes the raw material of following mass parts:Sulfuric acid ground-slag:100 parts;Acrylate copolymer breast Liquid:3 parts;Polyether polyurethane:10 parts.
The preparation method of above-mentioned modified industry inorganic powder comprises the following steps:Acrylate polymer emulsion, polyethers are birdsed of the same feather flock together Urethane is well mixed, and adds sulfuric acid ground-slag, is sufficiently mixed uniformly, is dried, obtain the industrial inorganic powder of coating modification.
A kind of composite of inorganic powder containing modified industry, includes the raw material of following mass parts:Above-mentioned modified industry is inorganic Powder:100 parts;Vinal:1 part;Methylcellulose:0.5 part;Pigment:2 parts;It is granulated water quenching steel-making slag powder:30 parts.
The preparation method of the composite of the above-mentioned inorganic powder containing modified industry comprises the following steps:Modified industry is inorganic Powder, vinal, methylcellulose, pigment and granulation water quenching steel-making slag powder are well mixed, and are added water and are modulated into slurry, are poured in In mould, it is stripped after dry solidification, obtains sheet material.
Embodiment 2:
A kind of modified industry inorganic powder, includes the raw material of following mass parts:Pitchers powder:100 parts;Redispersible latex Powder:10 parts;Polyether polyurethane:15 parts.
The preparation method of above-mentioned modified industry inorganic powder comprises the following steps:Redispersible latex powder, polyethers are birdsed of the same feather flock together Urethane is well mixed, and adds pitchers powder, is sufficiently mixed uniformly, is dried, obtain the industrial inorganic powder of coating modification.
A kind of composite of inorganic powder containing modified industry, includes the raw material of following mass parts:Above-mentioned modified industry is inorganic Powder:100 parts;Vinal:1.5 part;Methylcellulose:1 part;It is granulated electric furnace phosphoric slag powder:20 parts.
The preparation method of the composite of the above-mentioned inorganic powder containing modified industry comprises the following steps:Modified industry is inorganic Powder, vinal, methylcellulose and granulation electric furnace phosphoric slag powder are well mixed, and are added water and are modulated into slurry, are coated in mould It is interior, it is stripped after dry solidification, obtains sheet material.
Embodiment 3:
A kind of modified industry inorganic powder, includes the raw material of following mass parts:Chromium ground-slag:100 parts;Acrylate copolymer breast Liquid:30 parts;Polyether polyurethane:3 parts.
The preparation method of above-mentioned modified industry inorganic powder comprises the following steps:Acrylate polymer emulsion, polyethers are birdsed of the same feather flock together Urethane is well mixed, and adds chromium ground-slag, is sufficiently mixed uniformly, is dried, obtain the industrial inorganic powder of coating modification.
A kind of composite of inorganic powder containing modified industry, includes the raw material of following mass parts:Above-mentioned modified industry is inorganic Powder:100 parts;Vinal:3 parts;Methylcellulose:0.8 part;Pigment:3 parts;It is granulated nickel ground-slag:40 parts.
The preparation method of the composite of the above-mentioned inorganic powder containing modified industry comprises the following steps:Modified industry is inorganic Powder, vinal, methylcellulose, pigment and granulation nickel ground-slag are well mixed, and are added water and are modulated into slurry, are poured in mould It is interior, it is stripped after dry solidification, obtains sheet material.
Embodiment 4:
A kind of modified industry inorganic powder, includes the raw material of following mass parts:Titanium slag powder:100 parts;Acrylate copolymer breast Liquid:40 parts;Polyether polyurethane:20 parts.
The preparation method of above-mentioned modified industry inorganic powder comprises the following steps:Acrylate polymer emulsion, polyethers are birdsed of the same feather flock together Urethane is well mixed, and adds titanium slag powder, is sufficiently mixed uniformly, is dried, obtain the industrial inorganic powder of coating modification.
A kind of composite of inorganic powder containing modified industry, includes the raw material of following mass parts:Above-mentioned modified industry is inorganic Powder:100 parts;Vinal:2 parts;Methylcellulose:0.5 part;Pigment:2.5 part;Elastic printing paste:10 parts.
The preparation method of the composite of the above-mentioned inorganic powder containing modified industry comprises the following steps:Modified industry is inorganic Powder, vinal, methylcellulose, pigment and elastic printing paste are well mixed, and are added water and are modulated into slurry, are poured in mould It is interior, it is stripped after dry solidification, obtains athletic floor.
Embodiment 5:
A kind of modified industry inorganic powder, includes the raw material of following mass parts:Electroplate ground-slag:100 parts;Redispersible latex Powder:10 parts;Polyether polyurethane:5 parts.
The preparation method of above-mentioned modified industry inorganic powder comprises the following steps:Redispersibility latex powder, polyethers are birdsed of the same feather flock together ammonia Ester is well mixed, and adds plating ground-slag, is sufficiently mixed uniformly, is dried, obtain the industrial inorganic powder of coating modification.
A kind of composite of inorganic powder containing modified industry, includes the raw material of following mass parts:Above-mentioned modified industry is inorganic Powder:100 parts;Vinal:1.5 part;Methylcellulose:1 part;Flexible foaming is starched:15 parts.
The preparation method of the composite of the above-mentioned inorganic powder containing modified industry comprises the following steps:Modified industry is inorganic Powder, vinal, methylcellulose and flexible foaming slurry are well mixed, add water and are modulated into slurry, coat or be poured in mould In tool, it is stripped after dry solidification, obtains athletic tracks.
Embodiment 6:
A kind of modified industry inorganic powder, includes the raw material of following mass parts:Red mud powder:100 parts;Redispersible latex Powder:5 parts;Polyether polyurethane:30 parts.
The preparation method of above-mentioned modified industry inorganic powder comprises the following steps:Redispersible latex powder, polyethers are birdsed of the same feather flock together Urethane is well mixed, and adds red mud powder, is sufficiently mixed uniformly, is dried, obtain the industrial inorganic powder of coating modification.
A kind of composite of inorganic powder containing modified industry, includes the raw material of following mass parts:Above-mentioned modified industry is inorganic Powder:100 parts;Vinal:1 part;Methylcellulose:0.5 part;Pigment:5 parts;Acrylate polymer emulsion:50 parts;It is poly- Ether polyurethane:10 parts.
The preparation method of the composite of the above-mentioned inorganic powder containing modified industry comprises the following steps:Modified industry is inorganic Powder, vinal, methylcellulose, pigment, acrylate polymer emulsion and polyether-polyurethane are well mixed, and add water modulation Into slurry, it is coated in mould, is stripped after dry solidification, obtains section bar.
Embodiment 7:
A kind of modified industry inorganic powder, includes the raw material of following mass parts:Urban construction roach:100 parts;Acrylate copolymer breast Liquid:10 parts;Redispersible latex powder:1 part;Polyether polyurethane:15 parts.
The preparation method of above-mentioned modified industry inorganic powder comprises the following steps:By acrylate polymer emulsion, redispersible Property latex powder, polyether polyurethane be well mixed, add urban construction roach, be sufficiently mixed uniform, dry, obtain coating modification Industrial inorganic powder.
A kind of composite of inorganic powder containing modified industry, includes the raw material of following mass parts:Above-mentioned modified industry is inorganic Powder:100 parts;Vinal:3 parts;Methylcellulose:0.7 part;Pigment:2 parts;Acrylate polymer emulsion:15 parts;It is poly- Ether polyurethane:50 parts.
The preparation method of the composite of the above-mentioned inorganic powder containing modified industry comprises the following steps:Modified industry is inorganic Powder, vinal, methylcellulose, pigment, acrylate polymer emulsion and polyether-polyurethane are well mixed, and add water modulation Into slurry, it is poured in mould, is stripped after dry solidification, obtains section bar.
Test case:
Performance test is carried out to composite prepared by embodiment 1~7, test result is as shown in table 1~3:
The performance test results of the composite of the embodiment 1~3 of table 1
The performance test results of the composite of the embodiment 4~5 of table 2
The performance test results of the composite of the embodiment 6~7 of table 3
Above-described embodiment is preferably embodiment, but embodiments of the present invention are not by above-described embodiment of the invention Limitation, other any Spirit Essences without departing from the present invention and the change made under principle, modification, replacement, combine, simplification, Equivalent substitute mode is should be, is included within protection scope of the present invention.

Claims (10)

1. a kind of modified industry inorganic powder, it is characterised in that:Include the raw material of following mass parts:
Inorganic 100 parts of waste residue powder;
1~10 part of 3~40 parts of acrylate polymer emulsion or/and redispersible latex powder;
3~30 parts of polyether polyurethane.
2. modified industry inorganic powder according to claim 1, it is characterised in that:Described inorganic waste residue powder is tailings Powder, sulfuric acid ground-slag, colliery powder, pitchers powder, chromium ground-slag, titanium slag powder, plating ground-slag, red mud powder, waste stone dust, urban construction roach, water Mud abandons at least one of block powder.
3. modified industry inorganic powder according to claim 1, it is characterised in that:Described acrylate polymer emulsion is consolidated Content is 35%~55%.
4. modified industry inorganic powder according to claim 1, it is characterised in that:The solid content of described polyether polyurethane For 10%~48%.
5. the preparation method of the modified industry inorganic powder in Claims 1 to 4 described in any one, it is characterised in that:Including with Lower step:Acrylate polymer emulsion or/and redispersible latex powder, polyether polyurethane are well mixed, nothing is added Machine waste residue powder, is sufficiently mixed uniformly, dries, obtain the industrial inorganic powder of coating modification.
6. a kind of composite of inorganic powder containing modified industry, it is characterised in that:Include the raw material of following mass parts:
100 parts of modified industry inorganic powder;0~3 part of fiber;0~1 part of methylcellulose;0~5 part of pigment;Active inorganic powder 20 ~60 parts;
Or, 100 parts of modified industry inorganic powder;0~3 part of fiber;0~1 part of methylcellulose;0~5 part of pigment;Flexible polymer 3~60 parts of thing;
Or, 100 parts of modified industry inorganic powder;0~3 part of fiber;0~1 part of methylcellulose;0~5 part of pigment;Acrylic acid gathers 3~60 parts of compound emulsion;1~50 part of polyether-polyurethane.
7. the composite of the inorganic powder according to claim 6 containing modified industry, it is characterised in that:Described fiber is poly- Alcohol fibers.
8. the composite of the inorganic powder according to claim 6 containing modified industry, it is characterised in that:Described active inorganic Powder is granulation electric furnace phosphoric slag powder, granulation water-quenched manganese slag powder, granulation water quenching steel-making slag powder, granulation cinder powder, granulation granulated copper slag powder, It is granulated at least one of water quenching magnesium-reduced ground-slag, granulation nickel ground-slag, cement.
9. the composite of the inorganic powder according to claim 8 containing modified industry, it is characterised in that:Described active inorganic The specific surface area of powder is not less than 410m2/kg。
10. the composite of the inorganic powder according to claim 6 containing modified industry, it is characterised in that:Described elasticity is gathered Compound is at least one of elastic printing paste, flexible foaming slurry.
CN201710432380.XA 2017-06-09 2017-06-09 A kind of composite material of modified industry inorganic powder and the inorganic powder containing modified industry Active CN107311505B (en)