CN107311470A - A kind of Multifunctional straight print formula coating heats glass and its manufacture method - Google Patents
A kind of Multifunctional straight print formula coating heats glass and its manufacture method Download PDFInfo
- Publication number
- CN107311470A CN107311470A CN201710479463.4A CN201710479463A CN107311470A CN 107311470 A CN107311470 A CN 107311470A CN 201710479463 A CN201710479463 A CN 201710479463A CN 107311470 A CN107311470 A CN 107311470A
- Authority
- CN
- China
- Prior art keywords
- glass
- layer
- minutes
- heats
- heating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention is that a kind of Multifunctional straight print formula coating heats glass and its manufacture method, this heats the layer structure that glass is multilayer, in the surface of glass basis (1) successively printing decorative layer (2) by way of silk-screen printing on glass basis (1), heating layer (3), current carrying layer (4), insulating barrier (5) and anticorrosive coat (6), wherein current carrying layer (4) is not completely covered by insulating barrier (5) and anticorrosive coat (6), its both sides is exposed independent from one section and gives over to electrode, current carrying layer (4) is set to be connected with power supply (7), heating layer (3) is just heatable, the present invention is a kind of high thermal effect, low cost, Environmental Safety, simple installation, it is not take up space, it is easy to the one kind for embodying 3D stereoeffects to heat glass.
Description
Technical field
The present invention relates to a kind of structure of heating glass and manufacture method, specifically one kind is mainly used in family, hotel, doctor
The electric energy such as institute, sauna house change into the glass that the heating and decoration of heat energy are integrated.
Background technology
In the prior art, indoor heating includes various mode, for example:
Boiler heating installation is warmed oneself:
Have the disadvantage:It is used for a long time, easily causes indoor environment drying, makes one to feel that air is dull uncomfortable, the temperature of heating
Do not controlled with the time by oneself, three-dimensional fin unsightly, take up space, indoor finishing effect is influenceed, during heating
It is front and rear without thermal source, the leaving water temperature of fin heating is about more than 70 degrees Celsius, but when the temperature of fin reaches 80 degree
When will produce grey sludge pellet, make the metope above radiator be covered with dust all over and heat supply it is unbalanced, some heat, what is had is cold, not side
Just adjust, gradually replaced in house by floor heating.
Heated water re-circulation's device is warmed oneself:
Have the disadvantage:Programming rate is slow, normal need 4-6 hours, it is impossible to Discrete control;Wall-mounted heating stove service life
In l5 or so, updating maintenance cost will be undertaken by owner;Family in nobody when, it is necessary to retain the cold operation of 4 degrees centigrades
(antifreeze effect);Heat pump starts and flame combustion, and noise is larger, and there is certain air pollution problems inherent.
Spontaneous heating ceramic tile device is warmed oneself:
It is a kind of electro-heat equipment that a kind of PET electrothermal films are pasted onto below ceramic tile
Have the disadvantage:Need that PET Electric radiant Heating Films and ceramic tile are sticked together with glue, bring that cost of manufacture is high, it is inconvenient to install,
Contain formaldehyde in glue.
Self-heating wood floor device is warmed oneself:
It is a kind of electro-heat equipment that a kind of carbon fiber cable is clipped in the middle of timber floor
Have the disadvantage:Typically all use wood floors or plastic floor or composite floor board, the formaldehyde having in these floors
Content overproof, some installation safeguards heavy, and some costs are high, and some installation specifications are high, and there is potential safety hazard,
Conductive obstructed and plate face not acid and alkali-resistance, road surface crocking the problems such as.
Although above-mentioned several ways serve good heating effect, but the thermal losses that above-mentioned heating mode has is high, consumption
Electricity is more, and service life is short, or even electric leakage, there is potential safety hazard.So the heating heating installation used at present is necessary to be changed
Enter, to meet high thermal effect, low cost, Environmental Safety, demand elegant in appearance.
The content of the invention
Technical problem:The technical problems to be solved by the invention are to provide that a kind of Environmental Safety, manufacturing process be simple, system
Cause a uniform low, conductive exothermal, the heating of ultra-thin body, Ultralight, be easy to show the Multifunctional straight print formula coating of 3D stereoeffects
Heat glass and its manufacture method.
Technical scheme:To achieve these goals, the present invention is achieved through the following technical solutions:It is characterized in that in glass
It is printed on decorative layer, heating layer, current carrying layer, insulating barrier and anticorrosive coat on glass matrix successively by way of printing.In energization situation
Under, the far red light that wavelength is 8-15 microns can be sent, approximate solar spectrum is easy to absorption of human body, beneficial health.
A kind of Multifunctional straight print formula coating of the present invention heats glass, and this heats the layer structure that glass is multilayer, in glass
The surface of glass matrix is sequentially provided with decorative layer, heating layer, current carrying layer, insulating barrier and anticorrosive coat.
Described decorative layer is a kind of coloured coating of the acrylic resin modified ink of wire mark type, decoration glass front
Outward appearance, covers the carbon slurry coating that simultaneously support is heated.
The heating layer is a kind of wire mark type conductive carbon paste ink, and effect can generate heat after being switched on, and its figure that generates heat is adopted
With go here and there and combine it is latticed, its firing rate is fast, radiating is uniform, and coating local defect or short circuit do not influence overall to heat effect
Really.
The current carrying layer is a kind of solderable conductive copper paste ink of wire mark type, and effect is to provide electric current for heating layer, its property
Energy conductive capability is good, durable, water-fast, resistance to oxidation, hardness are high, fastness is good, can weld.
The insulating barrier is a kind of wire mark type dielectric ink, for protecting heating layer, preventing from leaking electricity, ensure safety.
The anticorrosive coat is a kind of wire mark type epoxy resin-matrix ink, for other printing layers of covering protection.
The current carrying layer is not completely covered by insulating barrier and anticorrosive coat, and its both sides is exposed independent from giving over to the part of electrode, energy
It is connected with power supply.
The Multifunctional straight print formula coating of the present invention heats the manufacture method of glass, by silk-screen printing side on glass basis
Formula printing decorative layer, heating layer, current carrying layer, insulating barrier and anticorrosive coat successively, specific printing method is:
Step 1.a, cutting, according to technical requirements, cutting glass is carried out with computer cutter's table;B, edge trimming, according to technology
It is required that, using linear edge grinder can two-sided grinding equipment to product carry out edge trimming, glass edge through roughly grind chamfered edge, fine grinding fall
Enter after rib, fine-grinding and polishing chamfered edge, corase grind round edge, corase grind round edge, the processing of corner round edge and develop a film process, after washing through tempering in case
With;C. tempering is handled:According to technical requirements, tempering processing is carried out to glass using annealing furnace, during tempering processing, cooling wind pressure:
7KPa-13KPa;Heat time:100-180 seconds/stove;Cool time:20-50 seconds;Chilling period:20-40 seconds;Ensure product
Flatness, granularity;
Step 2.a, with glass basis 1 be base material according to the color confirmed in glass surface printed decoration pattern, then print whole
Face confirms color and is protected by the background color of product, and the next process progress that will be allowed for access after drying is printed each time
Printing;B, drying:According to the good drying time of Properties Control of the black institute's spent material of synthesis and the drying temperature of setting, warm area is dried
At 120 degree Celsius~200 degree, drying time at 10 minutes~15 minutes,
The far infrared heating carbon that step 3. mixes up resistance is starched passes through printing machine even print with the half tone of 100~200 mesh
In the bottom of decorative layer 2, then dry, drying temperature at 150 degree Celsius~200 degree, drying time at 10 minutes~15 minutes,
Step 4. by solderable conductive copper paste with the half tone of 100~200 mesh by printing machine even print at the bottom of heating layer 3
Portion, is then dried, drying temperature at 150 degree Celsius~200 degree, drying time at 10 minutes~15 minutes,
Step 5. by dielectric ink with the half tones of 100~250 mesh by printing machine even print in the bottom of current carrying layer 4, so
After dry, drying temperature at 150 degree Celsius~200 degree, drying time at 10 minutes~15 minutes,
Step 6. will protect the black half tone with 100~250 mesh of base oil by printing machine even print in the bottom of insulating barrier 5,
Then dry, drying temperature is at 120 degree Celsius~200 degree, and drying time was at 10 minutes~15 minutes.
Beneficial effect:The present invention has the advantage of various heating installations concurrently, and solves in the past by diaphragm stickup, cable sandwich
Carry out heating service device etc. complicated procedures of forming, it, which also has, is easy to show 3D stereoeffects, intensity in clear glass substrate positive and negative
Many advantages, such as height, environmental protection and energy saving, low cost, the raising to people's quality of life, saving the energy, there is provided good a kind of existing
It is the developing direction of following heating installation for product.
Brief description of the drawings
The present invention is further illustrated below in conjunction with the accompanying drawings.
Fig. 1 is that Multifunctional straight of the present invention prints the structural representation that formula coating heats glass.
Fig. 2 is structural representation of the heating layer 3 using the latticed circuit gone here and there and combined.
Have in figure:Glass basis 1, decorative layer 2, heating layer 3, current carrying layer 4, insulating barrier 5, anticorrosive coat 6, power supply 7.
Embodiment
Embodiment:Step 1. is clean by the glass cleaning of the good corner angle in milled side;Clean glass is passed through 650 by step 2.
Degree Celsius annealing furnace tempering;Step 3. stamps decorative layer in the Glass base that tempering is crossed, and is placed on 200 degrees Celsius of infrared bakings
Walked in stove 10-15 minutes;Step 4. stamps heating layer in the bottom of decorative layer, is placed in 200 degrees Celsius of infrared drying stoves
10-15 minutes;In order to allow this block glass surface temperature to reach required temperature, so the sheet resistance of adjustment nano-graphite is come in printing
Ensure the heating layer resistance on glass to reach required heating power, heating figure uses connection in series-parallel, makes surface heating rates fast,
Heating is uniform, such as Fig. 2;Step 5. stamps current carrying layer in heating layer bottom, is placed in 200 degrees Celsius of infrared drying stoves and walks 10-
15 minutes;Step 6. stamps insulating barrier in current carrying layer bottom, is placed in 200 degrees Celsius of infrared drying stoves to walk 10-15 minutes;Step
Rapid 7. stamp anticorrosive coat in insulating barrier bottom, are placed in 200 degrees Celsius of infrared drying stoves to walk 10-15 minutes;This kind of glass is only
It is one of which case study on implementation, both house can be decorated with heating service again.
The present invention suitable each hospitals of family hotels, sauna house etc. are used, easy to use, effective when temperature is not enough indoors
Ground helps people's heating, improves the ice-cold defect of ceramic tile, wall brick, while also playing decoration function, gives people life and bring
It is convenient and attractive in appearance.
Above-described embodiment is not as a limitation of the invention, all modifications made within the scope of the present invention, improvement, equally replaces
Change and belong to the scope of protection of the invention.
Claims (8)
1. a kind of Multifunctional straight print formula coating heats glass, it is characterised in that this heats the layer structure that glass is multilayer, in glass
Glass matrix(1)Surface be sequentially provided with decorative layer(2), heating layer(3), current carrying layer(4), insulating barrier(5)And anticorrosive coat(6).
2. a kind of Multifunctional straight print formula coating according to claim 1 heats glass, it is characterized in that:Described decorative layer
(2)It is a kind of coloured coating of the acrylic resin modified ink of wire mark type, decoration glass front outward appearance is covered and support system
The carbon slurry coating of heat.
3. a kind of Multifunctional straight print formula coating according to claim 1 heats glass, it is characterized in that:The heating layer(3)
It is a kind of wire mark type conductive carbon paste ink, effect can generate heat after being switched on, it is latticed that its figure that generates heat uses string and combined,
Its firing rate is fast, radiating is uniform, and coating local defect or short circuit do not influence overall heating effect.
4. a kind of Multifunctional straight print formula coating according to claim 1 heats glass, it is characterized in that:The current carrying layer(4)
It is a kind of solderable conductive copper paste ink of wire mark type, effect is to provide electric current for heating layer, its performance conductive capability is good, durable,
Water-fast, resistance to oxidation, hardness are high, fastness is good, can weld.
5. a kind of Multifunctional straight print formula coating according to claim 1 heats glass, it is characterized in that:The insulating barrier(5)
It is a kind of wire mark type dielectric ink, for protecting heating layer, preventing from leaking electricity, ensure safety.
6. a kind of Multifunctional straight print formula coating according to claim 1 heats glass, it is characterized in that:The anticorrosive coat(6)
It is a kind of wire mark type epoxy resin-matrix ink, for other printing layers of covering protection.
7. a kind of Multifunctional straight print formula coating according to claim 1 heats glass, it is characterized in that:The current carrying layer(4)
Not by insulating barrier(5)And anticorrosive coat(6)It is completely covered, its both sides is exposed independent from giving over to the part of electrode, energy and power supply(7)Even
Connect.
8. a kind of Multifunctional straight print formula coating as claimed in claim 1 heats the manufacture method of glass, it is characterized in that:In glass
Matrix(1)It is upper to pass through screen printing mode successively printing decorative layer(2), heating layer(3), current carrying layer(4), insulating barrier(5)With it is anti-
Rotten layer(6), specific printing method is:
Step 1. a, cutting, according to technical requirements, cutting glass is carried out with computer cutter's table;B, edge trimming, will according to technology
Ask, using linear edge grinder can two-sided grinding equipment to product carry out edge trimming, glass edge through roughly grind chamfered edge, fine grinding chamfered edge,
Enter process of developing a film after fine-grinding and polishing chamfered edge, corase grind round edge, corase grind round edge, the processing of corner round edge, through tempering with standby after washing;
C. tempering is handled:According to technical requirements, tempering processing is carried out to glass using annealing furnace, during tempering processing, cooling wind pressure:
7KPa-13KPa;Heat time:100-180 seconds/stove;Cool time:20-50 seconds;Chilling period:20-40 seconds;Ensure product
Flatness, granularity;
Step 2. a, with glass basis 1 be base material according to the color confirmed in glass surface printed decoration pattern, then to print whole face true
Recognize color and be protected by the background color of product, the next process that will be allowed for access after drying is printed each time and is printed
Brush;B, drying:According to the good drying time of Properties Control of the black institute's spent material of synthesis and the drying temperature of setting, warm area is dried
At 120 degree Celsius~200 degree, drying time at 10 minutes~15 minutes,
The far infrared heating carbon slurry that step 3. mixes up resistance is with the half tone of 100~200 mesh by printing machine even print in dress
Adorn layer 2 bottom, then dry, drying temperature at 150 degree Celsius~200 degree, drying time at 10 minutes~15 minutes,
Step 4. by solderable conductive copper paste with the half tone of 100~200 mesh by printing machine even print in the bottom of heating layer 3,
Then dry, drying temperature at 150 degree Celsius~200 degree, drying time at 10 minutes~15 minutes,
Step 5. by dielectric ink with the half tone of 100~250 mesh by printing machine even print in the bottom of current carrying layer 4, then dry
It is dry, drying temperature at 150 degree Celsius~200 degree, drying time at 10 minutes~15 minutes,
Step 6. will protect base oil ink with the half tones of 100~250 mesh by printing machine even print in the bottom of insulating barrier 5, then
Drying, drying temperature is at 120 degree Celsius~200 degree, and drying time was at 10 minutes~15 minutes.