CN107299533A - A kind of preparation method of potted plant automatic water supplement water suction cotton thread - Google Patents
A kind of preparation method of potted plant automatic water supplement water suction cotton thread Download PDFInfo
- Publication number
- CN107299533A CN107299533A CN201710619357.1A CN201710619357A CN107299533A CN 107299533 A CN107299533 A CN 107299533A CN 201710619357 A CN201710619357 A CN 201710619357A CN 107299533 A CN107299533 A CN 107299533A
- Authority
- CN
- China
- Prior art keywords
- cotton thread
- water suction
- preparation
- water
- potted plant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of potted plant automatic water supplement preparation method of water suction cotton thread, it is related to potted plant growth technical field, comprises the following steps：(1) cotton thread is soaked, and (2) cotton thread drying, (3) cotton thread spraying, (4) cotton thread is twisted together, the cutting of (5) cotton thread.The present invention is by carrying out water suction enhancing processing and mould proof processing to cotton thread, to assign the water absorbing properties and fungicidal properties that made water suction cotton thread is excellent；And the use of liquid and mould inhibitor is strengthened by the water suction, the water suction stability and mould proof stability of water suction cotton thread is improved.
Description
Technical field：
The present invention relates to potted plant growth technical field, and in particular to a kind of system of potted plant automatic water supplement water suction cotton thread
Preparation Method.
Background technology：
It is potted plant, it is a kind of distinctive cultural method of flower gardening, refers to cultivate various flowers with flowerpot, make flowers in flowerpot
Middle normal development, yield positive results, meet people and demand is viewed and admired to flowers.Potted plant bucket is used as flowers Potted-plant container, its structure, matter
The factor such as ground and size directly affects the various physiological activities of flowers.
With people's living standard and household, office and the continuous improvement of PE, consumption of the people to pot flowers
Demand develops to light direction；And with the continuous quickening of modern life rhythm, many people in planting pot often
There is no the excessive time to go to look after to potted plant, unlikely potted plant realization is periodically watered.Therefore, in the market starts to release
Automatic water absorbing type potting, using absorbent material from Potted-plant container bottom automatic ink-suction, so that can ensure after once watering potted plant
Plant can meet growth demand within some time by automatic ink-suction.
Water suction cotton thread belongs to a kind of most common absorbent material, is formed by multiply cotton thread is twisted, cheap.But it is this by
The water absorbing capacity that pure cotton fiber processes made cotton thread is limited, and its water absorbing capacity is gradually reduced with the extension of use time, together
There is the phenomenon that cotton thread goes mouldy and rotted in Shi Rongyi, so that preferable soaking effect can not be played, influences the normal of potted plant
Growth.
The content of the invention：
The technical problems to be solved by the invention are to provide a kind of raising water suction stability, prevent the putrefactive phenomenon hair that goes mouldy
The preparation method of the raw potted plant automatic water supplement water suction cotton thread to ensure water absorbing properties.
The technical problems to be solved by the invention are realized using following technical scheme：
A kind of potted plant automatic water supplement preparation method of water suction cotton thread, comprises the following steps：
(1) cotton thread soaks：First cotton thread is immersed in 40-50 DEG C of warm water, taken out after 10-15min, then cotton thread is transferred to
In 40-50 DEG C of water suction enhancing liquid, taken out after immersion 5-10min；
(2) cotton thread is dried：Cotton thread after soaking processing is separated one by one, and slowly dried in 55-65 DEG C of environment
It is dry, until cotton thread water content is less than 5%；
(3) cotton thread is sprayed：Cotton thread after drying is handled constantly is rubbing the ethanol solution of lower penetrating mould inhibitor, and
Volatilized naturally under room temperature condition；
(4) cotton thread is twisted together：Cotton thread after 3-5 stock-traders' know-how spraying treatments is formed into water suction cotton thread by being uniformly twisted together；
(5) cotton thread is cut：Above-mentioned made water suction cotton thread is cut into different length according to use demand, is then installed on double
In layer Potted-plant container, so that potted plant is from container bottom automatic sucking moisture.
Cotton thread, the quality amount ratio of mould inhibitor are 20-25 in the step (3):0.1-0.5.
The water suction enhancing liquid is made up of the raw material of following parts by weight：Poly-aspartic-acid/poly glycol monomethyl ether 10-
15 parts, 5-10 parts of hydroxyethyl cellulose, 0.5-2 parts of molecular sieve micro mist, 0.5-2 parts of polyethylene glycol oxide, rilanit special 0.05-
0.5 part, 0.05-0.5 parts of hexamethylolmelamine pregnancy ether, 80-120 parts of deionized water, its preparation method is：Under grinding to
Deionized water is added dropwise until being completely dissolved in hydroxyethyl cellulose, adds polyethylene glycol oxide and rilanit special, is warming up to back
In stream mode insulation mixing 30min, gained mixed liquor feeding spray dryer, dry gained particle is made micro- through micronizer
Powder, produces modified hydroxyethylcellulosadsorbing；Poly-aspartic-acid/poly glycol monomethyl ether and six hydroxyls are added into remaining deionized water
Methyl melamine pregnancy ether, is warming up to reflux state insulation mixing 15min, adds after naturally cool to after room temperature after being sufficiently mixed
Enter in modified hydroxyethylcellulosadsorbing and molecular sieve micro mist, gained mixture feeding ball mill, be milled to discharging-material size less than 30 μm.
The molecular sieve micro mist is made by the modified processing of molecular screen primary powder, and its specific preparation method is：By molecular sieve
Former powder takes out after naturally cool to after 110-120 DEG C in being calcined 2h at 500-550 DEG C, adds polyglutamic acid and ethylene glycol
Diglycidyl ether, and in insulation mixing 30min at 110-120 DEG C, gained mixture sends into sealing and standing in -15 DEG C of environment
3h, is finally made micro mist using micronizer, produces molecular sieve micro mist.
The molecular screen primary powder, polyglutamic acid, the quality amount ratio of ethylene glycol diglycidylether are 1-5:0.1-1:
0.05-0.5。
The mould inhibitor is formed by mould proof composition through carrier loaded, and its specific preparation method is：By chili meal point under stirring
Dissipate in deionized water, stand and microcrystalline cellulose and N hydroxymethyl acrylamide, grinding at room temperature 15min, gained are added after 5min
In mixture feeding freeze drier, dry gained solid and micro mist is made through micronizer, produce mould inhibitor.
The chili meal, deionized water, microcrystalline cellulose, the quality amount ratio of N hydroxymethyl acrylamide are 0.5-2:
10-20:1-10:0.05-0.5。
The beneficial effects of the invention are as follows：The present invention is by carrying out water suction enhancing processing and mould proof processing to cotton thread, to assign
Made water suction cotton thread excellent water absorbing properties and fungicidal properties；And the use of liquid and mould inhibitor is strengthened by the water suction, carried
The water suction stability and mould proof stability of high water absorption cotton thread, it is ensured that the water absorbing properties for the cotton thread that absorbed water in service life, to meet
The growth demand of potted plant, while extending its service life by preventing water suction cotton thread from going mouldy and rotting.
Embodiment：
In order that the technical means, the inventive features, the objects and the advantages of the present invention are easy to understand, tie below
Specific embodiment is closed, the present invention is expanded on further.
Embodiment 1
(1) cotton thread soaks：First cotton thread is immersed in 40-50 DEG C of warm water, taken out after 10min, then cotton thread is transferred to 40-50
DEG C water suction enhancing liquid in, immersion 10min after take out；
(2) cotton thread is dried：Cotton thread after soaking processing is separated one by one, and slowly dried in 55-65 DEG C of environment
It is dry, until cotton thread water content is less than 5%；
(3) cotton thread is sprayed：Cotton thread after drying is handled constantly is rubbing the ethanol solution of lower penetrating mould inhibitor, and
Volatilized naturally under room temperature condition；Wherein cotton thread quality 20g, mould inhibitor quality 0.5g；
(4) cotton thread is twisted together：Cotton thread after 5 stock-traders' know-how spraying treatments is formed into water suction cotton thread by being uniformly twisted together；
(5) cotton thread is cut：Above-mentioned made water suction cotton thread is cut into different length according to use demand, is then installed on double
In layer Potted-plant container, so that potted plant is from container bottom automatic sucking moisture.
The preparation of water suction enhancing liquid：Deionized water is added dropwise until being completely dissolved into 10g hydroxyethyl celluloses under grinding, then
0.8g polyethylene glycol oxides and 0.1g rilanit specials are added, reflux state insulation mixing 30min, gained mixed liquor feeding is warming up to
In spray dryer, dry gained particle and micro mist is made through micronizer, produce modified hydroxyethylcellulosadsorbing；To residue go from
15g poly-aspartic-acids/poly glycol monomethyl ether and 0.2g hexamethylolmelamine pregnancy ethers are added in sub- water, is sufficiently mixed
After be warming up to reflux state insulation mixing 15min, after naturally cool to adding modified hydroxyethylcellulosadsorbing and 0.5g points after room temperature
In son sieve micro mist, gained mixture feeding ball mill, discharging-material size is milled to less than 30 μm；The wherein total consumption of deionized water
120g。
The preparation of molecular sieve micro mist：By 5g molecular screen primary powders in being calcined 2h at 500-550 DEG C, after naturally cool to 110-
Taken out after 120 DEG C, add 0.3g polyglutamic acids and 0.05g ethylene glycol diglycidylethers, and in insulation at 110-120 DEG C
30min is mixed, gained mixture sends into sealing and standing 3h in -15 DEG C of environment, micro mist finally is made using micronizer, produces
Molecular sieve micro mist.
The preparation of mould inhibitor：1g chili meals are scattered in 20g deionized waters under stirring, addition 10g after 5min are stood micro-
In crystalline cellulose and 0.2g N hydroxymethyl acrylamides, grinding at room temperature 15min, gained mixture feeding freeze drier, dry
Micro mist is made through micronizer in gained solid, produces mould inhibitor.
Embodiment 2
(1) cotton thread soaks：First cotton thread is immersed in 40-50 DEG C of warm water, taken out after 15min, then cotton thread is transferred to 40-50
DEG C water suction enhancing liquid in, immersion 10min after take out；
(2) cotton thread is dried：Cotton thread after soaking processing is separated one by one, and slowly dried in 55-65 DEG C of environment
It is dry, until cotton thread water content is less than 5%；
(3) cotton thread is sprayed：Cotton thread after drying is handled constantly is rubbing the ethanol solution of lower penetrating mould inhibitor, and
Volatilized naturally under room temperature condition；Wherein cotton thread quality 25g, mould inhibitor quality 0.5g；
(4) cotton thread is twisted together：Cotton thread after 5 stock-traders' know-how spraying treatments is formed into water suction cotton thread by being uniformly twisted together；
(5) cotton thread is cut：Above-mentioned made water suction cotton thread is cut into different length according to use demand, is then installed on double
In layer Potted-plant container, so that potted plant is from container bottom automatic sucking moisture.
The preparation of water suction enhancing liquid：Deionized water is added dropwise until being completely dissolved into 8g hydroxyethyl celluloses under grinding, then
0.5g polyethylene glycol oxides and 0.05g rilanit specials are added, reflux state insulation mixing 30min is warming up to, gained mixed liquor is sent
Enter in spray dryer, dry gained particle and micro mist is made through micronizer, produce modified hydroxyethylcellulosadsorbing；Gone to residue
15g poly-aspartic-acids/poly glycol monomethyl ether and 0.1g hexamethylolmelamine pregnancy ethers are added in ionized water, it is fully mixed
Reflux state insulation mixing 15min is warming up to after conjunction, after naturally cool to addition modified hydroxyethylcellulosadsorbing and 0.5g after room temperature
In molecular sieve micro mist, gained mixture feeding ball mill, discharging-material size is milled to less than 30 μm；The wherein total consumption of deionized water
80g。
The preparation of molecular sieve micro mist：By 5g molecular screen primary powders in being calcined 2h at 500-550 DEG C, after naturally cool to 110-
Taken out after 120 DEG C, add 0.5g polyglutamic acids and 0.1g ethylene glycol diglycidylethers, and in insulation at 110-120 DEG C
30min is mixed, gained mixture sends into sealing and standing 3h in -15 DEG C of environment, micro mist finally is made using micronizer, produces
Molecular sieve micro mist.
The preparation of mould inhibitor：0.5g chili meals are scattered in 10g deionized waters under stirring, addition 5g after 5min are stood micro-
In crystalline cellulose and 0.1g N hydroxymethyl acrylamides, grinding at room temperature 15min, gained mixture feeding freeze drier, dry
Micro mist is made through micronizer in gained solid, produces mould inhibitor.
Reference examples 1
(1) cotton thread soaks：First cotton thread is immersed in 40-50 DEG C of warm water, taken out after 15min, then cotton thread is transferred to 40-50
DEG C water suction enhancing liquid in, immersion 10min after take out；
(2) cotton thread is dried：Cotton thread after soaking processing is separated one by one, and slowly dried in 55-65 DEG C of environment
It is dry, until cotton thread water content is less than 5%；
(3) cotton thread is sprayed：Cotton thread after drying is handled constantly is rubbing the ethanol solution of lower penetrating mould inhibitor, and
Volatilized naturally under room temperature condition；Wherein cotton thread quality 25g, mould inhibitor quality 0.5g；
(4) cotton thread is twisted together：Cotton thread after 5 stock-traders' know-how spraying treatments is formed into water suction cotton thread by being uniformly twisted together；
(5) cotton thread is cut：Above-mentioned made water suction cotton thread is cut into different length according to use demand, is then installed on double
In layer Potted-plant container, so that potted plant is from container bottom automatic sucking moisture.
The preparation of water suction enhancing liquid：Deionized water is added dropwise until being completely dissolved into 8g hydroxyethyl celluloses under grinding, then
0.5g polyethylene glycol oxides and 0.05g rilanit specials are added, reflux state insulation mixing 30min is warming up to, gained mixed liquor is sent
Enter in spray dryer, dry gained particle and micro mist is made through micronizer, produce modified hydroxyethylcellulosadsorbing；Gone to residue
15g poly-aspartic-acids/poly glycol monomethyl ether and 0.1g hexamethylolmelamine pregnancy ethers are added in ionized water, it is fully mixed
Reflux state insulation mixing 15min is warming up to after conjunction, after naturally cool to addition modified hydroxyethylcellulosadsorbing and 0.5g after room temperature
In molecular screen primary powder, gained mixture feeding ball mill, discharging-material size is milled to less than 30 μm；The wherein total consumption of deionized water
80g。
The preparation of mould inhibitor：0.5g chili meals are scattered in 10g deionized waters under stirring, addition 5g after 5min are stood micro-
In crystalline cellulose and 0.1g N hydroxymethyl acrylamides, grinding at room temperature 15min, gained mixture feeding freeze drier, dry
Micro mist is made through micronizer in gained solid, produces mould inhibitor.
Reference examples 2
(1) cotton thread soaks：First cotton thread is immersed in 40-50 DEG C of warm water, taken out after 15min, then cotton thread is transferred to 40-50
DEG C water suction enhancing liquid in, immersion 10min after take out；
(2) cotton thread is dried：Cotton thread after soaking processing is separated one by one, and slowly dried in 55-65 DEG C of environment
It is dry, until cotton thread water content is less than 5%；
(3) cotton thread is sprayed：Cotton thread after drying is handled constantly is rubbing the ethanol solution of lower penetrating mould inhibitor, and
Volatilized naturally under room temperature condition；Wherein cotton thread quality 25g, mould inhibitor quality 0.5g；
(4) cotton thread is twisted together：Cotton thread after 5 stock-traders' know-how spraying treatments is formed into water suction cotton thread by being uniformly twisted together；
(6) cotton thread is cut：Above-mentioned made water suction cotton thread is cut into different length according to use demand, is then installed on double
In layer Potted-plant container, so that potted plant is from container bottom automatic sucking moisture.
The preparation of water suction enhancing liquid：15g poly-aspartic-acids/poly glycol monomethyl ether and 0.1g are added into deionized water
Hexamethylolmelamine pregnancy ether, is warming up to reflux state insulation mixing 15min, after naturally cool to room temperature after being sufficiently mixed
Add afterwards in 8g hydroxyethyl celluloses and 0.5g molecular sieve micro mists, gained mixture feeding ball mill, be milled to discharging-material size small
In 30 μm；The wherein total consumption 80g of deionized water.
The preparation of molecular sieve micro mist：By 5g molecular screen primary powders in being calcined 2h at 500-550 DEG C, after naturally cool to 110-
Taken out after 120 DEG C, add 0.5g polyglutamic acids and 0.1g ethylene glycol diglycidylethers, and in insulation at 110-120 DEG C
30min is mixed, gained mixture sends into sealing and standing 3h in -15 DEG C of environment, micro mist finally is made using micronizer, produces
Molecular sieve micro mist.
The preparation of mould inhibitor：0.5g chili meals are scattered in 10g deionized waters under stirring, addition 5g after 5min are stood micro-
In crystalline cellulose and 0.1g N hydroxymethyl acrylamides, grinding at room temperature 15min, gained mixture feeding freeze drier, dry
Micro mist is made through micronizer in gained solid, produces mould inhibitor.
Reference examples 3
(1) cotton thread soaks：First cotton thread is immersed in 40-50 DEG C of warm water, taken out after 15min, then cotton thread is transferred to 40-50
DEG C water suction enhancing liquid in, immersion 10min after take out；
(2) cotton thread is dried：Cotton thread after soaking processing is separated one by one, and slowly dried in 55-65 DEG C of environment
It is dry, until cotton thread water content is less than 5%；
(3) cotton thread is sprayed：Cotton thread after drying is handled constantly is rubbing the ethanol solution of lower penetrating mould inhibitor, and
Volatilized naturally under room temperature condition；Wherein cotton thread quality 25g, mould inhibitor quality 0.5g；
(4) cotton thread is twisted together：Cotton thread after 5 stock-traders' know-how spraying treatments is formed into water suction cotton thread by being uniformly twisted together；
(5) cotton thread is cut：Above-mentioned made water suction cotton thread is cut into different length according to use demand, is then installed on double
In layer Potted-plant container, so that potted plant is from container bottom automatic sucking moisture.
The preparation of water suction enhancing liquid：Deionized water is added dropwise until being completely dissolved into 8g hydroxyethyl celluloses under grinding, then
0.5g polyethylene glycol oxides and 0.05g rilanit specials are added, reflux state insulation mixing 30min is warming up to, gained mixed liquor is sent
Enter in spray dryer, dry gained particle and micro mist is made through micronizer, produce modified hydroxyethylcellulosadsorbing；Gone to residue
15g poly-aspartic-acids/poly glycol monomethyl ether and 0.1g hexamethylolmelamine pregnancy ethers are added in ionized water, it is fully mixed
Reflux state insulation mixing 15min is warming up to after conjunction, after naturally cool to addition modified hydroxyethylcellulosadsorbing and 0.5g after room temperature
In molecular sieve micro mist, gained mixture feeding ball mill, discharging-material size is milled to less than 30 μm；The wherein total consumption of deionized water
80g。
The preparation of molecular sieve micro mist：By 5g molecular screen primary powders in being calcined 2h at 500-550 DEG C, after naturally cool to 110-
Taken out after 120 DEG C, add 0.5g polyglutamic acids and 0.1g ethylene glycol diglycidylethers, and in insulation at 110-120 DEG C
30min is mixed, gained mixture sends into sealing and standing 3h in -15 DEG C of environment, micro mist finally is made using micronizer, produces
Molecular sieve micro mist.
The preparation of mould inhibitor：0.5g chili meals are scattered in 10g deionized waters under stirring, grinding at room temperature after 5min is stood
In 15min, gained mixture feeding freeze drier, dry gained solid and micro mist is made through micronizer, produce mould inhibitor.
Reference examples 4
(1) cotton thread soaks：First cotton thread is immersed in 40-50 DEG C of warm water, taken out after 15min；
(2) cotton thread is dried：Cotton thread after soaking processing is separated one by one, and slowly dried in 55-65 DEG C of environment
It is dry, until cotton thread water content is less than 5%；
(3) cotton thread is sprayed：Cotton thread after drying is handled constantly is rubbing the ethanol solution of lower penetrating mould inhibitor, and
Volatilized naturally under room temperature condition；Wherein cotton thread quality 25g, mould inhibitor quality 0.5g；
(4) cotton thread is twisted together：Cotton thread after 5 stock-traders' know-how spraying treatments is formed into water suction cotton thread by being uniformly twisted together；
(5) cotton thread is cut：Above-mentioned made water suction cotton thread is cut into different length according to use demand, is then installed on double
In layer Potted-plant container, so that potted plant is from container bottom automatic sucking moisture.
The preparation of mould inhibitor：0.5g chili meals are scattered in 10g deionized waters under stirring, addition 5g after 5min are stood micro-
In crystalline cellulose and 0.1g N hydroxymethyl acrylamides, grinding at room temperature 15min, gained mixture feeding freeze drier, dry
Micro mist is made through micronizer in gained solid, produces mould inhibitor.
Embodiment 3
Embodiment 1, embodiment 2, reference examples 1, reference examples 2, reference examples 3, the made water suction cotton thread of reference examples 4 are carried out respectively
Performance is tested, as a result as shown in table 1.
Water absorbing properties test condition：Equivalent water suction cotton thread is soaked in water, taken after 20 groups of parallel test groups, 5min are set
Go out, determine its water absorption rate first；Continue water suction cotton thread being soaked in water, taken out after 3 months, determine its water absorption rate after 3 months；
Continue water suction cotton thread being soaked in water, taken out after 6 months, determine its water absorption rate after 6 months.
Fungicidal properties test condition：Cotton thread is absorbed water to mould of the same race progress inhibiting rate and the immersion in water first using equivalent
Tested after 6 months.
The performance of the made water suction cotton thread of the embodiment of the present invention of table 1
The general principle and principal character and advantages of the present invention of the present invention has been shown and described above.The technology of the industry
Personnel are it should be appreciated that the present invention is not limited to the above embodiments, and the simply explanation described in above-described embodiment and specification is originally
The principle of invention, without departing from the spirit and scope of the present invention, various changes and modifications of the present invention are possible, these changes
Change and improvement all fall within the protetion scope of the claimed invention.The claimed scope of the invention by appended claims and its
Equivalent thereof.
Claims (7)
1. a kind of preparation method of potted plant automatic water supplement water suction cotton thread, it is characterised in that：Comprise the following steps：
(1) cotton thread soaks：First cotton thread is immersed in 40-50 DEG C of warm water, taken out after 10-15min, then cotton thread is transferred to 40-50
DEG C water suction enhancing liquid in, immersion 5-10min after take out；
(2) cotton thread is dried：Cotton thread after soaking processing is separated one by one, and slowly dried in 55-65 DEG C of environment, directly
It is less than 5% to cotton thread water content；
(3) cotton thread is sprayed：Cotton thread after drying is handled constantly is rubbing the ethanol solution of lower penetrating mould inhibitor, and in room temperature
Under the conditions of volatilize naturally；
(4) cotton thread is twisted together：Cotton thread after 3-5 stock-traders' know-how spraying treatments is formed into water suction cotton thread by being uniformly twisted together；
(5) cotton thread is cut：Above-mentioned made water suction cotton thread is cut into different length according to use demand, double-deck basin is then installed on
In cultivation receptacle, so that potted plant is from container bottom automatic sucking moisture.
2. the preparation method of potted plant automatic water supplement water suction cotton thread according to claim 1, it is characterised in that：It is described
Cotton thread, the quality amount ratio of mould inhibitor are 20-25 in step (3):0.1-0.5.
3. the preparation method of potted plant automatic water supplement water suction cotton thread according to claim 1, it is characterised in that：It is described
Water suction enhancing liquid is made up of the raw material of following parts by weight：Poly-aspartic-acid/10-15 parts of poly glycol monomethyl ether, ethoxy
5-10 parts of cellulose, 0.5-2 parts of molecular sieve micro mist, 0.5-2 parts of polyethylene glycol oxide, 0.05-0.5 parts of rilanit special, six hydroxyl first
0.05-0.5 parts of base melamine pregnancy ether, 80-120 parts of deionized water, its preparation method is：To hydroxyethyl cellulose under grinding
Middle dropwise addition deionized water adds polyethylene glycol oxide and rilanit special up to being completely dissolved, and is warming up to reflux state insulation mixed
Close in 30min, gained mixed liquor feeding spray dryer, dry gained particle and micro mist is made through micronizer, produce modification
Hydroxyethyl cellulose；Poly-aspartic-acid/poly glycol monomethyl ether and hexamethylol melamine are added into remaining deionized water
Amine pregnancy ether, is warming up to reflux state insulation mixing 15min, hydroxyl second is modified after naturally cool to being added after room temperature after being sufficiently mixed
In base cellulose and molecular sieve micro mist, gained mixture feeding ball mill, discharging-material size is milled to less than 30 μm.
4. the preparation method of potted plant automatic water supplement water suction cotton thread according to claim 3, it is characterised in that：It is described
Molecular sieve micro mist is made by the modified processing of molecular screen primary powder, and its specific preparation method is：By molecular screen primary powder in 500-550
2h is calcined at DEG C, is taken out after naturally cool to after 110-120 DEG C, adds polyglutamic acid and ethylene glycol diglycidylether,
And in insulation mixing 30min at 110-120 DEG C, gained mixture sends into sealing and standing 3h in -15 DEG C of environment, finally utilizes ultra micro
Micro mist is made in pulverizer, produces molecular sieve micro mist.
5. the preparation method of potted plant automatic water supplement water suction cotton thread according to claim 4, it is characterised in that：It is described
Molecular screen primary powder, polyglutamic acid, the quality amount ratio of ethylene glycol diglycidylether are 1-5:0.1-1:0.05-0.5.
6. the preparation method of potted plant automatic water supplement water suction cotton thread according to claim 1, it is characterised in that：It is described
Mould inhibitor is formed by mould proof composition through carrier loaded, and its specific preparation method is：Chili meal is scattered in deionized water under stirring
In, stand and microcrystalline cellulose and N hydroxymethyl acrylamide are added after 5min, grinding at room temperature 15min, gained mixture feeding is cold
In lyophilizer, dry gained solid and micro mist is made through micronizer, produce mould inhibitor.
7. the preparation method of potted plant automatic water supplement water suction cotton thread according to claim 6, it is characterised in that：It is described
Chili meal, deionized water, microcrystalline cellulose, the quality amount ratio of N hydroxymethyl acrylamide are 0.5-2:10-20:1-10:
0.05-0.5。