CN107299243A - Aluminium alloy produces composition adjustment compound prescription - Google Patents
Aluminium alloy produces composition adjustment compound prescription Download PDFInfo
- Publication number
- CN107299243A CN107299243A CN201710577221.9A CN201710577221A CN107299243A CN 107299243 A CN107299243 A CN 107299243A CN 201710577221 A CN201710577221 A CN 201710577221A CN 107299243 A CN107299243 A CN 107299243A
- Authority
- CN
- China
- Prior art keywords
- aluminium
- composite metal
- metal powder
- powder
- aluminium alloy
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Aluminium alloy produces composition adjustment compound prescription, including composite metal powder, aluminium powder, sodium-free refining agent, potassium nitrate and calcium carbonate, and wherein each component represents composite metal powder 70%~90% with weight percentage;Aluminium powder 5%~15%;Sodium-free refining agent 1%~3%;Potassium nitrate 0.5%~1.5%;Calcium carbonate 5%~10%, composite metal powder includes iron, manganese, copper, titanium, chromium, silicon and nickel, iron, manganese, copper, titanium, chromium, silicon, the nickel of composite metal powder be made it is powdered after, aluminium powder, sodium-free refining agent, potassium nitrate and calcium carbonate and composite metal powder are forced to mix, packaging of aluminium foil bag is used.The present invention by composite in use, be directly spilled into molten bath, and stirring stands can obtain aluminium alloy for a period of time, then, and composite of the present invention can be covered in aluminium liquid surface in the process, and cooling will not be caused to aluminium liquid, and influence aluminium alloy produces stable.
Description
Technical field
The present invention relates to aluminium alloy production technical field, and in particular to a kind of aluminium alloy production composition adjustment is matched somebody with somebody with compound
Side.
Background technology
Aluminium alloy is most widely used class non-ferrous metal structural material in industry, in Aeronautics and Astronautics, automobile, machinery
Widely applied in manufacture, ship and chemical industry.The adjustment of composition needs to use aluminium alloy during aluminum current alloy production
Additive or aluminium intermediate alloy, these additives are all block, block additive is present feed intake after under be sunken in aluminium liquid, cause
Aluminium liquid cools, it is necessary to which secondary temperature elevation, the situation of increase cost, these block additive components are relatively simple in addition, it is impossible to simultaneously
Meet demand of the aluminium alloy production for each metallic element.
The content of the invention
In view of the deficiencies of the prior art, the present invention provides a kind of aluminium alloy produces composition adjustment compound prescription.
The technical solution adopted for the present invention to solve the technical problems is:
A kind of aluminium alloy produces composition adjustment compound prescription, including composite metal powder, aluminium powder, sodium-free refining agent, nitric acid
Potassium and calcium carbonate, wherein each component represent composite metal powder 70%~90% with weight percentage;Aluminium powder 5%~15%;Nothing
Sodium refining agent 1%~3%;Potassium nitrate 0.5%~1.5%;Calcium carbonate 5%~10%, composite metal powder include iron, manganese, copper,
Titanium, chromium, silicon and nickel, iron, manganese, copper, titanium, chromium, silicon, the nickel of composite metal powder be made it is powdered after, by aluminium powder, sodium-free refining agent,
Potassium nitrate and calcium carbonate are forced to mix with composite metal powder, use packaging of aluminium foil bag.
Powder is made by ball milling method or to roller rolled-on method in above-mentioned composite metal powder.
The present invention by composite in use, be directly spilled into molten bath, and stirring is stood for a period of time, then can obtain aluminium conjunction
Gold, in the process composite of the present invention can be covered in aluminium liquid surface, cooling will not be caused to aluminium liquid, influence aluminium alloy production is steady
It is fixed.
Embodiment
A kind of aluminium alloy produces composition adjustment compound prescription, including composite metal powder, aluminium powder, sodium-free refining agent, nitric acid
Potassium and calcium carbonate, wherein each component represent composite metal powder 70%~90% with weight percentage;Aluminium powder 5%~15%;Nothing
Sodium refining agent 1%~3%;Potassium nitrate 0.5%~1.5%;Calcium carbonate 5%~10%, composite metal powder include iron, manganese, copper,
Powder is made by ball milling method or to roller rolled-on method in titanium, chromium, silicon and nickel, iron, manganese, copper, titanium, chromium, silicon, the nickel of composite metal powder
After last shape, aluminium powder, sodium-free refining agent, potassium nitrate and calcium carbonate and composite metal powder are forced to mix, packaging of aluminium foil bag is used.
The present invention by composite in use, be directly spilled into molten bath, and stirring is stood for a period of time, then can obtain aluminium conjunction
Gold, in the process composite of the present invention can be covered in aluminium liquid surface, cooling will not be caused to aluminium liquid, influence aluminium alloy production is steady
It is fixed.
Claims (2)
1. a kind of aluminium alloy produces composition adjustment compound prescription, it is characterized in that including composite metal powder, aluminium powder, without sodium refining
Agent, potassium nitrate and calcium carbonate, wherein each component represent composite metal powder 70%~90% with weight percentage;Aluminium powder 5%~
15%;Sodium-free refining agent 1%~3%;Potassium nitrate 0.5%~1.5%;Calcium carbonate 5%~10%, composite metal powder include iron,
Manganese, copper, titanium, chromium, silicon and nickel, iron, manganese, copper, titanium, chromium, silicon, the nickel of composite metal powder be made it is powdered after, by aluminium powder, without sodium essence
Refine agent, potassium nitrate and calcium carbonate and composite metal powder is forced to mix, use packaging of aluminium foil bag.
2. aluminium alloy according to claim 1 produces composition adjustment compound prescription, it is characterized in that composite metal powder passes through
Powder is made to roller rolled-on method in ball milling method.