CN107286875A - A kind of one-component ceramic tile interface adhesive material and preparation method thereof - Google Patents
A kind of one-component ceramic tile interface adhesive material and preparation method thereof Download PDFInfo
- Publication number
- CN107286875A CN107286875A CN201710616958.7A CN201710616958A CN107286875A CN 107286875 A CN107286875 A CN 107286875A CN 201710616958 A CN201710616958 A CN 201710616958A CN 107286875 A CN107286875 A CN 107286875A
- Authority
- CN
- China
- Prior art keywords
- ceramic tile
- adhesive material
- interface adhesive
- component ceramic
- filler
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of one-component ceramic tile interface adhesive material, it includes following component, and following components is mass ratio：Binding agent 25%, the first filler 20%, the second filler 45%, dispersant 1%, suspending agent 3%, thickener 1%, water 5%.
Description
Technical field
The present invention relates to tile laying materials industry technical field, especially a kind of one-component ceramic tile interface adhesive material and
Its preparation method.
Background technology
The high speed development of ceramic tile industry, ceramic tile manufacturing process increasingly lean density more and more higher, ceramic tile new product, which updates, to be changed
Fast for speed, water absorption rate is but more and more lower, causes the requirement more and more higher to paving material, and tile laying Materials at present
It is delayed, therefore the difficult situation of tile laying is occurred in that, the serious hollowing of appearance is mainly manifested in, comes off, falls the phenomenons such as brick.Background skill
The shortcoming of art, is two-component gum, it is necessary to could paving after grade of having been constructed after blending is dry.
Therefore there is existing ceramic tile particularly vitrified tile in the prior art causes ceramic tile to come off because water absorption rate is low, interface is smooth
The problem of.
The content of the invention
In view of this, the present invention provides a kind of improvement ceramic tile interface performance and the one-component ceramic tile interfacial adhesion of workability
Material and preparation method thereof.
A kind of one-component ceramic tile interface adhesive material, it includes following component, and following components is mass ratio：
Binding agent 25%, the first filler 20%, the second filler 45%, dispersant 1%, suspending agent 3%, thickener 1%, water
5%.
In component ceramic tile interface adhesive material of the present invention, first filler is silica, described second
Filler is calcium carbonate, and the calcium carbonate is the calcium carbonate of 600 mesh.
In component ceramic tile interface adhesive material of the present invention, it is characterised in that
The binding agent is emulsion acrylic resin, and the dispersant is Sodium Polyacrylate, and the suspending agent is manosil AS
Salt, the thickener is polyurethane.
This also invention also provides a kind of preparation method of above-mentioned one-component ceramic tile interface adhesive material, and it includes following step
Suddenly：The number appeared below is weight ratio,
S1, take emulsion acrylic resin 25%, silica 20%, the calcium carbonate 45% of 600 mesh, Sodium Polyacrylate 1%,
Aluminosilicate 3%, polyurethane 1%, water 5% are used as raw materials of compound；
S2, the raw materials of compound in step S1 is inserted in mixer be stirred；
S3, the mixing time in rate-determining steps S2 and rotating speed；The mixing time is 1 hour；The mixing time is
400-500 revs/min.
In the preparation method of one-component ceramic tile interface adhesive material of the present invention,
Mixing speed is 450 revs/min in the step S3.
One-component ceramic tile interface adhesive material of the present invention and preparation method thereof can realize the two-component gum from before
Need A groups and B groups to blend and use, be now one-component；Ability paving after waiting is needed after construction before, is now pasted for i.e. brush.
Embodiment
The principle of the present invention is as follows, a kind of one-component ceramic tile interface adhesive material, and it includes following component, and following components is equal
For mass ratio：
Binding agent 25%, the first filler 20%, the second filler 45%, dispersant 1%, suspending agent 3%, thickener 1%, water
5%.
In component ceramic tile interface adhesive material of the present invention, first filler is that silica (is commonly called as quartz
Sand), second filler is calcium carbonate, and the calcium carbonate is the calcium carbonate of 600 mesh.
In component ceramic tile interface adhesive material of the present invention, it is characterised in that
The binding agent is emulsion acrylic resin (being commonly called as styrene-acrylic resin emulsion), and the dispersant is Sodium Polyacrylate,
The suspending agent is aluminosilicate (being commonly called as kaolin), and the thickener is polyurethane.
This also invention also provides a kind of preparation method of above-mentioned one-component ceramic tile interface adhesive material, and it includes following step
Suddenly：The number appeared below is weight ratio,
S1, take emulsion acrylic resin 25%, silica 20%, the calcium carbonate 45% of 600 mesh, Sodium Polyacrylate 1%,
Aluminosilicate 3%, polyurethane 1%, water 5% are used as raw materials of compound；
S2, the raw materials of compound in step S1 is inserted in mixer be stirred；
S3, the mixing time in rate-determining steps S2 and rotating speed；The mixing time is 1 hour；The mixing time is
400-500 revs/min.
In the preparation method of one-component ceramic tile interface adhesive material of the present invention,
Mixing speed is 450 revs/min in the step S3.
One-component ceramic tile interface adhesive material of the present invention and preparation method thereof can realize the two-component gum from before
Need A groups and B groups to blend and use, be now one-component；Ability paving after waiting is needed after construction before, is now pasted for i.e. brush.
The principle of the embodiment of the present invention is as follows：The adhesive theory of the embodiment of the present invention is as follows：Binding material molecule and cement
That starches surface molecular is pasted with two processes, and the first stage is the binding material molecule for brushing the ceramic tile back side by means of Brownian movement
To cement mortar diffusion into the surface, make the polar group at two interfaces or link close to each other, in the process, heating, apply pressure
Power and reduction tile bonding viscosity of material are all conducive to the reinforcement of Brownian movement；Second stage is the generation of absorption affinity, works as ceramic tile
When back side binding material reaches 5-10nm with cement mortar molecule distance, attractive interaction is just produced between interfacial molecular, is made intermolecular
Distance further shorten in maximum stable state, so as to reach superpower adherence force.So as to solve vitreous in existing design
Brick causes the problem of ceramic tile comes off because water absorption rate is low, interface is smooth.
It is understood that for the person of ordinary skill of the art, can be done with technique according to the invention design
Go out other various corresponding changes and deformation, and all these changes and deformation should all belong to the protection model of the claims in the present invention
Enclose.
Claims (5)
1. a kind of one-component ceramic tile interface adhesive material, it is characterised in that it includes following component, following components is quality
Than：
Binding agent 25%, the first filler 20%, the second filler 45%, dispersant 1%, suspending agent 3%, thickener 1%, water 5%.
2. component ceramic tile interface adhesive material as claimed in claim 1, it is characterised in that first filler is titanium dioxide
Silicon, second filler is calcium carbonate, and the calcium carbonate is the calcium carbonate of 600 mesh.
3. one-component ceramic tile interface adhesive material as claimed in claim 1 or 2, it is characterised in that
The binding agent is emulsion acrylic resin, and the dispersant is Sodium Polyacrylate, and the suspending agent is aluminosilicate, institute
Thickener is stated for polyurethane.
4. the preparation method of the one-component ceramic tile interface adhesive material described in a kind of claim 3, it is characterised in that it is included such as
Lower step：The number appeared below is weight ratio,
S1, take emulsion acrylic resin 25%, silica 20%, the calcium carbonate 45% of 600 mesh, Sodium Polyacrylate 1%, aluminium silicon
Hydrochlorate 3%, polyurethane 1%, water 5% are used as raw materials of compound；
S2, the raw materials of compound in step S1 is inserted in mixer be stirred；
S3, the mixing time in rate-determining steps S2 and rotating speed；The mixing time is 1 hour；The mixing time is 400-
500 revs/min.
5. the preparation method of one-component ceramic tile interface adhesive material as claimed in claim 1, it is characterised in that
Mixing speed is 450 revs/min in the step S3.