CN107282651B - 隆起缺陷检查判定方法 - Google Patents
隆起缺陷检查判定方法 Download PDFInfo
- Publication number
- CN107282651B CN107282651B CN201610196997.1A CN201610196997A CN107282651B CN 107282651 B CN107282651 B CN 107282651B CN 201610196997 A CN201610196997 A CN 201610196997A CN 107282651 B CN107282651 B CN 107282651B
- Authority
- CN
- China
- Prior art keywords
- protuberance
- steel ruler
- ridge
- coil
- bump height
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明涉及带卷领域,具体为一种隆起缺陷检查判定方法。采用的检查工具包括钢板尺、塞尺,检查方法如下:用钢板尺垂直轧制方向放置在隆起部位,使用塞尺测量隆起部位最高点与水平带钢间间隙。若光线不足时,使用手电在钢板尺后方打光,观察光线透射情况。为了解决产品在用户使用时,出现了开卷浪形,影响使用的问题,本发明通过不断积累经验,结合用户反馈信息,制定了隆起缺陷的检查方法和判定标准,适用于冷轧、镀锌、电镀锌产品隆起缺陷的检查判定。
Description
技术领域
本发明涉及带卷领域,具体为一种隆起缺陷检查判定方法。
背景技术
带卷隆起是沿轧制方向带状增厚,特别是当带钢被卷起时,可导致不均匀的程度增加,好像带卷直径增大;在极端情况下,带卷隆起可能导致波浪、厚度起伏、带卷破裂或粘结撕裂。
如图1(a)-图1(b)所示,带卷隆起主要发生在热轧机上,而且一旦发生,则在随后的冷轧中也不能消除。因为带钢卷取时,厚度增加会因放大效应而变的越来越明显。
冷轧带钢检查,一般是通过在线立式检查或水平检查的方式进行,可以对带钢表面质量、板型、尺寸精度等进行检查。但针对隆起缺陷,在立式及水平检查台检查时,均不能直观的检查到此缺陷,而在进行钢卷外观检查时,也仅仅能够通过手触的方式,进行触觉判定,无法通过量化的方法,与用户使用感受结合起来。
以往检查判定方法是:以手感程度(轻、中、重)进行判定,不同质检员对手感程度的感受不同,并且不同部位的隆起缺陷,对用户的使用影响不同。部分产品在用户使用时,出现了开卷浪形,影响使用的问题。使用手触检查,质检员判定标准不一致,导致用户使用抱怨。
发明内容
本发明的目的是提供一种隆起缺陷检查判定方法,实现对不同隆起缺陷的量化判定。
本发明的技术方案是:
一种隆起缺陷检查判定方法,采用的检查工具包括钢板尺、塞尺,检查方法如下:用钢板尺垂直轧制方向放置在隆起部位,使用塞尺测量隆起部位最高点与水平带钢间间隙。
所述的隆起缺陷检查判定方法,若光线不足时,使用手电在钢板尺后方打光,观察光线透射情况。
所述的隆起缺陷检查判定方法,钢板尺的规格长度在100-1000mm均可。
所述的隆起缺陷检查判定方法,热轧原料检查判定过程如下:
(1)对于各规格边部存在有隆起原料,不符合上机标准;
(2)对于原料肋部和中部的隆起,隆起高度≥0.08mm时,不符合上机标准。
所述的隆起缺陷检查判定方法,冷轧、镀锌、电镀锌隆起判定标准如下:
(1)肋部、中部隆起
钢卷厚度≤0.6mm,隆起高度≥0.05mm时,不符合要求;
0.6mm<钢卷厚度≤1.0mm,隆起高度≥0.08mm时,不符合要求;
钢卷厚度>1.0mm时,隆起高度≥0.1mm时,不符合要求;
(2)边部隆起
在卷取后,重新开卷时,出现边部隆起,均不能满足判定要求。
本发明的优点及有益效果是:
1、为了解决产品在用户使用时,出现了开卷浪形,影响使用的问题,本发明通过不断积累经验,结合用户反馈信息,制定了隆起缺陷的检查方法和判定标准,适用于冷轧、镀锌、电镀锌产品隆起缺陷的检查判定。
附图说明
图1(a)-图1(b)为带卷隆起示意图。其中,图1(a)为热轧卷;图1(b)为冷轧卷。
图2(a)-图2(b)为隆起部位及对应位置测量情况示意图。其中,图2(a)为隆起部位;图2(b)为横向厚度变化趋势分析图,横坐标为指数,纵坐标为厚度(mm)。
图3(a)-图3(b)为本发明隆起检查方法示意图。其中,图3(a)为整体图;图3(b)为局部放大图。
具体实施方式
如图2(a)-图2(b)所示,从测量数据分析来看,靠近隆起部位,厚度有增加趋势,测量高点部位与隆起部位对应。隆起缺陷出现时,一般无明显规律性,缺陷分布可划分为三种情况,边部(距离带钢边部200mm以内)、肋部(中部与边部之间部位)、中部(距离中心距离200mm以内)。
缺陷出现后,起初通过手触方式,以手感程度(轻、中、重)进行判定,不同质检员对手感程度感觉不同,并且不同部位的隆起缺陷,对用户的使用影响不同。部分产品在用户使用时,出现了开卷浪形,影响使用的问题。
在具体实施过程中,本发明隆起缺陷检查判定方法,采用的检查工具包括:钢板尺(100-1000mm均可)、塞尺、手电等。如图3(a)-图3(b)所示,检查方法如下:用钢板尺垂直轧制方向放置在隆起部位,使用塞尺测量隆起部位最高点与水平带钢间的间隙。若光线不足时,使用手电在钢板尺后方打光,观察光线透射情况,进一步计算和判断隆起部位最高点与水平带钢间的间隙。
本发明中,热轧原料检查判定过程如下:
(1)对于各规格边部存在有隆起原料,不符合上机标准。
(2)对于原料肋部和中部的隆起,隆起高度≥0.08mm时,不符合上机标准。
本发明中,冷轧、镀锌、电镀锌隆起判定标准如下:
1、肋部、中部隆起
(1)钢卷厚度≤0.6mm,隆起高度≥0.05mm时,不符合要求;
(2)0.6mm<钢卷厚度≤1.0mm,隆起高度≥0.08mm时,不符合要求;
(3)钢卷厚度>1.0mm时,隆起高度≥0.1mm时,不符合要求。
2、边部隆起
针对边部隆起,一般靠近隆起部位,在卷取后,重新开卷时,在隆起部位出现浪距较小的浪形,并且随着钢卷直径变小,程度减轻。通过现场检查经验来看,边部隆起出现后,均不能满足判定要求。
Claims (1)
1.一种隆起缺陷检查判定方法,其特征在于,采用的检查工具包括钢板尺、塞尺,检查方法如下:用钢板尺垂直轧制方向放置在隆起部位,使用塞尺测量隆起部位最高点与水平带钢间间隙;
若光线不足时,使用手电在钢板尺后方打光,观察光线透射情况;
钢板尺的规格长度在100-1000mm均可;
热轧原料检查判定过程如下:
(1)对于各规格边部存在有隆起原料,不符合上机标准;
(2)对于原料肋部和中部的隆起,隆起高度≥0.08mm时,不符合上机标准;
冷轧或镀锌隆起判定标准如下:
(1)肋部、中部隆起
钢卷厚度≤0.6mm,隆起高度≥0.05mm时,不符合要求;
0.6mm<钢卷厚度≤1.0mm,隆起高度≥0.08mm时,不符合要求;
钢卷厚度>1.0mm时,隆起高度≥0.1mm时,不符合要求;
(2)边部隆起
在卷取后,重新开卷时,出现边部隆起,均不能满足判定要求。