CN107265917A - A kind of new high pressure-bearing decoration panel material and preparation method - Google Patents
A kind of new high pressure-bearing decoration panel material and preparation method Download PDFInfo
- Publication number
- CN107265917A CN107265917A CN201710296197.1A CN201710296197A CN107265917A CN 107265917 A CN107265917 A CN 107265917A CN 201710296197 A CN201710296197 A CN 201710296197A CN 107265917 A CN107265917 A CN 107265917A
- Authority
- CN
- China
- Prior art keywords
- parts
- high pressure
- new high
- powder
- decoration panel
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses the new high pressure-bearing decoration panel material of one kind, the material includes the raw material of following composition by weight：10 15 parts of metal powder material, 5 12 parts of fiber material, 25 parts of curing agent, 12 18 parts of oxide powder, 36 parts of plasticizer, 35 65 parts of solvent, 58 parts of stabilizer, 0.1 0.5 parts of nitrogen.This material itself is difficult to be oxidized, and service life is long, and the manufacture craft of this programme is simple, by adding nitrogen, and material internal can be made to produce tiny bubble, and the deadweight of lightening material is suitable as decoration panel material and used.
Description
Technical field
It is specially a kind of new high pressure-bearing decoration panel material and preparation method the present invention relates to field of new materials.
Background technology
The existing material for being used to make decoration panel is typically all to use wood material, this raw material ecosystem, to ring
Border pollution is small, but there is following defect：1. cost is higher, forest is destroyed, the theme of current social environmental protection is not met；2.
The anti-pressure ability of wood materials is poor, is easily damaged；3. the existing technique for making decoration panel is exactly that wood materials are carried out
Polishing, not suitable for the panel manufacture craft of new material.
The content of the invention
It is an object of the invention to provide the new high pressure-bearing decoration panel material of one kind and preparation method, to solve the above-mentioned back of the body
The problem of being proposed in scape technology.
To achieve the above object, the present invention provides following technical scheme：A kind of new high pressure-bearing decoration panel material, the material
Material includes the raw material of following composition by weight：10-15 parts of metal powder material, 5-12 parts of fiber material, 2-5 parts of curing agent, oxide powder
12-18 parts, 3-6 parts of plasticizer, 35-65 parts of solvent, 5-8 parts of stabilizer, 0.1-0.5 parts of nitrogen.
It is preferred that, the metal powder material includes copper powder 20%, zinc powder 15%, cobalt powder 16%, nickel powder 14%, iron powder 25%, titanium valve
10%。
It is preferred that, the particle diameter range of the metal powder material is 20-50 microns.
It is preferred that, the fiber material includes wood fibre 20%, soybean fiber 30%, polytetrafluoroethylene fibre 50%, and
It is a diameter of 10-20 microns and described fiber material length is 800-1000 microns.
It is preferred that, the curing agent uses epoxy resin.
It is preferred that, the oxide powder includes titanium white 30%, iron oxide 20%, cupric oxide 10%, calcium oxide 10%, aluminum oxide
30%。
It is preferred that, the plasticizer uses ditridecyl phthalate.
It is preferred that, the solvent includes ethanol 20%, glycerine 30%, dimethylbenzene 10%, water 40%.
It is preferred that, the stabilizer includes aluminum stearate 35%, potassium stearate 40%, magnesium stearate 25%.
The preparation method that a kind of new high pressure-bearing as described above decorates panel material, comprises the following steps：
S1：Weigh proportioning：Raw material, and sealed storage respectively are weighed according to above-mentioned composition by weight；
S2：Prepare solvent：The ethanol weighed, glycerine, dimethylbenzene and water are added sequentially to be stirred in mixing plant,
Speed of agitator control is 200-300 revs/min, is stirred 20-30 minutes, stops stirring when being sufficiently mixed to raw material；
S3：Add primary raw material：Wood fibre, soybean fiber, polytetrafluoroethylene fibre are added to mixing plant simultaneously
It is middle to continue to stir 10-20 minutes, then sequentially add titanium white, iron oxide, cupric oxide %, calcium oxide, aluminum oxide, 20-30 points of stirring
Clock, adds metal powder material, plasticizer, then seals equipment, and the air inside extraction then passes to nitrogen to vacuum state,
And pressurize, it is 800-900 kPas to control pressure, is stirred 20 minutes, adds curing agent and stabilizer, carries out heating stirring, control
Speed of agitator is 400-500 revs/min, and it is 80-90 degrees Celsius to control temperature, keeps pressure, and the reaction time is 30 minutes, and liquid is made
State raw material；
S4：It is cooled and shaped：By liquid material pressure release made from previous step, the internal pressure of equipment was down to 1 in 10 minutes
Atmospheric pressure, then injects mould using Shooting Technique, is cooled and shaped, surface spikes of then polishing, you can new high pressure-bearing is made
Decorate panel.
Compared with prior art, the beneficial effects of the invention are as follows：The present invention is used as fibre using a variety of natural Organic Ingredients
Dimension, it is possible to increase the intensity of decoration panel, and environmental pollution is small, and by adding various metals powder and oxidate powder
Material, it is possible to increase the stability and anti-stress energy of this material, this material itself are difficult to be oxidized, and service life is long, and this
The manufacture craft of scheme is simple, by adding nitrogen, the bubble that material internal generation can be made tiny, the deadweight of lightening material,
Decoration panel material is suitable as to use.
Embodiment
The technical scheme in the embodiment of the present invention will be clearly and completely described below, it is clear that described implementation
Example only a part of embodiment of the invention, rather than whole embodiments.Based on the embodiment in the present invention, this area is common
The every other embodiment that technical staff is obtained under the premise of creative work is not made, belongs to the model that the present invention is protected
Enclose.
Embodiment one
The present invention provides a kind of technical scheme：A kind of new high pressure-bearing decoration panel material, the material includes following composition by weight
Raw material：10 parts of metal powder material, 5 parts of fiber material, 2 parts of curing agent, 12 parts of oxide powder, 3 parts of plasticizer, 35 parts of solvent, surely
Determine 5 parts of agent, 0.1 part of nitrogen.Wherein, metal powder material includes copper powder 20%, zinc powder 15%, cobalt powder 16%, nickel powder 14%, iron powder 25%, titanium
Powder 10%.The particle diameter range of metal powder material is 20 microns.Fiber material includes wood fibre 20%, soybean fiber 30%, gathered
Tetrafluoroethylene fiber 50%, and described fiber material length is 800 microns, a diameter of 10 microns.Curing agent uses asphalt mixtures modified by epoxy resin
Fat.Oxide powder includes titanium white 30%, iron oxide 20%, cupric oxide 10%, calcium oxide 10%, aluminum oxide 30%.Plasticizer is using adjacent
Ester.Solvent includes ethanol 20%, glycerine 30%, dimethylbenzene 10%, water 40%.Stabilizer comprising aluminum stearate 35%,
Potassium stearate 40%, magnesium stearate 25%.
The preparation method that a kind of new high pressure-bearing as described above decorates panel material, comprises the following steps：
S1：Weigh proportioning：Raw material, and sealed storage respectively are weighed according to above-mentioned composition by weight；
S2：Prepare solvent：The ethanol weighed, glycerine, dimethylbenzene and water are added sequentially to be stirred in mixing plant,
Speed of agitator control is 200 revs/min, is stirred 20 minutes, stops stirring when being sufficiently mixed to raw material；
S3：Add primary raw material：Wood fibre, soybean fiber, polytetrafluoroethylene fibre are added to mixing plant simultaneously
It is middle to continue to stir 10 minutes, titanium white, iron oxide, cupric oxide %, calcium oxide, aluminum oxide are then sequentially added, is stirred 20 minutes, plus
Enter metal powder material, plasticizer, then seal equipment, the air inside extraction then passes to nitrogen, and add to vacuum state
Pressure, it is 800 kPas to control pressure, is stirred 20 minutes, adds curing agent and stabilizer, carries out heating stirring, controls speed of agitator
For 400 revs/min, it is 80 degrees Celsius to control temperature, keeps pressure, and the reaction time is 30 minutes, and liquid material is made；
S4：It is cooled and shaped：By liquid material pressure release made from previous step, the internal pressure of equipment was down to 1 in 10 minutes
Atmospheric pressure, then injects mould using Shooting Technique, is cooled and shaped, surface spikes of then polishing, you can new high pressure-bearing is made
Decorate panel.
Embodiment two
The present invention provides a kind of technical scheme：A kind of new high pressure-bearing decoration panel material, the material includes following composition by weight
Raw material：12 parts of metal powder material, 8 parts of fiber material, 3 parts of curing agent, 16 parts of oxide powder, 5 parts of plasticizer, 45 parts of solvent, surely
Determine 6 parts of agent, 0.3 part of nitrogen.Wherein, metal powder material includes copper powder 20%, zinc powder 15%, cobalt powder 16%, nickel powder 14%, iron powder 25%, titanium
Powder 10%.The particle diameter range of metal powder material is 40 microns.Fiber material includes wood fibre 20%, soybean fiber 30%, gathered
Tetrafluoroethylene fiber 50%, and described fiber material length is 900 microns, a diameter of 15 microns.Curing agent uses asphalt mixtures modified by epoxy resin
Fat.Oxide powder includes titanium white 30%, iron oxide 20%, cupric oxide 10%, calcium oxide 10%, aluminum oxide 30%.Plasticizer is using adjacent
Ester.Solvent includes ethanol 20%, glycerine 30%, dimethylbenzene 10%, water 40%.Stabilizer comprising aluminum stearate 35%,
Potassium stearate 40%, magnesium stearate 25%.
The preparation method that a kind of new high pressure-bearing as described above decorates panel material, comprises the following steps：
S1：Weigh proportioning：Raw material, and sealed storage respectively are weighed according to above-mentioned composition by weight；
S2：Prepare solvent：The ethanol weighed, glycerine, dimethylbenzene and water are added sequentially to be stirred in mixing plant,
Speed of agitator control is 270 revs/min, is stirred 28 minutes, stops stirring when being sufficiently mixed to raw material；
S3：Add primary raw material：Wood fibre, soybean fiber, polytetrafluoroethylene fibre are added to mixing plant simultaneously
It is middle to continue to stir 18 minutes, titanium white, iron oxide, cupric oxide %, calcium oxide, aluminum oxide are then sequentially added, is stirred 26 minutes, plus
Enter metal powder material, plasticizer, then seal equipment, the air inside extraction then passes to nitrogen, and add to vacuum state
Pressure, it is 860 kPas to control pressure, is stirred 20 minutes, adds curing agent and stabilizer, carries out heating stirring, controls speed of agitator
For 460 revs/min, it is 85 degrees Celsius to control temperature, keeps pressure, and the reaction time is 30 minutes, and liquid material is made；
S4：It is cooled and shaped：By liquid material pressure release made from previous step, the internal pressure of equipment was down to 1 in 10 minutes
Atmospheric pressure, then injects mould using Shooting Technique, is cooled and shaped, surface spikes of then polishing, you can new high pressure-bearing is made
Decorate panel.
Embodiment three
The present invention provides a kind of technical scheme：A kind of new high pressure-bearing decoration panel material, the material includes following composition by weight
Raw material：15 parts of metal powder material, 12 parts of fiber material, 5 parts of curing agent, 18 parts of oxide powder, 6 parts of plasticizer, 65 parts of solvent, surely
Determine 8 parts of agent, 0.5 part of nitrogen.Wherein, metal powder material includes copper powder 20%, zinc powder 15%, cobalt powder 16%, nickel powder 14%, iron powder 25%, titanium
Powder 10%.The particle diameter range of metal powder material is 50 microns.Fiber material includes wood fibre 20%, soybean fiber 30%, gathered
Tetrafluoroethylene fiber 50%, and described fiber material length is 1000 microns, a diameter of 20 microns.Curing agent uses epoxy
Resin.Oxide powder includes titanium white 30%, iron oxide 20%, cupric oxide 10%, calcium oxide 10%, aluminum oxide 30%.Plasticizer is used
Ditridecyl phthalate.Solvent includes ethanol 20%, glycerine 30%, dimethylbenzene 10%, water 40%.Stabilizer includes aluminum stearate
35%th, potassium stearate 40%, magnesium stearate 25%.
The preparation method that a kind of new high pressure-bearing as described above decorates panel material, comprises the following steps：
S1：Weigh proportioning：Raw material, and sealed storage respectively are weighed according to above-mentioned composition by weight；
S2：Prepare solvent：The ethanol weighed, glycerine, dimethylbenzene and water are added sequentially to be stirred in mixing plant,
Speed of agitator control is 300 revs/min, is stirred 30 minutes, stops stirring when being sufficiently mixed to raw material；
S3：Add primary raw material：Wood fibre, soybean fiber, polytetrafluoroethylene fibre are added to mixing plant simultaneously
It is middle to continue to stir 20 minutes, titanium white, iron oxide, cupric oxide %, calcium oxide, aluminum oxide are then sequentially added, is stirred 30 minutes, plus
Enter metal powder material, plasticizer, then seal equipment, the air inside extraction then passes to nitrogen, and add to vacuum state
Pressure, it is 900 kPas to control pressure, is stirred 20 minutes, adds curing agent and stabilizer, carries out heating stirring, controls speed of agitator
For 500 revs/min, it is 90 degrees Celsius to control temperature, keeps pressure, and the reaction time is 30 minutes, and liquid material is made；
S4：It is cooled and shaped：By liquid material pressure release made from previous step, the internal pressure of equipment was down to 1 in 10 minutes
Atmospheric pressure, then injects mould using Shooting Technique, is cooled and shaped, surface spikes of then polishing, you can new high pressure-bearing is made
Decorate panel.
The wooden decoration panel material traditional to three groups of above-mentioned embodiments and one group is tested, wood materials used
For white birch material, intensity is tested, following form is drawn：
It was found from from test result form, the decoration panel material of this programme, compression strength is high, and the raw material that the present invention is used
It is mostly natural material, the pollution that production process is caused is small, more environmental protection, is suitable as decoration panel and uses.
Although an embodiment of the present invention has been shown and described, for the ordinary skill in the art, can be with
A variety of changes, modification can be carried out to these embodiments, replace without departing from the principles and spirit of the present invention by understanding
And modification, the scope of the present invention is defined by the appended.
Claims (10)
1. a kind of new high pressure-bearing decoration panel material, it is characterised in that the material includes the raw material of following composition by weight：Metal
10-15 parts of powder, 5-12 parts of fiber material, 2-5 parts of curing agent, 12-18 parts of oxide powder, 3-6 parts of plasticizer, solvent 35-65
Part, 5-8 parts of stabilizer, 0.1-0.5 parts of nitrogen.
2. the new high pressure-bearing decoration panel material of one kind according to claim 1, it is characterised in that：The metal powder material bag
Containing copper powder 20%, zinc powder 15%, cobalt powder 16%, nickel powder 14%, iron powder 25%, titanium valve 10%.
3. the new high pressure-bearing decoration panel material of one kind according to claim 2, it is characterised in that：The metal powder material
Particle diameter range is 20-50 microns.
4. the new high pressure-bearing decoration panel material of one kind according to claim 1, it is characterised in that：The fiber material is included
Wood fibre 20%, soybean fiber 30%, polytetrafluoroethylene fibre 50%, and described fiber material length is 800-
It is 1000 microns, a diameter of 10-20 microns.
5. the new high pressure-bearing decoration panel material of one kind according to claim 1, it is characterised in that：The curing agent is used
Epoxy resin.
6. the new high pressure-bearing decoration panel material of one kind according to claim 1, it is characterised in that：The oxide powder
Include titanium white 30%, iron oxide 20%, cupric oxide 10%, calcium oxide 10%, aluminum oxide 30%.
7. the new high pressure-bearing decoration panel material of one kind according to claim 1, it is characterised in that：The plasticizer is used
Ditridecyl phthalate.
8. the new high pressure-bearing decoration panel material of one kind according to claim 1, it is characterised in that：The solvent includes second
Alcohol 20%, glycerine 30%, dimethylbenzene 10%, water 40%.
9. the new high pressure-bearing decoration panel material of one kind according to claim 1, it is characterised in that：The stabilizer is included
Aluminum stearate 35%, potassium stearate 40%, magnesium stearate 25%.
10. the preparation method that a kind of new high pressure-bearing as described in claim 1-9 any one decorates panel material, its feature
It is, comprises the following steps：
S1：Weigh proportioning：Raw material, and sealed storage respectively are weighed according to above-mentioned composition by weight；
S2：Prepare solvent：The ethanol weighed, glycerine, dimethylbenzene and water are added sequentially to be stirred in mixing plant,
Speed of agitator control is 200-300 revs/min, is stirred 20-30 minutes, stops stirring when being sufficiently mixed to raw material；
S3：Add primary raw material：Wood fibre, soybean fiber, polytetrafluoroethylene fibre are added to mixing plant simultaneously
It is middle to continue to stir 10-20 minutes, then sequentially add titanium white, iron oxide, cupric oxide %, calcium oxide, aluminum oxide, 20-30 points of stirring
Clock, adds metal powder material, plasticizer, then seals equipment, and the air inside extraction then passes to nitrogen to vacuum state,
And pressurize, it is 800-900 kPas to control pressure, is stirred 20 minutes, adds curing agent and stabilizer, carries out heating stirring, control
Speed of agitator is 400-500 revs/min, and it is 80-90 degrees Celsius to control temperature, keeps pressure, and the reaction time is 30 minutes, and liquid is made
State raw material；
S4：It is cooled and shaped：By liquid material pressure release made from previous step, the internal pressure of equipment was down to 1 in 10 minutes
Atmospheric pressure, then injects mould using Shooting Technique, is cooled and shaped, surface spikes of then polishing, you can new high pressure-bearing is made
Decorate panel.