CN107265893A - A kind of dry powder clay - Google Patents
A kind of dry powder clay Download PDFInfo
- Publication number
- CN107265893A CN107265893A CN201710484181.3A CN201710484181A CN107265893A CN 107265893 A CN107265893 A CN 107265893A CN 201710484181 A CN201710484181 A CN 201710484181A CN 107265893 A CN107265893 A CN 107265893A
- Authority
- CN
- China
- Prior art keywords
- slag
- somehow
- gypsum
- calcium aluminate
- useless
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to environment-friendly materials technical field, specifically a kind of dry powder clay.Main constituent be produce useless of phosphorus slag, boiler slag, production calcium aluminate powder somehow and gypsum mix in proportion, wearing into micropowders using ball mill after mixing forms, and constituent precentagewise amount part composition is as follows：It is useless somehow 35%~40%, gypsum 1%~5% that phosphorus slag 30%~35%, boiler slag 25%~29%, production calcium aluminate powder are produced.The present invention have the advantages that it is applied widely, make waste recovery recycle, production cost it is low, insulation, prevent fires and acidproof corrosion resistance and good.
Description
Technical field
The present invention relates to building material technical field, specifically a kind of dry powder clay.
Background technology
Use natural rock or industrial residue for primary raw material, be made through processes such as dispensing, melting, cast, heat treatments
Crystal arrangement is regular, quality is hard, fine and smooth nonmetallic industrial materials.Cast stone has good corrosion-resistant, anti-wear performance, but its
Toughness, impact resistance are poor, and machining is difficult.Cast stone product mainly has glass-ceramic tubre, cast stone multi-unit tube, glass cermaic plate and cast stone
Material, has been widely used in heavy wear, the corrosion location of the industrial departments such as electric power, coal, mine, metallurgy, chemical industry, building.
The service life of extendable portion part or equipment is more than ten times or even tens times of other materials.
Because the toughness of cast stone product is poor, hardness is higher, it is difficult to machining, typically presses definite shape and dimensioned
Product.Its fixed form is using the method built by laying bricks or stones and inlayed.The tradition peace block method of cast stone is to make to bond material using cement mortar
Material, defective in terms of wear-resisting and anti-corrosion, particularly anti-corrosion capability is special poor, does not give full play of cast stone in this respect
Superiority.In terms of the decorations of exterior wall, what existing technical scheme was used mostly is concrete material as its exterior wall
Finishing and rendering, but its insulation, fire prevention and acidproof decay resistance are all poor.
The content of the invention
In order to overcome drawbacks described above, the technical problem to be solved in the present invention is to provide one kind it is applied widely, make waste material return
Receive the dry powder clay of low recycling, production cost, insulation, fire prevention and acidproof corrosion resistance and good.
To achieve the above object, dry powder clay of the invention, main constituent is phosphorus slag, boiler slag, production calcium aluminate powder
Produce useless somehow and gypsum mix in proportion, wearing into micropowders using ball mill after mixing forms, constituent precentagewise
Measure part composition as follows：Produce useless of phosphorus slag 30%~35%, boiler slag 25%~29%, production calcium aluminate powder somehow 35%~
40%th, gypsum 1%~5%.
It is preferred that, constituent precentagewise amount part composition is as follows：Phosphorus slag 30%, boiler slag 25%, production calcium aluminate powder production
Raw is useless somehow 40%, gypsum 5%.
It is preferred that, constituent precentagewise amount part composition is as follows：Phosphorus slag 35%, boiler slag 29%, production calcium aluminate powder production
Raw is useless somehow 35%, gypsum 1%.
Beneficial effects of the present invention are：In the rendering of exterior wall, have high insulating effect, fire-protection rating high using the present invention
And the good advantage of acidproof anticorrosion effect, than insulation, fire prevention and the acidproof decay resistance of the exterior wall painted using ordinary cement
More than one times is higher by, meanwhile, materials'use of the invention is the waste material in industrial production, has reached the mesh of resource recycling
, production cost is reduced, so that the production efficiency of enterprise is improved, with wide market prospects.
Embodiment
With reference to embodiment, the embodiment to the present invention is further described.Following examples are only used for more
Plus technical scheme is clearly demonstrated, and can not be limited the scope of the invention with this.
Embodiment 1
A kind of dry powder clay, main constituent be produce useless of phosphorus slag, boiler slag, production calcium aluminate powder somehow and gypsum press
Ratio is mixed, and is worn into micropowders using ball mill after mixing and is formed, and constituent precentagewise amount part composition is as follows：Phosphorus slag
What the 30%th, boiler slag 25%, production calcium aluminate powder were produced is useless somehow 40%, gypsum 5%.
Embodiment 2
A kind of dry powder clay, main constituent be produce useless of phosphorus slag, boiler slag, production calcium aluminate powder somehow and gypsum press
Ratio is mixed, and is worn into micropowders using ball mill after mixing and is formed：Phosphorus slag 35%, boiler slag 29%, production calcium aluminate powder production
Raw is useless somehow 35%, gypsum 1%.
From embodiment 1 and embodiment 2, above-described embodiment 1 and embodiment 2 are painted using on exterior wall, its with it is general
Water flowing mud paints to obtain table 1 on exterior wall,
The embodiment 1 of table 1, embodiment 2 and ordinary cement identical environment and under the conditions of use the contrast in external rendering to imitate
Really
Can be with when dry powder clay of the invention is used on exterior wall, than the acidproof decay resistance of ordinary cement by table 1
Good, flameproof effect is good and high insulating effect, meanwhile, we pass through under the same conditions to ordinary cement and embodiments of the invention
1 exterior wall painted with embodiment 2 is contrast experiment and obtains table 2
The exterior wall of exterior wall and the embodiments of the invention 1 that the ordinary cement of table 2 is painted and the rendering of embodiment 2 it is mutually synthermal,
The contrast experiment sprayed under damp condition using extremely strong acidic materials
As shown in Table 2, sprayed under identical temperature, damp condition using extremely strong acidic materials, use the reality of the present invention
The decay resistance for the exterior wall that example 1 is painted with embodiment 2 is applied apparently higher than the decay resistance of ordinary cement.
Described above is only the preferred embodiment of the present invention, it is noted that for the ordinary skill people of the art
For member, without departing from the technical principles of the invention, some improvement can also be made, these improvement also should be regarded as this hair
Bright protection domain.
Claims (3)
1. a kind of dry powder clay, main constituent be produce useless of phosphorus slag, boiler slag, production calcium aluminate powder somehow and gypsum press than
Example mixing, it is characterised in that：Micropowders are worn into after mixing using ball mill to form, constituent precentagewise amount part composition is such as
Under：It is useless somehow 35%~40%, gypsum 1% that phosphorus slag 30%~35%, boiler slag 25%~29%, production calcium aluminate powder are produced
~5%.
2. a kind of dry powder clay according to claim 1, it is characterised in that：Constituent precentagewise amount part composition is as follows：
It is useless somehow 40%, gypsum 5% that phosphorus slag 30%, boiler slag 25%, production calcium aluminate powder are produced.
3. a kind of dry powder clay according to claim 1, it is characterised in that：Constituent precentagewise amount part composition is as follows：
It is useless somehow 35%, gypsum 1% that phosphorus slag 35%, boiler slag 29%, production calcium aluminate powder are produced.