CN102898098B - Preparation technology of flame retardant partition board containing waste glass powder - Google Patents

Preparation technology of flame retardant partition board containing waste glass powder Download PDF

Info

Publication number
CN102898098B
CN102898098B CN201210354073.1A CN201210354073A CN102898098B CN 102898098 B CN102898098 B CN 102898098B CN 201210354073 A CN201210354073 A CN 201210354073A CN 102898098 B CN102898098 B CN 102898098B
Authority
CN
China
Prior art keywords
powder
cullet
weight
fineness
technology
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN201210354073.1A
Other languages
Chinese (zh)
Other versions
CN102898098A (en
Inventor
刘春梅
汪祖强
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ANHUI BUYETIAN INTERLLIGENT DISPLAY TECHNOLOGY Co Ltd
Original Assignee
ANHUI BUYETIAN INTERLLIGENT DISPLAY TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ANHUI BUYETIAN INTERLLIGENT DISPLAY TECHNOLOGY Co Ltd filed Critical ANHUI BUYETIAN INTERLLIGENT DISPLAY TECHNOLOGY Co Ltd
Priority to CN201210354073.1A priority Critical patent/CN102898098B/en
Publication of CN102898098A publication Critical patent/CN102898098A/en
Application granted granted Critical
Publication of CN102898098B publication Critical patent/CN102898098B/en
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The invention discloses a preparation technology of a flame retardant partition board containing waste glass powder. The flame retardant partition board is prepared from the following raw materials by weight part: 15-20 of portland cement, 38-40 of waste glass powder, 10-15 of Magan soil, 8-12 of phosphogypsum powder, 4-6 of kaolin, 8-10 of mineral mixture burned powder, 1-1.5 of sodium hexametaphosphate, 1-2 of magnesium hydroxide, 6-10 of hydrogen peroxide with a concentration of 30-40%, and a proper amount of water. The partition board provided in the invention has the advantages of high strength, good shock resistance, good flame retardance, and low volume weight, etc.

Description

A kind of preparation technology of the fire-retardant partition plate that contains cullet powder
Technical field
The present invention relates to building material field, is exactly a kind of preparation technology of the fire-retardant partition plate that contains cullet powder.
Background technology
Light cellular partition board is a kind of novel energy-conserving walling material, the walling that it is a kind of external form as the cassette ceiling, but there is male and female falcon groove on its both sides, during installation, only sheet material need be erected, and male and female falcon is coated after a small amount of filleting mortar assembled.It is comprised of various industrial waste residues such as innoxious phosphogypsum, lightweight slag, flyash, through the maintenance of frequency conversion steam pressurized, forms.Current partition plate ubiquity wallboard intensity is low, and anti-folding, shock resistance are poor, the shortcoming such as soundproof effect, water resistance are poor.
Glass is VIO (Very Important Object) too busy to get away in people's daily life, yet just becomes very unmanageable environmental pollutant once glass cullet and cullet goods are arbitrarily thrown out without care, and a large amount of cullet are full of the refuse tip in city, has also won the bad reputation of one " dodging look pollutes ".
The solid slag that phosphogypsum produces while referring in phosphoric acid production with sulfuric acid treating phosphorite, its main component is calcium sulfate.
Summary of the invention
The object of the present invention is to provide the preparation technology of the fire-retardant partition plate that contains cullet powder that a kind of intensity is high, shock resistance is good.
Above-mentioned purpose realizes by following scheme:
A preparation technology for the fire-retardant partition plate that contains cullet powder, is characterized in that:
(1) batching: the described fire-retardant partition plate that contains cullet powder is that the raw material by following weight parts makes:
Silicate cement 15-20, cullet powder 38-40, horse liver soil 10-15, phosphogypsum powder 8-12, kaolin 4-6, mineral mix scaling loss powder 8-10, Sodium hexametaphosphate 99 1-1.5, magnesium hydroxide 1-2, the hydrogen peroxide 6-10 that concentration is 30-40%, water is appropriate;
Described mineral mix scaling loss powder by 4-6 weight part fluorite slag, after 3-5 weight part expanded vermiculite powder, 3-5 weight part snake rock dust mix, scaling loss 3-4 hour at 800-950 ℃, after grind to form nanometer powder and obtain;
Described cullet powder is that cullet is calcined to 4-6 hour at 800-900 ℃, and rear grinding adds 1-2% Zinc Stearate, and 1-2% dioctadecylamine, 1-2% dispersing agent MF, 3-4% methyl-silicone oil mix to dry are pulverized, and crosses 100-200 mesh sieve and obtains;
(2) get by weight silicate cement, add suitable quantity of water and stir, obtain grout;
(3) grout, hydrogen peroxide are mixed, finally add all the other raw materials to stir, obtain slurry;
(4) slurry is dropped into wall slab squeezing former moulding, cutting, natural curing, obtain.
The preparation technology of described a kind of fire-retardant partition plate that contains cullet powder, it is characterized in that: described cullet powder fineness is 80-100 order, described phosphogypsum powder fineness is 100-180 order, and described horse liver soil fineness is 80-100 order, and described kaolin fineness is 100-200 order.
Beneficial effect of the present invention is: cullet is drawn materials easily, with low cost, solves refuse reclamation problem, and energy-conserving and environment-protective increase the intensity of partition plate simultaneously.The present invention has the advantages such as intensity is high, shock resistance good, and flame retardant properties is good, and unit weight is low.Magnesium hydroxide has certain flame retardant effect.The dried unit weight of hardened material is at 300-500kg/m 3scope, ultimate compression strength is between 5-7.3MPa.
Embodiment
Embodiment 1:
A preparation technology for the fire-retardant partition plate that contains cullet powder,
(1) batching: the described fire-retardant partition plate that contains cullet powder is that the raw material by following weight parts (kg) makes:
Silicate cement 20, cullet powder 40, horse liver soil 15, phosphogypsum powder 12, kaolin 6, mineral mix scaling loss powder 10, Sodium hexametaphosphate 99 1, magnesium hydroxide 1, the hydrogen peroxide 10 that concentration is 30%, water is appropriate;
Described mineral mix scaling loss powder by 4 weight part fluorite slags, and after 3 weight part expanded vermiculite powders, 3 weight part snake rock dust mix, at 950 ℃, scaling loss is 4 hours, after grind to form nanometer powder and obtain;
Described cullet powder is that cullet is calcined to 4-6 hour at 800-900 ℃, and rear grinding adds 1-2% Zinc Stearate, and 1-2% dioctadecylamine, 1-2% dispersing agent MF, 3-4% methyl-silicone oil mix to dry are pulverized, and crosses 100-200 mesh sieve and obtains;
(2) get by weight silicate cement, add suitable quantity of water and stir, obtain grout;
(3) grout, hydrogen peroxide are mixed, finally add all the other raw materials to stir, obtain slurry;
(4) slurry is dropped into wall slab squeezing former moulding, cutting, natural curing, obtain.
Described cullet powder fineness is 100 orders, and described phosphogypsum powder fineness is 100 orders, and described horse liver soil fineness is 100 orders, and described kaolin fineness is 100 orders.
The unit weight of the present embodiment is 410Kg/m 3, ultimate compression strength is 6.3MPa. ?????
Embodiment 2:
A preparation technology for the fire-retardant partition plate that contains cullet powder,
(1) batching: the described fire-retardant partition plate that contains cullet powder is that the raw material by following weight parts makes:
Silicate cement 15, cullet powder 38, horse liver soil 10, phosphogypsum powder 8, kaolin 4, mineral mix scaling loss powder 10, Sodium hexametaphosphate 99 1.5, magnesium hydroxide 2, the hydrogen peroxide 6 that concentration is 40%, water 25;
Described mineral mix scaling loss powder by 6 weight part fluorite slags, and after 5 weight part expanded vermiculite powders, 5 weight part snake rock dust mix, at 950 ℃, scaling loss is 3 hours, after grind to form nanometer powder and obtain;
Described cullet powder is that cullet is calcined to 4-6 hour at 800-900 ℃, and rear grinding adds 1-2% Zinc Stearate, and 1-2% dioctadecylamine, 1-2% dispersing agent MF, 3-4% methyl-silicone oil mix to dry are pulverized, and crosses 100-200 mesh sieve and obtains;
(2) get by weight silicate cement, add suitable quantity of water and stir, obtain grout;
(3) grout, hydrogen peroxide are mixed, finally add all the other raw materials to stir, obtain slurry;
(4) slurry is dropped into wall slab squeezing former moulding, cutting, natural curing, obtain.
Described cullet powder fineness is 100 orders, and described phosphogypsum powder fineness is 180 orders, and described horse liver soil fineness is 80 orders, and described kaolin fineness is 100 orders.
The unit weight of the present embodiment is 500Kg/m 3, ultimate compression strength is 6.7MPa.

Claims (2)

1. a preparation technology who contains the fire-retardant partition plate of cullet powder, is characterized in that:
(1) batching: the described fire-retardant partition plate that contains cullet powder is that the raw material by following weight parts makes:
Silicate cement 15-20, cullet powder 38-40, horse liver soil 10-15, phosphogypsum powder 8-12, kaolin 4-6, mineral mix scaling loss powder 8-10, Sodium hexametaphosphate 99 1-1.5, magnesium hydroxide 1-2, the hydrogen peroxide 6-10 that concentration is 30-40%, water is appropriate;
Described mineral mix scaling loss powder by 4-6 weight part fluorite slag, after 3-5 weight part expanded vermiculite powder, 3-5 weight part snake rock dust mix, scaling loss 3-4 hour at 800-950 ℃, after grind to form nanometer powder and obtain;
Described cullet powder is that cullet is calcined to 4-6 hour at 800-900 ℃, and rear grinding adds 1-2% Zinc Stearate, and 1-2% dioctadecylamine, 1-2% dispersing agent MF, 3-4% methyl-silicone oil mix to dry are pulverized, and crosses 100-200 mesh sieve and obtains;
(2) get by weight silicate cement, add suitable quantity of water and stir, obtain grout;
(3) grout, hydrogen peroxide are mixed, finally add all the other raw materials to stir, obtain slurry;
(4) slurry is dropped into wall slab squeezing former moulding, cutting, natural curing, obtain.
2. the preparation technology of a kind of fire-retardant partition plate that contains cullet powder according to claim 1, it is characterized in that: described cullet powder fineness is 80-100 order, described phosphogypsum powder fineness is 100-180 order, described horse liver soil fineness is 80-100 order, and described kaolin fineness is 100-200 order.
CN201210354073.1A 2012-09-21 2012-09-21 Preparation technology of flame retardant partition board containing waste glass powder Expired - Fee Related CN102898098B (en)