CN107264100A - A kind of water writes coating and printing integrated technique - Google Patents
A kind of water writes coating and printing integrated technique Download PDFInfo
- Publication number
- CN107264100A CN107264100A CN201710362367.1A CN201710362367A CN107264100A CN 107264100 A CN107264100 A CN 107264100A CN 201710362367 A CN201710362367 A CN 201710362367A CN 107264100 A CN107264100 A CN 107264100A
- Authority
- CN
- China
- Prior art keywords
- ink
- water
- parts
- printing
- write
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Coating and printing integrated technique is write the invention belongs to a kind of water；Comprise the following steps：White developing layer water-based ink is prepared, the raw material that white developing layer water-based ink includes following parts by weight is formulated：25~40 parts of deionized water, 0.1~0.5 part of polyethylene glycol, 0.2~0.4 part of polyethylene glycol oxide, 0.5~1.2 part of polyacrylamide, 0.2~0.6 part of propylene-glycol ethyl ether, 0.2~0.45 part of dimethyl silicone polymer, 0.2~0.35 part of trimethylglycine, 20~40 parts of kaolin, by first time red ink, Yellow ink, blue ink, black ink, white developing layer water-based ink and second of red ink is various is sequentially placed in ink tank or pump, paper to be printed is put into, printing machine is opened and is routinely printed；There is reduction water writing paper production cost, suitable for water writing paper industrialized production, the printing efficiency of raising water writing paper.
Description
Technical field
The invention belongs to water writing paper printing technology, and in particular to a kind of water writes coating and printing integrated technique.
Background technology
With water writing paper, water writing cloth, double-surface writing water writing paper (ink writing technology) birth, and widely used with it,
The energy-conservation practice calligraphy, painted, cleaning problems are addressed.But due to water writing cloth be entire volume cloth, water writing paper whole cylinder into
On the basis of product paper, formed through multiple coating waste water；Water writing cloth can only use silk-screen printing, and water writing paper powder in printing process
Dirt is big, scumming frequency is high, print speed printing speed is slow, defect rate is high, into book cost it is higher；Also having resulted in water writing cloth can not print very
The books cost of books, water writing paper printing in justice meaning is high.
The content of the invention
It is an object of the invention to overcome existing water to write the defect in coating technique and waste there is provided one kind to pass through to aqueous
Printing-ink formula is transformed and in printing process by typesetting and using fixed printing process, by the painting of water writing paper
Cloth technique is changed into the painting print integrated technique completed in printing process, without coating again to the whole area of whole paper progress, and
It is to write area of practising handwriting according to the water being actually needed, arbitrarily adjustment water writes the size of spreading area, is retouched so as to reduce write note, water of water
Model painting book books production cost, satisfaction quickly prints various drills to improve one's handwriting, a kind of water of the books printing demand of painting practice and writes painting
Cloth prints integrated technique.
The present invention is achieved through the following technical solutions above-mentioned purpose：Comprise the following steps：
Step one：White developing layer water-based ink is prepared, white developing layer water-based ink includes the original of following parts by weight
Material is formulated：25~40 parts of deionized water, 0.1~0.5 part of polyethylene glycol, 0.2~0.4 part of polyethylene glycol oxide, polyacrylamide
0.5~1.2 part of amine, 0.2~0.6 part of propylene-glycol ethyl ether, 0.2~0.45 part of dimethyl silicone polymer, trimethylglycine 0.2~
0.35 part, 20~40 parts of kaolin, 2~5 parts of calcium carbonate, 2~5 parts of propyl benzene emulsion, 1~3 part of titanium dioxide, 0.5~2 part of china clay,
0.3~1.0 part of 0.1~0.3 part of plant amylum, 20~45 parts of grind resin liquid and dimethyl amine, by above-mentioned raw materials deionization
Water, polyethylene glycol, polyethylene glycol oxide, polyacrylamide, propylene-glycol ethyl ether, dimethyl silicone polymer, trimethylglycine, kaolinite
Soil, calcium carbonate, propyl benzene emulsion, titanium dioxide, china clay, plant amylum, grind resin liquid and dimethyl amine mix be placed in proportion
In ink grinder, after grinding 1~1.5 hour, it is placed in container standby after resting 24 hours；Described plant amylum is beans
One of class or potato starch；
Step 2：By first time red ink, Yellow ink, blue ink, black ink, white developing layer water-based ink
With second of red ink is various is sequentially placed in ink tank or pump, be put into paper to be printed, open printing machine routinely
Printed；
Step 3：On paper to be printed determine water write surface area and it is non-aqueous write surface area, write area non-aqueous
Region carries out normal color matching to four colors of first time red ink, Yellow ink, blue ink and black ink and printed；Write in water
Printing blue ink in surface area, after blue ink is finished printing, in the upper print black ink of blue ink, blueness
Ink and black ink are collectively forming the development bottom that water writes position；It can be respectively 1.5cm that the water, which writes surface area,2~
20cm2；
Step 4：Write in step 3 reclaimed water and white developing layer water-based ink is printed on the black ink in surface area；
Step 5：Write in step 4 reclaimed water and print second of reddish oil on the white developing layer water-based ink in surface area
The double check with a core of ink or well-behaved white silk line；
Step 6：Make to print second of red ink double check with a core in step 5 or the well-behaved paper practiced after line enters drying baker
It is interior to be dried, the printing paper of drying solidification, respectively through cutting, folding, binding is into book；The drying temperature of the drying baker
For：100 DEG C~220 DEG C；Drying time is 1~3 second.
It is of the invention compared with existing water writing paper, it is possible to reduce more than 80% cost of manufacture；On the printing time, using this
1 hour of invention can be printed as books, and adopting existing water writing paper printing at least needs 5 working days to complete；Compiled in books
On volume, the calligraphy skill explanation of existing water writing paper can not possibly write exercise terrain feature edit in the same page with water, and water writes coating print
Brush integrated technique, can arbitrarily edit the explanation of calligraphy skill, water and write exercise region, and water is write the size in region and can arbitrarily adjusted
It is whole；The present invention can effectively reduce that dust in printing process is big, scumming frequency is high, print speed printing speed is slow, defect rate is high and into book
The problem of cost is high；Imitated with reduction water writing paper production cost, suitable for the printing of water writing paper industrialized production, raising water writing paper
The advantage of rate.
Embodiment
The present invention writes coating and printing integrated technique for a kind of water, comprises the following steps：
Step one：White developing layer water-based ink is prepared, white developing layer water-based ink includes the original of following parts by weight
Material is formulated：25~40 parts of deionized water, 0.1~0.5 part of polyethylene glycol, 0.2~0.4 part of polyethylene glycol oxide, polyacrylamide
0.5~1.2 part of amine, 0.2~0.6 part of propylene-glycol ethyl ether, 0.2~0.45 part of dimethyl silicone polymer, trimethylglycine 0.2~
0.35 part, 20~40 parts of kaolin, 2~5 parts of calcium carbonate, 2~5 parts of propyl benzene emulsion, 1~3 part of titanium dioxide, 0.5~2 part of china clay,
0.3~1.0 part of 0.1~0.3 part of plant amylum, 20~45 parts of grind resin liquid and dimethyl amine, by above-mentioned raw materials deionization
Water, polyethylene glycol, polyethylene glycol oxide, polyacrylamide, propylene-glycol ethyl ether, dimethyl silicone polymer, trimethylglycine, kaolinite
Soil, calcium carbonate, propyl benzene emulsion, titanium dioxide, china clay, plant amylum, grind resin liquid and dimethyl amine mix be placed in proportion
In ink grinder, after grinding 1~1.5 hour, it is placed in container standby after resting 24 hours；Described plant amylum is beans
One of class or potato starch；
Step 2：By first time red ink, Yellow ink, blue ink, black ink, white developing layer water-based ink
With second of red ink is various is sequentially placed in ink tank or pump, be put into paper to be printed, open printing machine routinely
Printed；
Step 3：On paper to be printed determine water write surface area and it is non-aqueous write surface area, write area non-aqueous
Region carries out normal color matching to four colors of first time red ink, Yellow ink, blue ink and black ink and printed；Write in water
Printing blue ink in surface area, after blue ink is finished printing, in the upper print black ink of blue ink, blueness
Ink and black ink are collectively forming the development bottom that water writes position；It can be respectively 1.5cm that the water, which writes surface area,2~
20cm2；
Step 4：Write in step 3 reclaimed water and white developing layer water-based ink is printed on the black ink in surface area；
Step 5：Write in step 4 reclaimed water and print second of reddish oil on the white developing layer water-based ink in surface area
The double check with a core of ink or well-behaved white silk line；
Step 6：Make to print second of red ink double check with a core in step 5 or the well-behaved paper practiced after line enters drying baker
It is interior to be dried, the printing paper of drying solidification, respectively through cutting, folding, binding is into book；The drying temperature of the drying baker
For：100 DEG C~220 DEG C；Drying time is 1~3 second.
It is of the invention compared with existing water writing paper, it is possible to reduce more than 80% cost of manufacture；On the printing time, using this
The finished product books of 1 hour printing of invention, 5 are at least needed using existing either double water writing paper or one side water writing paper printings
Working day could complete；On book editor, the calligraphy skill explanation of existing water writing paper can not possibly write exercise terrain feature edit with water
In the same page, and the present invention can arbitrarily edit the word explanation region of arrangement calligraphy skill, water in the same page and write exercise
Region, and water writes the size in region and can arbitrarily adjust；The present invention can effectively reduce that dust in printing process is big, scumming
Frequency is high, print speed printing speed is slow, defect rate is high and into book cost it is high the problem of；Water writes coating and printing integrated technique, is particularly suitable for use in
《Drills to improve one's handwriting are instructed》The editor of voluntary textbook and short time, the production of large batch of industrialization quick print.
Below in conjunction with embodiments of the invention, the technical scheme in embodiments of the invention is carried out clearly and completely
Description, it is clear that described embodiment is only a part of embodiment of the present invention, rather than whole embodiments.Based on this
Embodiment in invention, it is all that one of ordinary skilled in the art is obtained on the premise of creative work is not made
Other embodiments, belong to the scope of protection of the invention.
Embodiment one
A kind of water writes coating and printing integrated technique, comprises the following steps：
Step one：White developing layer water-based ink is prepared, white developing layer water-based ink includes the original of following parts by weight
Material is formulated：25 parts of deionized water, 0.1 part of polyethylene glycol, 0.2 part of polyethylene glycol oxide, 0.5 part of polyacrylamide, propane diols
0.2 part of ether, 0.2 part of dimethyl silicone polymer, 0.2 part of trimethylglycine, 20 parts of kaolin, 2 parts of calcium carbonate, propyl benzene emulsion
0.3 part of 2 parts, 1 part of titanium dioxide, 0.5 part of china clay, 0.1 part of plant amylum, 20 parts of grind resin liquid and dimethyl amine, will be above-mentioned
Raw material deionized water, polyethylene glycol, polyethylene glycol oxide, polyacrylamide, propylene-glycol ethyl ether, dimethyl silicone polymer, trimethyl
Glycine, kaolin, calcium carbonate, propyl benzene emulsion, titanium dioxide, china clay, plant amylum, grind resin liquid and dimethyl amine press than
Example mixing is placed in ink grinder, after grinding 1~1.5 hour, is placed in container standby after resting 24 hours；Described plant
Thing starch is bean starch；
Step 2：By first time red ink, Yellow ink, blue ink, black ink, white developing layer water-based ink
With second of red ink is various is sequentially placed in ink tank or pump, be put into paper to be printed, open printing machine routinely
Printed；
Step 3：On paper to be printed determine water write surface area and it is non-aqueous write surface area, write area non-aqueous
Region carries out normal color matching to four colors of first time red ink, Yellow ink, blue ink and black ink and printed；Write in water
Printing blue ink in surface area, after blue ink is finished printing, in the upper print black ink of blue ink, blueness
Ink and black ink are collectively forming the development bottom that water writes position；It can be respectively 1.5cm that the water, which writes surface area,2~
20cm2；
Step 4：Write in step 3 reclaimed water and white developing layer water-based ink is printed on the black ink in surface area；
Step 5：Write in step 4 reclaimed water and print second of reddish oil on the white developing layer water-based ink in surface area
The double check with a core of ink or well-behaved white silk line；
Step 6：Make to print second of red ink double check with a core in step 5 or the well-behaved paper practiced after line enters drying baker
It is interior to be dried, the printing paper of drying solidification, respectively through cutting, folding, binding is into book；The drying temperature of the drying baker
For：220℃；Drying time is 1 second.
Embodiment two
A kind of water writes coating and printing integrated technique, comprises the following steps：
Step one：White developing layer water-based ink is prepared, white developing layer water-based ink includes the original of following parts by weight
Material is formulated：40 parts of deionized water, 0.5 part of polyethylene glycol, 0.4 part of polyethylene glycol oxide, 1.2 parts of polyacrylamide, propane diols
0.6 part of ether, 0.45 part of dimethyl silicone polymer, 0.35 part of trimethylglycine, 40 parts of kaolin, 5 parts of calcium carbonate, propyl benzene breast
1.0 parts of 5 parts of liquid, 3 parts of titanium dioxide, 2 parts of china clay, 0.3 part of plant amylum, 45 parts of grind resin liquid and dimethyl amine, will be above-mentioned
Raw material deionized water, polyethylene glycol, polyethylene glycol oxide, polyacrylamide, propylene-glycol ethyl ether, dimethyl silicone polymer, trimethyl
Glycine, kaolin, calcium carbonate, propyl benzene emulsion, titanium dioxide, china clay, plant amylum, grind resin liquid and dimethyl amine press than
Example mixing is placed in ink grinder, after grinding 1~1.5 hour, is placed in container standby after resting 24 hours；Described plant
Thing starch is potato starch；
Step 2：By first time red ink, Yellow ink, blue ink, black ink, white developing layer water-based ink
With second of red ink is various is sequentially placed in ink tank or pump, be put into paper to be printed, open printing machine routinely
Printed；
Step 3：On paper to be printed determine water write surface area and it is non-aqueous write surface area, write area non-aqueous
Region carries out normal color matching to four colors of first time red ink, Yellow ink, blue ink and black ink and printed；Write in water
Printing blue ink in surface area, after blue ink is finished printing, in the upper print black ink of blue ink, blueness
Ink and black ink are collectively forming the development bottom that water writes position；It can be respectively 1.5cm that the water, which writes surface area,2~
20cm2；
Step 4：Write in step 3 reclaimed water and white developing layer water-based ink is printed on the black ink in surface area；
Step 5：Write in step 4 reclaimed water and print second of reddish oil on the white developing layer water-based ink in surface area
The double check with a core of ink or well-behaved white silk line；
Step 6：Make to print second of red ink double check with a core in step 5 or the well-behaved paper practiced after line enters drying baker
It is interior to be dried, the printing paper of drying solidification, respectively through cutting, folding, binding is into book；The drying temperature of the drying baker
For：100℃；Drying time is：3 seconds.
Embodiment three
A kind of water writes coating and printing integrated technique, comprises the following steps：
Step one：White developing layer water-based ink is prepared, white developing layer water-based ink includes the original of following parts by weight
Material is formulated：32.5 parts of deionized water, 0.6 part of polyethylene glycol, 0.3 part of polyethylene glycol oxide, 0.85 part of polyacrylamide, the third two
0.4 part of alcohol ether, 0.325 part of dimethyl silicone polymer, 0.275 part of trimethylglycine, 30 parts of kaolin, 3.5 parts of calcium carbonate,
3.5 parts of propyl benzene emulsion, 2 parts of titanium dioxide, 1.25 parts of china clay, 0.2 part of plant amylum, 32.5 parts of grind resin liquid and dimethyl amine
0.65 part, by above-mentioned raw materials deionized water, polyethylene glycol, polyethylene glycol oxide, polyacrylamide, propylene-glycol ethyl ether, poly dimethyl
Siloxanes, trimethylglycine, kaolin, calcium carbonate, propyl benzene emulsion, titanium dioxide, china clay, plant amylum, grind resin liquid and
Dimethyl amine is mixed in proportion to be placed in ink grinder, after grinding 1~1.5 hour, is placed in container and is rested 24 hours
It is standby afterwards；Described plant amylum is bean starch；
Step 2：By first time red ink, Yellow ink, blue ink, black ink, white developing layer water-based ink
With second of red ink is various is sequentially placed in ink tank or pump, be put into paper to be printed, open printing machine routinely
Printed；
Step 3：On paper to be printed determine water write surface area and it is non-aqueous write surface area, write area non-aqueous
Region carries out normal color matching to four colors of first time red ink, Yellow ink, blue ink and black ink and printed；Write in water
Printing blue ink in surface area, after blue ink is finished printing, in the upper print black ink of blue ink, blueness
Ink and black ink are collectively forming the development bottom that water writes position；It can be respectively 1.5cm that the water, which writes surface area,2~
20cm2；
Step 4：Write in step 3 reclaimed water and white developing layer water-based ink is printed on the black ink in surface area；
Step 5：Write in step 4 reclaimed water and print second of reddish oil on the white developing layer water-based ink in surface area
The double check with a core of ink or well-behaved white silk line；
Step 6：Make to print second of red ink double check with a core in step 5 or the well-behaved paper practiced after line enters drying baker
It is interior to be dried, the printing paper of drying solidification, respectively through cutting, folding, binding is into book；The drying temperature of the drying baker
For：160℃；Drying time is 2 seconds.
Heretofore described bean starch includes mung bean, pea, broad bean, red bean etc.；Potato starch include potato,
Sweet potato, cassava etc..
Foregoing detailed description is illustrated only for the feasibility embodiment of the present invention, and they are simultaneously not used to
Limit the scope of the invention, all equivalent implementations made without departing from skill spirit of the present invention, change and transformation all should
Within protection scope of the present invention.
Claims (1)
1. a kind of water writes coating and printing integrated technique, it is characterised in that：The integrated technique comprises the following steps：
Step one：White developing layer water-based ink is prepared, the raw material that white developing layer water-based ink includes following parts by weight is matched somebody with somebody
System is formed：25~40 parts of deionized water, 0.1~0.5 part of polyethylene glycol, 0.2~0.4 part of polyethylene glycol oxide, polyacrylamide 0.5
~1.2 parts, 0.2~0.6 part of propylene-glycol ethyl ether, 0.2~0.45 part of dimethyl silicone polymer, trimethylglycine 0.2~0.35
Part, 20~40 parts of kaolin, 2~5 parts of calcium carbonate, 2~5 parts of propyl benzene emulsion, 1~3 part of titanium dioxide, 0.5~2 part of china clay, plant
0.3~1.0 part of 0.1~0.3 part of starch, 20~45 parts of grind resin liquid and dimethyl amine, by above-mentioned raw materials deionized water, gather
Ethylene glycol, polyethylene glycol oxide, polyacrylamide, propylene-glycol ethyl ether, dimethyl silicone polymer, trimethylglycine, kaolin, carbon
Sour calcium, propyl benzene emulsion, titanium dioxide, china clay, plant amylum, grind resin liquid and dimethyl amine are mixed in proportion to be placed in ink and grinds
In grinding machine, after grinding 1~1.5 hour, it is placed in container standby after resting 24 hours；Described plant amylum is beans or potato
One of kind of starch；
Step 2：By first time red ink, Yellow ink, blue ink, black ink, white developing layer water-based ink and the
Secondary red ink is various to be sequentially placed in ink tank or pump, is put into paper to be printed, is opened printing machine and is routinely carried out
Printing；
Step 3：On paper to be printed determine water write surface area and it is non-aqueous write surface area, write surface area non-aqueous
Normal color matching printing is carried out to four colors of first time red ink, Yellow ink, blue ink and black ink；Area is write in water
Blue ink is printed in region, after blue ink is finished printing, in the upper print black ink of blue ink, blue ink
The development bottom that water writes position is collectively forming with black ink；It can be respectively 1.5cm that the water, which writes surface area,2~20cm2；
Step 4：Write in step 3 reclaimed water and white developing layer water-based ink is printed on the black ink in surface area；
Step 5：Write in step 4 reclaimed water and second red ink is printed on the white developing layer water-based ink in surface area
Double check with a core or well-behaved white silk line；
Step 6：Make to print second of red ink double check with a core in step 5 or the well-behaved paper practiced after line is put into drying baker
Row drying, the printing paper of drying solidification, respectively through cutting, folding, binding is into book；The drying temperature of the drying baker is：
100 DEG C~220 DEG C；Drying time is 1~3 second.