CN107263664A - A kind of preparation method of lightweight clothes hanger - Google Patents
A kind of preparation method of lightweight clothes hanger Download PDFInfo
- Publication number
- CN107263664A CN107263664A CN201710498111.3A CN201710498111A CN107263664A CN 107263664 A CN107263664 A CN 107263664A CN 201710498111 A CN201710498111 A CN 201710498111A CN 107263664 A CN107263664 A CN 107263664A
- Authority
- CN
- China
- Prior art keywords
- parts
- clothes hanger
- preparation
- lightweight
- glue
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention discloses a kind of preparation method of lightweight clothes hanger, including following operating procedure：（1）Wood skin is made in timber rotary-cut after drying；（2）Strengthen liquid in obtained veneer surface uniformly sprinkling, dry 46 days；（3）Wood skin positive and negative after drying is handled uniformly applies glue, hot-forming then by after the shape of wood skin and the stacked stand for ready-made clothes of batten, and lightweight clothes hanger is made after cutting.The preparation method for the lightweight clothes hanger that the present invention is provided, operating method is simple, and technique is simple, and required equipment cost is relatively low, obtained wooden clothes hanger, and not only intensity is higher, and light weight, it is easy to carry.
Description
Technical field
The invention belongs to clothes hanger preparation field, and in particular to a kind of preparation method of lightweight clothes hanger.
Background technology
In recent years, with the raising of people's quality of the life, it can give people to get close to naturally, warm, graceful feels wooden clothes hanger
Received by increasing people.Producing the timber of wooden clothes tree will can typically produce below 18 degree of humidity, use
Before will carry out drying and processing, if fund allow, timber can be hoarded, done naturally to be best.The timber for having small holes caused by worms is then refused
Using wooden clothes tree production procedure is mainly four big processes, and blank, frosted, paint, assembling, presently commercially available most of clothes hanger are equal
It is made of that, using solid wood, the cost so not only made is higher, and obtained clothes hanger, weight is big, whether carries or deposits
Storage is all more inconvenient.
The content of the invention
In order to solve the above problems, the present invention provides a kind of preparation method for the lightweight yoke for reducing production cost.
The present invention is achieved by the following technical solutions.
A kind of preparation method of lightweight clothes hanger, including following operating procedure：
（1）Wood skin is made in timber rotary-cut after drying；
（2）Strengthen liquid in obtained veneer surface uniformly sprinkling, dry 4-6 days, wherein strengthening liquid by following parts by weight
Component is made：15-20 parts of 4- halogen trimethylsilylbenzene ethene, 10-13 parts of N- octyl groups diaminoethyl glycine hydrochloride, O-phthalic
14-16 parts of dioctyl phthalate, 38-42 parts of sodium alginate, 100-120 parts of ethanol, 200-220 parts of water；
（3）Wood skin positive and negative after drying is handled uniformly applies glue, then by wood skin and the shape of the stacked stand for ready-made clothes of batten
It is hot-forming after shape, lightweight clothes hanger is made after cutting, wherein glue is made up of the component of following parts by weight：Oxidized starch is bonded
It is 40-50 parts of agent, 2-4 parts of tetrabutyl ammonium fluoride, 3-6 parts of methylpropene sodium sulfonate, 6-9 parts of citric acid stearoyl monoglyceride, double
5-7 parts of methylol diethyl malonate.
Specifically, step（1）The thickness of wood skin made from middle rotary-cut is 1-2mm.
Specifically, step（2）In reinforcement liquid be made of following methods：By second alcohol and water it is well mixed after, successively to
Wherein add 4- halogen trimethylsilylbenzenes ethene, N- octyl group diaminoethyls glycine hydrochloride, dioctyl phthalate, alginic acid
After sodium is mixed evenly, it is made and strengthens liquid.
Specifically, the consumption for strengthening liquid is 150-200ml/m2。
Specifically, the glue is made of following methods：Tetrabutyl fluorination is added into oxidized starch binding agent successively
Ammonium, methylpropene sodium sulfonate, citric acid stearoyl monoglyceride, double methylol diethyl malonates, after being mixed evenly, system
Obtain glue.
Specifically, the consumption of above-mentioned glue is 200-250g/m2。
Specifically, temperature when above-mentioned hot-forming is 90-95 DEG C, and the time of pressurization is 15-20min.
Technical scheme more than, the beneficial effects of the invention are as follows：
The preparation method for the lightweight clothes hanger that the present invention is provided, operating method is simple, and technique is simple, and required equipment cost is relatively low, system
The wooden clothes hanger obtained, not only intensity is higher, and light weight, it is easy to carry.Timber is peeled into wood skin, Ran Houre in the present invention
Molded, then clothes hanger is made after shearing, technique is simple, it is to avoid complicated operating procedure prepared by conventional wooden clothes hanger；Step
（2）In reinforcement liquid, can effectively lift the intensity of wood skin so that the fibre structure in wood skin is even closer, lifting wood skin
Every mechanical property；The present invention uses oxidized starch glue as binding agent, not only with low cost, and safety and environmental protection, four fourths
After base ammonium fluoride, methylpropene sodium sulfonate, citric acid stearoyl monoglyceride, double methylol diethyl malonates synergy,
The adhesive property of oxidized starch not only can be effectively lifted, its heat resistance is lifted, prevents it from being failed in hot pressing, and it can be carried
The water resistance of glue is risen, clothes hanger is prevented during use, after bubble, glue cracking greatly improves lightweight
The service life of clothes hanger.
Embodiment
In order to make the purpose , technical scheme and advantage of the present invention be clearer, following examples are carried out to the present invention
It is further described.It should be appreciated that specific embodiment party example described herein is not used to limit only to explain the present invention
The fixed present invention.
Embodiment 1
A kind of preparation method of lightweight clothes hanger, including following operating procedure：
（1）Wood skin is made in timber rotary-cut after drying；
（2）Strengthen liquid in obtained veneer surface uniformly sprinkling, dry 4 days, wherein strengthening group of the liquid by following parts by weight
Divide and be made：15 parts of 4- halogen trimethylsilylbenzenes ethene, 10 parts of N- octyl group diaminoethyls glycine hydrochloride, dioctyl phthalate
14 parts, 38 parts of sodium alginate, 100 parts of ethanol, 200 parts of water；
（3）Wood skin positive and negative after drying is handled uniformly applies glue, then by wood skin and the shape of the stacked stand for ready-made clothes of batten
It is hot-forming after shape, lightweight clothes hanger is made after cutting, wherein glue is made up of the component of following parts by weight：Oxidized starch is bonded
40 parts of agent, 2 parts of tetrabutyl ammonium fluoride, 3 parts of methylpropene sodium sulfonate, 6 parts of citric acid stearoyl monoglyceride, double methylols the third two
5 parts of diethyl phthalate.
Specifically, step（1）The thickness of wood skin made from middle rotary-cut is 1mm.
Specifically, step（2）In reinforcement liquid be made of following methods：By second alcohol and water it is well mixed after, successively to
Wherein add 4- halogen trimethylsilylbenzenes ethene, N- octyl group diaminoethyls glycine hydrochloride, dioctyl phthalate, alginic acid
After sodium is mixed evenly, it is made and strengthens liquid.
Specifically, the consumption for strengthening liquid is 150ml/m2。
Specifically, the glue is made of following methods：Tetrabutyl fluorination is added into oxidized starch binding agent successively
Ammonium, methylpropene sodium sulfonate, citric acid stearoyl monoglyceride, double methylol diethyl malonates, after being mixed evenly, system
Obtain glue.
Specifically, the consumption of above-mentioned glue is 200g/m2。
Specifically, temperature when above-mentioned hot-forming is 90 DEG C, and the time of pressurization is 15min.
Embodiment 2
A kind of preparation method of lightweight clothes hanger, including following operating procedure：
（1）Wood skin is made in timber rotary-cut after drying；
（2）Strengthen liquid in obtained veneer surface uniformly sprinkling, dry 5 days, wherein strengthening group of the liquid by following parts by weight
Divide and be made：17 parts of 4- halogen trimethylsilylbenzenes ethene, 12 parts of N- octyl group diaminoethyls glycine hydrochloride, dioctyl phthalate
15 parts, 40 parts of sodium alginate, 110 parts of ethanol, 210 parts of water；
（3）Wood skin positive and negative after drying is handled uniformly applies glue, then by wood skin and the shape of the stacked stand for ready-made clothes of batten
It is hot-forming after shape, lightweight clothes hanger is made after cutting, wherein glue is made up of the component of following parts by weight：Oxidized starch is bonded
45 parts of agent, 3 parts of tetrabutyl ammonium fluoride, 5 parts of methylpropene sodium sulfonate, 8 parts of citric acid stearoyl monoglyceride, double methylols the third two
6 parts of diethyl phthalate.
Specifically, step（1）The thickness of wood skin made from middle rotary-cut is 1mm.
Specifically, step（2）In reinforcement liquid be made of following methods：By second alcohol and water it is well mixed after, successively to
Wherein add 4- halogen trimethylsilylbenzenes ethene, N- octyl group diaminoethyls glycine hydrochloride, dioctyl phthalate, alginic acid
After sodium is mixed evenly, it is made and strengthens liquid.
Specifically, the consumption for strengthening liquid is 170ml/m2。
Specifically, the glue is made of following methods：Tetrabutyl fluorination is added into oxidized starch binding agent successively
Ammonium, methylpropene sodium sulfonate, citric acid stearoyl monoglyceride, double methylol diethyl malonates, after being mixed evenly, system
Obtain glue.
Specifically, the consumption of above-mentioned glue is 230g/m2。
Specifically, temperature when above-mentioned hot-forming is 93 DEG C, and the time of pressurization is 17min.
Embodiment 3
A kind of preparation method of lightweight clothes hanger, including following operating procedure：
（1）Wood skin is made in timber rotary-cut after drying；
（2）Strengthen liquid in obtained veneer surface uniformly sprinkling, dry 6 days, wherein strengthening group of the liquid by following parts by weight
Divide and be made：20 parts of 4- halogen trimethylsilylbenzenes ethene, 13 parts of N- octyl group diaminoethyls glycine hydrochloride, dioctyl phthalate
16 parts, 42 parts of sodium alginate, 120 parts of ethanol, 220 parts of water；
（3）Wood skin positive and negative after drying is handled uniformly applies glue, then by wood skin and the shape of the stacked stand for ready-made clothes of batten
It is hot-forming after shape, lightweight clothes hanger is made after cutting, wherein glue is made up of the component of following parts by weight：Oxidized starch is bonded
40-50 parts of agent, 4 parts of tetrabutyl ammonium fluoride, 6 parts of methylpropene sodium sulfonate, 9 parts of citric acid stearoyl monoglyceride, double methylols
7 parts of diethyl malonate.
Specifically, step（1）The thickness of wood skin made from middle rotary-cut is 2mm.
Specifically, step（2）In reinforcement liquid be made of following methods：By second alcohol and water it is well mixed after, successively to
Wherein add 4- halogen trimethylsilylbenzenes ethene, N- octyl group diaminoethyls glycine hydrochloride, dioctyl phthalate, alginic acid
After sodium is mixed evenly, it is made and strengthens liquid.
Specifically, the consumption for strengthening liquid is 200ml/m2。
Specifically, the glue is made of following methods：Tetrabutyl fluorination is added into oxidized starch binding agent successively
Ammonium, methylpropene sodium sulfonate, citric acid stearoyl monoglyceride, double methylol diethyl malonates, after being mixed evenly, system
Obtain glue.
Specifically, the consumption of above-mentioned glue is 250g/m2。
Specifically, temperature when above-mentioned hot-forming is 95 DEG C, and the time of pressurization is 20min.
Clothes hanger is made with the mode of each embodiment respectively, in then being put goods on the market, follow-up Follow-up observation is found, this hair
Bright obtained clothes hanger service life is longer, during use, occurs without peeling, corrugated phenomenon, greatly improves clothing
The quality of frame.
Certainly, described above is not limitation of the present invention, and the present invention is also not limited to the example above, the art
Those of ordinary skill, in the essential scope of the present invention, the change made, changes, addition or replace, should all belong to of the invention
Protection domain.
Claims (7)
1. a kind of preparation method of lightweight clothes hanger, it is characterised in that including following operating procedure：
（1）Wood skin is made in timber rotary-cut after drying；
（2）Strengthen liquid in obtained veneer surface uniformly sprinkling, dry 4-6 days, wherein strengthening liquid by following parts by weight
Component is made：15-20 parts of 4- halogen trimethylsilylbenzene ethene, 10-13 parts of N- octyl groups diaminoethyl glycine hydrochloride, O-phthalic
14-16 parts of dioctyl phthalate, 38-42 parts of sodium alginate, 100-120 parts of ethanol, 200-220 parts of water；
（3）Wood skin positive and negative after drying is handled uniformly applies glue, then by wood skin and the shape of the stacked stand for ready-made clothes of batten
It is hot-forming after shape, lightweight clothes hanger is made after cutting, wherein glue is made up of the component of following parts by weight：Oxidized starch is bonded
It is 40-50 parts of agent, 2-4 parts of tetrabutyl ammonium fluoride, 3-6 parts of methylpropene sodium sulfonate, 6-9 parts of citric acid stearoyl monoglyceride, double
5-7 parts of methylol diethyl malonate.
2. a kind of preparation method of lightweight clothes hanger according to claim 1, it is characterised in that step（1）Middle rotary-cut system
The thickness of the wood skin obtained is 1-2mm.
3. a kind of preparation method of lightweight clothes hanger according to claim 1, it is characterised in that step（2）In reinforcement
Liquid is made of following methods：After second alcohol and water is well mixed, 4- halogen trimethylsilylbenzenes ethene, N- are added thereto successively pungent
After base diaminoethyl glycine hydrochloride, dioctyl phthalate, sodium alginate are mixed evenly, it is made and strengthens liquid.
4. a kind of preparation method of lightweight clothes hanger according to claim 3, it is characterised in that the consumption of the reinforcement liquid
For 150-200ml/m2。
5. the preparation method of a kind of lightweight clothes hanger according to claim 1, it is characterised in that the glue is using following
Method is made：Tetrabutyl ammonium fluoride, methylpropene sodium sulfonate, citric acid stearoyl list are added into oxidized starch binding agent successively
Glyceride, double methylol diethyl malonates, after being mixed evenly, are made glue.
6. a kind of preparation method of lightweight clothes hanger according to claim 1, it is characterised in that the consumption of above-mentioned glue is
200-250g/m2。
7. a kind of preparation method of lightweight clothes hanger according to claim 1, it is characterised in that when above-mentioned hot-forming
Temperature is 90-95 DEG C, and the time of pressurization is 15-20min.