CN107471788A - A kind of soft decorating film and its UV coating process and application - Google Patents
A kind of soft decorating film and its UV coating process and application Download PDFInfo
- Publication number
- CN107471788A CN107471788A CN201610396816.XA CN201610396816A CN107471788A CN 107471788 A CN107471788 A CN 107471788A CN 201610396816 A CN201610396816 A CN 201610396816A CN 107471788 A CN107471788 A CN 107471788A
- Authority
- CN
- China
- Prior art keywords
- film
- layer
- soft
- base material
- coated
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of soft decorating film and its UV coating process and application, it is characterised in that：It includes soft base material film, adhesion layer, decorative layer, top coat layer, it is characterised in that：Adhesion layer, decorative layer and top coat layer are followed successively by described soft base material film, described soft base material film uses any one in PVC film, PET film, PE films or PP films, described adhesion layer uses UV adhesion primers, described decorative layer is formed by intaglio printing, described top coat layer uses dull finishing coat or high finish coat varnish, in addition to its manufacture method.The present invention have it is rich in color, pattern is true to nature, streamline continuous production can be realized, the finishing requirements of plane and special-shaped furniture can be met simultaneously, do not ftractureed indeformable, all kinds of furniture of making can be coated by vacuum forming and furniture surface need not carry out the advantages that application again.
Description
Technical field
The present invention relates to decoration material field, more particularly to a kind of soft decorating film and its UV coating process and application.
Background technology
The conventional two ways of furniture surface decoration is covering with paint and veneer.Covering with paint will be applied by certain technological operation code
Material is coated on the trailing on furniture surface.Because most of current furniture application uses traditional coating, organic containing solvent etc.
Volatile matter, environment is not only polluted, and influence the health of workmen；In addition over time, wooden crack will also draw
Play coating crack together, so as to influence the quality of furniture with it is attractive in appearance.Veneer is by the veneer with decorative effect, paper with adhesive
, paper tinsel, film be bonded at trailing on furniture surface.Contain the toxic gases such as formaldehyde in the conventional adhesive of veneer, from
And living environment and the health of user are influenceed, and the adhesive strength of bonding agent is also degenerated after long-term use, so as to
Ornament materials degumming is warped, can also influence the quality of furniture with it is attractive in appearance.
One entitled Wood sofa vacuum PVC-coated decorative membrance of patent of invention, number of patent application are
CN200410081229.9 patent also refer to：Vacuum PVC-coated decorative membrance is employed on some furniture, so that furniture is resistance to
High temperature, non-foaming, surface not breach, solid colour is attractive in appearance, pollution-free.But PVC-coated decorative membrance is to answer on existing furniture
With on flat board furniture, this to Wood sofa have flexure plane, exists with the presence of the direct PVC-coated decorative membrance of furniture progress of abnormity
In vacuum coating machines during overlay film, membrane element is coated to by by larger pressure, flexure plane covering member unbalance stress, will be made wooden coated
Part is subject to crushing；Additionally, due to coated membrane element exist bending, it is special-shaped the characteristics of so that film parts surface height span compared with
Greatly, to make each point all overlay films, the pulling force applied to PVC decorative diaphragm is larger, it is possible to draws bad diaphragm；So as to limit to PVC
The application of decorative membrance.
Although the patent provides a kind of production technology in Wood sofa surface PVC-coated decorative membrance, damage covering member by pressure
The probability of bad diaphragm is drawn to substantially reduce, but the production provided on the basis of being still easily subject to crushing in itself based on PVC decorative diaphragm
Technique, do not tackle the problem at its root.
The content of the invention
The purpose of the present invention is overcome the deficiencies in the prior art, there is provided one kind is rich in color, pattern is true to nature, it is possible to achieve stream
Waterline continuous production, the finishing requirements of plane and special-shaped furniture can be met simultaneously, do not ftractureed indeformable, vacuum forming can be passed through
Cladding makes all kinds of furniture and furniture surface need not carry out soft decorating film and its UV coating process and the application of application again.
In order to solve the above technical problems, the present invention uses following technical scheme：
The present invention includes soft base material film, adhesion layer, decorative layer, top coat layer, it is characterised in that：Described soft base material film
On be followed successively by adhesion layer, decorative layer and top coat layer.
Further improvement as above technical scheme：
Described soft base material film uses any one in PVC film, PET film, PE films or PP films, and wherein PVC film is
Polychloroethylene film, PET film are polyester film, and PE films are polyethylene film, and PP films are polypropylene screen.
Described adhesion layer uses UV adhesion primers.
Described decorative layer is formed by intaglio printing.
Described top coat layer uses dull finishing coat or high finish coat varnish.
Due to belonging to a total inventive concept, the invention also discloses a kind of UV coating process of soft decorating film：It
Including step 1, one layer of 6-12g/ ㎡ UV attachments bottom is coated with base material, then use UV curing or LED-UV curing with
150-200mj/cm2Solidification energy solidified；Step 2, one layer is coated with by the way of intaglio printing on UV attachments bottom
UV ink, the coating weight of UV ink is 2-5g/ ㎡, then uses UV curing or LED-UV curing with 100-200mj/cm2
Solidification energy solidified；Step 3, it is coated with finish paint：An aspect paint is coated with intaglio process brush layer, described finish paint uses UV
Bloom elasticity finish paint or UV dumb light elasticity finish paints, its coating weight are 10-30g/ ㎡.
Further improvement as above technical scheme：
When described step 3 is using UV bloom elasticity finish paints, carry out overlay film is painted in UV bloom elastic surfaces by laminating machine,
UV solidifications or LED-UV solidifications are carried out after overlay film, you can obtain the decorating film of light effect, during using UV dumb light elasticity finish paints, enter
The infrared levelling of row, a length of 5S-2min during the infrared levelling, then carries out UV solidifications or LED-UV solidifications, obtains matte effect
Decorating film.
The film that described overlay film uses is hyaline membrane, and the number of overlay film is one time or more than one time, is on the one hand passed through
Overlay film can make it that the surface of decorating film is more smooth, reach more preferable light effect, after another aspect hyaline membrane does not interfere with
Continuous solidification so that UV bloom elasticity finish paints can effectively be solidified, and be also used as temporary protective film.
One layer of temporary protective film is provided with the finish paint, the hyaline membrane that wherein UV blooms elastic surface is painted is protected as interim
During cuticula, without setting other temporary protective films again.
Solidification energy when described UV bloom elasticity finish paints or UV dumb light elasticity finish paints is solidified is 200-400mj/
cm2, described UV bloom elasticity finish paints or UV dumb light elasticity finish paints have good pliability, the elongation of its coating after solidification
For 120%-150%.
Compared with prior art, the advantage of the invention is that：
1. the soft decorating film surface of the present invention has been subjected to UV applications processing, it is convenient to omit falls furniture surface and carries out application
Process, cost can be not only reduced, save man-hour, also reduce the volatile matters such as the formaldehyde that antique traditional furniture coating contains in itself to ring
Protect the influence of index；
2nd, the present invention is that one kind is exempted to paint furniture decoration film, not only with good decorative effect, and has good bullet
Property, do not ftracture indeformable, can not only realize light effect but also matte effect can be realized, can almost meet the overlay film of all piece of furniture
It is required that can be directly by vacuum forming cladding applications in all kinds of planes and the incrustation of special-shaped furniture part, in timber, clothing
The fields such as cabinet, overall household, cabinet, wall body decoration have broad application prospects.
Embodiment
The present invention is described in further detail below with reference to specific embodiment.
Embodiment 1, the present invention include soft base material film, adhesion layer, decorative layer, top coat layer, it is characterised in that：Described is soft
Adhesion layer, decorative layer and top coat layer are followed successively by matter base material film.Described soft base material film uses PVC film.Described adhesion layer
Using UV adhesion primers.Described decorative layer is formed by intaglio printing.Described top coat layer uses dull finishing coat.
The invention also discloses a kind of UV coating process of soft decorating film：It includes step 1, and one layer is coated with base material
6g/ ㎡ UV attachments bottom, then uses UV curing with 150mj/cm2Solidification energy solidified；Step 2, adhere in UV
One layer of UV ink is coated with bottom by the way of intaglio printing, the coating weight of UV ink is 2g/ ㎡, then use UV curing with
100mj/cm2Solidification energy solidified；Step 3, it is coated with finish paint：An aspect paint is coated with intaglio process brush layer, it is described
Finish paint uses UV dumb light elasticity finish paints, and its coating weight is 10g/ ㎡.When described step 3 is using UV dumb light elasticity finish paints, carry out
Infrared levelling, a length of 5Smin during the infrared levelling, UV solidifications are then carried out, obtain the decorating film of matte effect.The finish paint
On be provided with one layer of temporary protective film.Solidification energy when described UV dumb light elasticity finish paints are solidified is 200mj/cm2, institute
The UV bloom elasticity finish paints or UV dumb light elasticity finish paints stated have good pliability, and the elongation of its coating is after solidification
120%.
Embodiment 2, the present invention include soft base material film, adhesion layer, decorative layer, top coat layer, it is characterised in that：Described is soft
Adhesion layer, decorative layer and top coat layer are followed successively by matter base material film.Described soft base material film uses PET film.Described adhesion layer
Using UV adhesion primers.Described decorative layer is formed by intaglio printing.Described top coat layer uses high finish coat varnish.
The invention also discloses a kind of UV coating process of soft decorating film：It includes step 1, and one layer is coated with base material
12g/ ㎡ UV attachments bottom, then uses LED-UV curing with 200mj/cm2Solidification energy solidified；Step 2, in UV
Attachment is coated with one layer of UV ink on bottom by the way of intaglio printing, and the coating weight of UV ink is 5g/ ㎡, then using LED-UV
Curing is with 200mj/cm2Solidification energy solidified；Step 3, it is coated with finish paint：An aspect is coated with intaglio process brush layer
Paint, described finish paint use UV bloom elasticity finish paints, and its coating weight is 30g/ ㎡.Described step 3 uses UV bloom elastic surfaces
During paint, carry out overlay film is painted in UV bloom elastic surfaces by laminating machine, UV solidifications or LED-UV solidifications are carried out after overlay film, you can
To the decorating film of light effect.The film that described overlay film uses is hyaline membrane, and the number of overlay film is one time or more than one time,
On the one hand by overlay film can decorating film surface it is more smooth, reach more preferable light effect, another aspect hyaline membrane
Follow-up solidification is not interfered with so that UV bloom elasticity finish paints can effectively be solidified, and be also used as protecting temporarily
Film.When the hyaline membrane that wherein UV blooms elastic surface is painted is as temporary protective film, without setting other temporary protective films again.Institute
Solidification energy when the UV bloom elasticity finish paints stated are solidified is 400mj/cm2, described UV bloom elasticity finish paint is with very
Good pliability, the elongation of its coating is 150% after solidification.
Embodiment 3, the present invention include soft base material film, adhesion layer, decorative layer, top coat layer, it is characterised in that：Described is soft
Adhesion layer, decorative layer and top coat layer are followed successively by matter base material film.Described soft base material film uses PE films.Described adhesion layer is adopted
With UV adhesion primers.Described decorative layer is formed by intaglio printing.Described top coat layer uses dull finishing coat.
The invention also discloses a kind of UV coating process of soft decorating film：It includes step 1, and one layer is coated with base material
9g/ ㎡ UV attachments bottom, then uses UV curing with 170mj/cm2Solidification energy solidified；Step 2, adhere in UV
One layer of UV ink is coated with bottom by the way of intaglio printing, the coating weight of UV ink is 3g/ ㎡, then use UV curing with
150mj/cm2Solidification energy solidified；Step 3, it is coated with finish paint：An aspect paint is coated with intaglio process brush layer, it is described
Finish paint uses UV dumb light elasticity finish paints, and its coating weight is 20g/ ㎡.When described step 3 is using UV dumb light elasticity finish paints, carry out
Infrared levelling, a length of 2min during the infrared levelling, UV solidifications are then carried out, obtain the decorating film of matte effect.The finish paint
On be provided with one layer of temporary protective film.Solidification energy when described UV dumb light elasticity finish paints are solidified is 300mj/cm2, institute
The UV dumb light elasticity finish paints stated have good pliability, and the elongation of its coating is 130% after solidification.
Embodiment 4, the present invention include soft base material film, adhesion layer, decorative layer, top coat layer, it is characterised in that：Described is soft
Adhesion layer, decorative layer and top coat layer are followed successively by matter base material film.Described soft base material film uses PP films.Described adhesion layer is adopted
With UV adhesion primers.Described decorative layer is formed by intaglio printing.Described top coat layer uses high finish coat varnish.
The invention also discloses a kind of UV coating process of soft decorating film：It includes step 1, and one layer is coated with base material
10g/ ㎡ UV attachments bottom, then uses LED-UV curing with 180mj/cm2Solidification energy solidified；Step 2, in UV
Attachment is coated with one layer of UV ink on bottom by the way of intaglio printing, and the coating weight of UV ink is 4g/ ㎡, then using LED-UV
Curing is with 180mj/cm2Solidification energy solidified；Step 3, it is coated with finish paint：An aspect is coated with intaglio process brush layer
Paint, described finish paint use UV bloom elasticity finish paints, and its coating weight is 15g/ ㎡.Described step 3 uses UV bloom elastic surfaces
During paint, carry out overlay film is painted in UV bloom elastic surfaces by laminating machine, carries out LED-UV solidifications after overlay film, you can obtain light effect
The decorating film of fruit.The film that described overlay film uses is hyaline membrane, and the number of overlay film is one time or more than one time, on the one hand logical
Crossing overlay film can make it that the surface of decorating film is more smooth, reach more preferable light effect, and another aspect hyaline membrane does not interfere with
Follow-up solidification so that UV bloom elasticity finish paints can effectively be solidified, and be also used as temporary protective film.Wherein UV
When the hyaline membrane that bloom elastic surface is painted is as temporary protective film, without setting other temporary protective films again.Described UV is high
Solidification energy when photoelasticity finish paint is solidified is 350mj/cm2, described UV bloom elasticity finish paint has flexible well
Property, the elongation of its coating is 140% after solidification.
Above-mentioned simply presently preferred embodiments of the present invention, not makees any formal limitation to the present invention.It is although of the invention
It is disclosed above with preferred embodiment, but it is not limited to the present invention.Any those skilled in the art, do not taking off
In the case of from technical solution of the present invention scope, all technical solution of the present invention is made perhaps using the technology contents of the disclosure above
More possible changes and modifications, or it is revised as the equivalent embodiment of equivalent variations.Therefore, it is every without departing from technical solution of the present invention
Content, according to the technology of the present invention essence to any simple modifications, equivalents, and modifications made for any of the above embodiments, all should fall
In the range of technical solution of the present invention protection.
Claims (10)
1. a kind of soft decorating film, it includes soft base material film, adhesion layer, decorative layer, top coat layer, it is characterised in that：Described
Adhesion layer, decorative layer and top coat layer are followed successively by soft base material film.
A kind of 2. soft decorating film according to claim 1, it is characterised in that：Described soft base material film using PVC film,
Any one in PET film, PE films or PP films, wherein PVC film is polychloroethylene film, and PET film is polyester film, and PE films are
Polyethylene film, PP films are polypropylene screen.
A kind of 3. soft decorating film according to claim 1, it is characterised in that：Described adhesion layer is using UV attachments bottom
Paint.
A kind of 4. soft decorating film according to claim 1, it is characterised in that：Described decorative layer by intaglio printing and
Into.
A kind of 5. soft decorating film according to claim 1, it is characterised in that：Described top coat layer using dull finishing coat or
High finish coat varnish.
A kind of 6. UV coating process of soft decorating film, it is characterised in that：It includes step 1, and one layer of 6- is coated with base material
12g/ ㎡ UV attachments bottom, then uses UV curing or LED-UV curing with 150-200mj/cm2Solidification energy carry out
Solidification；Step 2, one layer of UV ink is coated with by the way of intaglio printing on UV attachments bottom, the coating weight of UV ink is 2-5g/
㎡, UV curing or LED-UV curing are then used with 100-200mj/cm2Solidification energy solidified；Step 3, it is coated with
Finish paint：An aspect paint is coated with intaglio process brush layer, described finish paint uses UV bloom elasticity finish paints or UV dumb light elasticity finish paints,
Its coating weight is 10-30g/ ㎡.
A kind of 7. UV coating process of soft decorating film according to claim 6, it is characterised in that：Described step 3 is adopted
During with UV bloom elasticity finish paints, carry out overlay film is painted in UV bloom elastic surfaces by laminating machine, carried out after overlay film UV solidifications or
LED-UV solidifies, and during using UV dumb light elasticity finish paints, carries out infrared levelling, a length of 5S-2min, Ran Houjin during the infrared levelling
Row UV solidifies or LED-UV solidifications.
A kind of 8. UV coating process of soft decorating film according to claim 7, it is characterised in that：Described overlay film uses
Film be hyaline membrane, and the number of overlay film is one time or more than one time.
A kind of 9. UV coating process of soft decorating film according to claim 6, it is characterised in that：Set on the finish paint
There is one layer of temporary protective film, when the hyaline membrane that wherein UV blooms elastic surface is painted is as temporary protective film, without setting other again
Temporary protective film.
A kind of 10. UV coating process of soft decorating film according to claim 7, it is characterised in that：Described UV blooms
Solidification energy when elastic finish paint or UV dumb light elasticity finish paint is solidified is 200-400mj/cm2, the high photoelasticity of described UV
Finish paint or UV dumb light elasticity finish paints have good pliability, and the elongation of its coating is 120%-150% after solidification.