CN108972803A - A method of promoting rattan mechanical property - Google Patents
A method of promoting rattan mechanical property Download PDFInfo
- Publication number
- CN108972803A CN108972803A CN201810882173.9A CN201810882173A CN108972803A CN 108972803 A CN108972803 A CN 108972803A CN 201810882173 A CN201810882173 A CN 201810882173A CN 108972803 A CN108972803 A CN 108972803A
- Authority
- CN
- China
- Prior art keywords
- parts
- rattan
- mechanical property
- promoting
- drying
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention discloses a kind of method for promoting rattan mechanical property; including following operating procedure: (1) after gathering in rattan; natural drying is handled 3-4 days; then soak is used to carry out immersion treatment, wherein soak is made of the component of following parts by weight: 14-19 parts of calcium cyclamate, 18-24 parts of acesulfame potassium, 12-17 parts of methylpropene sodium sulfonate, 28-32 parts of sodium hexafluoro phosphate, 3-6 parts of magnesium citrate, 240-300 parts of water；(2) it after the spraying modified liquid in rattan surface for crossing immersion treatment, is put into baking oven, drying and processing.A kind of method promoting rattan mechanical property provided by the invention, environmentally protective, simple process can effectively promote every mechanical property of rattan, improve the stability of cane furniture, extend the service life of cane furniture.
Description
Technical field
The invention belongs to rattan processing technique fields, and in particular to a method of promote rattan mechanical property.
Background technique
Rattan, woven natural material are also named " rattan is slightd ", a kind of liana that strong but pliable in texture, figure is extremely long.Rattan crust
Bright in luster, feel is smooth, and elasticity is splendid, seemingly slights rather than slights, and also commonly uses the daily apparatus such as this establishment rattan chair, rattan case.Existing skill
In art, the rattan furniture of establishment, during use, the phenomenon that easily deforming, main cause is weaving for rattan
Before, treatment process is relatively simple, causes its mechanical property poor.
Summary of the invention
In order to solve the above technical problem, the present invention provides a kind of methods for promoting rattan mechanical property.
The present invention is achieved by the following technical solutions.
A method of promoting rattan mechanical property, including following operating procedure:
(1) after gathering in rattan, natural drying is handled 3-4 days, is then used soak to carry out immersion treatment, wherein impregnating
Liquid is made of the component of following parts by weight: 14-19 parts of calcium cyclamate, 18-24 parts of acesulfame potassium, metering system
12-17 parts of sodium sulfonate, 28-32 parts of sodium hexafluoro phosphate, 3-6 parts of magnesium citrate, 240-300 parts of water；
(2) after the spraying modified liquid in rattan surface for crossing immersion treatment, be put into baking oven, drying and processing, wherein modification liquid by with
The component of lower parts by weight is made: 11-15 parts of N- octyl diaminoethyl glycine hydrochlorides, 2-4 parts of nano ATOs, 22-26 parts poly- third
Olefin(e) acid sodium, 150-200 part water.
Specifically, in above-mentioned steps (1), the mass ratio of rattan and soak is 1:5-7.
Specifically, in above-mentioned steps (2), the modification liquid of every kilogram of rattan sprinkling 250-300g.
Specifically, in above-mentioned steps (2), nano ATO is the ratio group of 9:1 according to mass ratio by tin oxide and antimony oxide
At.
Specifically, in above-mentioned steps (2), the temperature of baking oven drying is 75-80 DEG C, and the time of drying is 2-3 hours.
From the above technical scheme, it can be seen that the beneficial effects of the present invention are:
A kind of method promoting rattan mechanical property provided by the invention, environmentally protective, simple process can effectively promote rattan
Every mechanical property, improve the stability of cane furniture, extend the service life of cane furniture.Wherein, in step (1)
Modification liquid, can effectively be promoted cane furniture surface can, enhancing modification liquid cane furniture surface permeability, while again
The consistency that rattan interior tissue can be enhanced enhances its every mechanical property；Modification liquid in step (2), can effectively be promoted
The stability of rattan space structure promotes the active force between rattan interior molecules, and then effectively improves the items of rattan
Mechanical property.
Specific embodiment
The following examples are intended to illustrate the invention but are not intended to limit the scope of the invention.Reality used in the examples
The condition of applying can be for further adjustments according to the condition of producer, and unaccounted implementation condition is usually conventional laboratory conditions.
Embodiment 1
A method of promoting rattan mechanical property, including following operating procedure:
(1) after gathering in rattan, natural drying is handled 3 days, is then used soak to carry out immersion treatment, wherein soak
It is made of the component of following parts by weight: 14 parts of calcium cyclamate, 18 parts of acesulfame potassium, methylpropene sodium sulfonate 12
Part, 28 parts of sodium hexafluoro phosphate, 3 parts of magnesium citrate, 240 parts of water；
(2) after the spraying modified liquid in rattan surface for crossing immersion treatment, be put into baking oven, drying and processing, wherein modification liquid by with
The component of lower parts by weight is made: 11 parts of N- octyl diaminoethyl glycine hydrochlorides, 2 parts of nano ATOs, 22 parts of Sodium Polyacrylates,
150 parts of water.
Specifically, in above-mentioned steps (1), the mass ratio of rattan and soak is 1:5.
Specifically, in above-mentioned steps (2), the modification liquid of every kilogram of rattan sprinkling 250g.
Specifically, in above-mentioned steps (2), nano ATO is the ratio group of 9:1 according to mass ratio by tin oxide and antimony oxide
At.
Specifically, in above-mentioned steps (2), the temperature of baking oven drying is 75 DEG C, and the time of drying is 2 hours.
Embodiment 2
A method of promoting rattan mechanical property, including following operating procedure:
(1) after gathering in rattan, natural drying is handled 4 days, is then used soak to carry out immersion treatment, wherein soak
It is made of the component of following parts by weight: 16 parts of calcium cyclamate, 22 parts of acesulfame potassium, methylpropene sodium sulfonate 15
Part, 30 parts of sodium hexafluoro phosphate, 5 parts of magnesium citrate, 260 parts of water；
(2) after the spraying modified liquid in rattan surface for crossing immersion treatment, be put into baking oven, drying and processing, wherein modification liquid by with
The component of lower parts by weight is made: 13 parts of N- octyl diaminoethyl glycine hydrochlorides, 3 parts of nano ATOs, 24 parts of Sodium Polyacrylates,
180 parts of water.
Specifically, in above-mentioned steps (1), the mass ratio of rattan and soak is 1:6.
Specifically, in above-mentioned steps (2), the modification liquid of every kilogram of rattan sprinkling 280g.
Specifically, in above-mentioned steps (2), nano ATO is the ratio group of 9:1 according to mass ratio by tin oxide and antimony oxide
At.
Specifically, in above-mentioned steps (2), the temperature of baking oven drying is 78 DEG C, and the time of drying is 2.5 hours.
Embodiment 3
A method of promoting rattan mechanical property, including following operating procedure:
(1) after gathering in rattan, natural drying is handled 4 days, is then used soak to carry out immersion treatment, wherein soak
It is made of the component of following parts by weight: 19 parts of calcium cyclamate, 24 parts of acesulfame potassium, methylpropene sodium sulfonate 17
Part, 32 parts of sodium hexafluoro phosphate, 6 parts of magnesium citrate, 300 parts of water；
(2) after the spraying modified liquid in rattan surface for crossing immersion treatment, be put into baking oven, drying and processing, wherein modification liquid by with
The component of lower parts by weight is made: 15 parts of N- octyl diaminoethyl glycine hydrochlorides, 4 parts of nano ATOs, 26 parts of Sodium Polyacrylates,
200 parts of water.
Specifically, in above-mentioned steps (1), the mass ratio of rattan and soak is 1:7.
Specifically, in above-mentioned steps (2), the modification liquid of every kilogram of rattan sprinkling 300g.
Specifically, in above-mentioned steps (2), nano ATO is the ratio group of 9:1 according to mass ratio by tin oxide and antimony oxide
At.
Specifically, in above-mentioned steps (2), the temperature of baking oven drying is 80 DEG C, and the time of drying is 3 hours.
Comparative example 1
Soak in step (1) is clear water, remaining operating procedure is identical with embodiment 1.
Comparative example 2
Modification liquid in step (2) is clear water, remaining operating procedure is identical with embodiment 2.
Handle rattan with the method for each embodiment and comparative example respectively, then after test processes rattan every mechanical property
Can, test result is as shown in table 1:
1 rattan mechanical experimental results of table
As shown in Table 1, method provided in this embodiment can effectively promote every mechanical property of rattan.
Certainly, the above description is not a limitation of the present invention, and the present invention is also not limited to the example above, the art
Those of ordinary skill, within the essential scope of the present invention, variation, change, addition or the replacement made all should belong to the present invention
Protection scope.
Claims (5)
1. a kind of method for promoting rattan mechanical property, which is characterized in that including following operating procedure:
(1) after gathering in rattan, natural drying is handled 3-4 days, is then used soak to carry out immersion treatment, wherein impregnating
Liquid is made of the component of following parts by weight: 14-19 parts of calcium cyclamate, 18-24 parts of acesulfame potassium, metering system
12-17 parts of sodium sulfonate, 28-32 parts of sodium hexafluoro phosphate, 3-6 parts of magnesium citrate, 240-300 parts of water；
(2) after the spraying modified liquid in rattan surface for crossing immersion treatment, be put into baking oven, drying and processing, wherein modification liquid by with
The component of lower parts by weight is made: 11-15 parts of N- octyl diaminoethyl glycine hydrochlorides, 2-4 parts of nano ATOs, 22-26 parts poly- third
Olefin(e) acid sodium, 150-200 part water.
2. a kind of method for promoting rattan mechanical property according to claim 1, which is characterized in that in above-mentioned steps (1),
The mass ratio of rattan and soak is 1:5-7.
3. a kind of method for promoting rattan mechanical property according to claim 1, which is characterized in that in above-mentioned steps (2),
The modification liquid of every kilogram of rattan sprinkling 250-300g.
4. a kind of method for promoting rattan mechanical property according to claim 1, which is characterized in that in above-mentioned steps (2),
Nano ATO is made of tin oxide and antimony oxide according to the ratio that mass ratio is 9:1.
5. a kind of method for promoting rattan mechanical property according to claim 1, which is characterized in that in above-mentioned steps (2),
The temperature of baking oven drying is 75-80 DEG C, and the time of drying is 2-3 hours.