CN107254209A - A kind of special high wear resistance coatings of plant equipment - Google Patents
A kind of special high wear resistance coatings of plant equipment Download PDFInfo
- Publication number
- CN107254209A CN107254209A CN201710593424.7A CN201710593424A CN107254209A CN 107254209 A CN107254209 A CN 107254209A CN 201710593424 A CN201710593424 A CN 201710593424A CN 107254209 A CN107254209 A CN 107254209A
- Authority
- CN
- China
- Prior art keywords
- parts
- ethylene glycol
- plant equipment
- wear resistance
- high wear
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of special high wear resistance coatings of plant equipment, include the component of following mass fraction：8~12 parts of epoxy resin, 2~4 parts of trioctyl phosphate, 2~4 parts of acrylic resin, 4~8 parts of tributoxyethyl phosphate, 6~9 parts of linoleic acid, 2~8 parts of ethylene glycol monobutyl ether (EGMBE), 28~16 parts of toluene di-isocyanate(TDI), 4~8 parts of dibutyl phthalate, 2~6 parts of ethylene glycol, 8~12 parts of modified graphene, 4~12 parts of nonyl phenol, 2~4 parts of methanol, 10~20 parts of vinyl benzene, 3~6 parts of isopropyl acrylate, 12~15 parts of butyl acetate, 5~10 parts of ammonium persulfate, dry 2~5 parts of triol.The fungicidal paint that the present invention is provided, cost is low, and manufacture craft is simple, can be to effectively preventing acid and alkali corrosion, it is adaptable to all kinds of plant equipment.
Description
Technical field
The present invention relates to machinery manufacturing technology field, and in particular to a kind of special high wear resistance coatings of plant equipment.
Background technology
Coating is a kind of material, and this material can be coated in object surface with different construction technologies, forms adhesion jail
Gu, with some strength, continuous solid film.The film common name film so formed, also known as paint film or coating.Belong to and organise
Work high polymer material, the film formed belongs to high-molecular compound type.The classification for the chemical products passed through according to the modern times, is applied
Material belongs to fine chemical product.Modern coating progressively turns into the multi-functional engineering material of a class, in being chemical industry
An important industry.Coating function at present on the market is relatively simple, it is impossible to meet the demand of people.
The content of the invention
Goal of the invention：The present invention proposes a kind of special high wear resistance coatings of plant equipment for deficiency, and cost is low, makes work
Skill is simple, can be to effectively preventing acid and alkali corrosion, it is adaptable to all kinds of plant equipment.
Technical scheme：The special high wear resistance coatings of a kind of plant equipment of the present invention, include the group of following mass fraction
Point：8~12 parts of epoxy resin, 2~4 parts of trioctyl phosphate, 2~4 parts of acrylic resin, 4~8 parts of tributoxyethyl phosphate,
6~9 parts of linoleic acid, 2~8 parts of ethylene glycol monobutyl ether (EGMBE), 2 8~16 parts of toluene di-isocyanate(TDI), dibutyl phthalate 4
~8 parts, 2~6 parts of ethylene glycol, 8~12 parts of modified graphene, 4~12 parts of nonyl phenol, 2~4 parts of methanol, vinyl benzene 10
~20 parts, 3~6 parts of isopropyl acrylate, 12~15 parts of butyl acetate, 5~10 parts of ammonium persulfate, dry 2~5 parts of triol.
Further, the component of following mass fraction is included：10~12 parts of epoxy resin, 3~4 parts of trioctyl phosphate, third
3~4 parts of olefin(e) acid resin, 6~8 parts of tributoxyethyl phosphate, 7~9 parts of linoleic acid, 4~8 parts of ethylene glycol monobutyl ether (EGMBE), toluene
2 10~16 parts of diisocyanate, 6~8 parts of dibutyl phthalate, 4~6 parts of ethylene glycol, modified graphene 10~12
Part, 8~12 parts of nonyl phenol, 3~4 parts of methanol, 15~20 parts of vinyl benzene, 4~6 parts of isopropyl acrylate, butyl acetate 13
~15 parts, 7~10 parts of ammonium persulfate, dry 3~5 parts of triol.
Further, the component of following mass fraction is included：11 parts of epoxy resin, 3.5 parts of trioctyl phosphate, acrylic acid tree
3.5 parts of fat, 7 parts of tributoxyethyl phosphate, 8 parts of linoleic acid, 6 parts of ethylene glycol monobutyl ether (EGMBE), 214 parts of toluene di-isocyanate(TDI),
7 parts of dibutyl phthalate, 5 parts of ethylene glycol, 11 parts of modified graphene, 10 parts of nonyl phenol, 3.5 parts of methanol, vinyl benzene
17 parts, 5 parts of isopropyl acrylate, 14 parts of butyl acetate, 9 parts of ammonium persulfate, dry 4 parts of triol.
Beneficial effect：The fungicidal paint that the present invention is provided, cost is low, and manufacture craft is simple, can be to effectively preventing soda acid
Corrosion, it is adaptable to all kinds of plant equipment.
Embodiment
With reference to specific embodiment, the invention will be further described：
Embodiment 1
A kind of special high wear resistance coatings of plant equipment, include the component of following mass fraction：8 parts of epoxy resin, trioctyl phosphate 2
Part, 2 parts of acrylic resin, 4 parts of tributoxyethyl phosphate, 6 parts of linoleic acid, 2 parts of ethylene glycol monobutyl ether (EGMBE), toluene diisocyanate
28 parts of acid esters, 4 parts of dibutyl phthalate, 2 parts of ethylene glycol, 8 parts of modified graphene, 4 parts of nonyl phenol, 2 parts of methanol, second
10 parts of alkenyl benzene, 3 parts of isopropyl acrylate, 12 parts of butyl acetate, 5 parts of ammonium persulfate, dry 2 parts of triol.
Embodiment 2
A kind of special high wear resistance coatings of plant equipment, include the component of following mass fraction：12 parts of epoxy resin, tricresyl phosphate is pungent
4 parts of ester, 4 parts of acrylic resin, 8 parts of tributoxyethyl phosphate, 9 parts of linoleic acid, 8 parts of ethylene glycol monobutyl ether (EGMBE), toluene two is different
216 parts of cyanate, 8 parts of dibutyl phthalate, 6 parts of ethylene glycol, 2 parts of phosphatase 11,12 parts of nonyl phenol, 4 parts of methanol, second
20 parts of alkenyl benzene, 6 parts of isopropyl acrylate, 15 parts of butyl acetate, 10 parts of ammonium persulfate, dry 5 parts of triol.
Embodiment 3
A kind of special high wear resistance coatings of plant equipment, include the component of following mass fraction：11 parts of epoxy resin, trioctyl phosphate
3.5 parts, 3.5 parts of acrylic resin, 7 parts of tributoxyethyl phosphate, 8 parts of linoleic acid, 6 parts of ethylene glycol monobutyl ether (EGMBE), toluene two
214 parts of isocyanates, 7 parts of dibutyl phthalate, 5 parts of ethylene glycol, 11 parts of modified graphene, 10 parts of nonyl phenol, methanol
3.5 parts, 17 parts of vinyl benzene, 5 parts of isopropyl acrylate, 14 parts of butyl acetate, 9 parts of ammonium persulfate, dry 4 parts of triol.
The fungicidal paint that the present invention is provided, cost is low, and manufacture craft is simple, can be applicable effectively preventing acid and alkali corrosion
In all kinds of plant equipment.
The above described is only a preferred embodiment of the present invention, any formal limitation not is made to the present invention, though
So the present invention is disclosed above with preferred embodiment, but is not limited to the present invention, any to be familiar with this professional technology people
Member, without departing from the scope of the present invention, when the technology contents using the disclosure above make a little change or modification
For the equivalent embodiment of equivalent variations, as long as being the content without departing from technical solution of the present invention, the technical spirit according to the present invention
Any simple modification, equivalent variations and the modification made to above example, in the range of still falling within technical solution of the present invention.
Claims (3)
1. a kind of special high wear resistance coatings of plant equipment, it is characterised in that：Include the component of following mass fraction：Epoxy resin 8
~12 parts, 2~4 parts of trioctyl phosphate, 2~4 parts of acrylic resin, 4~8 parts of tributoxyethyl phosphate, linoleic acid 6~9
Part, 2~8 parts of ethylene glycol monobutyl ether (EGMBE), 2 8~16 parts of toluene di-isocyanate(TDI), 4~8 parts of dibutyl phthalate, second two
2~6 parts of alcohol, 8~12 parts of modified graphene, 4~12 parts of nonyl phenol, 2~4 parts of methanol, 10~20 parts of vinyl benzene, propylene
3~6 parts of isopropyl propionate, 12~15 parts of butyl acetate, 5~10 parts of ammonium persulfate, dry 2~5 parts of triol.
2. the special high wear resistance coatings of a kind of plant equipment according to claim 1, it is characterised in that：Including following mass parts
Several components：10~12 parts of epoxy resin, 3~4 parts of trioctyl phosphate, 3~4 parts of acrylic resin, tributoxyethyl phosphate
6~8 parts, 7~9 parts of linoleic acid, 4~8 parts of ethylene glycol monobutyl ether (EGMBE), 2 10~16 parts of toluene di-isocyanate(TDI), phthalic acid
6~8 parts of dibutyl ester, 4~6 parts of ethylene glycol, 10~12 parts of modified graphene, 8~12 parts of nonyl phenol, 3~4 parts of methanol, second
15~20 parts of alkenyl benzene, 4~6 parts of isopropyl acrylate, 13~15 parts of butyl acetate, 7~10 parts of ammonium persulfate, dry triol 3~5
Part.
3. the special high wear resistance coatings of a kind of plant equipment according to claim 1, it is characterised in that：Including following mass parts
Several components：11 parts of epoxy resin, 3.5 parts of trioctyl phosphate, 3.5 parts of acrylic resin, 7 parts of tributoxyethyl phosphate is sub-
8 parts of oleic acid, 6 parts of ethylene glycol monobutyl ether (EGMBE), 214 parts of toluene di-isocyanate(TDI), 7 parts of dibutyl phthalate, ethylene glycol 5
Part, 11 parts of modified graphene, 10 parts of nonyl phenol, 3.5 parts of methanol, 17 parts of vinyl benzene, 5 parts of isopropyl acrylate, acetic acid fourth
14 parts of ester, 9 parts of ammonium persulfate, dry 4 parts of triol.