CN107652792A - A kind of solar energy reflection mirror mirror-back protective coating - Google Patents
A kind of solar energy reflection mirror mirror-back protective coating Download PDFInfo
- Publication number
- CN107652792A CN107652792A CN201610583002.7A CN201610583002A CN107652792A CN 107652792 A CN107652792 A CN 107652792A CN 201610583002 A CN201610583002 A CN 201610583002A CN 107652792 A CN107652792 A CN 107652792A
- Authority
- CN
- China
- Prior art keywords
- protective coating
- agent
- mirror
- solar energy
- energy reflection
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of solar energy reflection mirror mirror-back protective coating, the percentage by weight of the protective coating is:Fluorocarbon resin F 400 40 60%, various pigments 2 10%, talcum powder 5 10%, powdered whiting 6 12%, trbasic zinc phosphate 4 8%, aluminium triphosphate 5 8%, organobentonite 2 5%, wetting dispersing agent 2 8%, levelling agent 1 3%, defoamer 1 2%, silane coupler Z 6,030 1 2%, diluent 20 30% and curing agent N 75 10 16%.The present invention be applied to solar energy reflection mirror mirror-back protective coating, both can showering, also can roller coat, brushing and spraying.Product performance is:Fast drying, compact in paint film, adhesive force are strong, high-low temperature resistant, water-fast wet-heat resisting, corrosion-resistant, cutting is good, resistance to edging.
Description
【Technical field】
The present invention relates to a kind of speculum mirror-back protective coating, more particularly to a kind of solar energy reflection mirror is carried on the back protection with mirror and applied
Material.
【Background technology】
Anticorrosive paint is that the departments such as modern industry, traffic, the energy, ocean engineering apply a kind of extremely wide coating.By its painting
Expect the corrosion resistant degree of corrosion and requirement of film layer, anticorrosive coating is generally divided into the universal and class of heavy antisepsis type two.According to making
Different types of anticorrosive coating is selected with the situation of environmental corrosion medium.Under the etching condition of normal atmospheric environment, such as machine
The industries such as bed, automobile, rolling stock, engineering machinery, frequently with universal anticorrosive coating, it is higher now also to require that coating has
Decoration functions;Under industry or Marine atmosphere corrosion working conditions, such as chemical industry, petrochemical industry, metallurgy, ocean engineering row
Industry, more using heavy-duty anticorrosive coating.Anticorrosive paint occupies critical role in Coating Industry in Our Country, shared by coatings industry
Ratio has ranked among the best.In recent years, China is in various fields such as building, communications and transportation, petrochemical industry, water power and ocean engineerings,
All occur being skyrocketed through, and then driven the rapid growth of related auxiliary products demand, China anticorrosive paint market also occurs
Gratifying situation, market scale have been only second to building coating and have occupied second, still, the protection occurred in existing market
Coating has poor adhesive force mostly, and paint film is excessively dilute, not water resistant, high temperature resistant, it is perishable the problems such as.A kind of therefore, it is proposed that solar energy
Speculum mirror-back protective coating.
【The content of the invention】
It is a primary object of the present invention to provide a kind of solar energy reflection mirror mirror-back protective coating, suitable for solar energy reflection mirror
With mirror-back protective coating, both can showering, also can roller coat, brushing and spraying.Product performance is:Fast drying, compact in paint film, adhesive force
By force, high-low temperature resistant, water-fast wet-heat resisting, corrosion-resistant, cutting is good, resistance to edging, effectively can solve the problems, such as in background technology.
To achieve the above object, the technical scheme taken of the present invention is:
A kind of solar energy reflection mirror mirror-back protective coating, the percentage by weight of the protective coating are:
Fluorocarbon resin F-400 40-60%, various pigments 2-10%, talcum powder 5-10%, powdered whiting 6-12%, trbasic zinc phosphate 4-
8%th, aluminium triphosphate 5-8%, organobentonite 2-5%, wetting dispersing agent 2-8%, levelling agent 1-3%, defoamer 1-2%, silane are even
Join agent Z-6030 1-2%, diluent 20-30% and curing agent N-75 10-16%.
Further, the percentage by weight of the protective coating is:
Fluorocarbon resin F-400 40%, various pigments 2%, talcum powder 5%, powdered whiting 6%, trbasic zinc phosphate 4%, aluminium triphosphate
5%th, organobentonite 2%, wetting dispersing agent 2%, levelling agent 1%, defoamer 1%, silane coupler Z-6030 1%, diluent 20%
With curing agent N-75 10%.
Further, the percentage by weight of the protective coating is:
Fluorocarbon resin F-400 60%, various pigments 10%, talcum powder 10%, powdered whiting 12%, trbasic zinc phosphate 8%, tripolyphosphate
Aluminium 8%, organobentonite 5%, wetting dispersing agent 8%, levelling agent 3%, defoamer 2%, silane coupler Z-6030 2%, diluent
30% and curing agent N-75 16%.
Further, the percentage by weight of the protective coating is:
Fluorocarbon resin F-400 50%, various pigments 6%, talcum powder 7.5%, powdered whiting 9%, trbasic zinc phosphate 6%, aluminium triphosphate
6.5%th, organobentonite 3.5%, wetting dispersing agent 5%, levelling agent 2%, defoamer 1.5%, silane coupler Z-6030 1.5%, dilute
Release agent 25% and curing agent N-75 13%.
Compared with prior art, the present invention has the advantages that:Protection is carried on the back suitable for solar energy reflection mirror with mirror to apply
Material, both can showering, also can roller coat, brushing and spraying.Product performance is:Fast drying, compact in paint film, adhesive force are strong, high-low temperature resistant,
Water-fast wet-heat resisting, corrosion-resistant, cutting is good, resistance to edging.
【Embodiment】
To be easy to understand the technical means, the inventive features, the objects and the advantages of the present invention, with reference to specific
Embodiment, the present invention is expanded on further.
Specific embodiment 1:
Fluorocarbon resin F-400 40%, various pigments 2%, talcum powder 5%, powdered whiting 6%, trbasic zinc phosphate 4%, aluminium triphosphate 5%,
Organobentonite 2%, wetting dispersing agent 2%, levelling agent 1%, defoamer 1%, silane coupler Z-6030 1%, diluent 20% and solid
Agent N-75 10%.
Specific embodiment 2:
Fluorocarbon resin F-400 60%, various pigments 10%, talcum powder 10%, powdered whiting 12%, trbasic zinc phosphate 8%, aluminium triphosphate
8%th, organobentonite 5%, wetting dispersing agent 8%, levelling agent 3%, defoamer 2%, silane coupler Z-6030 2%, diluent 30%
With curing agent N-75 16%.
Specific embodiment 3:
Fluorocarbon resin F-400 50%, various pigments 6%, talcum powder 7.5%, powdered whiting 9%, trbasic zinc phosphate 6%, aluminium triphosphate
6.5%th, organobentonite 3.5%, wetting dispersing agent 5%, levelling agent 2%, defoamer 1.5%, silane coupler Z-6030 1.5%, dilute
Release agent 25% and curing agent N-75 13%.
The general principle and principal character and advantages of the present invention of the present invention has been shown and described above.The technology of the industry
Personnel are it should be appreciated that the present invention is not limited to the above embodiments, and the simply explanation described in above-described embodiment and specification is originally
The principle of invention, without departing from the spirit and scope of the present invention, various changes and modifications of the present invention are possible, these changes
Change and improvement all fall within the protetion scope of the claimed invention.The claimed scope of the invention by appended claims and its
Equivalent thereof.
Claims (4)
- A kind of 1. solar energy reflection mirror mirror-back protective coating, it is characterised in that:The percentage by weight of the protective coating is:Fluorocarbon resin F-400 40-60%, various pigments 2-10%, talcum powder 5-10%, powdered whiting 6-12%, trbasic zinc phosphate 4- 8%th, aluminium triphosphate 5-8%, organobentonite 2-5%, wetting dispersing agent 2-8%, levelling agent 1-3%, defoamer 1-2%, silane are even Join agent Z-6030 1-2%, diluent 20-30% and curing agent N-75 10-16%.
- 2. solar energy reflection mirror mirror-back protective coating according to claim 1, it is characterised in that:The protective coating Percentage by weight is:Fluorocarbon resin F-400 40%, various pigments 2%, talcum powder 5%, powdered whiting 6%, trbasic zinc phosphate 4%, aluminium triphosphate 5%, Organobentonite 2%, wetting dispersing agent 2%, levelling agent 1%, defoamer 1%, silane coupler Z-6030 1%, diluent 20% and solid Agent N-75 10%.
- 3. solar energy reflection mirror mirror-back protective coating according to claim 1, it is characterised in that:The protective coating Percentage by weight is:Fluorocarbon resin F-400 60%, various pigments 10%, talcum powder 10%, powdered whiting 12%, trbasic zinc phosphate 8%, aluminium triphosphate 8%th, organobentonite 5%, wetting dispersing agent 8%, levelling agent 3%, defoamer 2%, silane coupler Z-6030 2%, diluent 30% With curing agent N-75 16%.
- 4. solar energy reflection mirror mirror-back protective coating according to claim 1, it is characterised in that:The protective coating Percentage by weight is:Fluorocarbon resin F-400 50%, various pigments 6%, talcum powder 7.5%, powdered whiting 9%, trbasic zinc phosphate 6%, aluminium triphosphate 6.5%th, organobentonite 3.5%, wetting dispersing agent 5%, levelling agent 2%, defoamer 1.5%, silane coupler Z-6030 1.5%, dilute Release agent 25% and curing agent N-75 13%.