CN107236999A - A kind of method that fish skin collagen is self-assembled into fiber - Google Patents
A kind of method that fish skin collagen is self-assembled into fiber Download PDFInfo
- Publication number
- CN107236999A CN107236999A CN201710582757.XA CN201710582757A CN107236999A CN 107236999 A CN107236999 A CN 107236999A CN 201710582757 A CN201710582757 A CN 201710582757A CN 107236999 A CN107236999 A CN 107236999A
- Authority
- CN
- China
- Prior art keywords
- fish skin
- solution
- skin collagen
- self
- fiber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention belongs to wire cable material technical field there is provided a kind of method that fish skin collagen is self-assembled into fiber, comprise the following steps:(1)Extract fish skin collagen powder;(2)Fish skin collagen powder is dissolved in citric acid solution;(3)Mixed liquor is centrifuged, supernatant is taken;(4)Supernatant is mixed in ice bath with acetate buffer solution, stirred, solution PH is adjusted;(5)The water-bath in water-bath by mixed liquor, produces self-assembly collagenous fibres.The method that the present invention inquires into aquatic products collagen assembly formation fiber, the collagenous fibres as obtained by the inventive method are filamentary fibers, extremely similar to naturally occurring collagenous fibres form in deep-sea fish skin, have very high application prospect in biomaterial for medical purpose field.
Description
Technical field
The invention belongs to technical field of biological materials, in particular it relates to a kind of method that fish skin collagen is self-assembled into fiber.
Background technology
Collagen is the class formation albumen in animal tissue, accounts for the 1/3 of total protein concentration, is distributed widely in the skin of animal
The positions such as skin, bone, cartilage, connective tissue, tendon, cornea, gut cell interstitial, flesh chamber, ligament, sclera.Because it has uniqueness
Triple helix structure, low antigenicity, nontoxicity, good biocompatibility and the features such as biodegradability, it is extensive
Cured applied to the biology such as tissue engineering bracket material, styptic sponge, medicine control slow-released system, gene delivery vector, aesthetic surgery
Use field.But, the collagen used at present is mainly derived from pigskin, ox-hide and pig bone, ox bone, in recent years due to crazy ox
People and animals' cross-current such as disease, aftosa row is sick to be taken place frequently, and the application for the collagen originated in pig and ox is restricted.In addition,
In some religion crowds, the collagen in pig source is prohibited from using.In this case, aquatic collagen protein is due to raw material
Enrich, be easy to extraction, low antigenicity, low irritability, highly soluble, without infectious disease is dangerous and religion obstacle and by extensive
Concern.Wherein deep-sea fish skin collagen, as the term suggests it is exactly the collagen extracted by raw material of deep-sea fish fish-skin.Due to
The low-temp low-pressure at deep-sea, makes this kind of collagen have common terrestrial animal collagen and fresh-water fishes, shallow sea collagen
Special nature not available for albumen.Difference is the temperature of collagen activity excitation first.The glue extracted in terrestrial animal
Former protein active could will all be excited at 35 degree active.That is the effect that absorbed more than 35 degree can just reach most
It is good.And the activity excitation temperature that fish is extracted will be much lower, more than ten degree just can play best effect.
Self assembly is the key property of collagen.Generally, the collagen being dissolved in solution is free polypeptide chain, rather than
Triple helix chain.Collagen can form triple helix structure by self assembly, and then form fiber etc., and this is it in biomaterial
The basis of field application.Terrestrial mammal collagen is directed to the conventional research on collagen assembly more, it is collagenogenic to water
Inquire into less.
The content of the invention
For defect of the prior art, it is an object of the invention to provide the side that a kind of fish skin collagen is self-assembled into fiber
Collagen powder as raw material is dissolved reaction to it by method, the present invention using citric acid, eventually through being self-assembly of fibre
Dimension.
To solve prior art problem, the method that a kind of fish skin collagen of offer of the invention is self-assembled into fiber, the fish
The method that collagen is self-assembled into fiber comprises the following steps:
(1)Extract fish skin collagen powder;
(2)By the step(1)In fish skin collagen powder be dissolved in citric acid solution;
(3)To the step(2)In mixed liquor centrifuged, take supernatant;
(4)By the step(3)In supernatant mixed with acetate buffer solution in ice bath, stir, adjust solution PH;
(5)By the step(4)In mixed liquor water-bath in water-bath, produce self-assembly collagenous fibres.
Preferably, the preparation method of the fish skin collagen powder comprises the following steps:
(1)Fresh fish-skin is taken to clean, removal of impurities;
(2)The potassium hydroxide solution that the fish skin raw material after cleaning is 0.16-3.0mol/L with concentration is taken to be soaked under the conditions of 0-20 DEG C
1-20h is steeped, the potassium hydroxide solution and the envelope-bulk to weight ratio of fish skin raw material added is 10-20: 1, in immersion process, every
2-4h, changes immersion potassium hydroxide solution 1-2 times;After immersion is finished, clean, filtering;Clean in backward fish skin raw material and add
Organic solvent soaks 2-6h, plus clear water, and it is 5-10% to make fish skin raw material and the quality percent by volume of organic solvent;
(3)Take the step(2)Gained raw material mixed liquor, addition concentration is 0.36-1.68mol/L acetum at 0-20 DEG C
Under conditions of carry out swelling treatment 12-36h, the envelope-bulk to weight ratio of the acetum solution added and raw material mixed liquor is 10-
15∶1;Then 1-10h is freezed under the conditions of 0-30 DEG C;Freeze after finishing, the acetic acid for adding appropriate 0.15-0.45mol/L is molten
Liquid carries out mashing and crushed, and obtains particle diameter 2-4mm particle slurry;
(4)To the step(3)In particle slurry in add 0.05-3.56mol/L acetum extracted, added
The envelope-bulk to weight ratio of acetum and particle slurry be 15-30: 1,0-25 DEG C of Extracting temperature, extraction time is 24-48h;Carry
Take after finishing, filtered with 60-80 mesh gauze, obtain extract solution;Add acetum into filter residue, repeat to extract 1-2 by aforesaid operations
It is secondary, extract solution and filter residue are obtained, 1.5-2.5mol/L sodium chloride solutions are added into extract solution and carry out salt precipitation, after precipitation is dried
Produce fish skin collagen powder.
Preferably, the preparation method of the citric acid solution comprises the following steps:
(1)Material filtering and impurity removing:Orange juice is prepared, filter press press filtration is used, to orange juice filtering and impurity removing, orange juice sour water is obtained;
(2)Neutralize:Orange juice sour water is heated to 60-75 DEG C, progressively calcium carbonate serum, continuous heating 2-3h, initial temperature is filled to it
Control at 5-8 DEG C or so, can finally be increased to 90-100 DEG C, to solution be in dark green when, that is, show finished neutralization, Ran Houjing
Precipitation is put, gained precipitation is calcium citrate;
(3)Desalination:Gained calcium citrate is rich in salinity, is scrubbed with clear water, is heated to 60-70 DEG C, repeats 2-3 times, until salinity
Cleared to stop, dry calcium citrate slurries are standby;
(4)Acidolysis is decolourized:Calcium citrate slurries are heated to 60-70 DEG C, the hydrochloric acid that admixture mass fraction is 20-30 %, heating
2-3 hours, deposition is stood, supernatant liquor is citric acid solution, with 3-5% activated carbon decolorizing 20-30min, then obtain citric acid molten
Liquid.
Preferably, the step(2)Middle fish skin collagen powder is dissolved in 0.2-0.6mol/L citric acid solutions, dissolves 24-
48h, is made 2-6mg/mL collagen solution.
Preferably, the step(3)Middle centrifugal condition is 2000-2500r/min, and centrifugation time is 20-30min.
Preferably, the step(4)In acetate buffer solution be 0.2-0.4mol/L Acetic acid-sodium acetate buffer solution.
Preferably, the step(4)In supernatant and acetate buffer solution volume ratio be 2-3:1.
Preferably, the step(5)In bath temperature be 20-30 DEG C, water bath time is 12-36h.
Compared with prior art, the present invention has following beneficial effect:
(1)The method that the present invention inquires into aquatic products collagen assembly formation fiber, the collagenous fibres as obtained by the inventive method are silk
Shape fiber, it is extremely similar to naturally occurring collagenous fibres form in deep-sea fish skin, have in biomaterial for medical purpose field very high
Application prospect;
(2)The present invention dissolves collagen using citric acid solution, because citric acid has 3 carboxyls, can simultaneously with it is many
The hydroxyls dehydrate condensation of individual protein and peptide chain, and then make the helical structure of polypeptide chain even closer firmly, the fiber horizontal stroke of formation
Line is close and more, improves the performance of fiber.
Embodiment
With reference to specific embodiment, the present invention is expanded on further.It should be understood that these embodiments are merely to illustrate the present invention
Rather than limitation the scope of the present invention.
Embodiment 1
The method that the fish skin collagen that the present embodiment is provided is self-assembled into fiber, comprises the following steps:
(1)Extract fish skin collagen powder;
(2)By the step(1)In fish skin collagen powder be dissolved in citric acid solution, the fish skin collagen powder is dissolved in
In 0.6mol/L citric acid solutions, 24h is dissolved, 6mg/mL collagen solution is made;
(3)To the step(2)In mixed liquor centrifuged, take supernatant, centrifugal condition is 2000r/min, centrifugation time
For 30min;
(4)By the step(3)In supernatant mixed with acetate buffer solution in ice bath, stir, adjust solution PH, institute
The Acetic acid-sodium acetate buffer solution that acetate buffer solution is 0.2mol/L is stated, the supernatant is 3 with acetate buffer solution volume ratio:1;
(5)By the step(4)In mixed liquor water-bath in water-bath, produce self-assembly collagenous fibres, the water-bath temperature
Spend for 20 DEG C, water bath time is 36h.
Wherein, the preparation method of the fish skin collagen powder comprises the following steps:
(1)Fresh fish-skin is taken to clean, removal of impurities;
(2)The potassium hydroxide solution that the fish skin raw material after cleaning is 0.16mol/L with concentration is taken to soak 1h, institute under the conditions of 20 DEG C
The potassium hydroxide solution of addition and the envelope-bulk to weight ratio of fish skin raw material are 20: 1, in immersion process, every 2h, change immersion and use
Potassium hydroxide solution 2 times;After immersion is finished, clean, filtering;Clean in backward fish skin raw material and add organic solvent immersion 2h, plus
Clear water, it is 10% to make fish skin raw material and the quality percent by volume of organic solvent;
(3)Take the step(2)Gained raw material mixed liquor, adds condition of acetum of the concentration for 0.36mol/L at 20 DEG C
The envelope-bulk to weight ratio of lower progress swelling treatment 12h, the acetum solution added and raw material mixed liquor is 15: 1;Then 0
Freeze 10h under the conditions of DEG C;Freeze after finishing, the acetum for adding appropriate 0.15mol/L carries out being beaten broken, acquisition particle diameter
4mm particle slurry;
(4)To the step(3)In particle slurry in add 0.05mol/L acetum extracted, the vinegar added
The envelope-bulk to weight ratio of acid solution and particle slurry is 30: 1,0 DEG C of Extracting temperature, and extraction time is 48h;After extraction is finished, with 60
Mesh gauze is filtered, and obtains extract solution;Add acetum into filter residue, repeat to extract 2 times by aforesaid operations, obtain extract solution and filter residue,
1.5mol/L sodium chloride solutions are added into extract solution and carry out salt precipitation, precipitation produces fish skin collagen powder after drying.
Wherein, the preparation method of the citric acid solution comprises the following steps:
(1)Material filtering and impurity removing:Orange juice is prepared, filter press press filtration is used, to orange juice filtering and impurity removing, orange juice sour water is obtained;
(2)Neutralize:Orange juice sour water is heated to 75 DEG C, progressively calcium carbonate serum is filled to it, continuous heating 2h, initial temperature control exists
8 DEG C or so, can finally be increased to 90 DEG C, to solution be in dark green when, that is, show the neutralization that finished, then staticly settle, gained
Precipitation is calcium citrate;
(3)Desalination:Gained calcium citrate is rich in salinity, is scrubbed with clear water, is heated to 70 DEG C, is repeated 2 times, and stops until salinity is cleared
Only, dry calcium citrate slurries, standby;
(4)Acidolysis is decolourized:Calcium citrate slurries are heated to 70 DEG C, the hydrochloric acid that admixture mass fraction is 20% is heated 3 hours, quiet
Deposition is put, supernatant liquor is citric acid solution, with 3% activated carbon decolorizing 30min, then obtain citric acid solution.
Embodiment 2
The method that the fish skin collagen that the present embodiment is provided is self-assembled into fiber, comprises the following steps:
(1)Extract fish skin collagen powder;
(2)By the step(1)In fish skin collagen powder be dissolved in citric acid solution, the fish skin collagen powder is dissolved in
In 0.2mol/L citric acid solutions, 48h is dissolved, 2mg/mL collagen solution is made;
(3)To the step(2)In mixed liquor centrifuged, take supernatant, centrifugal condition is 2500r/min, centrifugation time
For 20min;
(4)By the step(3)In supernatant mixed with acetate buffer solution in ice bath, stir, adjust solution PH, institute
The Acetic acid-sodium acetate buffer solution that acetate buffer solution is 0.4mol/L is stated, the supernatant is 2 with acetate buffer solution volume ratio:1;
(5)By the step(4)In mixed liquor water-bath in water-bath, produce self-assembly collagenous fibres, the water-bath temperature
Spend for 30 DEG C, water bath time is 12h.
Wherein, the preparation method of the fish skin collagen powder comprises the following steps:
(1)Fresh fish-skin is taken to clean, removal of impurities;
(2)The potassium hydroxide solution that the fish skin raw material after cleaning is 3.0mol/L with concentration is taken to soak 20h, institute under the conditions of 0 DEG C
The potassium hydroxide solution of addition and the envelope-bulk to weight ratio of fish skin raw material are 10: 1, in immersion process, every 4h, change immersion and use
Potassium hydroxide solution 1 time;After immersion is finished, clean, filtering;Clean in backward fish skin raw material and add organic solvent immersion 6h, plus
Clear water, it is 5% to make fish skin raw material and the quality percent by volume of organic solvent;
(3)Take the step(2)Gained raw material mixed liquor, addition concentration is 1.68mol/L acetum under conditions of 0 DEG C
The envelope-bulk to weight ratio of progress swelling treatment 36h, the acetum solution added and raw material mixed liquor is 10: 1;Then at 30 DEG C
Under the conditions of freeze 1h;Freeze after finishing, the acetum for adding appropriate 0.45mol/L carries out being beaten broken, acquisition particle diameter 2mm
Particle slurry;
(4)To the step(3)In particle slurry in add 3.56mol/L acetum extracted, the vinegar added
The envelope-bulk to weight ratio of acid solution and particle slurry is 15: 1,25 DEG C of Extracting temperature, and extraction time is 24h;After extraction is finished, with 80
Mesh gauze is filtered, and obtains extract solution;Add acetum into filter residue, repeat to extract 1 time by aforesaid operations, obtain extract solution and filter residue,
2.5mol/L sodium chloride solutions are added into extract solution and carry out salt precipitation, precipitation produces fish skin collagen powder after drying.
Wherein, the preparation method of the citric acid solution comprises the following steps:
(1)Material filtering and impurity removing:Orange juice is prepared, filter press press filtration is used, to orange juice filtering and impurity removing, orange juice sour water is obtained;
(2)Neutralize:Orange juice sour water is heated to 60 DEG C, progressively calcium carbonate serum is filled to it, continuous heating 3h, initial temperature control exists
5 DEG C or so, can finally be increased to 100 DEG C, to solution be in dark green when, that is, show the neutralization that finished, then staticly settle, gained
Precipitation is calcium citrate;
(3)Desalination:Gained calcium citrate is rich in salinity, is scrubbed with clear water, is heated to 60 DEG C, is repeated 3 times, and stops until salinity is cleared
Only, dry calcium citrate slurries, standby;
(4)Acidolysis is decolourized:Calcium citrate slurries are heated to 60 DEG C, the hydrochloric acid that admixture mass fraction is 30 % is heated 2 hours,
Deposition is stood, supernatant liquor is citric acid solution, with 5% activated carbon decolorizing 20min, then obtain citric acid solution.
Embodiment 3
The method that the fish skin collagen that the present embodiment is provided is self-assembled into fiber, comprises the following steps:
(1)Extract fish skin collagen powder;
(2)By the step(1)In fish skin collagen powder be dissolved in citric acid solution, the fish skin collagen powder is dissolved in
In 0.4mol/L citric acid solutions, 40h is dissolved, 5mg/mL collagen solution is made;
(3)To the step(2)In mixed liquor centrifuged, take supernatant, centrifugal condition is 2200r/min, centrifugation time
For 25min;
(4)By the step(3)In supernatant mixed with acetate buffer solution in ice bath, stir, adjust solution PH, institute
The Acetic acid-sodium acetate buffer solution that acetate buffer solution is 0.3mol/L is stated, the supernatant is 3 with acetate buffer solution volume ratio:1;
(5)By the step(4)In mixed liquor water-bath in water-bath, produce self-assembly collagenous fibres, the water-bath temperature
Spend for 25 DEG C, water bath time is 30h.
Wherein, the preparation method of the fish skin collagen powder comprises the following steps:
(1)Fresh fish-skin is taken to clean, removal of impurities;
(2)The potassium hydroxide solution that the fish skin raw material after cleaning is 1.5mol/L with concentration is taken to soak 15h, institute under the conditions of 15 DEG C
The potassium hydroxide solution of addition and the envelope-bulk to weight ratio of fish skin raw material are 15: 1, in immersion process, every 3h, change immersion and use
Potassium hydroxide solution 1 time;After immersion is finished, clean, filtering;Clean in backward fish skin raw material and add organic solvent immersion 4h, plus
Clear water, it is 7% to make fish skin raw material and the quality percent by volume of organic solvent;
(3)Take the step(2)Gained raw material mixed liquor, addition concentration is 1.4mol/L acetum under conditions of 10 DEG C
The envelope-bulk to weight ratio of progress swelling treatment 30h, the acetum solution added and raw material mixed liquor is 13: 1;Then at 20 DEG C
Under the conditions of freeze 6h;Freeze after finishing, the acetum for adding appropriate 0.35mol/L carries out being beaten broken, acquisition particle diameter 3mm
Particle slurry;
(4)To the step(3)In particle slurry in add 0.25mol/L acetum extracted, the vinegar added
The envelope-bulk to weight ratio of acid solution and particle slurry is 20: 1,20 DEG C of Extracting temperature, and extraction time is 40h;After extraction is finished, with 70
Mesh gauze is filtered, and obtains extract solution;Add acetum into filter residue, repeat to extract 1 time by aforesaid operations, obtain extract solution and filter residue,
2.0mol/L sodium chloride solutions are added into extract solution and carry out salt precipitation, precipitation produces fish skin collagen powder after drying.
Wherein, the preparation method of the citric acid solution comprises the following steps:
(1)Material filtering and impurity removing:Orange juice is prepared, filter press press filtration is used, to orange juice filtering and impurity removing, orange juice sour water is obtained;
(2)Neutralize:Orange juice sour water is heated to 65 DEG C, progressively calcium carbonate serum is filled to it, continuous heating 3h, initial temperature control exists
7 DEG C or so, can finally be increased to 95 DEG C, to solution be in dark green when, that is, show the neutralization that finished, then staticly settle, gained
Precipitation is calcium citrate;
(3)Desalination:Gained calcium citrate is rich in salinity, is scrubbed with clear water, is heated to 66 DEG C, is repeated 3 times, and stops until salinity is cleared
Only, dry calcium citrate slurries, standby;
(4)Acidolysis is decolourized:Calcium citrate slurries are heated to 68 DEG C, the hydrochloric acid that admixture mass fraction is 24% is heated 2 hours, quiet
Deposition is put, supernatant liquor is citric acid solution, with 4% activated carbon decolorizing 28min, then obtain citric acid solution.
Embodiment 4
The method that the fish skin collagen that the present embodiment is provided is self-assembled into fiber, comprises the following steps:
(1)Extract fish skin collagen powder;
(2)By the step(1)In fish skin collagen powder be dissolved in citric acid solution, the fish skin collagen powder is dissolved in
In 0.3mol/L citric acid solutions, 42h is dissolved, 5mg/mL collagen solution is made;
(3)To the step(2)In mixed liquor centrifuged, take supernatant, centrifugal condition is 2100r/min, centrifugation time
For 22min;
(4)By the step(3)In supernatant mixed with acetate buffer solution in ice bath, stir, adjust solution PH, institute
The Acetic acid-sodium acetate buffer solution that acetate buffer solution is 0.3mol/L is stated, the supernatant is 2 with acetate buffer solution volume ratio:1;
(5)By the step(4)In mixed liquor water-bath in water-bath, produce self-assembly collagenous fibres, the water-bath temperature
Spend for 21 DEG C, water bath time is 17h.
Wherein, the preparation method of the fish skin collagen powder comprises the following steps:
(1)Fresh fish-skin is taken to clean, removal of impurities;
(2)The potassium hydroxide solution that the fish skin raw material after cleaning is 1.65mol/L with concentration is taken to soak 18h under the conditions of 15 DEG C,
The potassium hydroxide solution and the envelope-bulk to weight ratio of fish skin raw material added is 14: 1, in immersion process, every 2h, changes immersion
With potassium hydroxide solution 2 times;After immersion is finished, clean, filtering;Clean in backward fish skin raw material and add organic solvent immersion 3h,
Plus clear water, it is 6% to make fish skin raw material and the quality percent by volume of organic solvent;
(3)Take the step(2)Gained raw material mixed liquor, adds condition of acetum of the concentration for 0.78mol/L at 14 DEG C
The envelope-bulk to weight ratio of lower progress swelling treatment 23h, the acetum solution added and raw material mixed liquor is 12: 1;Then 12
Freeze 3h under the conditions of DEG C;Freeze after finishing, the acetum for adding appropriate 0.35mol/L carries out being beaten broken, acquisition particle diameter
3mm particle slurry;
(4)To the step(3)In particle slurry in add 2.56mol/L acetum extracted, the vinegar added
The envelope-bulk to weight ratio of acid solution and particle slurry is 19: 1,12 DEG C of Extracting temperature, and extraction time is 33h;After extraction is finished, with 64
Mesh gauze is filtered, and obtains extract solution;Add acetum into filter residue, repeat to extract 1 time by aforesaid operations, obtain extract solution and filter residue,
2.5mol/L sodium chloride solutions are added into extract solution and carry out salt precipitation, precipitation produces fish skin collagen powder after drying.
Wherein, the preparation method of the citric acid solution comprises the following steps:
(1)Material filtering and impurity removing:Orange juice is prepared, filter press press filtration is used, to orange juice filtering and impurity removing, orange juice sour water is obtained;
(2)Neutralize:Orange juice sour water is heated to 73 DEG C, progressively calcium carbonate serum is filled to it, continuous heating 3h, initial temperature control exists
6 DEG C or so, can finally be increased to 99 DEG C, to solution be in dark green when, that is, show the neutralization that finished, then staticly settle, gained
Precipitation is calcium citrate;
(3)Desalination:Gained calcium citrate is rich in salinity, is scrubbed with clear water, is heated to 61 DEG C, is repeated 3 times, and stops until salinity is cleared
Only, dry calcium citrate slurries, standby;
(4)Acidolysis is decolourized:Calcium citrate slurries are heated to 63 DEG C, the hydrochloric acid that admixture mass fraction is 23% is heated 3 hours, quiet
Deposition is put, supernatant liquor is citric acid solution, with 4% activated carbon decolorizing 26min, then obtain citric acid solution.
Embodiment 5
The method that the fish skin collagen that the present embodiment is provided is self-assembled into fiber, comprises the following steps:
(1)Extract fish skin collagen powder;
(2)By the step(1)In fish skin collagen powder be dissolved in citric acid solution, the fish skin collagen powder is dissolved in
In 0.4mol/L citric acid solutions, 46h is dissolved, 5mg/mL collagen solution is made;
(3)To the step(2)In mixed liquor centrifuged, take supernatant, centrifugal condition is 2400r/min, centrifugation time
For 23min;
(4)By the step(3)In supernatant mixed with acetate buffer solution in ice bath, stir, adjust solution PH, institute
The Acetic acid-sodium acetate buffer solution that acetate buffer solution is 0.3mol/L is stated, the supernatant is 2 with acetate buffer solution volume ratio:1;
(5)By the step(4)In mixed liquor water-bath in water-bath, produce self-assembly collagenous fibres, the water-bath temperature
Spend for 27 DEG C, water bath time is 23h.
Wherein, the preparation method of the fish skin collagen powder comprises the following steps:
(1)Fresh fish-skin is taken to clean, removal of impurities;
(2)The potassium hydroxide solution that the fish skin raw material after cleaning is 0.22mol/L with concentration is taken to soak 5h, institute under the conditions of 13 DEG C
The potassium hydroxide solution of addition and the envelope-bulk to weight ratio of fish skin raw material are 17: 1, in immersion process, every 3h, change immersion and use
Potassium hydroxide solution 2 times;After immersion is finished, clean, filtering;Clean in backward fish skin raw material and add organic solvent immersion 3h, plus
Clear water, it is 8% to make fish skin raw material and the quality percent by volume of organic solvent;
(3)Take the step(2)Gained raw material mixed liquor, adds condition of acetum of the concentration for 1.48mol/L at 13 DEG C
The envelope-bulk to weight ratio of lower progress swelling treatment 19h, the acetum solution added and raw material mixed liquor is 12: 1;Then 25
Freeze 9h under the conditions of DEG C;Freeze after finishing, the acetum for adding appropriate 0.25mol/L carries out being beaten broken, acquisition particle diameter
3mm particle slurry;
(4)To the step(3)In particle slurry in add 2.56mol/L acetum extracted, the vinegar added
The envelope-bulk to weight ratio of acid solution and particle slurry is 17: 1,13 DEG C of Extracting temperature, and extraction time is 37h;After extraction is finished, with 63
Mesh gauze is filtered, and obtains extract solution;Add acetum into filter residue, repeat to extract 1 time by aforesaid operations, obtain extract solution and filter residue,
1.9mol/L sodium chloride solutions are added into extract solution and carry out salt precipitation, precipitation produces fish skin collagen powder after drying.
Wherein, the preparation method of the citric acid solution comprises the following steps:
(1)Material filtering and impurity removing:Orange juice is prepared, filter press press filtration is used, to orange juice filtering and impurity removing, orange juice sour water is obtained;
(2)Neutralize:Orange juice sour water is heated to 65 DEG C, progressively calcium carbonate serum is filled to it, continuous heating 3h, initial temperature control exists
6 DEG C or so, can finally be increased to 98 DEG C, to solution be in dark green when, that is, show the neutralization that finished, then staticly settle, gained
Precipitation is calcium citrate;
(3)Desalination:Gained calcium citrate is rich in salinity, is scrubbed with clear water, is heated to 63 DEG C, is repeated 3 times, and stops until salinity is cleared
Only, dry calcium citrate slurries, standby;
(4)Acidolysis is decolourized:Calcium citrate slurries are heated to 67 DEG C, the hydrochloric acid that admixture mass fraction is 22 % is heated 2 hours,
Deposition is stood, supernatant liquor is citric acid solution, with 4% activated carbon decolorizing 24min, then obtain citric acid solution.
The specific embodiment of the present invention is described above.It is to be appreciated that the invention is not limited in above-mentioned
Particular implementation, those skilled in the art can make various deformations or amendments within the scope of the claims, this not shadow
Ring the substantive content of the present invention.
Claims (8)
1. a kind of method that fish skin collagen is self-assembled into fiber, it is characterised in that:The fish skin collagen is self-assembled into the side of fiber
Method comprises the following steps:
(1)Extract fish skin collagen powder;
(2)By the step(1)In fish skin collagen powder be dissolved in citric acid solution;
(3)To the step(2)In mixed liquor centrifuged, take supernatant;
(4)By the step(3)In supernatant mixed with acetate buffer solution in ice bath, stir, adjust solution PH;
(5)By the step(4)In mixed liquor water-bath in water-bath, produce self-assembly collagenous fibres.
2. the method that fish skin collagen according to claim 1 is self-assembled into fiber, it is characterised in that:The fish skin collagen powder
Preparation method comprise the following steps:
(1)Fresh fish-skin is taken to clean, removal of impurities;
(2)The potassium hydroxide solution that the fish skin raw material after cleaning is 0.16-3.0mol/L with concentration is taken to be soaked under the conditions of 0-20 DEG C
1-20h is steeped, the potassium hydroxide solution and the envelope-bulk to weight ratio of fish skin raw material added is 10-20: 1, in immersion process, every
2-4h, changes immersion potassium hydroxide solution 1-2 times;After immersion is finished, clean, filtering;Clean in backward fish skin raw material and add
Organic solvent soaks 2-6h, plus clear water, and it is 5-10% to make fish skin raw material and the quality percent by volume of organic solvent;
(3)Take the step(2)Gained raw material mixed liquor, addition concentration is 0.36-1.68mol/L acetum at 0-20 DEG C
Under conditions of carry out swelling treatment 12-36h, the envelope-bulk to weight ratio of the acetum solution added and raw material mixed liquor is 10-
15∶1;Then 1-10h is freezed under the conditions of 0-30 DEG C;Freeze after finishing, the acetic acid for adding appropriate 0.15-0.45mol/L is molten
Liquid carries out mashing and crushed, and obtains particle diameter 2-4mm particle slurry;
(4)To the step(3)In particle slurry in add 0.05-3.56mol/L acetum extracted, added
The envelope-bulk to weight ratio of acetum and particle slurry be 15-30: 1,0-25 DEG C of Extracting temperature, extraction time is 24-48h;Carry
Take after finishing, filtered with 60-80 mesh gauze, obtain extract solution;Add acetum into filter residue, repeat to extract 1-2 by aforesaid operations
It is secondary, extract solution and filter residue are obtained, 1.5-2.5mol/L sodium chloride solutions are added into extract solution and carry out salt precipitation, after precipitation is dried
Produce fish skin collagen powder.
3. the method that fish skin collagen according to claim 1 is self-assembled into fiber, it is characterised in that:The citric acid solution
Preparation method comprise the following steps:
(1)Material filtering and impurity removing:Orange juice is prepared, filter press press filtration is used, to orange juice filtering and impurity removing, orange juice sour water is obtained;
(2)Neutralize:The step(1)In orange juice sour water be heated to 60-75 DEG C, progressively to its fill calcium carbonate serum, hold
Continuous heating 2-3h, initial temperature is controlled at 5-8 DEG C or so, can finally be increased to 90-100 DEG C, when to solution being in dark green, that is, is shown
Finish neutralization, then staticly settles, and gained precipitation is calcium citrate;
(3)Desalination:Gained calcium citrate is rich in salinity, is scrubbed with clear water, is heated to 60-70 DEG C, repeats 2-3 times, until salinity
Cleared to stop, dry calcium citrate slurries are standby;
(4)Acidolysis is decolourized:Calcium citrate slurries are heated to 60-70 DEG C, the hydrochloric acid that admixture mass fraction is 20-30 %, heating
2-3 hours, deposition is stood, supernatant liquor is citric acid solution, with 3-5% activated carbon decolorizing 20-30min, then obtain citric acid molten
Liquid.
4. the method that fish skin collagen according to claim 1 is self-assembled into fiber, it is characterised in that:The step(2)In
Fish skin collagen powder is dissolved in 0.2-0.6mol/L citric acid solutions, dissolves 24-48h, 2-6mg/mL collagen solution is made.
5. the method that fish skin collagen according to claim 1 is self-assembled into fiber, it is characterised in that:The step(3)In
Centrifugal condition is 2000-2500r/min, and centrifugation time is 20-30min.
6. the method that fish skin collagen according to claim 1 is self-assembled into fiber, it is characterised in that:The step(4)In
Acetate buffer solution be 0.2-0.4mol/L Acetic acid-sodium acetate buffer solution.
7. the method that fish skin collagen according to claim 1 is self-assembled into fiber, it is characterised in that:The step(4)In
Supernatant and acetate buffer solution volume ratio be 2-3:1.
8. the method that fish skin collagen according to claim 1 is self-assembled into fiber, it is characterised in that:The step(5)In
Bath temperature be 20-30 DEG C, water bath time is 12-36h.