CN107226658A - A kind of environment protection architecture mortar and preparation method thereof - Google Patents
A kind of environment protection architecture mortar and preparation method thereof Download PDFInfo
- Publication number
- CN107226658A CN107226658A CN201710610676.6A CN201710610676A CN107226658A CN 107226658 A CN107226658 A CN 107226658A CN 201710610676 A CN201710610676 A CN 201710610676A CN 107226658 A CN107226658 A CN 107226658A
- Authority
- CN
- China
- Prior art keywords
- parts
- environment protection
- protection architecture
- powder
- architecture mortar
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention provides a kind of environment protection architecture mortar and preparation method thereof, the environment protection architecture mortar includes following raw material by weight：Calcium silicates sheet material discards 20 25 parts of powder, 40 60 parts of portland cement, 12 parts of silicon nitride, 30 50 parts of expanded perlite, 0.5 1 parts of dimethicone, 48 parts of composite assistant, 46 parts of cellulose ether, 5 15 parts of aggregate, 56 parts of carboxymethyl cellulose, 50 80 parts of waste liquid, 80 120 parts of water, 12 15 parts of modified bamboo powdered carbon, 03 parts of redispersable latex powder.The present invention is utilized to industrial waste, solves the problems, such as treatment of urban garbage, product thermal and insulating performance of the present invention is good, does not ftracture, not hollowing, anti-aging, service life is long.
Description
Technical field
The present invention relates to building material technical field, and in particular to a kind of environment protection architecture mortar and preparation method thereof.
Background technology
Various countries are in architectural design and construction, the development and application of new building insulation material, the formulation of Regulation of building energy-saving
With substantial amounts of work has been done in terms of implementation, further improved while considerable economic benefit is obtained it is for the survival of mankind from
Right environment.Thermal insulation mortar is generally coated on wall, thermal insulation mortar is a kind of heat-insulating construction material painted for inner-outer wall, with
Light thermal-insulation particle is as lightweight aggregate, plus the dry powder and mortar being made up of other fillers and additive etc., but thermal insulation mortar is sudden and violent
Dew in space easily splits by water suction, and this is accomplished by heat-insulation mortar bed setting anticracking grout, but existing anticracking grout
Effect is poor.
At the same time, in insulating decoration integral board for building exterior wall process, it can be sand flat by sander polishing, now
Substantial amounts of calcium silicate board can be produced and discard powder.And traditional discarded powder processing mode can destroy ecological environment, and produce big
The waste disposal expense of amount.When carrying out paint spraying technique on calcium silicate board surface, water paint production of articles line can also be produced greatly
The colorful discarded emulsion of amount, and traditional sewage treatment mode of this solution can make it have no use value.With environmental consciousness
Strengthen, to reach national industrial policies and the common people to the non-harmful demand of safety and environmental protection, construction material uses environmental protection raw material
Have become a kind of trend.
The content of the invention
The purpose of the present invention is that there is provided a kind of environment protection architecture mortar and preparation method thereof for problem of the prior art.
In order to achieve the above object, the present invention is achieved through the following technical solutions：
A kind of environment protection architecture mortar, the environment protection architecture mortar includes following raw material by weight：
Calcium silicates sheet material discards 20-25 parts of powder, 40-60 parts of portland cement,
1-2 parts of silicon nitride, 30-50 parts of expanded perlite,
0.5-1 parts of dimethicone, 4-8 parts of composite assistant,
4-6 parts of cellulose ether, 5-15 parts of aggregate,
5-6 parts of carboxymethyl cellulose, 50-80 parts of waste liquid,
80-120 parts of water, 12-15 parts of modified bamboo powdered carbon,
0-3 parts of redispersable latex powder.
Further, the environment protection architecture mortar includes following raw material by weight：
Calcium silicates sheet material discards 23 parts of powder, 50 parts of portland cement,
1 part of silicon nitride, 40 parts of expanded perlite,
0.8 part of dimethicone, 6 parts of composite assistant,
5 parts of cellulose ether, 10 parts of aggregate,
5 parts of carboxymethyl cellulose, 65 parts of waste liquid,
100 parts of water, 14 parts of modified bamboo powdered carbon,
1 part of redispersable latex powder.
Further, the aggregate is that river sand and calcium silicates sheet material discard powder.
Further, the preparation method of the waste liquid is：By the emulsus waste liquid produced by colorful water paint, by filtering,
Separation, respectively obtain solid suspended particles and isolating polymer emulsion, after suspended particles are blended, with isolating polymer emulsion or
Water is according to 3:5 ratio is mixed evenly and is made.
Further, the composite assistant is made from the following raw materials in parts by weight：3-8 parts of chitosan, 4-10 parts of kaolin,
0.5-1 parts of 2-4 parts of silica, 2-4 parts of sodium hydroxide, 1-3 parts of ammonium chloride and sodium tripolyphosphate.
Further, the composite assistant is made from the following raw materials in parts by weight：5 parts of chitosan, 7 parts of kaolin, dioxy
0.7 part of 3 parts of SiClx, 3 parts of sodium hydroxide, 2 parts of ammonium chloride and sodium tripolyphosphate.
Further, the preparation method of the composite assistant is：Dissolve the chitosan in appropriate 5% aqueous acetic acid, plus
Enter kaolin, Silica abrasive 30min, pH is adjusted to sequentially add sodium hydroxide, ammonium chloride after neutrality, 60 DEG C of stirrings
30min, pH is adjusted under neutrality, normal temperature to be spray-dried after adding sodium tripolyphosphate, stirring 30min, produced.
A kind of preparation method of environment protection architecture mortar, comprises the following steps：
（1）Ground after cellulose ether, carboxymethyl cellulose, modified bamboo powdered carbon, redispersable latex powder and aggregate are mixed, mistake
200 mesh sieves, obtain component A；
（2）Calcium silicates sheet material is discarded into powder, silicon nitride, expanded perlite, dimethicone, composite assistant, waste liquid and water to mix
Conjunction is incubated 3h after stirring at 40-60 DEG C, obtains component B；
（3）Component A, component B are mixed with remaining raw material, the environment protection architecture mortar is produced after stirring.
The present invention compared with prior art, with following beneficial effect：
The present invention is utilized existing calcium silicates sanding plate industrial waste, on the one hand reduces the discharge of waste material, is solved
Treatment of urban garbage problem, saves the energy, protects environment, on the other hand reduce the production of exterior-wall heat insulation adhesive mortar
Cost.In addition, there is the waste liquid in the adhesive mortar of the present invention water-loss reducer to act on and the effect of redispersable latex powder additive,
So as to which such additive need not be reused when supporting the use, using more convenient.The stable physical property of product of the present invention, heat conduction system
Number is small, and thermal and insulating performance is good, with certain gas permeability, does not ftracture, not hollowing, and anti-aging, service life is long.While this hair
Bright preparation method simple and fast, it is practical.
Embodiment
With reference to embodiment, the invention will be further described.
Embodiment 1
A kind of environment protection architecture mortar, the environment protection architecture mortar includes following raw material by weight：
Calcium silicates sheet material discards 20 parts of powder, 40 parts of portland cement,
1 part of silicon nitride, 30 parts of expanded perlite,
0.5 part of dimethicone, 4 parts of composite assistant,
4 parts of cellulose ether, 5 parts of aggregate,
5 parts of carboxymethyl cellulose, 50 parts of waste liquid,
80 parts of water, 12 parts of modified bamboo powdered carbon.
The aggregate is that river sand and calcium silicates sheet material discard powder.
The preparation method of the waste liquid is：By the emulsus waste liquid produced by colorful water paint, pass through filtering, separation, difference
Solid suspended particles and isolating polymer emulsion are obtained, after suspended particles are blended, with isolating polymer emulsion or water according to 3:5
Ratio be mixed evenly and be made.
The composite assistant is made from the following raw materials in parts by weight：3 parts of chitosan, 4 parts of kaolin, 2 parts of silica, hydrogen
0.5 part of 2 parts of sodium oxide molybdena, 1 part of ammonium chloride and sodium tripolyphosphate.
The preparation method of the composite assistant is：Dissolve the chitosan in appropriate 5% aqueous acetic acid, add kaolin,
Silica abrasive 30min, pH is adjusted to sequentially add sodium hydroxide, ammonium chloride after neutrality, 60 DEG C of stirring 30min, and pH is adjusted
To neutral, it is spray-dried, produces after sodium tripolyphosphate, stirring 30min are added under normal temperature.
A kind of preparation method of environment protection architecture mortar, comprises the following steps：
（1）Ground after cellulose ether, carboxymethyl cellulose, modified bamboo powdered carbon, redispersable latex powder and aggregate are mixed, mistake
200 mesh sieves, obtain component A；
（2）Calcium silicates sheet material is discarded into powder, silicon nitride, expanded perlite, dimethicone, composite assistant, waste liquid and water to mix
Conjunction is incubated 3h after stirring at 40 DEG C, obtains component B；
（3）Component A, component B are mixed with remaining raw material, the environment protection architecture mortar is produced after stirring.
Embodiment 2
A kind of environment protection architecture mortar, the environment protection architecture mortar includes following raw material by weight：
Calcium silicates sheet material discards 25 parts of powder, 60 parts of portland cement,
2 parts of silicon nitride, 50 parts of expanded perlite,
1 part of dimethicone, 8 parts of composite assistant,
6 parts of cellulose ether, 15 parts of aggregate,
6 parts of carboxymethyl cellulose, 80 parts of waste liquid,
120 parts of water, 15 parts of modified bamboo powdered carbon,
3 parts of redispersable latex powder.
The aggregate is that river sand and calcium silicates sheet material discard powder.
The preparation method of the waste liquid is：By the emulsus waste liquid produced by colorful water paint, pass through filtering, separation, difference
Solid suspended particles and isolating polymer emulsion are obtained, after suspended particles are blended, with isolating polymer emulsion or water according to 3:5
Ratio be mixed evenly and be made.
The composite assistant is made from the following raw materials in parts by weight：8 parts of chitosan, 10 parts of kaolin, 4 parts of silica,
1 part of 4 parts of sodium hydroxide, 3 parts of ammonium chloride and sodium tripolyphosphate.
The preparation method of the composite assistant is：Dissolve the chitosan in appropriate 5% aqueous acetic acid, add kaolin,
Silica abrasive 30min, pH is adjusted to sequentially add sodium hydroxide, ammonium chloride after neutrality, 60 DEG C of stirring 30min, and pH is adjusted
To neutral, it is spray-dried, produces after sodium tripolyphosphate, stirring 30min are added under normal temperature.
A kind of preparation method of environment protection architecture mortar, comprises the following steps：
（1）Ground after cellulose ether, carboxymethyl cellulose, modified bamboo powdered carbon, redispersable latex powder and aggregate are mixed, mistake
200 mesh sieves, obtain component A；
（2）Calcium silicates sheet material is discarded into powder, silicon nitride, expanded perlite, dimethicone, composite assistant, waste liquid and water to mix
Conjunction is incubated 3h after stirring at 60 DEG C, obtains component B；
（3）Component A, component B are mixed with remaining raw material, the environment protection architecture mortar is produced after stirring.
Embodiment 3
A kind of environment protection architecture mortar, the environment protection architecture mortar includes following raw material by weight：
Calcium silicates sheet material discards 23 parts of powder, 50 parts of portland cement,
1 part of silicon nitride, 40 parts of expanded perlite,
0.8 part of dimethicone, 6 parts of composite assistant,
5 parts of cellulose ether, 10 parts of aggregate,
5 parts of carboxymethyl cellulose, 65 parts of waste liquid,
100 parts of water, 14 parts of modified bamboo powdered carbon,
1 part of redispersable latex powder.
The aggregate is that river sand and calcium silicates sheet material discard powder.
The preparation method of the waste liquid is：By the emulsus waste liquid produced by colorful water paint, pass through filtering, separation, difference
Solid suspended particles and isolating polymer emulsion are obtained, after suspended particles are blended, with isolating polymer emulsion or water according to 3:5
Ratio be mixed evenly and be made.
The composite assistant is made from the following raw materials in parts by weight：5 parts of chitosan, 7 parts of kaolin, 3 parts of silica, hydrogen
0.7 part of 3 parts of sodium oxide molybdena, 2 parts of ammonium chloride and sodium tripolyphosphate.
The preparation method of the composite assistant is：Dissolve the chitosan in appropriate 5% aqueous acetic acid, add kaolin,
Silica abrasive 30min, pH is adjusted to sequentially add sodium hydroxide, ammonium chloride after neutrality, 60 DEG C of stirring 30min, and pH is adjusted
To neutral, it is spray-dried, produces after sodium tripolyphosphate, stirring 30min are added under normal temperature.
A kind of preparation method of environment protection architecture mortar, comprises the following steps：
（1）Ground after cellulose ether, carboxymethyl cellulose, modified bamboo powdered carbon, redispersable latex powder and aggregate are mixed, mistake
200 mesh sieves, obtain component A；
（2）Calcium silicates sheet material is discarded into powder, silicon nitride, expanded perlite, dimethicone, composite assistant, waste liquid and water to mix
Conjunction is incubated 3h after stirring at 40-60 DEG C, obtains component B；
（3）Component A, component B are mixed with remaining raw material, the environment protection architecture mortar is produced after stirring.
The present invention is utilized existing calcium silicates sanding plate industrial waste, on the one hand reduces the discharge of waste material,
Treatment of urban garbage is solved the problems, such as, the energy is saved, environment is protected, exterior-wall heat insulation adhesive mortar is on the other hand reduced
Production cost.In addition, there is the waste liquid in the adhesive mortar of the present invention water-loss reducer to act on and redispersable latex powder additive
Effect, so that such additive need not be reused when supporting the use, using more convenient.The stable physical property of product of the present invention,
Thermal conductivity factor is small, and thermal and insulating performance is good, with certain gas permeability, and comfortableness is high, does not ftracture, not hollowing, anti-aging, uses
Long lifespan.Preparation method simple and fast of the present invention, practical simultaneously.
The preferred embodiments of the present invention are these are only, are not intended to limit the invention, although with reference to the foregoing embodiments
The present invention is described in detail, for those skilled in the art, it still can be to foregoing embodiments institute
The technical scheme of record is modified, or carries out equivalent substitution to which part technical characteristic.It is all the present invention spirit and
Within principle, any modification, equivalent substitution and improvements made etc. should be included in the scope of the protection.
Claims (8)
1. a kind of environment protection architecture mortar, it is characterised in that the environment protection architecture mortar includes following raw material by weight：
Calcium silicates sheet material discards 20-25 parts of powder, 40-60 parts of portland cement,
1-2 parts of silicon nitride, 30-50 parts of expanded perlite,
0.5-1 parts of dimethicone, 4-8 parts of composite assistant,
4-6 parts of cellulose ether, 5-15 parts of aggregate,
5-6 parts of carboxymethyl cellulose, 50-80 parts of waste liquid,
80-120 parts of water, 12-15 parts of modified bamboo powdered carbon,
0-3 parts of redispersable latex powder.
2. a kind of environment protection architecture mortar according to claim 1, it is characterised in that the environment protection architecture mortar includes following
Raw material by weight：
Calcium silicates sheet material discards 23 parts of powder, 50 parts of portland cement,
1 part of silicon nitride, 40 parts of expanded perlite,
0.8 part of dimethicone, 6 parts of composite assistant,
5 parts of cellulose ether, 10 parts of aggregate,
5 parts of carboxymethyl cellulose, 65 parts of waste liquid,
100 parts of water, 14 parts of modified bamboo powdered carbon,
1 part of redispersable latex powder.
3. a kind of environment protection architecture mortar according to claim 1, it is characterised in that the aggregate is river sand and calcium silicate board
Material discards powder.
4. a kind of environment protection architecture mortar according to claim 1, it is characterised in that the preparation method of the waste liquid is：Will
Emulsus waste liquid produced by colorful water paint, by filtering, separation, respectively obtains solid suspended particles and isolating polymer breast
Liquid, after suspended particles are blended, with isolating polymer emulsion or water according to 3:5 ratio is mixed evenly and is made.
5. a kind of environment protection architecture mortar according to claim 1, it is characterised in that the composite assistant is by following parts by weight
Raw material be made：3-8 parts of chitosan, 4-10 parts of kaolin, 2-4 parts of silica, 2-4 parts of sodium hydroxide, 1-3 parts of ammonium chloride and
0.5-1 parts of sodium tripolyphosphate.
6. a kind of environment protection architecture mortar according to claim 1, it is characterised in that the composite assistant is by following parts by weight
Raw material be made：5 parts of chitosan, 7 parts of kaolin, 3 parts of silica, 3 parts of sodium hydroxide, 2 parts of ammonium chloride and sodium tripolyphosphate
0.7 part.
7. a kind of environment protection architecture mortar according to claim 1, it is characterised in that the preparation method of the composite assistant
It is：Dissolve the chitosan in appropriate 5% aqueous acetic acid, add kaolin, Silica abrasive 30min, pH is adjusted to neutrality
After sequentially add sodium hydroxide, ammonium chloride, pH is adjusted to add sodium tripolyphosphate under neutrality, normal temperature, stirred by 60 DEG C of stirring 30min
Mix and be spray-dried after 30min, produced.
8. a kind of preparation method of environment protection architecture mortar as described in claim 1-7 any one, it is characterised in that including with
Lower step：
（1）Ground after cellulose ether, carboxymethyl cellulose, modified bamboo powdered carbon, redispersable latex powder and aggregate are mixed, mistake
200 mesh sieves, obtain component A；
（2）Calcium silicates sheet material is discarded into powder, silicon nitride, expanded perlite, dimethicone, composite assistant, waste liquid and water to mix
Conjunction is incubated 3h after stirring at 40-60 DEG C, obtains component B；
（3）Component A, component B are mixed with remaining raw material, the environment protection architecture mortar is produced after stirring.