CN107216707A - 一种建筑涂料专用防沉增稠剂及其制备方法 - Google Patents
一种建筑涂料专用防沉增稠剂及其制备方法 Download PDFInfo
- Publication number
- CN107216707A CN107216707A CN201710308572.XA CN201710308572A CN107216707A CN 107216707 A CN107216707 A CN 107216707A CN 201710308572 A CN201710308572 A CN 201710308572A CN 107216707 A CN107216707 A CN 107216707A
- Authority
- CN
- China
- Prior art keywords
- thickener
- settling
- parts
- building coating
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种建筑涂料专用防沉增稠剂及其制备方法,增稠剂以重量份计,包括以下组分:聚乙二醇8‑12份,二异氰酸酯13‑16份,封端剂2‑4份,防沉添加剂6‑10份,水30‑60份,防沉添加剂为矿物土、胶类增稠剂、纤维素增稠剂和水,配比为0.1‑5:0.1‑5:0.1‑5:100。本发明还公开了该增稠剂的制备方法。通过本发明制备的增稠剂增稠性强,具有优异的稳定性和悬浮性,长时间放置无沉淀,防止颜料、填料沉积,用于建筑涂料起很好的防沉、增稠作用,增稠防沉效果好,有效防止水性涂料沉淀、分层,提高涂料的使用性能,且其制备方法简单,易操作,成本低。
Description
技术领域
本发明涉及增稠剂领域,特别涉及一种建筑涂料专用防沉增稠剂及其制备方法。
背景技术
水性涂料一般是由树脂的乳液粒子、颜料悬浮体粒子的分散体,通过粒子间的相互作用力而形成的。涂料的粘度是这些粒子相互作用力的表征。但是,这些作用力较弱,增稠剂的作用是增加粒子间的相互作用,形成网络结构。
目前建筑行业涂料的增稠剂种类繁多,但是大多存在悬浮性和防沉性差的缺点,导致涂料容易出现颜料、填料沉积现象,使得涂料在生产、贮存、施工、成膜过程中受到影响。因此,提高增稠剂的防沉性显得非常重要。
发明内容
本发明的目的是为了改变传统增稠剂存在的种种不足及沉降问题,提供一种建筑涂料专用防沉增稠剂及其制备方法,其增稠性强、稳定性好、防沉效果好,所增稠的涂料成膜性好,而且不会消光,不会发生微生物降解作用,且其制备方法简单,易操作,成本低。所述技术方案如下:一种建筑涂料专用防沉增稠剂,以重量份计,包括以下组分:
聚乙二醇8-12份,
二异氰酸酯13-16份,
封端剂2-4份,
防沉添加剂6-10份,
水30-60份;
防沉添加剂为矿物土、胶类增稠剂、纤维素增稠剂和水,配比为0.1-5:0.1-5:0.1-5:100。
作为上述技术方案的优选,一种建筑涂料专用防沉增稠剂,其特征在于,所述封端剂为壬基酚聚氧乙烯醚、壬基酚或者苯胺中的一种或几种。
作为上述技术方案的优选,一种建筑涂料专用防沉增稠剂,其特征在于,所述二异氰酸酯为异佛尔酮二异氰酸酯、二环己基甲烷二异氰酸酯、 六亚甲基二异氰酸酯、甲苯二异氰酸酯或二苯基甲烷二异氰酸酯中的一种或几种。
本发明所述的建筑涂料专用防沉增稠剂的制备方法,包括以下步骤:
(1)将聚乙二醇和封端剂加入到装有电动搅拌机的四口烧瓶中,开动低速搅拌,升温至120℃真空干燥脱水1h;
(2)将惰性气体缓慢地通入四口瓶中,降温至70-80℃,加入二异氰酸酯高速搅拌,搅拌速度为500r/min,于70-85℃反应1-2h,制得混合液;
(3)在混合液中缓慢加入防沉添加剂,边加边搅拌,直至完全溶解;
(4)加入适量水,充分搅拌1h,待物料中的溶剂分离完全以后得到的固体物即为合成的增稠剂。
作为上述技术方案的优选,步骤(2)中所述惰性气体为氮气。
作为上述技术方案的优选,步骤(4)中所述水为去离子水。
本发明具有以下有益效果:
本发明提供的建筑涂料专用防沉增稠剂增稠性强,具有优异的稳定性和悬浮性,长时间放置无沉淀,防止颜料、填料沉积,用于建筑涂料起很好的防沉、增稠作用,增稠防沉效果好,有效防止水性涂料沉淀、分层,提高涂料的使用性能,且其制备方法简单,易操作,成本低。
具体实施方式
为更好的理解本发明,下面通过实施例对本发明进一步说明,实 施例只用于解释本发明,不会对本发明构成任何的限定。
实施例1:
一种建筑涂料专用防沉增稠剂,以重量份计,包括以下组分:
聚乙二醇8份,
异佛尔酮二异氰酸酯13份,
壬基酚聚氧乙烯醚2份,
防沉添加剂6份,
水30份;
防沉添加剂为矿物土、胶类增稠剂、纤维素增稠剂和水,配比为0.1:0.1:0.1:100,
本发明所述的建筑涂料专用防沉增稠剂的制备方法,包括以下步骤:
(1)将聚乙二醇和封端剂壬基酚聚氧乙烯醚加入到装有电动搅拌机的四口烧瓶中,开动低速搅拌,升温至120℃真空干燥脱水1h;
(2)将氮气缓慢地通入四口瓶中,降温至70℃,加入异佛尔酮二异氰酸酯高速搅拌,搅拌速度为500r/min,于70℃反应1h,制得混合液;
(3)在混合液中缓慢加入防沉添加剂,边加边搅拌,直至完全溶解;
(4)加入适量去离子水,充分搅拌1h,待物料中的溶剂分离完全以后得到的固体物即为合成的增稠剂。
实施例2:
一种建筑涂料专用防沉增稠剂,以重量份计,包括以下组分:
聚乙二醇12份,
异佛尔酮二异氰酸酯16份,
壬基酚聚氧乙烯醚4份,
防沉添加剂10份,
水60份;
防沉添加剂为矿物土、胶类增稠剂、纤维素增稠剂和水,配比为5:5:5:100,
本实施例的制备方法与实施例1相同。
实施例3:
一种建筑涂料专用防沉增稠剂,以重量份计,包括以下组分:
聚乙二醇10份,
异佛尔酮二异氰酸酯14份,
壬基酚聚氧乙烯醚3份,
防沉添加剂8份,
水45份;
防沉添加剂为矿物土、胶类增稠剂、纤维素增稠剂和水,配比为2.5:2.5:2.5:100。
本实施例的制备方法与实施例1相同。
对上述实施例制备的建筑涂料专用防沉增稠剂与一种聚氨酯增稠剂的制备方法(CN200610100818.6)中的增稠剂做应用性能测试对比:
测试条件:将实施例1-3制得的增稠剂及对比例分别应用在苯丙乳胶漆涂料配方中制成测试试样,测试各试样不同温度的粘度以及其温度变化系数(40℃的粘度/20℃的粘度),苯丙乳胶漆重量百分组成如下:
表1 苯丙乳胶漆重量百分组成
测试方法:
将各测试试样在600转/min下搅拌15分钟。取出静置一晚,第二天用旋转式粘度仪测试粘度数据。
测试结果:见表2。
表2:性能测试对比
通过表中可以看出,经过15天的存储,4种涂料都无明显的沉降和分水现象,外观较好。但是,实施例1-3触变指数大于对比例,触变性大,防沉效果好。通过性能对比可看出,本发明制备的建筑涂料专用防沉增稠剂与国内外类似产品在建筑用涂料中增稠性能、热贮稳定性能、触变性和抗流挂性等方面具有相当的应用功能,具有优于同类市场产品的防沉效果,长时间放置无沉淀,防止颜料、填料沉积。本发明制备的增稠剂用于建筑涂料起很好的防沉、增稠作用,增稠防沉效果好,有效防止水性涂料沉淀、分层,提高涂料的使用性能,且其制备方法简单,易操作,成本低。
上述实施例为本发明较佳的实施方式,但本发明的实施方式并不受上述实施例的限制,其他的任何未背离本发明的精神实质与原理下所做的改变、修饰、替代、组合、化简,均应为等效的置换方式,都包含在本发明的保护范围内。
Claims (6)
1.一种建筑涂料专用防沉增稠剂,其特征在于,以重量份 计,包括以下组分:
聚乙二醇8-12份
二异氰酸酯13-16份
封端剂2-4份
防沉添加剂6-10份
水30-60份
防沉添加剂为矿物土、胶类增稠剂、纤维素增稠剂和水,配比为0.1-5:0.1-5:0.1-5:100。
2.一种权利要求1所述的建筑涂料专用防沉增稠剂,其特征在于,所述封端剂为壬基酚聚氧乙烯醚、壬基酚或者苯胺中的一种或几种。
3.一种权利要求1所述的建筑涂料专用防沉增稠剂,其特征在于,所述二异氰酸酯为异佛尔酮二异氰酸酯、二环己基甲烷二异氰酸酯、 六亚甲基二异氰酸酯、甲苯二异氰酸酯或二苯基甲烷二异氰酸酯中一种或几种。
4.一种权利要求1所述的建筑涂料专用防沉增稠剂的制备方法,其特征在于,包括以下步骤:
(1)将聚乙二醇和封端剂加入到装有电动搅拌机的四口烧瓶中,开动低速搅拌,升温至120℃真空干燥脱水1h;
(2)将惰性气体缓慢地通入四口瓶中,降温至70-80℃,加入二异氰酸酯高速搅拌,搅拌速度为500r/min,于70-85℃反应1-2h,制得混合液;
(3)在混合液中缓慢加入防沉添加剂,边加边搅拌,直至完全溶解;
(4)加入适量水,充分搅拌1h,待物料中的溶剂分离完全以后得到的固体物即为合成的增稠剂。
5.根据权利要求4所述的建筑涂料专用防沉增稠剂的制备方法,其特征在于,步骤(2)中所述惰性气体为氮气。
6.根据权利要求4所述的建筑涂料专用防沉增稠剂的制备方法,其特征在于,步骤(4)中所述水为去离子水。