CN107216081A - 一种耐火新型墙体保温材料及其制备方法 - Google Patents
一种耐火新型墙体保温材料及其制备方法 Download PDFInfo
- Publication number
- CN107216081A CN107216081A CN201710650129.0A CN201710650129A CN107216081A CN 107216081 A CN107216081 A CN 107216081A CN 201710650129 A CN201710650129 A CN 201710650129A CN 107216081 A CN107216081 A CN 107216081A
- Authority
- CN
- China
- Prior art keywords
- parts
- insulation material
- expanded perlite
- heat insulation
- wall body
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
本发明公开了一种耐火新型墙体保温材料，其特征在于，按照重量份包括以下原料：改性凹凸棒石粘土12~18份、矿棉渣15~25份、包膜膨胀珍珠岩10~25份、陶瓷空心微珠2~9份、玻璃纤维8~15份、硼化钛5~9份、二月桂酸二丁基锡1~6份、硅酸铝纤维2~5份、纳米二氧化硅3~6份、石墨1~3份、发泡剂1~2份、憎水剂1.5~2.3份、阻燃剂3~9份。本发明提供一种耐火新型墙体保温材料及其制备方法，添加了改性凹凸棒粘土、矿渣棉、包膜珍珠岩，改性凹凸棒粘土、矿渣棉、包膜珍珠岩之间相互协同作用，制得的保温材料的热导率低，膨胀系数低，并加入了阻燃剂，具有很好的防火性能。
Description
技术领域
本发明属于保温材料领域，具体涉及一种耐火新型墙体保温材料及其制备方法。
背景技术
随着工业的快速发展，经济发展也相当迅速，全世界对能源的需求也越来越大，在日益增大的总能源消耗中，建筑能耗特别大，约占总能源消耗的11～25%，大量的数据和实验都表明最快最有效的方法就是使用保温节能材料。
现在在国内外，有很多类型的保温材料。按材质分类，可将保温材料分为三类：金属保温材料、有机保温材料、无机保温材料。
金属保温材料但是这种材料的货源很少，价格很昂贵，作为建筑的保温材料而言会大大地提高成本，不能广泛的应用。
有机保温材料很容易燃烧，在高温时容易产生有毒的气体，耐老化、耐火性差，这些缺点都限制了有机保温材料的广泛的使用。
发明内容
针对上述问题，本发明要解决的技术问题是提供一种耐火新型墙体保温材料及其制备方法。
为实现上述目的，本发明的技术方案为：一种耐火新型墙体保温材料，按照重量份包括以下原料：改性凹凸棒石粘土12~18份、矿棉渣15~25份、包膜膨胀珍珠岩10~25份、陶瓷空心微珠2~9份、玻璃纤维8~15份、硼化钛5~9份、二月桂酸二丁基锡1~6份、硅酸铝纤维2~5份、纳米二氧化硅3~6份、石墨1~3份、发泡剂1~2份、憎水剂1.5~2.3份、阻燃剂3~9份。
进一步地，按照重量份包括以下原料：改性凹凸棒石粘土12份、矿棉渣15份、包膜膨胀珍珠岩10份、陶瓷空心微珠2份、玻璃纤维8份、硼化钛5份、二月桂酸二丁基锡1份、硅酸铝纤维2份、纳米二氧化硅3份、石墨1份、发泡剂1份、憎水剂1.5份、阻燃剂3份。
进一步地，所述包膜膨胀珍珠岩通过以下方式制得：取100目的膨胀珍珠岩，加入到包衣机中加热至200~250℃，并加入碳酸钙粉末，搅拌均匀，其中膨胀珍珠岩与碳酸钙粉末的质量比为20：1；接着包衣机的一端喷洒蒸馏水将膨胀珍珠岩浸湿，一端喷洒环氧树脂粉料，并不断搅拌20~40min，即得包膜膨胀珍珠岩。
进一步地，所述阻燃剂为磷酸三苯酯、聚磷酸铵、磷铵、磷酸三甲苯酯的一种或二种以上的混合物。
进一步地，所述发泡剂选自碳酸盐、碳化硅、十二烷基硫酸钠和石油醚中的一种或者多种。
一种耐火新型墙体保温材料的制备方法，主要包括以下步骤：
步骤1：按重量份数称取改性凹凸棒石粘土12~18份、矿棉渣15~25份、包膜膨胀珍珠岩10~25份、陶瓷空心微珠2~9份、玻璃纤维8~15份、硼化钛5~9份、二月桂酸二丁基锡1~6份、硅酸铝纤维2~5份、纳米二氧化硅3~6份、石墨1~3份、发泡剂1~2份、憎水剂1.5~2.3份、阻燃剂3~9份；
步骤2：将改性凹凸棒石粘土、矿棉渣、包膜膨胀珍珠岩、陶瓷空心微珠和适量的水加入到搅拌机内搅拌均匀，得到混合料；
步骤3：将步骤2得到的混合料以及玻璃纤维、硼化钛、二月桂酸二丁基锡、硅酸铝纤维、纳米二氧化硅、石墨、发泡剂、憎水剂、阻燃剂搅拌后加入到成型机内，加压成型即可，成型机中的温度为80~150℃。
进一步地，所述步骤2中搅拌机的搅拌速度为200~600r/min。
进一步地，所述步骤2中所述混合料与适量的水的重量比为1:2~4。
本发明的有益效果在于：本发明提供一种耐火新型墙体保温材料及其制备方法，添加了改性凹凸棒粘土、矿渣棉、包膜珍珠岩，改性凹凸棒粘土、矿渣棉、包膜珍珠岩之间相互协同作用，制得的保温材料的热导率低，膨胀系数低，并加入了阻燃剂，具有很好的防火性能。与卤素阻燃剂相比，磷系阻燃剂是一种较好的阻燃剂，具有添加量少、阻燃效率高、低烟、低毒、用途广泛等优点，作为保温材料的添加剂，可以更好地改良墙体保温材料的阻燃特性。
具体实施方式
为了使本发明的目的、技术方案及优点更加清楚明白，以下结合实施例，对本发明进行进一步的详细说明。应当理解，此处所描述的具体实施例仅仅用以解释本发明，并不限定本发明。
实施例1
一种耐火新型墙体保温材料，按照重量份包括以下原料：改性凹凸棒石粘土12份、矿棉渣15份、包膜膨胀珍珠岩10份、陶瓷空心微珠2份、玻璃纤维8份、硼化钛5份、二月桂酸二丁基锡1份、硅酸铝纤维2份、纳米二氧化硅3份、石墨1份、发泡剂1份、憎水剂1.5份、阻燃剂3份。
所述包膜膨胀珍珠岩通过以下方式制得：取100目的膨胀珍珠岩，加入到包衣机中加热至200℃，并加入碳酸钙粉末，搅拌均匀，其中膨胀珍珠岩与碳酸钙粉末的质量比为20：1；接着包衣机的一端喷洒蒸馏水将膨胀珍珠岩浸湿，一端喷洒环氧树脂粉料，并不断搅拌20min，即得包膜膨胀珍珠岩。
所述阻燃剂为磷酸三苯酯、聚磷酸铵、磷铵、磷酸三甲苯酯的一种或二种以上的混合物。
所述发泡剂选自碳酸盐、碳化硅、十二烷基硫酸钠和石油醚中的一种或者多种。
一种耐火新型墙体保温材料的制备方法，主要包括以下步骤：
步骤1：按重量份数称取改性凹凸棒石粘土12份、矿棉渣15份、包膜膨胀珍珠岩10份、陶瓷空心微珠2份、玻璃纤维8份、硼化钛5份、二月桂酸二丁基锡1份、硅酸铝纤维2份、纳米二氧化硅3份、石墨1份、发泡剂1份、憎水剂1.5份、阻燃剂3份；
步骤2：将改性凹凸棒石粘土、矿棉渣、包膜膨胀珍珠岩、陶瓷空心微珠和适量的水加入到搅拌机内搅拌均匀，得到混合料；
步骤3：将步骤2得到的混合料以及玻璃纤维、硼化钛、二月桂酸二丁基锡、硅酸铝纤维、纳米二氧化硅、石墨、发泡剂、憎水剂、阻燃剂搅拌后加入到成型机内，加压成型即可，成型机中的温度为80℃。
所述步骤2中搅拌机的搅拌速度为200r/min。
所述步骤2中所述混合料与适量的水的重量比为1:2。
实施例2
一种耐火新型墙体保温材料，按照重量份包括以下原料：改性凹凸棒石粘土15份、矿棉渣20份、包膜膨胀珍珠岩15份、陶瓷空心微珠6份、玻璃纤维11份、硼化钛7份、二月桂酸二丁基锡3份、硅酸铝纤维3份、纳米二氧化硅5份、石墨2份、发泡剂1份、憎水剂2.0份、阻燃剂6份。
所述包膜膨胀珍珠岩通过以下方式制得：取100目的膨胀珍珠岩，加入到包衣机中加热至230℃，并加入碳酸钙粉末，搅拌均匀，其中膨胀珍珠岩与碳酸钙粉末的质量比为20：1；接着包衣机的一端喷洒蒸馏水将膨胀珍珠岩浸湿，一端喷洒环氧树脂粉料，并不断搅拌30min，即得包膜膨胀珍珠岩。
所述阻燃剂为磷酸三苯酯、聚磷酸铵、磷铵、磷酸三甲苯酯的一种或二种以上的混合物。
所述发泡剂选自碳酸盐、碳化硅、十二烷基硫酸钠和石油醚中的一种或者多种。
一种耐火新型墙体保温材料的制备方法，主要包括以下步骤：
步骤1：按重量份数称取改性凹凸棒石粘土15份、矿棉渣20份、包膜膨胀珍珠岩15份、陶瓷空心微珠6份、玻璃纤维11份、硼化钛7份、二月桂酸二丁基锡3份、硅酸铝纤维3份、纳米二氧化硅5份、石墨2份、发泡剂1份、憎水剂2.0份、阻燃剂6份；
步骤2：将改性凹凸棒石粘土、矿棉渣、包膜膨胀珍珠岩、陶瓷空心微珠和适量的水加入到搅拌机内搅拌均匀，得到混合料；
步骤3：将步骤2得到的混合料以及玻璃纤维、硼化钛、二月桂酸二丁基锡、硅酸铝纤维、纳米二氧化硅、石墨、发泡剂、憎水剂、阻燃剂搅拌后加入到成型机内，加压成型即可，成型机中的温度为110℃。
所述步骤2中搅拌机的搅拌速度为400r/min。
所述步骤2中所述混合料与适量的水的重量比为1:3。
实施例3
一种耐火新型墙体保温材料，按照重量份包括以下原料：改性凹凸棒石粘土18份、矿棉渣25份、包膜膨胀珍珠岩25份、陶瓷空心微珠9份、玻璃纤维15份、硼化钛9份、二月桂酸二丁基锡6份、硅酸铝纤维5份、纳米二氧化硅6份、石墨3份、发泡剂2份、憎水剂2.3份、阻燃剂9份。
所述包膜膨胀珍珠岩通过以下方式制得：取100目的膨胀珍珠岩，加入到包衣机中加热至250℃，并加入碳酸钙粉末，搅拌均匀，其中膨胀珍珠岩与碳酸钙粉末的质量比为20：1；接着包衣机的一端喷洒蒸馏水将膨胀珍珠岩浸湿，一端喷洒环氧树脂粉料，并不断搅拌40min，即得包膜膨胀珍珠岩。
所述阻燃剂为磷酸三苯酯、聚磷酸铵、磷铵、磷酸三甲苯酯的一种或二种以上的混合物。
所述发泡剂选自碳酸盐、碳化硅、十二烷基硫酸钠和石油醚中的一种或者多种。
一种耐火新型墙体保温材料的制备方法，主要包括以下步骤：
步骤1：按重量份数称取改性凹凸棒石粘土18份、矿棉渣25份、包膜膨胀珍珠岩25份、陶瓷空心微珠9份、玻璃纤维15份、硼化钛9份、二月桂酸二丁基锡6份、硅酸铝纤维5份、纳米二氧化硅6份、石墨3份、发泡剂2份、憎水剂2.3份、阻燃剂9份；
步骤2：将改性凹凸棒石粘土、矿棉渣、包膜膨胀珍珠岩、陶瓷空心微珠和适量的水加入到搅拌机内搅拌均匀，得到混合料；
步骤3：将步骤2得到的混合料以及玻璃纤维、硼化钛、二月桂酸二丁基锡、硅酸铝纤维、纳米二氧化硅、石墨、发泡剂、憎水剂、阻燃剂搅拌后加入到成型机内，加压成型即可，成型机中的温度为150℃。
所述步骤2中搅拌机的搅拌速度为600r/min。
所述步骤2中所述混合料与适量的水的重量比为1:4。
以上所述仅为本发明的优选实施例而已，并不用于限制本发明，尽管参照前述实施例对本发明进行了详细的说明，对于本领域的技术人员来说，其依然可以对前述各实施例所记载的技术方案进行修改，或者对其中部分技术特征进行等同替换。凡在本发明的精神和原则之内，所作的任何修改、等同替换、改进等，均应包含在本发明的保护范围之内。
Claims (8)
1.一种耐火新型墙体保温材料，其特征在于，按照重量份包括以下原料：改性凹凸棒石粘土12~18份、矿棉渣15~25份、包膜膨胀珍珠岩10~25份、陶瓷空心微珠2~9份、玻璃纤维8~15份、硼化钛5~9份、二月桂酸二丁基锡1~6份、硅酸铝纤维2~5份、纳米二氧化硅3~6份、石墨1~3份、发泡剂1~2份、憎水剂1.5~2.3份、阻燃剂3~9份。
2.根据权利要求1所述的一种耐火新型墙体保温材料，其特征在于，按照重量份包括以下原料：改性凹凸棒石粘土12份、矿棉渣15份、包膜膨胀珍珠岩10份、陶瓷空心微珠2份、玻璃纤维8份、硼化钛5份、二月桂酸二丁基锡1份、硅酸铝纤维2份、纳米二氧化硅3份、石墨1份、发泡剂1份、憎水剂1.5份、阻燃剂3份。
3.根据权利要求1所述的一种耐火新型墙体保温材料，其特征在于，所述包膜膨胀珍珠岩通过以下方式制得：取100目的膨胀珍珠岩，加入到包衣机中加热至200~250℃，并加入碳酸钙粉末，搅拌均匀，其中膨胀珍珠岩与碳酸钙粉末的质量比为20：1；接着包衣机的一端喷洒蒸馏水将膨胀珍珠岩浸湿，一端喷洒环氧树脂粉料，并不断搅拌20~40min，即得包膜膨胀珍珠岩。
4.根据权利要求1所述的一种耐火新型墙体保温材料，其特征在于，所述阻燃剂为磷酸三苯酯、聚磷酸铵、磷铵、磷酸三甲苯酯的一种或二种以上的混合物。
5.根据权利要求1所述的一种耐火新型墙体保温材料，其特征在于，所述发泡剂选自碳酸盐、碳化硅、十二烷基硫酸钠和石油醚中的一种或者多种。
6.一种耐火新型墙体保温材料的制备方法，其特征在于，主要包括以下步骤：
步骤1：按重量份数称取改性凹凸棒石粘土12~18份、矿棉渣15~25份、包膜膨胀珍珠岩10~25份、陶瓷空心微珠2~9份、玻璃纤维8~15份、硼化钛5~9份、二月桂酸二丁基锡1~6份、硅酸铝纤维2~5份、纳米二氧化硅3~6份、石墨1~3份、发泡剂1~2份、憎水剂1.5~2.3份、阻燃剂3~9份；
步骤2：将改性凹凸棒石粘土、矿棉渣、包膜膨胀珍珠岩、陶瓷空心微珠和适量的水加入到搅拌机内搅拌均匀，得到混合料；
步骤3：将步骤2得到的混合料以及玻璃纤维、硼化钛、二月桂酸二丁基锡、硅酸铝纤维、纳米二氧化硅、石墨、发泡剂、憎水剂、阻燃剂搅拌后加入到成型机内，加压成型即可，成型机中的温度为80~150℃。
7.根据权利要求6所述的一种耐火新型墙体保温材料的制备方法，其特征在于，所述步骤2中搅拌机的搅拌速度为200~600r/min。
8.根据权利要求6所述的一种耐火新型墙体保温材料的制备方法，其特征在于，所述步骤2中所述混合料与适量的水的重量比为1:2~4。