CN107215019A - A kind of preparation technology of high collapsing high fashion dress shell fabric - Google Patents
A kind of preparation technology of high collapsing high fashion dress shell fabric Download PDFInfo
- Publication number
- CN107215019A CN107215019A CN201710582437.4A CN201710582437A CN107215019A CN 107215019 A CN107215019 A CN 107215019A CN 201710582437 A CN201710582437 A CN 201710582437A CN 107215019 A CN107215019 A CN 107215019A
- Authority
- CN
- China
- Prior art keywords
- fabric
- parts
- preparation technology
- dress shell
- shell fabric
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention discloses a kind of preparation technology of high collapsing high fashion dress shell fabric, belongs to field of textile.Including base cloth layer, bottom cloth layer, preparing printing screen layer, crumple gold stamping layer.The base fabric is non-woven fabrics.The bottom cloth layer is low elastic polyester filament.Described preparing printing screen layer is seaweed slurry and dispersion fuel and its solvent.Described crumples gold stamping layer for PU resins and antioxidant and stabilizer.The base cloth layer applies environment-friendly size on the surface of base fabric.The preparing printing screen layer applies seaweed slurry in preparing printing screen layer, by scalding film or gold stamping processing, obtains a kind of high collapsing high fashion dress shell fabric.The present invention discloses a kind of preparation technology of high collapsing high fashion dress shell fabric, and cost breadth can be stretched more than 10 times, and shape style novelty, fashion, beautiful in colour, easy cleaning, meet the requirement of liking to be beautiful of modern female by the fabric of the preparation technology；Production technology of the present invention is more complicated, it is not easy to be imitated, and fabric quality it is good, well-pressed, wear-resisting, it is quick-drying washable the advantages of.
Description
Technical field
Patent of the present invention is related to the preparation technology of weaving face fabric, more particularly to a kind of high collapsing high fashion dress shell fabric
Preparation technology.
Background technology
With the continuous improvement of living standard, people are existing to fabric beauty of dress sensitivity and Functional Requirement also more and more higher
Some dress shell fabrics are difficult that the demand that people are fully met in feel, weight, particularly female friend like purchase many not
The clothes of same type, while also more fastidious.As summer dress shell fabric, the dress shell fabric generally used currently on the market is with complete
Based on cotton, polyester-cotton blend, all-cotton fabric exist poor dimensional stability, the deformation that creases easily, it is on the high side the shortcomings of, and polyester-cotton fabric exist
Class is relatively low, poor air permeability the shortcomings of.Therefore an individual character and fashion and the material clothing deposited are by the first choice as them, completely newly
Develop a kind of fabric of high collapsing high fashion dress shell fabric very urgent.
The content of the invention
It is an object of the invention to overcome the deficiencies of the prior art and provide a kind of system of high collapsing high fashion dress shell fabric
Standby technique, by the PROCESS FOR TREATMENT to fabric, can make fabric have good drawing effect, more practicality.
The present invention solve the technical scheme that uses of above-mentioned technical problem for:A kind of high collapsing high fashion dress shell fabric
Preparation technology, including base cloth layer, bottom cloth layer, preparing printing screen layer, crumple gold stamping layer.The base fabric is non-woven fabrics.The bottom cloth layer
For low elastic polyester filament.Described preparing printing screen layer is seaweed slurry and dispersion fuel and its solvent.The described gold stamping layer that crumples is
PU resins and antioxidant and stabilizer.The base cloth layer applies environment-friendly size on the surface of base fabric.The preparing printing screen layer will
Seaweed slurry is applied in preparing printing screen layer, by gold stamping processing, obtains a kind of high collapsing high fashion dress shell fabric.
A kind of high collapsing high fashion dress shell fabric, it is characterised in that comprise the following steps：
1. a kind of preparation technology of high collapsing high fashion dress shell fabric, it is characterised in that the technological process of production by entering as follows
OK：Double twisting → weaving → clear water sizing → pre-setting → cash amount → dyeing → whole latitude sizing → stamp pre-setting → upper package → print
Spend → evaporate → being rolled up on whole latitude → and crumple → baking oven → cooling → gold stamping → cooling → stripping → clot.
2. double twisting weaving process, the double twisting twist is 3200, is weaved using the right hatching of a first from left.
3. dye, the fabric after 2. step is weaved carries out dyeing processing, the part parts by weights of dyeing is：Chelating
0.5-2 parts of agent, 1-2 parts of bleeding agent, 1-2 parts of dispersion fuel.
4. whole latitude setting process, the fabric after 3. step is dyed carries out whole latitude heat treatment, temperature control 160 DEG C-
180 DEG C, 70-90 ms/min of the fabric speed of service adds positive overfeeding 15-20, auxiliary agent is divided into proportion：Clear water 1:Softening agent
0.06-0.12：Silicone oil 0.003.
5. preparing printing screen technique, carries out preparing printing screen processing, temperature control is 110 by the fabric after step 4. whole latitude sizing
DEG C -120 DEG C, 4-10 ms/min of the fabric speed of service, the part parts by weights of stamp is：5-10 parts of clear water, marine alga agent
20-40 parts, 5-10 parts of disperse dyes.
6. step is rolled up on whole latitude, the fabric after step 5. preparing printing screen is cut into 80-160 meters/volume.
7. technique is crumpled, the fabric after being rolled up in step 6. whole latitude is carried out crumpling processing, the fabric rolled up on whole latitude is crumpled
In nonwoven layer, the fabric of 20-40 meters/volume is stitched into acrylics filament.Temperature control is in 180-220 DEG C, fabric speed of service control
System is in 0.5-3 ms/min, 0.2g/ square metres of sizing material, thickness 0.4mm.
8. baking oven process, the fabric after 7. step is crumpled is dried, cooling treatment, and oven temperature is controlled in 40-80
DEG C, time control was at 12-72 hours；The refrigerating work procedure, time control was at 6-48 hours.
9. gilding technology, 8. step is dried, cool down after fabric carry out gold stamping processing, gold stamping composition parts by weights
For：50-80 parts of PU resins, 3-8 parts of light-sensitive coloring agent, 0.1-0.3 parts of antioxidant, 0.2-0.05 parts of stabilizer, 100 parts of solvent.
10. stripping process, fabric of the step after 9. gold stamping is peeled off with low hyaline membrane, 10-40 ms/min of the fabric speed of service
Clock.
Beneficial benefit：
Beneficial effects of the present invention：The present invention relates to a kind of preparation technology of high collapsing high fashion dress shell fabric, the preparation work
The fabric of skill can stretch cost breadth more than 10 times, and shape style novelty, fashion, beautiful in colour, easy cleaning, meet
The requirement of liking to be beautiful of modern female；Production technology of the present invention is more complicated, it is not easy to be imitated, and fabric quality it is good, well-pressed, wear-resisting,
Quick-drying washable the advantages of.
The present invention has abandoned excessively simple method in existing production technology, solves the difficulty that existing production technology is present
Point, makes fabric structure more consolidate, further improves the fashion and novelty of overall fabric.
Embodiment
Clear, complete description is carried out to the technical scheme in the embodiment of the present invention below, it is clear that described embodiment
Only it is a part of embodiment of the present invention, rather than whole embodiments.Based on embodiments of the invention, ordinary skill people
The every other embodiment that member is obtained under the premise of creative work is not made, belongs to the scope of protection of the invention.
A kind of preparation technology of high collapsing high fashion dress shell fabric in the present embodiment, including base cloth layer, bottom cloth layer, print
Spend stratum reticulare processed, crumple gold stamping layer.The base fabric is non-woven fabrics.The bottom cloth layer is low elastic polyester filament.Described preparing printing screen layer
For seaweed slurry and dispersion fuel and its solvent.Described crumples gold stamping layer for PU resins and antioxidant and stabilizer.It is described
Base cloth layer applies environment-friendly size on the surface of base fabric.The preparing printing screen layer applies seaweed slurry in preparing printing screen layer.
Embodiment 1
A kind of preparation technology of high collapsing high fashion dress shell fabric.Specifically include following steps：
1. a kind of high collapsing high fashion dress shell fabric is through double twisting → weaving → clear water sizing → pre-setting → cash amount → dye
Color → whole latitude sizing → stamp pre-setting → upper package → stamp →, which evaporates → being rolled up on whole latitude → and crumples → baking oven → cooling →, scalds
The process of gold → cooling → stripping → clot is formed.
2. double twisting weaving process, the double twisting twist is 3200, is weaved using the right hatching of a first from left.
3. dye, the fabric after 2. step is weaved carries out dyeing processing, the part parts by weights of dyeing is：Chelating
0.5 part of agent, 1 part of bleeding agent, 1 part of dispersion fuel.
4. whole latitude setting process, the fabric after 3. step is dyed carries out whole latitude heat treatment, temperature control at 160 DEG C,
70 ms/min of the fabric speed of service, adds positive overfeeding 15, auxiliary agent is divided into proportion：Clear water 1:Softening agent 0.06：Silicone oil
0.003。
5. preparing printing screen technique, carries out preparing printing screen processing, temperature control is 110 by the fabric after step 4. whole latitude sizing
DEG C, 4 ms/min of the fabric speed of service, the part parts by weights of stamp is：5 parts of clear water, 20 parts of marine alga agent, disperse dyes 5
Part.
6. step is rolled up on whole latitude, the fabric after step 5. preparing printing screen is cut into 80 meters/volume.
7. technique is crumpled, the fabric after being rolled up in step 6. whole latitude is carried out crumpling processing, the fabric rolled up on whole latitude is crumpled
In nonwoven layer, the fabric of 20 meters/volume is stitched into acrylics filament.Temperature control is at 180 DEG C, and the fabric speed of service is controlled 0.5
M/min, 0.2g/ square metres of sizing material, thickness 0.4mm.
8. baking oven process, the fabric after 7. step is crumpled is dried, cooling treatment, and oven temperature is controlled at 40 DEG C,
Time control was at 12 hours；The refrigerating work procedure, time control was at 6 hours.
9. gilding technology, 8. step is dried, cool down after fabric carry out gold stamping processing, gold stamping composition parts by weights
For：50 parts of PU resins, 3 parts of light-sensitive coloring agent, 0.1 part of antioxidant, 0.2 part of stabilizer, 100 parts of solvent.
10. stripping process, fabric of the step after 9. gold stamping is peeled off with low hyaline membrane, 10 ms/min of the fabric speed of service.
Embodiment 2
A kind of preparation technology of high collapsing high fashion dress shell fabric.Specifically include following steps：
1. a kind of high collapsing high fashion dress shell fabric is through double twisting → weaving → clear water sizing → pre-setting → cash amount → dye
Color → whole latitude sizing → stamp pre-setting → upper package → stamp →, which evaporates → being rolled up on whole latitude → and crumples → baking oven → cooling →, scalds
The process of gold → cooling → stripping → clot is formed.
2. double twisting weaving process, the double twisting twist is 3200, is weaved using the right hatching of a first from left.
3. dye, the fabric after 2. step is weaved carries out dyeing processing, the part parts by weights of dyeing is：Chelating
1 part of agent, 1.5 parts of bleeding agent, 1.5 parts of dispersion fuel.
4. whole latitude setting process, the fabric after 3. step is dyed carries out whole latitude heat treatment, temperature control at 170 DEG C,
80 ms/min of the fabric speed of service, adds positive overfeeding 17, auxiliary agent is divided into proportion：Clear water 1:Softening agent 0.09：Silicone oil
0.003。
5. preparing printing screen technique, carries out preparing printing screen processing, temperature control is 115 by the fabric after step 4. whole latitude sizing
DEG C, 7 ms/min of the fabric speed of service, the part parts by weights of stamp is：8 parts of clear water, 30 parts of marine alga agent, disperse dyes 8
Part.
6. step is rolled up on whole latitude, the fabric after step 5. preparing printing screen is cut into 120 meters/volume.
7. technique is crumpled, the fabric after being rolled up in step 6. whole latitude is carried out crumpling processing, the fabric rolled up on whole latitude is crumpled
In nonwoven layer, the fabric of 30 meters/volume is stitched into acrylics filament.Temperature control is at 200 DEG C, and the fabric speed of service is controlled 1.5
M/min, 0.2g/ square metres of sizing material, thickness 0.4mm.
8. baking oven process, the fabric after 7. step is crumpled is dried, cooling treatment, and oven temperature is controlled at 60 DEG C,
Time control was at 24 hours；The refrigerating work procedure, time control was at 12 hours.
9. gilding technology, 8. step is dried, cool down after fabric carry out gold stamping processing, gold stamping composition parts by weights
For：60 parts of PU resins, 5 parts of light-sensitive coloring agent, 0.2 part of antioxidant, 0.4 part of stabilizer, 100 parts of solvent.
10. stripping process, fabric of the step after 9. gold stamping is peeled off with low hyaline membrane, 20 ms/min of the fabric speed of service.
Embodiment 3：
A kind of preparation technology of high collapsing high fashion dress shell fabric.Specifically include following steps：
1. a kind of high collapsing high fashion dress shell fabric is through double twisting → weaving → clear water sizing → pre-setting → cash amount → dye
Color → whole latitude sizing → stamp pre-setting → upper package → stamp →, which evaporates → being rolled up on whole latitude → and crumples → baking oven → cooling →, scalds
The process of gold → cooling → stripping → clot is formed.
2. double twisting weaving process, the double twisting twist is 3200, is weaved using the right hatching of a first from left.
3. dye, the fabric after 2. step is weaved carries out dyeing processing, the part parts by weights of dyeing is：Chelating
2 parts of agent, 2 parts of bleeding agent, 2 parts of dispersion fuel.
4. whole latitude setting process, the fabric after 3. step is dyed carries out whole latitude heat treatment, temperature control at 180 DEG C,
90 ms/min of the fabric speed of service, adds positive overfeeding 20, auxiliary agent is divided into proportion：Clear water 1:Softening agent 0.12：Silicone oil
0.003。
5. preparing printing screen technique, carries out preparing printing screen processing, temperature control is 120 by the fabric after step 4. whole latitude sizing
DEG C, 10 ms/min of the fabric speed of service, the part parts by weights of stamp is：10 parts of clear water, 40 parts of marine alga agent disperses dye
10 parts of material.
6. step is rolled up on whole latitude, the fabric after step 5. preparing printing screen is cut into 160 meters/volume.
7. technique is crumpled, the fabric after being rolled up in step 6. whole latitude is carried out crumpling processing, the fabric rolled up on whole latitude is crumpled
In nonwoven layer, the fabric of 40 meters/volume is stitched into acrylics filament.Temperature control at 220 DEG C, the control of the fabric speed of service 3 meters/
Minute, 0.2g/ square metres of sizing material, thickness 0.4mm.
8. baking oven process, the fabric after 7. step is crumpled is dried, cooling treatment, and oven temperature is controlled at 80 DEG C,
Time control was at 72 hours；The refrigerating work procedure, time control was at 48 hours.
9. gilding technology, 8. step is dried, cool down after fabric carry out gold stamping processing, gold stamping composition parts by weights
For：80 parts of PU resins, 8 parts of light-sensitive coloring agent, 0.3 part of antioxidant, 0.05 part of stabilizer, 100 parts of solvent.
10. stripping process, fabric of the step after 9. gold stamping is peeled off with low hyaline membrane, 40 ms/min of the fabric speed of service.
The present invention relates to a kind of preparation technology of high collapsing high fashion dress shell fabric, the fabric of the preparation technology can be by
Cost breadth stretches more than 10 times, and shape style novelty, fashion, beautiful in colour, easy cleaning, meets liking to be beautiful for modern female
It is required that；Production technology of the present invention is more complicated, it is not easy to be imitated, and fabric quality it is good, well-pressed, wear-resisting, it is quick-drying washable the advantages of.
The present invention has abandoned excessively simple method in existing production technology, solves the difficulty that existing production technology is present
Point, makes fabric structure more consolidate, further improves the fashion and novelty of overall fabric.
Embodiments of the invention are the foregoing is only, are not thereby limited the scope of the invention, it is every to utilize this hair
Equivalent structure or equivalent flow conversion that bright description is made, or directly or indirectly it is used in other related technology necks
Domain, is included within the scope of the present invention.
Claims (8)
1. a kind of preparation technology of high collapsing high fashion dress shell fabric, it is characterised in that the technological process of production by entering as follows
OK：Double twisting → weaving → clear water sizing → pre-setting → cash amount → dyeing → whole latitude sizing → stamp pre-setting → upper package → print
Spend → evaporate → rolling up → to crumple → baking oven → cooling → boiling hot film/gold stamping → cooling → stripping → clot on whole latitude.
2. the preparation technology of a kind of high collapsing high fashion dress shell fabric according to claim 1, it is characterised in that described
Double twisting weaving process, its double twisting twist is 3200, is weaved using the right hatching of a first from left.
3. the preparation technology of a kind of high collapsing high fashion dress shell fabric according to claim 1, it is characterised in that described
The part parts by weights of dyeing is：0.5-2 parts of chelating agent, 1-2 parts of bleeding agent, 1-2 parts of dispersion fuel.
4. the preparation technology of a kind of high collapsing high fashion dress shell fabric according to claim 1, it is characterised in that described
Whole latitude heat treatment, temperature control is at 160 DEG C -180 DEG C, and 70-90 ms/min of the fabric speed of service adds positive overfeeding 15-20
Individual, auxiliary agent is divided into proportion：Clear water 1:Softening agent 0.06-0.12：Silicone oil 0.003.
5. the preparation technology of a kind of high collapsing high fashion dress shell fabric according to claim 1, it is characterised in that described
Preparing printing screen processing, temperature control is at 110 DEG C -120 DEG C, and 4-10 ms/min of the fabric speed of service, the part of stamp presses weight
Amount is divided into：5-10 parts of clear water, 20-40 parts of marine alga agent, 5-10 parts of disperse dyes.
6. the preparation technology of a kind of high collapsing high fashion dress shell fabric according to claim 5, it is characterised in that by face
Material is cut into 80-160 meters/volume, then with 1：10 ratio is crumpled in nonwoven layer.
7. a kind of preparation technology of high collapsing high fashion dress shell fabric according to claim 6, it is characterised by described
Processing is crumpled, the fabric rolled up on whole latitude is crumpled in nonwoven layer, the fabric of 20-40 meters/volume, temperature control are stitched into acrylics filament
System is at 180-220 DEG C, and the fabric speed of service is controlled in 0.5-3 ms/min, 0.2g/ square metres of sizing material, thickness 0.4mm.
8. a kind of preparation technology of high collapsing high fashion dress shell fabric according to claim 1, is characterised by described and scalds
Gold composition parts by weights be：50-80 parts of PU resins, 3-8 parts of light-sensitive coloring agent, 0.1-0.3 parts of antioxidant, stabilizer 0.2-
0.05 part, 100 parts of solvent.