CN107214192A - High temperature wire drawing and the hybrid system of hot rolling - Google Patents
High temperature wire drawing and the hybrid system of hot rolling Download PDFInfo
- Publication number
- CN107214192A CN107214192A CN201710308577.2A CN201710308577A CN107214192A CN 107214192 A CN107214192 A CN 107214192A CN 201710308577 A CN201710308577 A CN 201710308577A CN 107214192 A CN107214192 A CN 107214192A
- Authority
- CN
- China
- Prior art keywords
- wire drawing
- high temperature
- sheet material
- hybrid system
- hot rolling
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses the hybrid system of a kind of high temperature wire drawing and hot rolling, including：High temperature furnace, its side is provided with raw material plate entrance, and opposite side is exported provided with production board, and carbon monoxide protection zone is provided with the high temperature furnace in the production board exit；Conveying cylinder；Wire drawing machine, it is in the high temperature furnace, at the carbon monoxide protection zone, and correspondence raw material plate to be processed is set, and Wire Drawing is carried out for the surface to the raw material plate；Milling train, it is set close to the high temperature furnace, positioned at the production board exit；And control system, it is used for the work to the high temperature furnace, carbon monoxide protection zone flame, the conveying cylinder, the wire drawing machine and the milling train and is controlled.The hybrid system of high temperature wire drawing and hot rolling of the present invention, is largely avoided being oxidized for metal surface to be composite.Composite effect is good, so as to can also solve the problems, such as the method hot rolling for the metal that material property and molten point differ greatly well.
Description
Technical field
The present invention relates to metal processing sectors, the hybrid system of more particularly to a kind of high temperature wire drawing and hot rolling.
Background technology
At present, in metal hot rolling recombination process both domestic and external, a major issue of facing, is exactly that metal material exists
It is easily oxidized in preheating process, and the oxidized time can become more and more faster with the continuous rise of temperature.
If pre-heating temperature is too low, the oxidized possibility in metal surface can be than relatively low, but metal surface molecule is difficult to be activated, firmly
Spend greatly, so the technical requirements of method hot rolling can not be met, therefore, composite effect is also bad, does not also reach metallurgical binding
Effect；Conversely, after temperature increases, oxidation on metal surface will be accelerated, while also can be the surface portion of wire drawing oxygen quickly
Melt, form that hardness is very big, barrier very strong oxide layer, therefore, recombination rate also can be lower, or even can not be combined, particularly
The metal differed greatly for material property and molten point, compound difficulty will be bigger, and such as titanium-aluminium-stainless steel is compound, copper-
Molybdenum-copper is compound etc..
The information for being disclosed in the background section is merely intended to understanding of the increase to the general background of the present invention, without answering
When the prior art for being considered as recognizing or implying the information structure in any form well known to persons skilled in the art.
The content of the invention
It is an object of the invention to provide the hybrid system of a kind of high temperature wire drawing and hot rolling, so as to overcome material property and molten
Put the metal hot rolling that differs greatly and be combined difficult shortcoming.
To achieve the above object, the invention provides the hybrid system of a kind of high temperature wire drawing and hot rolling, including：High temperature furnace,
Its side is provided with raw material plate entrance, and opposite side is exported provided with production board, is provided with the high temperature furnace in the production board exit
Carbon monoxide protection zone；Conveying cylinder, it is in the high temperature furnace, and for conveying, raw material plate to be processed is to the high temperature furnace
Production board exit；Wire drawing machine, it is in the high temperature furnace, at the carbon monoxide protection zone, and correspondence is to be processed
Raw material plate set, for carrying out Wire Drawing to the surface of the raw material plate；Milling train, it is set close to the high temperature furnace, position
In the production board exit；And control system, its be used for the high temperature furnace, carbon monoxide protection zone flame,
The conveying cylinder, the work of the wire drawing machine and the milling train are controlled.
Preferably, in above-mentioned technical proposal, in the state of the hybrid system is processed at least two blocks block sheet materials,
The hybrid system also includes vacuum plate sucking, and the vacuum plate sucking is correspondingly arranged above and below every block of block sheet material.
Preferably, in above-mentioned technical proposal, the vacuum plate sucking includes plate face, and the plate face is provided with multiple equally distributed
Suction hole, multiple suction holes are connected with air inlet.
Preferably, in above-mentioned technical proposal, wire drawing posting is provided with the carbon monoxide protection zone.
Preferably, in above-mentioned technical proposal, the method for processing at least two blocks block sheet materials using the hybrid system is as follows,
Comprise the following steps：
(1) cleaning and processing on surface are carried out to the block sheet material of raw material, surface and oil contaminant is removed, is grouped and is put into institute in order
State in high temperature furnace and preheated；
(2) promoted successively in the high temperature furnace, reach carbon monoxide protection zone；
(3) the block sheet material that compound tense is located at middle level is adsorbed upwards by the vacuum plate sucking, to the block board in middle level
The lower surface wire drawing of material, removes removing oxide layer, then is adsorbed the block sheet material positioned at middle level downwards by vacuum plate sucking, to middle level block
The upper surface of shape sheet material, the lower surface of the block sheet material in the upper surface of the block sheet material of lower floor and upper strata carry out wire drawing；
(4) after the completion of wire drawing, carbon monoxide flame protection is carried out to the surface of wire drawing, by the vacuum plate sucking by middle level
The block sheet material of block sheet material and upper strata is sequentially overlapped on the block sheet material of lower floor, and block sheet material is pushed down by the vacuum plate sucking,
Send into and the vacuum plate sucking is unclamped after the milling train, complete method hot rolling process.
Preferably, in above-mentioned technical proposal, in the state of the hybrid system is processed to two pieces of banding sheet materials, it is combined
When set the wire drawing machine positioned at the lower surface of upper strata banding material plate, be provided with institute positioned at the upper surface of lower floor's banding material plate
State wire drawing machine.
Preferably, in above-mentioned technical proposal, in the state of the hybrid system is processed at least three pieces banding sheet materials,
The lower surface that compound tense is located at upper strata banding material plate sets the wire drawing machine, positioned at the upper surface of middle level banding material plate and
Lower surface is located at the wire drawing machine, and the wire drawing machine is provided with positioned at the upper surface of lower floor's banding material plate.
Preferably, in above-mentioned technical proposal, the conveying cylinder is set for layering, and every layer of conveying cylinder is located at described
The lower surface of banding sheet material.
Compared with prior art, the present invention has the advantages that：
(1) hybrid system of high temperature wire drawing and hot rolling of the present invention, makes metal in preheating process, at high operating temperatures can
Quick wire drawing and the overlapping of plate of material of composite surface are quickly completed, and sends into milling train rapidly, is answered so as to quickly complete hot rolling
The overall process of conjunction, is largely avoided being oxidized for metal surface to be composite.Composite effect is good, so that also can be well
Solve the problems, such as the method hot rolling for the metal that material property and molten point differ greatly.And microcomputer control system is used, can be with
The work of control high temperature furnace, carbon monoxide protection zone flame, conveying cylinder, wire drawing machine and milling train well.
(2) hybrid system of high temperature wire drawing and hot rolling of the present invention, it is possible to achieve the method hot rolling of three plates or multilayer composite sheet
Production line balance, greatly improve product quality and productivity effect.
Brief description of the drawings
Fig. 1 is the structural representation of the hybrid system of the high temperature wire drawing of embodiments in accordance with the present invention 1 and hot rolling.
Fig. 2 be the high temperature wire drawing of embodiments in accordance with the present invention 1 and hot rolling hybrid system in vacuum plate sucking structural representation.
Fig. 3 is the structural representation of the hybrid system of the high temperature wire drawing of embodiments in accordance with the present invention 2 and hot rolling.
Fig. 4 be embodiments in accordance with the present invention 1 and the high temperature wire drawing of embodiment 2 and hot rolling hybrid system in wire drawing machine knot
Structure schematic diagram.
Embodiment
Below in conjunction with the accompanying drawings, the embodiment to the present invention is described in detail, it is to be understood that the guarantor of the present invention
Shield scope is not limited by embodiment.
Explicitly indicated that unless otherwise other, otherwise in entire disclosure and claims, term " comprising " or its change
Change such as "comprising" or " including " etc. and will be understood to comprise stated element or part, and do not exclude other members
Part or other parts.
Embodiment 1
As shown in Figure 1, Figure 2 and Figure 4, according to a kind of high temperature wire drawing of the specific embodiment of the invention and the compound system of hot rolling
System, is processed compound using the hybrid system to block sheet material.The hybrid system of the wire drawing of the present embodiment high temperature and hot rolling includes
High temperature furnace 1, conveying cylinder 2, wire drawing machine 3, vacuum plate sucking 4, milling train 5 and control system (not shown).The right side of high temperature furnace 1 is provided with original
Flitch entrance 11, left side is provided with production board outlet 12, and high temperature furnace 1 is provided with heating system, and the heating system is used to enter high temperature furnace 1
Row heating.Export and be provided with the high temperature furnace at 12 at carbon monoxide protection zone 6, carbon monoxide protection zone 6 close to the production board
Provided with wire drawing posting (not shown).Carbon monoxide protection zone 6 is provided with carbon monoxide flame control system, carbon monoxide flame control
System processed is used for the size for controlling flame.Conveying cylinder 2, positioned at the bottom of high temperature furnace 1, is treated in high temperature furnace 1 for conveying
At the raw material plate of processing to the production board outlet 12 of high temperature furnace.Conveying cylinder 2 is provided with roller induction system, for controlling conveying rolling
The rotation of cylinder 2, the transporting velocity of control material.Wire drawing machine 3 is in the high temperature furnace 1, positioned at the carbon monoxide protection zone 6
Place, correspondence raw material plate to be processed is set, and Wire Drawing is carried out for the surface to the raw material plate.Wire drawing machine 3 can level shifting
It is dynamic and moving up and down to be located in high temperature furnace 1.Wire drawing machine 3 is provided with Control system of drawing, and the Control system of drawing is used to control
The work of wire drawing machine processed.In drawing process is carried out, sheet material to be processed is adsorbed using vacuum plate sucking 4, so as to the work of wire drawing machine 3
Make.Vacuum plate sucking 4 is correspondingly arranged above and below every block of block sheet material that (underlying vacuum plate sucking does not show in figure
Go out).Vacuum plate sucking 4 is connected with vacuum plate sucking control system, and the work of vacuum plate sucking 4 is controlled by vacuum plate sucking control system.
Vacuum plate sucking 4 includes plate face 41, and the plate face is provided with multiple equally distributed suction holes 42, the multiple suction holes and air inlet
43 connections.After wire drawing comes out, block sheet material is overlapped by vacuum plate sucking 4, exports, enters by production board outlet 12
Enter milling train 5.Milling train 5 is set close to the high temperature furnace 1, at production board outlet 12.Milling train 5 controls system provided with milling train
System, the work of milling train 5 is controlled by mill control system.After the completion of hot rolling, the compound of sheet material is completed.
Control system and heating system, carbon monoxide flame control system, roller induction system, Control system of drawing,
Vacuum plate sucking control system and mill control system data cube computation, by control system to the high temperature furnace, the carbon monoxide
Protection zone flame, the conveying cylinder, the wire drawing machine, the work of vacuum plate sucking and the milling train are controlled.
Using the hybrid system of above-mentioned high temperature wire drawing and hot rolling to three blocks of block sheet materials (i.e. tri- blocks of sheet materials of A, B, C, three blocks of gold
Category sheet material) it is processed, the method for processing is as follows, comprises the following steps：
(1) pre-composite sheet metal is cut according to certain specification first, reaches that specification is consistent, it is smooth to overlap
One group of composite board；And then the cleaning and processing on surface are carried out, surface and oil contaminant is removed, surface is carried out to the block sheet material of raw material
Cleaning and processing, remove surface and oil contaminant, be grouped and be put into the high temperature furnace and preheated in order, sheet material is pressed successively
BCA order is sent into high temperature furnace preheated side by side simultaneously；
(2) continuous cycle type is preheated：The process is that sheet metal packet to be composite is sequentially sent to enter in high temperature furnace
Row heating, and forward impelling successively is grouped, until reaching the wire drawing posting front end of carbon monoxide protection zone；
(3) surface wire drawing, the one group of sheet material (tri- blocks of plates of BCA) for treating wire drawing, is exactly put into it by vacuum plate sucking
Corresponding (tri- blocks of plates of BCA) wire drawing inframe；Wire drawing machine is started, wire drawing first is carried out to B plates, method is：First B is held with suction disc
Plate, then to B plates carry out lower surface carry out surface wire drawing, remove removing oxide layer, after the completion of give lower suction disc B plates again, then again to B
The upper surface of plate carries out surface wire drawing, while upper surface and A plates lower surface also to C plates carries out quick wire drawing, removes to be composite
The oxide layer on surface.After the completion of wire drawing, carbon monoxide flame protection should be carried out to the surface of wire drawing rapidly；
(4) after the completion of wire drawing, on the premise of carbon monoxide flame is protected, B plates and A plates are carried out soon with vacuum plate sucking
Speed is superimposed on C plates, in centrally located C plate wire drawing postings, is then clamped by middle vacuum plate sucking up and down, fast
Unclamp after speed feeding milling train and rapidly, complete the overall process of method hot rolling.
Sent forward by the induction system in high temperature furnace, then another group of follow-up sheet material, and be sequentially completed the above (3) and
(4) all steps and program, it is possible to realize the production line balance of the method hot rolling of three plates or multilayer composite sheet, greatly improve
Product quality and productivity effect.
Embodiment 2
As shown in Figure 3 and Figure 4, a kind of hybrid system of high temperature wire drawing and hot rolling, using the present embodiment hybrid system to three
Block banding sheet material 7 (i.e. tri- blocks of sheet materials of D, E, F) is processed compound.Three pieces of banding sheet materials 7 present middle lower floor's distribution.The present embodiment
The hybrid system of high temperature wire drawing and hot rolling includes high temperature furnace 8, conveying cylinder 9, wire drawing machine 10, milling train 13 and control system, and (figure is not
Show).
The right side of high temperature furnace 8 is provided with raw material plate entrance 81, and left side is provided with production board outlet 82, and high temperature furnace 8 is provided with heating system,
The heating system is used to heat high temperature furnace 8.Exported close to the production board in the high temperature furnace at 82 and be provided with carbon monoxide
Protection zone 14.Carbon monoxide protection zone 12 is provided with carbon monoxide flame control system, and carbon monoxide flame control system is used to control
The size of flame processed.Conveying cylinder 9 is in high temperature furnace 8, and every layer of banding sheet material 7 is correspondingly provided with one group of conveying cylinder 9, conveying rolling
Cylinder 9 is set in high temperature furnace 8 in multilayer, located at the lower surface of banding sheet material 7.Conveying cylinder 9 is used to convey banding to be processed
Sheet material 7 is delivered at the production board of high temperature furnace outlet 82.Conveying cylinder 9 is provided with roller induction system, for controlling conveying cylinder 9
Rotation, the transporting velocity of control material.Wire drawing machine 10 is in the high temperature furnace 8, positioned at the carbon monoxide protection zone 14
Place, correspondence raw material plate to be processed is set, and the lower surface that compound tense is located at upper strata banding material plate sets wire drawing machine, positioned at middle level
The upper and lower surface of banding material plate is located at wire drawing machine, and wire drawing is provided with positioned at the upper surface of lower floor's banding material plate
Machine.Wire Drawing is carried out to the surface of the raw material plate by wire drawing machine.Entering wire drawing machine 10 provided with Control system of drawing, should
Control system of drawing is used for the work for controlling wire drawing machine.After wire drawing comes out, exported by production board outlet 82, into rolling
Machine 13.Milling train 13 is set close to the high temperature furnace 8, at production board outlet 82.Milling train 13 is provided with mill control system,
The work of milling train 13 is controlled by mill control system.After the completion of hot rolling, the compound of sheet material is completed.
Control system and heating system, carbon monoxide flame control system, roller induction system, Control system of drawing and
Mill control system data cube computation, by control system to the high temperature furnace, carbon monoxide protection zone flame, described defeated
Roller, the work of the wire drawing machine and the milling train is sent to be controlled.
Three pieces of banding sheet materials are processed using the hybrid system of above-mentioned high temperature wire drawing and hot rolling, the method for processing is such as
Under, comprise the following steps：
(1) same width is selected, is entered respectively from the series cylinder of upper, middle and lower three, and the surface of continous way is carried out in porch
Cleaning oil pollution, while being continuously introduced into high temperature furnace；
(2) when sheet material is reached at carbon monoxide protection zone, lower surface, middle level using wire drawing machine to upper strata band-like plate D materials
Banding sheet material E upper and lower surface, lower floor banding sheet material F upper surface carry out continuous wire drawing, remove surface to be composite
Oxide layer, and the interval position progress carbon monoxide flame protection between wire drawing machine and milling train, while continuously entering milling train, directly
Connect the continuous process for completing hot rolling.
It is foregoing to the present invention specific illustrative embodiment description be in order to illustrate and illustration purpose.These descriptions
It is not wishing to limit the invention to disclosed precise forms, and it will be apparent that according to above-mentioned teaching, can be much changed
And change.The purpose of selecting and describing the exemplary embodiment is that explaining that the certain principles and its reality of the present invention should
With so that those skilled in the art can realize and using the present invention a variety of exemplaries and
A variety of selections and change.The scope of the present invention is intended to be limited by claims and its equivalents.
Claims (8)
1. a kind of high temperature wire drawing and the hybrid system of hot rolling, it is characterised in that including：
High temperature furnace, its side is provided with raw material plate entrance, and opposite side is exported provided with production board, the height close to the production board exit
Carbon monoxide protection zone is provided with warm stove；
Conveying cylinder, it is in the high temperature furnace, and for conveying, the production board of raw material plate to be processed to the high temperature furnace goes out
At mouthful；
Wire drawing machine, it is in the high temperature furnace, at the carbon monoxide protection zone, and correspondence raw material plate to be processed is set
Put, Wire Drawing is carried out for the surface to the raw material plate；
Milling train, it is set close to the high temperature furnace, positioned at the production board exit；And
Control system, it is used for the high temperature furnace, carbon monoxide protection zone flame, the conveying cylinder, the drawing
The work of silk machine and the milling train is controlled.
2. high temperature wire drawing according to claim 1 and the hybrid system of hot rolling, it is characterised in that the hybrid system is to extremely
In the state of few two blocks of block sheet material is processed, the hybrid system also includes vacuum plate sucking, and the vacuum plate sucking correspondence is set
Above and below every block of block sheet material.
3. high temperature wire drawing according to claim 2 and the hybrid system of hot rolling, it is characterised in that the vacuum plate sucking includes
Plate face, the plate face is provided with multiple equally distributed suction holes, and multiple suction holes are connected with air inlet.
4. high temperature wire drawing according to claim 2 and the hybrid system of hot rolling, it is characterised in that the carbon monoxide protection
Wire drawing posting is provided with area.
5. high temperature wire drawing according to claim 2 and the hybrid system of hot rolling, it is characterised in that use the hybrid system
The method of the block sheet material of at least two blocks of processing is as follows, comprises the following steps：
(1) cleaning and processing on surface are carried out to the block sheet material of raw material, surface and oil contaminant is removed, is grouped and is put into the height in order
Preheated in warm stove；
(2) promoted successively in the high temperature furnace, reach carbon monoxide protection zone；
(3) the block sheet material that compound tense is located at middle level is adsorbed upwards by the vacuum plate sucking, to the block sheet material in middle level
Lower surface wire drawing, removes removing oxide layer, then is adsorbed the block sheet material positioned at middle level downwards by vacuum plate sucking, to middle level block board
The upper surface of material, the lower surface of the block sheet material in the upper surface of the block sheet material of lower floor and upper strata carry out wire drawing；
(4) after the completion of wire drawing, carbon monoxide flame protection is carried out to the surface of wire drawing, it is by the vacuum plate sucking that middle level is block
The block sheet material of sheet material and upper strata is sequentially overlapped on the block sheet material of lower floor, is pushed down block sheet material by the vacuum plate sucking, is sent into
The vacuum plate sucking is unclamped after the milling train, method hot rolling process is completed.
6. high temperature wire drawing according to claim 1 and the hybrid system of hot rolling, it is characterised in that the hybrid system is to two
In the state of block banding sheet material is processed, the lower surface that compound tense is located at upper strata banding material plate sets the wire drawing machine, position
The wire drawing machine is provided with the upper surface of lower floor's banding material plate.
7. high temperature wire drawing according to claim 1 and the hybrid system of hot rolling, it is characterised in that the hybrid system is to extremely
In the state of few three pieces of banding sheet materials are processed, the lower surface that compound tense is located at upper strata banding material plate sets the wire drawing
Machine, the upper and lower surface positioned at middle level banding material plate is located at the wire drawing machine, positioned at lower floor's banding material plate
Upper surface is provided with the wire drawing machine.
8. the hybrid system of the high temperature wire drawing and hot rolling according to claim 6 or 7, it is characterised in that the conveying cylinder
Set for layering, every layer of conveying cylinder is located at the lower surface of the banding sheet material.