CN107189626A - A kind of epoxide resin protective paint coating - Google Patents
A kind of epoxide resin protective paint coating Download PDFInfo
- Publication number
- CN107189626A CN107189626A CN201710445172.3A CN201710445172A CN107189626A CN 107189626 A CN107189626 A CN 107189626A CN 201710445172 A CN201710445172 A CN 201710445172A CN 107189626 A CN107189626 A CN 107189626A
- Authority
- CN
- China
- Prior art keywords
- resin protective
- epoxide resin
- micro mist
- protective paint
- paint coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of epoxide resin protective paint coating, the invention belongs to chemical technology field, its formula is characterized in:It is made up of the cyclohexanone solution of epoxy resin, IPD, phenol, toluene, calcium oxide micro mist, ultra-fine oxidized microcrystalline wax micro mist, pigment, hexenyl bis-stearamides, montmorillonite.The finished product of the present invention can apply to steel anti-corrosion, wood preservation erosion, concrete carbonization preventing and ship, bridge, the surface of all kinds of outdoor indoor hardware equipment and terrace, be the coating that its work is protected.The present invention has micron order and the dual coarse structure of nanoscale simultaneously, so just having the super-hydrophobic self-cleaning function of lotus leaf effect, after product using the present invention, the surface long term of object need not manually be cleaned and returned newly from overcoating brush, save substantial amounts of manpower and materials, also do not corroded simultaneously by wind and rain, the service life of 3 times of ordinary epoxy resin protective paints, strictly a kind of service life is permanent and super-hydrophobic epoxide resin protective paint coating of excellent performance.
Description
Technical field
The invention belongs to chemical field, the present invention relates to a kind of resin protective paint coating, and in particular to be a kind of epoxy
Resin protective paint coating.
Background technology
Epoxide resin protective paint coating is that one kind can apply to steel anti-corrosion, wood preservation erosion, concrete carbonization preventing, ship
The protective coating of the anti-planktonic organism in bottom, terrace and the structure such as deck is anti-wear.But epoxide resin protective lacquer coat is not dredged
Water self-cleaning function, will manually clean and be returned newly from overcoating brush in short term, service life is not long, wastes manpower and materials.
The content of invention
The purpose of the present invention is:There is provided it is a kind of there is self-cleaning function, need not manually clean for a long time and from overcoating brush return newly,
A large amount of manpower and materials can be saved, not by erosion by wind and rain, service life is permanent and super-hydrophobic epoxide resin protective paint of excellent performance
Coating.
To achieve the above object, the technical solution adopted in the present invention is a kind of epoxide resin protective paint coating, and it is formulated
It is characterized in:By the cyclohexanone solution of epoxy resin, IPD, phenol, toluene, calcium oxide micro mist (0.5um~
0.8um particle diameters), ultra-fine oxidized microcrystalline wax micro mist (13nm~75nm particle diameters), pigment, hexenyl bis-stearamides, montmorillonite group
Into.
The percentage by weight of its component is:
Beneficial effects of the present invention:The present invention is calcium oxide micro mist (0.5um~0.8um particle diameters), ultra-fine oxidation crystallite
The peptizaiton that wax micro mist (13nm~75nm particle diameters) is risen by dispersant hexenyl bis-stearamides, is highly dispersed in epoxy
In resin protective paint, distributive law more than 97%, using the present invention finished product after, paint film formation tool lotus leaf effect it is super-hydrophobic from
Clean surface, the paint film sample of multiple epoxide resin protective paints is determined with half ball, and the contact angle of its paint film sample and water exists
More than 150 °;Moreover, the observation that sample is carried out by using electron microscope, finds its surface while having micron order and nanoscale
Dual coarse structure.The present invention finished product can apply to steel anti-corrosion, wood preservation erosion, concrete carbonization preventing and ship,
The surface of bridge, all kinds of outdoor indoor hardware equipment and terrace, makes the surface of object have the super-hydrophobic self-cleaning work(of lotus leaf effect
Can, it need not can manually clean and be returned newly from overcoating brush for a long time, save substantial amounts of manpower and materials, and do not invaded by wind and rain
Erosion, the service life of 3 times of ordinary epoxy resin protective paints is that a kind of service life is permanent and super-hydrophobic epoxy of excellent performance
Resin protective paint coating.
Embodiment
The following examples are that the present invention is made further to prove, the invention is not restricted to this.
Embodiment one
A kind of epoxide resin protective paint coating, its component and weight proportion are as follows:
Embodiment two
A kind of epoxide resin protective paint coating, its component and weight proportion are as follows:
Embodiment three
A kind of epoxide resin protective paint coating, its component and weight proportion are as follows:
Finished product obtained by the three above embodiment of the present invention is respectively coated on three pieces of slides, surveyed with half ball
The contact angle of fixed these three samples and water:
1st, the contact angle of the slide sample of embodiment one and water is 150.5 °
2nd, the contact angle of the slide sample of embodiment two and water is 153.2 °
3rd, the contact angle of the slide sample of embodiment three and water is 152.1 °
The sample of three above embodiment is determined with half ball, finished product its surface wettability of the present invention is all showed
For superhydrophobic characteristic.
A kind of epoxide resin protective paint coating of the present invention, applies in western district of Guangdong, Duo Jia advertising companies has been supplied, at it
Used on the surface of outdoor large advertisement metal structure skeleton and the surface of terrace;Make to compare with common epoxide resin protective paint
Compared with, product of the invention has the super-hydrophobic self-cleaning function of lotus leaf effect, make metal structure surface and terrace surface not
By erosion by wind and rain, permanent light is such as new, saves substantial amounts of manpower and materials, product of the invention has 3 times of ordinary epoxy resins
The service life of protective paint, strictly a kind of service life is permanent and super-hydrophobic epoxide resin protective paint coating of excellent performance.
Claims (2)
1. a kind of epoxide resin protective paint coating, it is characterised in that:The percentage by weight of the formula each component is:Epoxy resin
Cyclohexanone solution 54%--80%, IPD 3%--22%, phenol 3%--24%, toluene 4%--23%, calcium oxide
Micro mist 3%--25%, ultra-fine oxidized microcrystalline wax micro mist 2%--26%, pigment 2%--22%, hexenyl bis-stearamides 2%--
24%th, montmorillonite 1%--23%.
2. a kind of epoxide resin protective paint coating according to claim 1, it is characterized in that:Calcium oxide micro mist 0.5um~
0.8um particle diameters, ultra-fine oxidized microcrystalline wax micro mist 13nm~75nm particle diameters, point risen by dispersant hexenyl bis-stearamides
Effect is dissipated, is highly dispersed in epoxide resin protective paint, distributive law is more than 97%, and using after this finished product, paint film formation has lotus
The super-hydrophobic self-cleaning surface of leaf effect, the paint film sample of multiple epoxide resin protective paints is determined with half ball, its paint film sample
Contact angle with water is more than 150 °.