CN109401390A - A kind of fast-drying type cast iron protective paint - Google Patents
A kind of fast-drying type cast iron protective paint Download PDFInfo
- Publication number
- CN109401390A CN109401390A CN201811367406.8A CN201811367406A CN109401390A CN 109401390 A CN109401390 A CN 109401390A CN 201811367406 A CN201811367406 A CN 201811367406A CN 109401390 A CN109401390 A CN 109401390A
- Authority
- CN
- China
- Prior art keywords
- parts
- fast
- powder
- cast iron
- drying type
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of fast-drying type cast iron protective paints, including styrene-acrylic emulsion, aqueous epoxy resins, tricresyl phosphate, benzyl ether, red lead powder, fine magnesium oxide micro-powder, isophorone diamine, hexenyl bis-stearamides, guar gum, Polyacrylate Emulsion and sepiolite powder.Casting can be effectively protected in the present invention, and anticorrosion effect is high, and rate of drying is fast, easy to use.
Description
Technical field
The present invention relates to a kind of fast-drying type cast iron protective paints, belong to protective paint technical field.
Background technique
The molding theoretical metal liquid condition shaping of casting be frequently referred to cast, Founding moldability technology it is with a long history.Early in 5000
Many years ago, our ancestors can cast red metal and bronze.Casting is most widely used metal liquid moulding process.It
It is to be poured into liquid metal in casting mold type chamber, after its cooled and solidified, the method that obtains the blank or part of certain shapes.Casting
Part technological flexibility is big, wide adaptability.The utilization of present casting is more and more wider, this is just higher and higher to the requirement of cast iron, some
Cast iron use environment is severe, and these cast irons just need special protective paint.Traditional defense paint protection effect is weak, has a single function.
Summary of the invention
To overcome above-mentioned deficiency, the object of the invention provides a kind of fast-drying type cast iron protective paint.
The solution of the present invention is as follows: a kind of fast-drying type cast iron protective paint is made of following raw material: benzene according to parts by weight
60 ~ 90 parts of acrylic emulsion, 30 ~ 70 parts of aqueous epoxy resins, 2.5 ~ 5 parts of tricresyl phosphate, 2 ~ 4 parts of benzyl ether, red lead powder 2 ~ 5
Part, 1 ~ 2 part of fine magnesium oxide micro-powder, 5 ~ 10 parts of isophorone diamine, 5 ~ 10 parts of hexenyl bis-stearamides, 3 ~ 8 parts of guar gum, poly- third
2 ~ 6 parts and 1 ~ 3 part of sepiolite powder of olefin(e) acid ester copolymer emulsion.
Further, it is made of following raw material according to parts by weight: 60 parts of styrene-acrylic emulsion, 3 parts of aqueous epoxy resins, tricresyl phosphate
2.5 parts of toluene ester, 2 parts of benzyl ether, 3 parts of red lead powder, 1 part of fine magnesium oxide micro-powder, 5 parts of isophorone diamine, hexenyl stearic bicine diester
5 parts of amine, 3 parts of guar gum, 2 parts of Polyacrylate Emulsion and 1 part of sepiolite powder.
Further, it is made of following raw material: being made of following raw material according to parts by weight according to parts by weight: styrene-acrylic emulsion
90 parts, 70 parts of aqueous epoxy resins, 5 parts of tricresyl phosphate, 4 parts of benzyl ether, 5 parts of red lead powder, 2 parts of fine magnesium oxide micro-powder, different Buddhist
10 parts of that ketone diamines, 10 parts of hexenyl bis-stearamides, 8 parts of guar gum, 6 parts of Polyacrylate Emulsion and sepiolite powder 3
Part.
Further, it is made of following raw material: being made of following raw material according to parts by weight according to parts by weight: styrene-acrylic emulsion
75 parts, 50 parts of aqueous epoxy resins, 3.5 parts of tricresyl phosphate, 3 parts of benzyl ether, 3.5 parts of red lead powder, fine magnesium oxide micro-powder 1.5
Part, 8 parts of isophorone diamine, 8 parts of hexenyl bis-stearamides, 6 parts of guar gum, 4 parts of Polyacrylate Emulsion and Hai Pao
2 parts of mountain flour.
Beneficial effects of the present invention: casting can be effectively protected in the present invention, and anticorrosion effect is high, and rate of drying is fast, makes
With conveniently.
Specific embodiment
Embodiment 1
A kind of fast-drying type cast iron protective paint, is made of following raw material according to parts by weight: 60 parts of styrene-acrylic emulsion, water-base epoxy tree
3 parts of rouge, 2.5 parts of tricresyl phosphate, 2 parts of benzyl ether, 3 parts of red lead powder, 1 part of fine magnesium oxide micro-powder, 5 parts of isophorone diamine, oneself
5 parts of alkenyl bis-stearamides, 3 parts of guar gum, 2 parts of Polyacrylate Emulsion and 1 part of sepiolite powder.
Embodiment 2
A kind of fast-drying type cast iron protective paint, is made of following raw material according to parts by weight: according to parts by weight by following raw material
Composition: 90 parts of styrene-acrylic emulsion, 70 parts of aqueous epoxy resins, 5 parts of tricresyl phosphate, 4 parts of benzyl ether, 5 parts of red lead powder, magnesia
2 parts of micro mist, 10 parts of isophorone diamine, 10 parts of hexenyl bis-stearamides, 8 parts of guar gum, 6 parts of Polyacrylate Emulsion
With 3 parts of sepiolite powder.
Embodiment 3
A kind of fast-drying type cast iron protective paint, is made of following raw material according to parts by weight: according to parts by weight by following raw material
Composition: 75 parts of styrene-acrylic emulsion, 50 parts of aqueous epoxy resins, 3.5 parts of tricresyl phosphate, 3 parts of benzyl ether, 3.5 parts of red lead powder, oxygen
Change 1.5 parts of magnesium micro mist, 8 parts of isophorone diamine, 8 parts of hexenyl bis-stearamides, 6 parts of guar gum, polyacrylate copolymerization cream
4 parts and 2 parts of sepiolite powder of liquid.
Although the detailed description and description of the specific embodiments of the present invention are given above, it should be noted that
We can carry out various equivalent changes and modification to above embodiment according to the concept of the present invention, and generated function is made
It, should all be within protection scope of the present invention when with the spirit still covered without departing from specification.
Claims (4)
1. a kind of fast-drying type cast iron protective paint, which is characterized in that be made of following raw material according to parts by weight: styrene-acrylic emulsion 60
~ 90 parts, 30 ~ 70 parts of aqueous epoxy resins, 2.5 ~ 5 parts of tricresyl phosphate, 2 ~ 4 parts of benzyl ether, 2 ~ 5 parts of red lead powder, magnesia
1 ~ 2 part of micro mist, 5 ~ 10 parts of isophorone diamine, 5 ~ 10 parts of hexenyl bis-stearamides, 3 ~ 8 parts of guar gum, polyacrylate are total
2 ~ 6 parts and 1 ~ 3 part of sepiolite powder of poly- lotion.
2. a kind of fast-drying type cast iron protective paint according to claim 1, which is characterized in that according to parts by weight by following original
Material composition: 60 parts of styrene-acrylic emulsion, 3 parts of aqueous epoxy resins, 2.5 parts of tricresyl phosphate, 2 parts of benzyl ether, 3 parts of red lead powder, oxygen
Change 1 part of magnesium micro mist, 5 parts of isophorone diamine, 5 parts of hexenyl bis-stearamides, 3 parts of guar gum, Polyacrylate Emulsion 2
Part and 1 part of sepiolite powder.
3. a kind of fast-drying type cast iron protective paint according to claim 1, which is characterized in that according to parts by weight by following original
Material composition: 90 parts of styrene-acrylic emulsion, 70 parts of aqueous epoxy resins, 5 parts of tricresyl phosphate, 4 parts of benzyl ether, 5 parts of red lead powder, oxidation
2 parts of magnesium micro mist, 10 parts of isophorone diamine, 10 parts of hexenyl bis-stearamides, 8 parts of guar gum, Polyacrylate Emulsion 6
Part and 3 parts of sepiolite powder.
4. a kind of fast-drying type cast iron protective paint according to claim 1, which is characterized in that according to parts by weight by following original
Material composition: 75 parts of styrene-acrylic emulsion, 50 parts of aqueous epoxy resins, 3.5 parts of tricresyl phosphate, 3 parts of benzyl ether, 3.5 parts of red lead powder,
1.5 parts of fine magnesium oxide micro-powder, 8 parts of isophorone diamine, 8 parts of hexenyl bis-stearamides, 6 parts of guar gum, polyacrylate copolymerization
4 parts and 2 parts of sepiolite powder of lotion.