CN107189600A - A kind of outdoor heat insulation and heat control coating used for textiles and preparation method thereof - Google Patents
A kind of outdoor heat insulation and heat control coating used for textiles and preparation method thereof Download PDFInfo
- Publication number
- CN107189600A CN107189600A CN201710396828.7A CN201710396828A CN107189600A CN 107189600 A CN107189600 A CN 107189600A CN 201710396828 A CN201710396828 A CN 201710396828A CN 107189600 A CN107189600 A CN 107189600A
- Authority
- CN
- China
- Prior art keywords
- parts
- heat insulation
- control coating
- heat control
- coating used
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides outdoor heat insulation and heat control coating used for textiles of one kind and preparation method thereof, the raw material of the coating includes:Sodium metasilicate, ethylene glycol, nano alumina sol, water, filler, surfactant, polyacrylate coatings glue, dispersant, levelling agent, defoamer, graphene, cellulose;Its preparation method is first to mix sodium metasilicate, ethylene glycol, nano alumina sol, water, and grinding obtains mixed liquor A;Filler, surfactant and polyacrylate coatings glue are mixed again, ultrasonic disperse obtains mixed liquid B;Then mixed liquor A, mixed liquid B, dispersant, levelling agent, defoamer are mixed, grinding is produced.The heat insulation and heat control coating of the present invention has good heat insulation and heat control resultant effect, and the fabric after processing has good uvioresistant, water repellent, tensile strength and tearing brute force.
Description
Technical field
The invention belongs to outdoor field of fabric producing technology, and in particular to a kind of outdoor heat insulation and heat control coating used for textiles and its
Preparation method.
Background technology
Object can gather amount of heat under the prolonged exposure of sunlight, cause its surface and inner side temperature to raise, especially
In hot summer and high temperature area, the production and life given people brings inconvenience and harm.With global warming trend
Aggravation, all over the world again and again report there is historical high temperature;Depletion of the ozone layer, causes global dermatosis patient to increase, especially
It is the Southern Hemisphere and China In Guangdong Province.Outdoor production that these environmental problems give people, life bring inconvenience.It is same with this
When, as the improvement of people's living standards, the implementation with the trend that goes back to nature, people increasingly like participating in outdoor activities.
Therefore in the market requires related product occur, to solve this problem or weaken the harm that this phenomenon is brought.One is full
The basic production of sufficient people, living needs are also adapted to present outdoor environment in addition, make it have antiultraviolet, waterproof, logical
Gas moisture-inhibiting, the specific function such as inflaming-retarding antifouling and shading reflection.
To solve this problem, the method that people design a variety of protection heat radiations, wherein conventional one kind is that infrared heat is anti-
Penetrate coating, so-called infrared thermal reflective coating refer to be coated on body surface, have to the infrared band in radiation high reflectance, from
And suppress Coated Surface Temperature and rise and while reduce the coating of covering internal temperature.At present, it is domestic to be applied for heat insulation and heat control
The development of material, produce mainly for fields such as building trade, industrial equipment and aviations, it is few be applied to outdoor textile every
Heat drop thermo-paint.
The content of the invention
The technical problem of solution:It is an object of the invention to provide the outdoor heat insulation and heat control coating used for textiles of one kind and its preparation
Method, gained heat insulation and heat control coating has good heat insulation and heat control resultant effect.
Technical scheme:A kind of outdoor heat insulation and heat control coating used for textiles, raw material includes in parts by weight:Sodium metasilicate 0.8-
1.5 parts, 0.4-1.2 parts of ethylene glycol, 0.3-0.9 parts of nano alumina sol, 5-10 parts of water, 2-6 parts of filler, surfactant
0.8-1.5 parts, 1-3 parts of polyacrylate coatings glue, 0.5-1 parts of dispersant, 0.3-0.7 parts of levelling agent, defoamer 0.2-0.7
Part, 0.2-0.5 parts of graphene, 0.4-0.8 parts of cellulose.
Further, the surfactant is neopelex.
Further, the filler is the mass ratioes such as titanium dioxide, glass microballoon, reflecting microbead, bentonite and calcium carbonate
The mixture of composition.
Further, the cellulose is hydroxymethyl cellulose.
The preparation method of above-mentioned outdoor heat insulation and heat control coating used for textiles, comprises the following steps:
Step 1, sodium metasilicate, ethylene glycol, nano alumina sol, water are mixed, grinding obtains mixed liquor A;
Step 2, filler, surfactant and polyacrylate coatings glue are mixed, ultrasonic disperse obtains mixed liquid B;
Step 3, step 1 gained mixed liquor A, step 2 gained mixed liquid B, dispersant, levelling agent, defoamer are mixed, ground
Mill, is produced.
Further, the power of ultrasonic disperse is 300-500W in step 2.
Beneficial effect:The heat insulation and heat control coating of the present invention has good heat insulation and heat control resultant effect, the fabric after processing
With good uvioresistant, water repellent, tensile strength and tearing brute force.
Embodiment
Embodiment 1
A kind of outdoor heat insulation and heat control coating used for textiles, raw material includes in parts by weight:0.8 part of sodium metasilicate, ethylene glycol 0.4
It is part, 0.3 part of nano alumina sol, 5 parts of water, 2 parts of filler, 0.8 part of surfactant, 1 part of polyacrylate coatings glue, scattered
0.5 part of agent, 0.3 part of levelling agent, 0.2 part of defoamer, 0.2 part of graphene, 0.4 part of cellulose.
Wherein, the surfactant is neopelex, and the filler is titanium dioxide, glass microballoon, anti-
The mixture of the mass ratioes such as light microballon, bentonite and calcium carbonate composition, the cellulose is hydroxymethyl cellulose.
The preparation method of above-mentioned outdoor heat insulation and heat control coating used for textiles, comprises the following steps:
Step 1, sodium metasilicate, ethylene glycol, nano alumina sol, water are mixed, grinding obtains mixed liquor A;
Step 2, filler, surfactant and polyacrylate coatings glue are mixed, ultrasonic disperse obtains mixed liquid B;
Step 3, step 1 gained mixed liquor A, step 2 gained mixed liquid B, dispersant, levelling agent, defoamer are mixed, ground
Mill, is produced.
Wherein, the power of ultrasonic disperse is 300-500W in step 2.
Gained coating is coated on cloth, dried, after testing:The temperature of cloth is after irradiation 120min at 42 DEG C
24.35 DEG C, the transmitance that UPF values are 375, UVA is 3.5%, and water pressure resistance is 62375Pa.
Embodiment 2
A kind of outdoor heat insulation and heat control coating used for textiles, raw material includes in parts by weight:1.1 parts of sodium metasilicate, ethylene glycol 0.6
Part, 0.4 part of nano alumina sol, 7 parts of water, 3 parts of filler, 1.1 parts of surfactant, polyacrylate coatings glue 1.7 part, point
0.6 part of powder, 0.5 part of levelling agent, 0.3 part of defoamer, 0.3 part of graphene, 0.5 part of cellulose.
Wherein, the surfactant is neopelex, and the filler is titanium dioxide, glass microballoon, anti-
The mixture of the mass ratioes such as light microballon, bentonite and calcium carbonate composition, the cellulose is hydroxymethyl cellulose.
The preparation method of above-mentioned outdoor heat insulation and heat control coating used for textiles, comprises the following steps:
Step 1, sodium metasilicate, ethylene glycol, nano alumina sol, water are mixed, grinding obtains mixed liquor A;
Step 2, filler, surfactant and polyacrylate coatings glue are mixed, ultrasonic disperse obtains mixed liquid B;
Step 3, step 1 gained mixed liquor A, step 2 gained mixed liquid B, dispersant, levelling agent, defoamer are mixed, ground
Mill, is produced.
Wherein, the power of ultrasonic disperse is 300-500W in step 2.
Gained coating is coated on cloth, dried, after testing:The temperature of cloth is after irradiation 120min at 42 DEG C
26.17 DEG C, the transmitance that UPF values are 417, UVA is 4.1%, and water pressure resistance is 61758Pa.
Embodiment 3
A kind of outdoor heat insulation and heat control coating used for textiles, raw material includes in parts by weight:1.3 parts of sodium metasilicate, ethylene glycol 0.9
It is part, 0.7 part of nano alumina sol, 8 parts of water, 6 parts of filler, 1.3 parts of surfactant, 2 parts of polyacrylate coatings glue, scattered
0.8 part of agent, 0.6 part of levelling agent, 0.5 part of defoamer, 0.4 part of graphene, 0.6 part of cellulose.
Wherein, the surfactant is neopelex, and the filler is titanium dioxide, glass microballoon, anti-
The mixture of the mass ratioes such as light microballon, bentonite and calcium carbonate composition, the cellulose is hydroxymethyl cellulose.
The preparation method of above-mentioned outdoor heat insulation and heat control coating used for textiles, comprises the following steps:
Step 1, sodium metasilicate, ethylene glycol, nano alumina sol, water are mixed, grinding obtains mixed liquor A;
Step 2, filler, surfactant and polyacrylate coatings glue are mixed, ultrasonic disperse obtains mixed liquid B;
Step 3, step 1 gained mixed liquor A, step 2 gained mixed liquid B, dispersant, levelling agent, defoamer are mixed, ground
Mill, is produced.
Wherein, the power of ultrasonic disperse is 300-500W in step 2.
Gained coating is coated on cloth, dried, after testing:The temperature of cloth is after irradiation 120min at 42 DEG C
25.67 DEG C, the transmitance that UPF values are 450, UVA is 3.7%, and water pressure resistance is 58975Pa.
Embodiment 4
A kind of outdoor heat insulation and heat control coating used for textiles, raw material includes in parts by weight:1.5 parts of sodium metasilicate, ethylene glycol 1.2
Part, 0.9 part of nano alumina sol, 10 parts of water, 6 parts of filler, 1.5 parts of surfactant, polyacrylate coatings glue 3 part, point
1 part of powder, 0.7 part of levelling agent, 0.7 part of defoamer, 0.5 part of graphene, 0.8 part of cellulose.
Wherein, the surfactant is neopelex, and the filler is titanium dioxide, glass microballoon, anti-
The mixture of the mass ratioes such as light microballon, bentonite and calcium carbonate composition, the cellulose is hydroxymethyl cellulose.
The preparation method of above-mentioned outdoor heat insulation and heat control coating used for textiles, comprises the following steps:
Step 1, sodium metasilicate, ethylene glycol, nano alumina sol, water are mixed, grinding obtains mixed liquor A;
Step 2, filler, surfactant and polyacrylate coatings glue are mixed, ultrasonic disperse obtains mixed liquid B;
Step 3, step 1 gained mixed liquor A, step 2 gained mixed liquid B, dispersant, levelling agent, defoamer are mixed, ground
Mill, is produced.
Wherein, the power of ultrasonic disperse is 300-500W in step 2.
Gained coating is coated on cloth, dried, after testing:The temperature of cloth is after irradiation 120min at 42 DEG C
26.15 DEG C, the transmitance that UPF values are 385, UVA is 4.2%, and water pressure resistance is 63870Pa.
Claims (6)
1. a kind of outdoor heat insulation and heat control coating used for textiles, it is characterised in that:Raw material includes in parts by weight:Sodium metasilicate 0.8-
1.5 parts, 0.4-1.2 parts of ethylene glycol, 0.3-0.9 parts of nano alumina sol, 5-10 parts of water, 2-6 parts of filler, surfactant
0.8-1.5 parts, 1-3 parts of polyacrylate coatings glue, 0.5-1 parts of dispersant, 0.3-0.7 parts of levelling agent, defoamer 0.2-0.7
Part, 0.2-0.5 parts of graphene, 0.4-0.8 parts of cellulose.
2. outdoor heat insulation and heat control coating used for textiles according to claim 1, it is characterised in that:The surfactant is
Neopelex.
3. outdoor heat insulation and heat control coating used for textiles according to claim 1, it is characterised in that:The filler is titanium dioxide
The mixture of the mass ratioes such as titanium, glass microballoon, reflecting microbead, bentonite and calcium carbonate composition.
4. outdoor heat insulation and heat control coating used for textiles according to claim 1, it is characterised in that:The cellulose is hydroxyl first
Base cellulose.
5. the preparation method of the outdoor heat insulation and heat control coating used for textiles described in claim 1, it is characterised in that:Including following step
Suddenly:
Step 1, sodium metasilicate, ethylene glycol, nano alumina sol, water are mixed, grinding obtains mixed liquor A;
Step 2, filler, surfactant and polyacrylate coatings glue are mixed, ultrasonic disperse obtains mixed liquid B;
Step 3, step 1 gained mixed liquor A, step 2 gained mixed liquid B, dispersant, levelling agent, defoamer are mixed, grinding,
Produce.
6. the preparation method of outdoor heat insulation and heat control coating used for textiles according to claim 5, it is characterised in that:Step 2
The power of middle ultrasonic disperse is 300-500W.