CN107187262A - A kind of carving technique of aluminium alloy tracery - Google Patents
A kind of carving technique of aluminium alloy tracery Download PDFInfo
- Publication number
- CN107187262A CN107187262A CN201710647127.6A CN201710647127A CN107187262A CN 107187262 A CN107187262 A CN 107187262A CN 201710647127 A CN201710647127 A CN 201710647127A CN 107187262 A CN107187262 A CN 107187262A
- Authority
- CN
- China
- Prior art keywords
- aluminium alloy
- drying
- tracery
- time
- carving
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of carving technique of aluminium alloy tracery, comprise the following steps：（1）Aluminium alloy plate is first subjected to first time drying and processing after prerinse, cleaning,（2）The oxidation of aluminium alloy plate,（3）Computer stamp air brushing, using copper powder, the style in computer is printed in aluminium alloy plate face,（4）Punching carving processing, the style and speed of computer control carving, processing is punched out on aluminium alloy plate, style is retained,（5）Arc and polishing are rolled,（6）First time japanning,（7）Second of japanning, through the above way, the carving technique of aluminium alloy tracery of the present invention makes simple, success rate height, environmental protection does not have pressure to environment, the aluminium alloy window being made realizes the diversity of aluminum alloy doors and windows moulding, both the sturdy and durable performance of aluminum alloy doors and windows had been met, the monotonicity of aluminum alloy doors and windows moulding is overcome again, can meet the use demand of different consumers.
Description
Technical field
The present invention relates to aluminium alloy tracery field, more particularly to a kind of carving technique of aluminium alloy tracery.
Background technology
Aluminium alloy tracery enjoys user to favor due to lightweight, sturdy and durable, good airproof performance, still, aluminium alloy tracery
Moulding is simple, there is no decorative element, and solid wood door and window various shapes, elegant in appearance, because material is heavy, to handware
It is required that higher, humidity and temperature difference are too big, also easily make its mouldy deformation, therefore, in finishing, in aluminium alloy tracery performance
It is better than solid wood door and window, it is but attractive in appearance without solid wood door and window in appearance.
The content of the invention
The present invention solves the technical problem of provide a kind of carving for making the high aluminium alloy tracery of simple, success rate
Technique.
In order to solve the above technical problems, the present invention provides a kind of carving technique of aluminium alloy tracery, comprise the following steps：
（1）Aluminium alloy plate is first subjected to first time drying and processing after prerinse, cleaning,
（2）The oxidation of aluminium alloy plate, oxidization time is 20-30 minutes,
（3）Computer stamp air brushing, using copper powder, the style in computer is printed in aluminium alloy plate face,
（4）Punching carving processing, the style and speed of computer control carving, processing is punched out on aluminium alloy plate, is retained
Style,
（5）Arc and polishing are rolled, polishing tool is changed and rolling arc and grinding process is carried out to style,
（6）Then first time japanning, first priming carries out second of drying and processing,
（7）Then second of japanning, brush finish paint carries out third time drying and processing.
In a preferred embodiment of the present invention, the first time drying temperature is 30-40 degrees Celsius, and drying time is
10-15 minutes.
In a preferred embodiment of the present invention, the thickness of the aluminium alloy plate is 1.2-2.8mm.
In a preferred embodiment of the present invention, second of drying temperature is 85-105 degrees Celsius, and drying time is
25-45 minutes, oxygen volume ratio was 30-35% during drying.
In a preferred embodiment of the present invention, the third time drying temperature is 50-75 degrees Celsius, and drying time is
50-70 minutes, oxygen volume ratio was 25-30% during drying.
The beneficial effects of the invention are as follows：It is high, environmentally friendly right that the carving technique of aluminium alloy tracery of the present invention makes simple, success rate
Environment does not have pressure, and the aluminium alloy window being made realizes the diversity of aluminum alloy doors and windows moulding, both meets aluminium alloy
The sturdy and durable performance of door and window, overcomes the monotonicity of aluminum alloy doors and windows moulding again, can meet the use need of different consumers
Ask.
Embodiment
The technical scheme in the embodiment of the present invention will be clearly and completely described below, it is clear that described implementation
Example is only a part of embodiment of the present invention, rather than whole embodiments.Based on the embodiment in the present invention, this area is common
All other embodiment that technical staff is obtained under the premise of creative work is not made, belongs to the model that the present invention is protected
Enclose.
The embodiment of the present invention includes：A kind of carving technique of aluminium alloy tracery, comprises the following steps：
（1）Aluminium alloy plate is first subjected to first time drying and processing after prerinse, cleaning,
（2）The oxidation of aluminium alloy plate, oxidization time is 20-30 minutes,
（3）Computer stamp air brushing, using copper powder, the style in computer is printed in aluminium alloy plate face,
（4）Punching carving processing, the style and speed of computer control carving, processing is punched out on aluminium alloy plate, is retained
Style,
（5）Arc and polishing are rolled, polishing tool is changed and rolling arc and grinding process is carried out to style,
（6）Then first time japanning, first priming carries out second of drying and processing,
（7）Then second of japanning, brush finish paint carries out third time drying and processing.
The aluminium alloy tracery being made by this carving technique, realizes the diversity of aluminum alloy doors and windows moulding, and
Carving outer surface can resist the erosion of outside climatic for a long time, and durable had both met the durability of aluminum alloy doors and windows
Can, the monotonicity of aluminum alloy doors and windows moulding is overcome again, can meet the use demand of different consumers.
In addition, the first time drying temperature is 30-40 degrees Celsius, drying time is 10-15 minutes, for the first time drying master
Will in order to allow aluminium alloy surface keep cleaning and a certain degree of oxidation.
In addition, the thickness of the aluminium alloy plate is 1.2-2.8mm.
In addition, second of drying temperature is 85-105 degrees Celsius, drying time is 25-45 minutes, oxygen during drying
Volume ratio is 30-35%.Second of drying can form the paint film of densification on the surface of aluminium alloy, so as to ensure that aluminium alloy tracery exists
It will not be etched during use.
In addition, the third time drying temperature is 50-75 degrees Celsius, drying time is 50-70 minutes, carrier of oxygen during drying
Product is than being 25-30%.Third time drying to adhere to uniformity between paint and aluminium alloy plate.
Prior art is different from, the carving technique of aluminium alloy tracery of the present invention makes simple, success rate height, environmental protection to environment
There is no pressure, the aluminium alloy window being made realizes the diversity of aluminum alloy doors and windows moulding, both meets aluminum alloy doors and windows
Sturdy and durable performance, the monotonicity of aluminum alloy doors and windows moulding is overcome again, the use demand of different consumers can be met.
Embodiments of the invention are the foregoing is only, are not intended to limit the scope of the invention, it is every to utilize this hair
Equivalent structure or equivalent flow conversion that bright description is made, or directly or indirectly it is used in other related technology necks
Domain, is included within the scope of the present invention.
Claims (5)
1. a kind of carving technique of aluminium alloy tracery, it is characterised in that comprise the following steps：
（1）Aluminium alloy plate is first subjected to first time drying and processing after prerinse, cleaning,
（2）The oxidation of aluminium alloy plate, oxidization time is 20-30 minutes,
（3）Computer stamp air brushing, using copper powder, the style in computer is printed in aluminium alloy plate face,
（4）Punching carving processing, the style and speed of computer control carving, processing is punched out on aluminium alloy plate, is retained
Style,
（5）Arc and polishing are rolled, polishing tool is changed and rolling arc and grinding process is carried out to style,
（6）Then first time japanning, first priming carries out second of drying and processing,
（7）Then second of japanning, brush finish paint carries out third time drying and processing.
2. the carving technique of aluminium alloy tracery according to claim 1, it is characterised in that the first time drying temperature is
30-40 degrees Celsius, drying time is 10-15 minutes.
3. the carving technique of aluminium alloy tracery according to claim 1, it is characterised in that the thickness of the aluminium alloy plate is
1.2-2.8mm。
4. the carving technique of aluminium alloy tracery according to claim 1, it is characterised in that second of drying temperature be
85-105 degrees Celsius, drying time is 25-45 minutes, and oxygen volume ratio is 30-35% during drying.
5. the carving technique of aluminium alloy tracery according to claim 1, it is characterised in that the third time drying temperature is
50-75 degrees Celsius, drying time is 50-70 minutes, and oxygen volume ratio is 25-30% during drying.