CN104085245A - Baroque retro-style color-coated metal plate with stereoscopic incised lines and coating method thereof - Google Patents
Baroque retro-style color-coated metal plate with stereoscopic incised lines and coating method thereof Download PDFInfo
- Publication number
- CN104085245A CN104085245A CN201410328495.0A CN201410328495A CN104085245A CN 104085245 A CN104085245 A CN 104085245A CN 201410328495 A CN201410328495 A CN 201410328495A CN 104085245 A CN104085245 A CN 104085245A
- Authority
- CN
- China
- Prior art keywords
- coating
- decorative
- overwrought
- metal plate
- solid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to a baroque retro-style color-coated metal plate with stereoscopic incised lines and a coating method thereof, belongs to the production field of a color-coated metal plate and particularly relates to the baroque retro-style color-coated metal plate with a similar stereoscopic incised line effect. According to the coating method, a normal metal plate belt is taken as a base material based on a traditional coating process, a modified specific functional coating system is utilized to carry out design remolding and process adjustment on the coating system so as to produce the baroque retro-style color-coated metal plate, surface patterns and composition lines of the color-coated metal plate look like incised or etched ones, and the color-coated metal plate has spatial mismatch feel and obvious hand feel and texture.
Description
Technical field:
The invention belongs to color coating metallic plate production field, relate to the color coating metallic plate of the overwrought line effect of similar solid of the pseudo-classic style of a kind of Ba Luoke of having.Be specifically related to a kind of on traditional coating process basis, take common metal strip as base material, use modification dedicated functionality coating system, by the design improvement of finishing system and technique being adjusted, being produced, there is the pseudo-classic style of Ba Luoke, there is spatial offset and obviously color coating metallic plate and the coating process thereof of the stereo decoration line of feel texture as surface detail and the similar engraving of composition lines or etching.
Background technology:
At present, for color coating metal plate product, by finishing system being carried out to the identical design improvement of similar common printed mask-making technology, adopt common roll coat enamel, can produce the color coating metallic plate that decorative cover has various plane decorative patterns (being that decorative cover is smooth), as the color coating metallic plates such as imitative wood grain, bag and stamp of common plane decorative pattern.But owing to being subject to rigidly adhering to of traditional mask-making technology, coating process and the raw and auxiliary material that uses, the color coating metal plate product of this plane decorative pattern, decorative effect is stiff flat, the artistic charm and the spiritual tension force that lack exaggeration, texture, spatial offset and pseudo-classic vicissitudes, be difficult to meet all trades and professions different product, different designs, different user to decoration requirement, particularly ancient building, the old and new church, artistic decoration and design and other archaized decoration and American-European style house ornamentation etc. that this type of color coating metal plate product is constantly promoted.Therefore, American-European and market, Central Asia and West Asia calls the color coating metal plate product of the overwrought line effect of similar solid with the pseudo-classic style of Ba Luoke to emerge as early as possible very early strongly, and urgent call had also been sent to this series products in recent years in domestic market.But there is no at present, can supply this type of color coating metal plate product of architectural engineering, product exterior and interior packing, design and Art Design practical application to occur also there is no related process and technology introduction.
Summary of the invention:
Main purpose of the present invention is to provide a kind of overwrought line color coating of the solid with the pseudo-classic style of Ba Luoke metallic plate that has three-dimensional decorative effect.
The overwrought line color coating of a solid metallic plate with the pseudo-classic style of Ba Luoke, comprises metal plate and belt base material and the decorative coveringn that is attached to this substrate surface, and described decorative coveringn is the special decorative effect with the overwrought line of similar solid of the pseudo-classic style of Ba Luoke.
Decorative coveringn is by primary colours coating and be attached to and on primary coat primary color plane, protrude from this plane decorative pattern spaced apart or colo(u)r streak forms.
Described primary colours coating covered metal plate band base material, its film thickness is 5 μ m~30 μ m, and apparent smooth.
The height that described decorative pattern or colo(u)r streak protrude from primary colours painting layer plane is 3~50 μ m.
Different decorative patterns or colo(u)r streak height equate or are unequal.
Described decorative coveringn is distributed in the single or double of metal plate and belt base material.
The color coating metallic plate that this has the overwrought line decorative effect of solid of the pseudo-classic style of Ba Luoke, comprises smooth metal plate and belt base material and the decorative coveringn that is attached to this base material single or double; This decorative coveringn consists of primary colours coat side and decorative pattern (or composition lines), and the two is baking paint curing molding.Primary colours coat side is smooth, and decorative pattern and composition lines are attached to the effect that primary colours coating plane forms similar embossment.
Another object of the present invention is to provide the production method of the overwrought line color coating of the solid metallic plate of the pseudo-classic style of a kind of described Ba Luoke.
The production method of the overwrought line color coating of the solid metallic plate of the pseudo-classic style of Ba Luoke of the present invention, finishing system based on traditional, on metal plate and belt base material, according to design effect, prepare functional three-dimensional pattern application roller and auxiliary process system and install or be attached on finishing system, in conjunction with modification dedicated functionality coating, carrying out the application of three-dimensional overwrought line.
This production method comprises that processing installation function three-dimensional pattern application roller and auxiliary process system, blowing, cleaning, epithelium, primary colours primary coat, primary coat baking, primary coat are cooling, three-dimensional pattern application, flower are coated with baking, flower is coated with cooling, rewinding operation.
Described functional three-dimensional pattern application roller roller surface is with recessed decorative pattern or composition lines; According to decorative effect, design, while preparing functional three-dimensional pattern application roller and auxiliary process system, the decorative pattern of three-dimensional pattern application roller or colo(u)r streak width are slightly larger than decorative effect design 2~5 μ m of application finished product, decorative pattern or colo(u)r streak height are slightly larger than decorative effect design 3~10 μ m of application finished product, decorative pattern or colo(u)r streak spacing dimension and design deviation≤50 μ m.
In the modification dedicated functionality coating using, each component is (by quality percentage composition): resin 17%~20%, mill base 65%~70%, cenosphere 3%~20%, auxiliary agent 1%~5% and solvent 3%~7%.
The present invention is on traditional coating process basis, provide a kind of and take common metal strip as base material, use modification dedicated functionality coating system, by designing and preparing to install additional to have, make modification dedicated functionality coating coat by design decorative pattern and composition lines the finishing system that primary colours are coated with layer plane and produce anaglyph, be enough to realize the coating process of the color coating metallic plate of producing the overwrought line decorative effect of solid with the pseudo-classic style of Ba Luoke.
The color coating metallic plate that the present invention produces, by adopting modification dedicated functionality coating system as the special coating of decorative pattern and composition lines, solved common roll coat enamel and no matter adopted what technique, be all difficult to realize decorative pattern and composition colo(u)r streak by plane roller coat and protrude from primary colours and be coated with the difficult problem that layer plane produces anaglyph; Pass through technological transformation, in finishing system, designing and preparing to install additional to have makes modification dedicated functionality coating coat primary colours painting layer plane the protruding straight roll painting roller of standing on primary colours painting layer plane by design decorative pattern and composition lines, finally at coating primary colours coating surface, form in addition and a kind ofly there is composition function and protrude from again decorative pattern and the colo(u)r streak that primary colours are coated with layer plane simultaneously, thereby on coating decoration face, obtain the special decorative effect that is similar to engraving or patterned etch and colo(u)r streak of real match volume.Because its decorative pattern and composition colo(u)r streak spatial altitude that protrudes from primary colours painting layer plane only has 3~50 μ m, so, when both having solved application and secondary operations and producing, a difficult problem for rolling and the industrialization high-speed production that unreels, can prolong molded with other materials Compound Machining or bending again; Both can be separately for veneer, decorating and use (as color steel veneer, aluminum curtain walls veneer, house ornamentation smallpox veneer, engineering smallpox veneer, electrical equipment, car and boat, advertisement, door and window, defend kitchen furniture, product exterior and interior packing and technological design, design and other form purposes veneer etc.), can be that composite board decorated is used (as color-steel composite board, composited aluminum and plastic decking, aluminium zinc composite plate, aluminum-steel composite board, aluminium-wood composite board, polyurethane foam composite plate and other composite plate etc.) with other Material cladding again.In its decorative art, the functional and good manufacturability of uniqueness in the pseudo-classic style of Ba Luoke of uniqueness and engineering, is worth the extensive concern of the aspects such as domestic and international different industries, different application field, different market and even artistic creation, image design and expects earnestly.
Accompanying drawing explanation:
Figure 1A is the formation schematic diagram (overlooking) of the color coating metallic plate of the present invention's overwrought line decorative effect of solid with the pseudo-classic style of Ba Luoke;
Figure 1B is the formation schematic diagram (section) of the color coating metallic plate of the present invention's overwrought line decorative effect of solid with the pseudo-classic style of Ba Luoke;
Fig. 2 A is that the present invention's functional three-dimensional pattern application roller used forms schematic diagram (solid);
Fig. 2 B is that the present invention's functional three-dimensional pattern application roller used forms schematic diagram (section);
Fig. 3 is the coating process flow chart of the color coating metal plate product of the present invention's overwrought line decorative effect of solid with the pseudo-classic style of Ba Luoke.
Fig. 4 is the part photo in kind of the color coating metal plate product of the present invention's overwrought line decorative effect of solid with the pseudo-classic style of Ba Luoke.
The specific embodiment:
The present invention is mainly color coating metallic plate and the coating process thereof of the overwrought line decorative effect of solid with the pseudo-classic style of Ba Luoke.
The color coating metallic plate that the present invention produces, by adopting modification dedicated functionality coating system as the special coating of decorative pattern and composition lines, solved common roll coat enamel and no matter adopted what technique, be all difficult to realize decorative pattern and the protruding difficult problem of standing on primary colours painting layer plane of composition colo(u)r streak by plane roller coat; Pass through technological transformation, in finishing system, designing and preparing to install additional to have makes modification dedicated functionality coating coat by design decorative pattern and composition lines the application roller that primary colours are coated with layer plane and protrude this plane function, finally on coating primary colours surface, form in addition a kind of composition function that has, spatially protrude from again decorative pattern and colo(u)r streak that primary colours are coated with layer plane, thereby obtain the special decorative effect that is similar to engraving or patterned etch and colo(u)r streak with the pseudo-classic style match volume of Ba Luoke simultaneously on coating decoration face.
Shown in Figure 1A and Figure 1B, show that the present invention has the color coating aluminium (part) of the overwrought line decorative effect of solid of the pseudo-classic style of Ba Luoke, it comprises: metal base 20, can be aluminium base, form is common metal coiled material or sheet material; At the single or double of aluminium base 20, whole face is attached with primary colours coating 30, and this primary colours coating 30 has design or the needed primary colours of order; On the thickness direction of metal base 20, the thickness of primary colours coating 30 in 5 μ m~30 μ m according to market demand adjustment, but integral body reaches unanimity, apparent smooth, and primary colours coating 30 meets 0 grade of cross-hatching (comprising dry type, wet type and boiling water boiling) with the ply adhesion of metal base 20; In primary colours coating 30 planes, decorative pattern colo(u)r streak or the composition colo(u)r streak 40 of being attached with spaced apart, the color of this decorative pattern colo(u)r streak or composition colo(u)r streak and distribution meet design or order requirements, and decorative pattern or composition colo(u)r streak 40 protrude from primary colours coating 30 planes, its protrusion height needs within the scope of 3~50 μ m, to adjust according to design and order.
The coating process flow process of using in the present invention, in the product painting technique traditional, increases three-dimensional pattern coating process and forms.Three-dimensional pattern coating process need be prepared and install to have makes modification dedicated functionality coating coat equably by design decorative pattern and composition lines the straight roll painting roller (hereinafter to be referred as " functional three-dimensional pattern application roller " or " roller ") that primary colours are coated with layer plane and protruding vertical function, and is that important document forms finishing system by this roller and auxiliary process system.The preparation of functional three-dimensional pattern application roller need be according to the design of order, by being coated on common coating roller surface after cloudy carving technology plate-making, form roller, shown in Figure 2, roller 21 surfaces are with recessed decorative pattern or composition lines 22, in concrete application, the decorative pattern that roller is recessed on or composition lines 22 can be attached with modification dedicated functionality coating, during primary colours coating 30 plane contact on roller 21 and metal base, by the paint spraying in recessed lines 22 to corresponding decorative pattern colo(u)r streak or the composition colo(u)r streak 40 of primary colours coating 30 formation.
In the present invention, coating process flow process, referring to Fig. 3, comprises following operation: blowing 1, clean 2, epithelium 3, primary colours primary coat 4, primary coat baking 5, primary coat are cooling 6, the preparation of functional three-dimensional pattern finishing system and installation and debugging 7, three-dimensional pattern application 8, flower are coated with baking 9, flower is coated with cooling 10, rolling 11.By above combination, form the coating process using in the present invention on roller coating production line.All the other various production lines and techniques thereof all can slightly adjust on above basis.This technique is suitable for producing the application of the overwrought line color coating of the solid product of the pseudo-classic style of Ba Luoke on all metal plate and belt materials.
Modified function coating in the present invention, comprise resin, mill base, cenosphere (Cenosphere), auxiliary agent, solvent etc., each component can be carried out assembly by following quality percentage composition: resin 17%~20%, mill base 65%~70%, cenosphere 3%~20%, auxiliary agent 1%~5%, solvent 3%~7%.
Here, coating composition is all purchased.Wherein: resin can be selected the variety classeses such as PE, PVDF, AC; Mill base can be selected from the shades of colour of fluorine carbon or the shades of colour of polyester; Cenosphere (Cenosphere), is the nonmetal multifunctional material of a kind of lightweight, and main component is SiO2 and Al2O3, diameter is between 0.01-400 micron, and outward appearance is greyish white or grey, loose, spherical, good fluidity, hollow, there is hard shell, can in paint, coating, apply; Auxiliary agent can be selected from wetting dispersing agent, levelling agent, defoamer, adhesion promoter, delustering agent, curing agent etc., and solvent can be selected ester class: butyl acetate, ethyl acetate, amyl acetate; Ether alcohol class: ethylene glycol monobutyl ether; Ketone: acetone, cyclohexanone etc.
Concrete, the color coating aluminium that utilizes this coating process to carry out the overwrought line decorative effect of solid of the pseudo-classic style of Ba Luoke is produced, and is in existing paint line, to improve formation, comprises operation shown in following table 1:
Table 1: coating process flow process
Wherein, operation three-dimensional pattern application 8 is used functional three-dimensional pattern application roller to carry out.Functional three-dimensional pattern application roller designing requirement and parameter are in Table 2:
Table 2: functional three-dimensional pattern application roller designing requirement and parameter
The functional three-dimensional pattern application roller preparing is replaced to the common application roller of original production line, utilize modification dedicated functionality coating (see above and state) to carry out three-dimensional pattern application operation by operation 8.
Example:
Produce the color coating aluminium of decorative effect as shown in Figure 4, with reference to above-mentioned production stage, employing table 3 technological parameter is produced, wherein in three-dimensional pattern application 8 operations, process and installation function three-dimensional pattern application roller and auxiliary process system the decorative pattern colo(u)r streak width of three-dimensional pattern application roller and aspect ratio finished product designing requirement+5 μ m.
Table 3: production instance coating process is controlled parameter
The color coating metallic plate of this examples produce is carried out to the evaluation of index of correlation detection and effect, comprise primary colours primary coat thickness, primary coat and aluminium base ply adhesion, composition colo(u)r streak protrusion height and sensory effects etc., table 4 has provided coherent detection data:
Table 4: production instance product index detects and effect assessment
Table 4 data show, the decorative pattern and the composition colo(u)r streak spatial altitude that protrude from primary colours painting layer plane are 3~8 μ m, within the scope of 50 μ m, can not affect high-speed and continuous while utilizing this coating sheet material to carry out secondary operations production and unreel operation, can prolong molded with other materials Compound Machining or bending again; On the other hand, sense of touch and visual perception evaluate and show, the feel that its decorative pattern and composition colo(u)r streak protrude from primary color plane is obvious, and visual stitching protrudes, and root is clear, and space multistory sense is distinct, and the effect that is similar to embossment or engraving lines is true to nature.Reach designing requirement of the present invention completely, realized the decorative effect on the sense organ that the present invention pursues with anaglyphy or the sculpture art of space multistory sense.
Fig. 4 shows the floral designs of producing color coating aluminium (part) surface obtaining, can find out the decorative effect of three-dimensional overwrought line.
Claims (10)
1. the overwrought line color coating of the solid with the pseudo-classic style of a Ba Luoke metallic plate, it is characterized in that, comprise metal plate and belt base material and the decorative coveringn that is attached to this substrate surface, described decorative coveringn is the special decorative effect with the overwrought line of similar solid of the pseudo-classic style of Ba Luoke.
2. the overwrought line color coating of solid according to claim 1 metallic plate, is characterized in that, decorative coveringn is by primary colours coating and be attached to and on primary coat primary color plane, protrude from this plane decorative pattern spaced apart or colo(u)r streak forms.
3. the overwrought line color coating of solid according to claim 2 metallic plate, is characterized in that, described primary colours coating covered metal plate band base material, and its film thickness is 5 μ m~30 μ m, and apparent smooth.
4. the overwrought line color coating of solid according to claim 3 metallic plate, is characterized in that, the height that described decorative pattern or colo(u)r streak protrude from primary colours painting layer plane is 3~50 μ m.
5. the overwrought line color coating of solid according to claim 4 metallic plate, is characterized in that, different decorative patterns or colo(u)r streak height equate or be unequal.
6. according to the overwrought line color coating of the arbitrary described solid of claim 1 to 5 metallic plate, it is characterized in that, described decorative coveringn is distributed in the single or double of metal plate and belt base material.
7. the production method of the overwrought line color coating of the solid of the pseudo-classic style of the arbitrary described Ba Luoke of claim 1 to 6 metallic plate, finishing system based on traditional, it is characterized in that, on metal plate and belt base material, according to design effect, prepare functional three-dimensional pattern application roller and auxiliary process system and install or be attached on finishing system, in conjunction with modification dedicated functionality coating, carrying out the application of three-dimensional overwrought line.
8. production method according to claim 7, it is characterized in that, comprise that processing installation function three-dimensional pattern application roller and auxiliary process system, blowing, cleaning, epithelium, primary colours primary coat, primary coat baking, primary coat are cooling, three-dimensional pattern application, flower are coated with baking, flower is coated with cooling, rewinding operation.
9. production method according to claim 8, is characterized in that, described functional three-dimensional pattern application roller roller surface is with recessed decorative pattern or composition lines; According to decorative effect, design, while preparing functional three-dimensional pattern application roller and auxiliary process system, the decorative pattern of three-dimensional pattern application roller or colo(u)r streak width are slightly larger than decorative effect design 2~5 μ m of application finished product, decorative pattern or colo(u)r streak height are slightly larger than decorative effect design 3~10 μ m of application finished product, decorative pattern or colo(u)r streak spacing dimension and design deviation≤50 μ m.
10. the production method of the overwrought line color coating of the solid of the pseudo-classic style of Ba Luoke metallic plate according to claim 8, it is characterized in that, in the modification dedicated functionality coating using, each component is (by quality percentage composition): resin 17%~20%, mill base 65%~70%, cenosphere 3%~20%, auxiliary agent 1%~5% and solvent 3%~7%.