CN107162569A - A kind of composite ceramic material - Google Patents
A kind of composite ceramic material Download PDFInfo
- Publication number
- CN107162569A CN107162569A CN201710364508.3A CN201710364508A CN107162569A CN 107162569 A CN107162569 A CN 107162569A CN 201710364508 A CN201710364508 A CN 201710364508A CN 107162569 A CN107162569 A CN 107162569A
- Authority
- CN
- China
- Prior art keywords
- parts
- ceramic material
- composite
- nano
- present
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of composite ceramic material, in parts by weight, ceramic material includes:80 100 parts of kaolin, 25 45 parts of carborundum, 6 10 parts of boron nitride, 18 parts of nano zircite, 2 10 parts of glass fibre, 13 parts of carbon fiber, 59 parts of nano zirconium dioxide, 36 parts of magnesia, 24 parts of gallium oxide, 24 parts of silane coupler, 59 parts of polyethylene glycol, 58 parts of methyl triacetoxysilane.The composite of the present invention is after high temperature sintering, the characteristics of with corrosion-resistant, resistance to thermal change, hardness high, thermal shock resistance and good shock resistance, and the ceramic material also has certain absorption property, is a kind of Environment protection type ceramic material.
Description
Technical field
The present invention relates to ceramic field, and in particular to a kind of composite ceramic material.
Background technology
Traditional alumino silicate ceramic, purity is poor, and grain graininess is uneven, and typed pressure is not high, it is impossible to meet market need
Ask.With the development of ceramic fabrication technique, the performance of ceramic material is also become better and better.Ceramic material has certain porosity,
Porosity is not only able to ensure that ceramic material has special excellent properties, and can mitigate the weight of ceramic material, different
The ceramic properties that prepare of raw material it is different, how to improve the property such as mechanical property, thermal characteristics, electrical characteristics of ceramic material
Can, it is the problem of ceramic material needs further solve.
Composite ceramic material has the premium properties such as hardness is high, wearability is good, thermo-chemical stability is strong, is used in numerous
In field.
The content of the invention
It is an object of the invention to the problem above for overcoming prior art presence, there is provided a kind of composite ceramic material, this hair
Preferably, hardness is high, corrosion resistance and good for the combination property of bright ceramic material, and with preferable porosity.
To realize above-mentioned technical purpose and the technique effect, the present invention is achieved through the following technical solutions:
A kind of composite ceramic material, in parts by weight, ceramic material includes:
Preferably, composite ceramic material according to claim 1, the component of ceramic material includes:
Embodiment 3
A kind of composite ceramic material is disclosed in the present embodiment, in parts by weight, ceramic material includes:
Further comprise, the particle diameter of the nano zircite is 50-100nm.
Preferably, the particle diameter of the nano zirconium dioxide is 10-50nm.
The beneficial effects of the invention are as follows:
1. the composite of the present invention is after high temperature sintering, with corrosion-resistant, resistance to thermal change, hardness height, thermal shock resistance
With shock resistance it is good the characteristics of, and the ceramic material also have certain absorption property, be a kind of Environment protection type ceramic material.
2. the ceramic material of the present invention has good high temperature resistant, decay resistance, and its mechanical strength is higher, ceramics
Inside has uniform porosity, improves the combination property of ceramic material.
3. the present invention ceramic material be on the basis of original aluminium nitride, boron nitride, with the addition of nano zircite and
The nano-components such as nano zirconium dioxide, the nano ceramic of preparation has the Optimalities such as high rigidity, high intensity, high temperature resistant
Can, it disclosure satisfy that the manufacture processing request of ceramic material subsequently.
Described above is only the general introduction of technical solution of the present invention, in order to better understand the technological means of the present invention,
And can be practiced according to the content of specification, described in detail below with presently preferred embodiments of the present invention as after.
Embodiment
The technical scheme in the embodiment of the present invention will be clearly and completely described below, it is clear that described implementation
Example only a part of embodiment of the invention, rather than whole embodiments.Based on the embodiment in the present invention, this area is common
The every other embodiment that technical staff is obtained under the premise of creative work is not made, belongs to the model that the present invention is protected
Enclose.
Embodiment 1
A kind of composite ceramic material is disclosed in the present embodiment, in parts by weight, ceramic material includes:
Embodiment 2
A kind of composite ceramic material is disclosed in the present embodiment, the component of ceramic material includes:
Embodiment 3
Present embodiment discloses a kind of composite ceramic material, in parts by weight, ceramic material includes:
Further, the particle diameter of the nano zircite is 50-100nm.
Further, the particle diameter of the nano zirconium dioxide is 10-50nm.
Composite in above-described embodiment is after high temperature sintering, with corrosion-resistant, resistance to thermal change, hardness height, anti-thermal shock
The characteristics of performance and good shock resistance, and the ceramic material also has certain absorption property, is a kind of environment-friendly ceramic
Material.
Ceramic material in above-described embodiment has good high temperature resistant, decay resistance, and its mechanical strength is higher,
It is ceramic internal with uniform porosity, improve the combination property of ceramic material.
Ceramic material in above-described embodiment is on the basis of original aluminium nitride, boron nitride, to the addition of nano oxidized
The nano-component such as zirconium and nano zirconium dioxide, the nano ceramic of preparation has high rigidity, high intensity, high temperature resistant etc. excellent
Performance, disclosure satisfy that the manufacture processing request of ceramic material subsequently.
The foregoing description of the disclosed embodiments, enables professional and technical personnel in the field to realize or using the present invention.
A variety of modifications to these embodiments will be apparent for those skilled in the art, as defined herein
General Principle can be realized in other embodiments without departing from the spirit or scope of the present invention.Therefore, it is of the invention
The embodiments shown herein is not intended to be limited to, and is to fit to and principles disclosed herein and features of novelty phase one
The most wide scope caused.
Claims (4)
1. a kind of composite ceramic material, it is characterised in that in parts by weight, ceramic material includes:
2. composite ceramic material according to claim 1, it is characterised in that the component of ceramic material includes:
3. composite ceramic material according to claim 1, it is characterised in that the particle diameter of the nano zircite is 50-
100nm。
4. composite ceramic material according to claim 1, it is characterised in that the particle diameter of the nano zirconium dioxide is 10-
50nm。