CN108117394A - A kind of novel fire resistant nano ceramic coat - Google Patents
A kind of novel fire resistant nano ceramic coat Download PDFInfo
- Publication number
- CN108117394A CN108117394A CN201711443305.XA CN201711443305A CN108117394A CN 108117394 A CN108117394 A CN 108117394A CN 201711443305 A CN201711443305 A CN 201711443305A CN 108117394 A CN108117394 A CN 108117394A
- Authority
- CN
- China
- Prior art keywords
- parts
- nano
- component
- fire resistant
- novel fire
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of mass fraction of novel fire resistant nano ceramic coat, component and each component be 20 30 parts of carborundum, 15 20 parts of land plaster, 5 10 parts of titanium dioxide, 8 13 parts of silicon nitride, 10 15 parts of nano aluminium oxide, 15 18 parts of nano magnesia, 5 10 parts of nano zircite, 15 parts of nano-nickel oxide.By above-mentioned technical proposal, a kind of novel fire resistant nano ceramic coat of the present invention is that existing ceramics are modified using nano material technology, by adding nano-scale particle in component, crystal grain, crystal boundary and the combination between them is made all to reach nanometer level, greatly improve intensity, the toughness of material, ensure that ceramic coating has good intensity and toughness, while have both excellent high temperature resistant, wear-resisting property.
Description
Technical field
The invention belongs to Material Field, more particularly to a kind of novel fire resistant nano ceramic coat.
Background technology
Ceramic coating, is the ceramic material for being able to receive significant attention in recent years, and traditional ceramic material has larger
Brittleness, does not utilize being processed further for ceramic material, and ceramic material is also caused to show slightly deficiency in the performance of numerous areas.Nanometer
Ceramics are the strategy approaches for solving brittleness of ceramics, and nanometer refractory ceramics powder coating material is that one kind is formed by chemically reacting
The material of refractory ceramics coating.Using nanometer technology develop nano ceramic material be using nano-powder to it is existing ceramics into
Row is modified, by toward adding in or generating nano-scale particle, whisker, chip fiber etc. in ceramics, making crystal grain, crystal boundary and they it
Between combination all reach nanometer level, increase substantially the intensity, toughness and superplasticity of material.It overcomes engineering ceramics
Many deficiencies, and the performances such as the mechanics to material, electricity, calorifics, magnetooptics have an important influence on.
The content of the invention
It is an object of the present invention to propose a kind of novel fire resistant nano ceramic coat, the technical problem to be solved is that
Good high temperature resistant, wear-resisting property are made it have, thus more suitable for practicality.
The object of the invention to solve the technical problems is realized using following technical scheme.According to proposed by the present invention
A kind of mass fraction of novel fire resistant nano ceramic coat, component and each component be 20-30 parts of carborundum, land plaster 15-
20 parts, 5-10 parts of titanium dioxide, 8-13 parts of silicon nitride, 10-15 parts of nano aluminium oxide, 15-18 parts of nano magnesia is nano oxidized
5-10 parts of zirconium, 1-5 parts of nano-nickel oxide.
The object of the invention to solve the technical problems is also further realized using following technical scheme.
The mass fraction of a kind of foregoing novel fire resistant nano ceramic coat, component and each component is carborundum 20
Part, 15 parts of land plaster, 5 parts of titanium dioxide, 8 parts of silicon nitride, 10 parts of nano aluminium oxide, 15 parts of nano magnesia, nano zircite 5
Part, 1 part of nano-nickel oxide.
The mass fraction of a kind of foregoing novel fire resistant nano ceramic coat, component and each component is carborundum 30
Part, 20 parts of land plaster, 10 parts of titanium dioxide, 13 parts of silicon nitride, 15 parts of nano aluminium oxide, 18 parts of nano magnesia are nano oxidized
10 parts of zirconium, 5 parts of nano-nickel oxide.
By above-mentioned technical proposal, a kind of novel fire resistant nano ceramic coat of the present invention is to utilize nano material technology pair
Existing ceramics are modified, and by adding nano-scale particle in component, crystal grain, crystal boundary and the combination between them are made all to reach
To nanometer level, intensity, the toughness of material are greatly improved, ensures that ceramic coating has good intensity and toughness, has both simultaneously
Excellent high temperature resistant, wear-resisting property.
Above description is only the general introduction of technical solution of the present invention, in order to better understand the technological means of the present invention,
And can be practiced according to the content of specification, and in order to allow the above and other objects, features and advantages of the present invention can
It is clearer and more comprehensible, it is special below to lift preferred embodiment detailed description.
Specific embodiment
Further to illustrate the present invention to reach the technological means and effect that predetermined goal of the invention is taken, below in conjunction with
Preferred embodiment, to according to a kind of its specific embodiment of novel fire resistant nano ceramic coat proposed by the present invention, structure, spy
Sign and its effect are described in detail as after.
Embodiment 1
A kind of mass fraction of novel fire resistant nano ceramic coat, component and each component be 20 parts of carborundum, gypsum
15 parts of powder, 5 parts of titanium dioxide, 8 parts of silicon nitride, 10 parts of nano aluminium oxide, 15 parts of nano magnesia, 5 parts of nano zircite, nanometer
1 part of nickel oxide.
Embodiment 2
A kind of mass fraction of novel fire resistant nano ceramic coat, component and each component be 30 parts of carborundum, gypsum
20 parts of powder, 10 parts of titanium dioxide, 13 parts of silicon nitride, 15 parts of nano aluminium oxide, 18 parts of nano magnesia, 10 parts of nano zircite,
5 parts of nano-nickel oxide.
The above described is only a preferred embodiment of the present invention, limitation in any form is not done to the present invention, though
So the present invention is disclosed above with preferred embodiment, however is not limited to the present invention, any to be familiar with this professional technology people
Member, without departing from the scope of the present invention, when the technology contents using the disclosure above make a little change or modification
For the equivalent embodiment of equivalent variations, as long as being the content without departing from technical solution of the present invention, technical spirit according to the invention
To any simple modification, equivalent change and modification made for any of the above embodiments, in the range of still falling within technical solution of the present invention.
Claims (3)
1. a kind of novel fire resistant nano ceramic coat, it is characterised in that:The mass fraction of its component and each component is carborundum
20-30 parts, 15-20 parts of land plaster, 5-10 parts of titanium dioxide, 8-13 parts of silicon nitride, 10-15 parts of nano aluminium oxide is nano oxidized
15-18 parts of magnesium, 5-10 parts of nano zircite, 1-5 parts of nano-nickel oxide.
2. a kind of novel fire resistant nano ceramic coat according to claim 1, it is characterised in that:Its component and each component
Mass fraction for 20 parts of carborundum, 15 parts of land plaster, 5 parts of titanium dioxide, 8 parts of silicon nitride, 10 parts of nano aluminium oxide, nano oxygen
Change 15 parts of magnesium, 5 parts of nano zircite, 1 part of nano-nickel oxide.
3. a kind of novel fire resistant nano ceramic coat according to claim 1, it is characterised in that:Its component and each component
Mass fraction for 30 parts of carborundum, 20 parts of land plaster, 10 parts of titanium dioxide, 13 parts of silicon nitride, 15 parts of nano aluminium oxide, nanometer
18 parts of magnesia, 10 parts of nano zircite, 5 parts of nano-nickel oxide.