CN107149925A - Heavy metal absorbent prepared by a kind of utilization bog moss and preparation method thereof - Google Patents
Heavy metal absorbent prepared by a kind of utilization bog moss and preparation method thereof Download PDFInfo
- Publication number
- CN107149925A CN107149925A CN201710573328.6A CN201710573328A CN107149925A CN 107149925 A CN107149925 A CN 107149925A CN 201710573328 A CN201710573328 A CN 201710573328A CN 107149925 A CN107149925 A CN 107149925A
- Authority
- CN
- China
- Prior art keywords
- parts
- heavy metal
- bog moss
- utilization
- metal absorbent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses heavy metal absorbent prepared by a kind of utilization bog moss, heavy metal absorbent prepared by the utilization bog moss is mainly made up of following parts by weight material:65 85 parts of bog moss, 5 10 parts of modified alta-mud, 58 parts of modification infusorial earth, 10 20 parts of seawood meal, 5 10 parts of feather meal, 5 10 parts of citric acid, 58 parts of oligosaccharide, 58 parts of chitosan, 20 30 parts of silica gel, 5 10 parts of sesbania gum, 15 20 parts of propolis;The present invention is using primary raw material of the bog moss as adsorbent, it is divided into 2 parts, a copy of it has significant suction-operated with modified alta-mud, modification infusorial earth mixed sintering formation peat synergy heavy metal ion, heavy metal ion carries out chelating with feather meal, seawood meal, oligosaccharide, chitosan and forms macromolecular, the particle being made by sesbania gum, silica gel and propolis is tightly adsorbed, and reaches the effect of effective heavy-metal ion removal.
Description
Technical field
The present invention relates to pollution processing technology field.It is more particularly related to prepared by a kind of utilization bog moss
Heavy metal absorbent and preparation method thereof.
Background technology
The big bog moss of bog moss alias, fountain moss, sphagna, sweater, distribution is most wide and common species.It is common in mountain region moistening ground
In area or marsh, more into the single phytobiocoenose of large area cushion.It is the main component source for generating peat.Due to such mass-planting
Thing have distinctive water cell, storage capacity be other mosses several times to tens times.
Heavy metal original meaning refers to the metal (density be more than 4.5 grams metals per cubic centimeter) that proportion is more than 5, including gold,
Silver, copper, iron, lead etc..Heavy metal pollution is different from the pollution of other organic compounds.Many organic compounds can pass through nature
Boundary physics itself, chemistry or biological purification, makes harmfulness reduce or release.And heavy metal has enriching, it is difficult to
Degraded in environment.
At present China due in the exploitation, smelting, process of heavy metal, cause many heavy metals for example lead, mercury, cadmium,
Cobalt etc. enters big gas and water, soil and causes serious environmental pollution.The heavy metal such as discharged with waste water, also can be even if concentration is small
Accumulate, adsorbed by fish and shellfish body surface in algae and bed mud, food chain concentration is produced, so as to cause public hazards.
In human body with protein and various enzymes strong interaction can occur for heavy metal, them is lost activity,
It may be enriched with some organs of human body, if it exceeds the limit that human body is resistant to, can cause human body acute poisoning, Asia anxious
Property poisoning, slow poisoning etc., people is known from experience and causes very big harm, for example, minamata disease (mercury pollution) and ostalgia that Japan occurs
Nuisance diseases such as sick (cadmium pollutions), is all as caused by heavy metal pollution.
The content of the invention
Present invention aim to address above mentioned problem, there is provided a kind of significant weight prepared using bog moss of cost ineffective fruit
Metal absorbent, the present invention is divided into 2 parts using primary raw material of the bog moss as adsorbent, a copy of it and modified alta-mud,
Modification infusorial earth mixed sintering formation peat synergy heavy metal ion there is significant suction-operated, another without
Effect of the processing with absorption oil slick, heavy metal ion can also carry out chelating shape with feather meal, seawood meal, oligosaccharide, chitosan
Into macromolecular, the particle being made by sesbania gum, silica gel and propolis is tightly adsorbed, and reaches the effect of effective heavy-metal ion removal,
The present invention can significantly remove the heavy metal ion in sewage, have remarkable result for removing the heavy metal ion in sewage.
The technical scheme that the present invention is provided is:
A kind of heavy metal absorbent prepared by utilization bog moss, heavy metal absorbent prepared by the utilization bog moss is main
It is made up of following parts by weight material:65-85 parts of bog moss, 5-10 parts of modified alta-mud, 5-8 parts of modification infusorial earth, seawood meal 10-
20 parts, 5-10 parts of feather meal, 5-10 parts of citric acid, 5-8 parts of oligosaccharide, 5-8 parts of chitosan, 20-30 parts of silica gel, sesbania gum 5-10
Part, 15-20 parts of propolis.
Preferably, the heavy metal absorbent that prepared by the utilization bog moss is mainly made up of following parts by weight material:Mud
75 parts of charcoal moss, 8 parts of modified alta-mud, 7 parts of modification infusorial earth, 15 parts of seawood meal, 8 parts of feather meal, 8 parts of citric acid, oligosaccharide 7
Part, 6 parts of chitosan, 25 parts of silica gel, 8 parts of sesbania gum, 17 parts of propolis.
Preferably, the modified alta-mud is made up of following methods:Bentonite is added into 2 times of heavy deionized waters, then
Add after sodium acid carbonate regulation PH to 11-12, add 10-15% organic silicone oils, ball milling is placed in calcining furnace after 20-30 minutes
Temperature is increased to 300-450 DEG C, after calcining 1-4 hours, and taking-up is cooled to room temperature, adds isometric concentration for mass fraction
95% ethanol, ball milling ignition in 20-30 minutes to ethanol is burnt out, and re-dry obtains the modified alta-mud.
Preferably, the modification infusorial earth is made up of following methods:Diatomite is added into 2 times of heavy deionized waters, plus
Enter citric acid regulation PH to 3-5, ball milling stands 20-30 minutes after 20-30 minutes, add sodium acid carbonate regulation PH to 11-12
Afterwards, after ball milling 20-30 minutes, it is placed in temperature in calcining furnace and is increased to 300-450 DEG C, after calcining 1-4 hours, taking-up is cooled to room
Temperature obtains the modification infusorial earth.
The present invention also provides a kind of preparation method of heavy metal absorbent prepared by described utilization bog moss, the preparation
Method comprises the following steps:
Step 1: after bog moss is dried, crushing 100 mesh sieve, bog moss powder is obtained, is divided into 2 parts etc. weight, its
Middle a bog moss powder is placed in 200-300 DEG C of sintering furnace after being mixed with modified alta-mud, modification infusorial earth and sintered 2-4 hours
Afterwards, cooling obtains powders A and is well mixed with another bog moss powder to obtain powder B;
Step 2: being heated to after sesbania gum, silica gel are mixed with propolis after molten condition, stir 30 minutes, nitrogen is used afterwards
Gas cooling immediately after high-pressure nozzle spraying is scattered obtains particle C, and the pressure of its mesohigh is 100-200Mpa;
Step 3: after powder B, particle C, seawood meal, feather meal, citric acid, oligosaccharide and chitosan are mixed, adding
Isometric deionized water, after being uniformly mixed, is passed through carbon dioxide 20mg/L, the heavy metal absorbent is obtained after drying.
The present invention at least includes following beneficial effect:
The present invention is divided into 2 parts using primary raw material of the bog moss as adsorbent, a copy of it and modified alta-mud, changes
Property diatomite mixed sintering formation peat synergy heavy metal ion there is significant suction-operated, another is without place
Effect of the reason with absorption oil slick, wherein heavy metal ion carry out chelating formation with feather meal, seawood meal, oligosaccharide, chitosan
Macromolecular, the particle being made by sesbania gum, silica gel and propolis is tightly adsorbed, and reaches the effect of effective heavy-metal ion removal, this
Invention can significantly remove the heavy metal ion in sewage, have remarkable result, this hair for removing the heavy metal ion in sewage
The modified alta-mud of bright addition is added after organosilicon by using ethanol combustion after calcining, significantly improves bentonitic hole
Degree so that space is uniform, significantly increasing for bentonitic specific surface area, improves heavy metal ion adsorbed property, present invention environmental protection is not
Water resource secondary pollution can be caused;
The present invention also provides a kind of preparation method of heavy metal absorbent prepared by utilization bog moss, which part bog moss
Mixed with modified alta-mud, modification infusorial earth after high temperature sintering, bog moss carbonization is cooperateed with without the bog moss of processing
Effect, significantly improves heavy metal ion adsorption capacity, and sesbania gum, silica gel and propolis form little particle silica gel by high-pressure fog
Propolis is significantly improved for the adsorption capacity of macromolecular.
Further advantage, target and the feature of the present invention embodies part by following explanation, and part will also be by this
The research and practice of invention and be understood by the person skilled in the art.
Embodiment
With reference to example below, the present invention is described in further detail, to make those skilled in the art with reference to specification
Word can be implemented according to this.
Wherein 1 part of the embodiment of the present invention is 1kg
Embodiment 1
Heavy metal absorbent prepared by a kind of utilization bog moss, is mainly made up of following parts by weight material:65 parts of bog moss,
5 parts of modified alta-mud, 5 parts of modification infusorial earth, 10 parts of seawood meal, 5 parts of feather meal, 5 parts of citric acid, 5 parts of oligosaccharide, chitosan 5
Part, 20 parts of silica gel, 5 parts of sesbania gum, 15 parts of propolis.
Wherein, the modified alta-mud is made up of following methods:Bentonite is added into 2 times of heavy deionized waters, added
After sodium acid carbonate regulation PH to 11,10% organic silicone oil is added, ball milling is placed in temperature in calcining furnace and is increased to 300 after 20 minutes
DEG C, after calcining 1 hour, taking-up is cooled to room temperature, adds isometric concentration for the ethanol of mass fraction 95%, 20 minutes points of ball milling
Fire burning to ethanol is burnt out, and re-dry obtains the modified alta-mud.
The modification infusorial earth is made up of following methods:Diatomite is added into 2 times of heavy deionized waters, citric acid is added and adjusts
PH to 3 is saved, ball milling stands 20 minutes after 20 minutes, added after sodium acid carbonate regulation PH to 11, ball milling is placed in after 20 minutes
Temperature is increased to 300 DEG C in calcining furnace, after calcining 1 hour, and taking-up is cooled to room temperature and obtains the modification infusorial earth.
The preparation method of heavy metal absorbent prepared by described utilization bog moss, comprises the following steps:
Step 1: after bog moss is dried, crushing 100 mesh sieve, bog moss powder is obtained, is divided into 2 parts etc. weight, its
Middle a bog moss powder is placed in sintering in 200 DEG C of sintering furnace after being mixed with modified alta-mud, modification infusorial earth cold after 2 hours
But obtain powders A and be well mixed with another bog moss powder to obtain powder B;
Step 2: being heated to after sesbania gum, silica gel are mixed with propolis after molten condition, stir 30 minutes, nitrogen is used afterwards
Gas cooling immediately after high-pressure nozzle spraying is scattered obtains particle C, and the pressure of its mesohigh is 100Mpa;
Step 3: after powder B, particle C, seawood meal, feather meal, citric acid, oligosaccharide and chitosan are mixed, adding
Isometric deionized water, after being uniformly mixed, is passed through carbon dioxide 20mg/L, the heavy metal absorbent is obtained after drying.
Embodiment 2
A kind of heavy metal absorbent prepared by utilization bog moss, heavy metal absorbent prepared by the utilization bog moss is main
It is made up of following parts by weight material:85 parts of bog moss, 10 parts of modified alta-mud, 8 parts of modification infusorial earth, 20 parts of seawood meal, feather
10 parts of powder, 10 parts of citric acid, 8 parts of oligosaccharide, 8 parts of chitosan, 30 parts of silica gel, 10 parts of sesbania gum, 20 parts of propolis.
Wherein, the modified alta-mud is made up of following methods:Bentonite is added into 2 times of heavy deionized waters, added
After sodium acid carbonate regulation PH to 12,15% organic silicone oil is added, ball milling is placed in temperature in calcining furnace and is increased to 450 after 30 minutes
DEG C, after calcining 4 hours, taking-up is cooled to room temperature, adds isometric concentration for the ethanol of mass fraction 95%, 30 minutes points of ball milling
Fire burning to ethanol is burnt out, and re-dry obtains the modified alta-mud.
The modification infusorial earth is made up of following methods:Diatomite is added into 2 times of heavy deionized waters, citric acid is added and adjusts
PH to 5 is saved, ball milling stands 30 minutes after 30 minutes, added after sodium acid carbonate regulation PH to 12, ball milling is placed in after 30 minutes
Temperature is increased to 450 DEG C in calcining furnace, after calcining 4 hours, and taking-up is cooled to room temperature and obtains the modification infusorial earth.
The preparation method of heavy metal absorbent prepared by described utilization bog moss, comprises the following steps:
Step 1: after bog moss is dried, crushing 100 mesh sieve, bog moss powder is obtained, is divided into 2 parts etc. weight, its
Middle a bog moss powder is placed in sintering in 300 DEG C of sintering furnace after being mixed with modified alta-mud, modification infusorial earth cold after 4 hours
But obtain powders A and be well mixed with another bog moss powder to obtain powder B;
Step 2: being heated to after sesbania gum, silica gel are mixed with propolis after molten condition, stir 30 minutes, nitrogen is used afterwards
Gas cooling immediately after high-pressure nozzle spraying is scattered obtains particle C, and the pressure of its mesohigh is 200Mpa;
Step 3: after powder B, particle C, seawood meal, feather meal, citric acid, oligosaccharide and chitosan are mixed, adding
Isometric deionized water, after being uniformly mixed, is passed through carbon dioxide 20mg/L, the heavy metal absorbent is obtained after drying.
Embodiment 3
Heavy metal absorbent prepared by a kind of utilization bog moss, is mainly made up of following parts by weight material:75 parts of bog moss,
8 parts of modified alta-mud, 7 parts of modification infusorial earth, 15 parts of seawood meal, 8 parts of feather meal, 8 parts of citric acid, 7 parts of oligosaccharide, chitosan 6
Part, 25 parts of silica gel, 8 parts of sesbania gum, 17 parts of propolis.
Wherein, the modified alta-mud is made up of following methods:Bentonite is added into 2 times of heavy deionized waters, added
After sodium acid carbonate regulation PH to 11.5,13% organic silicone oil is added, ball milling is placed in temperature in calcining furnace and be increased to after 22 minutes
350 DEG C, after calcining 2 hours, taking-up is cooled to room temperature, adds isometric concentration for the ethanol of mass fraction 95%, 22 points of ball milling
Clock ignition to ethanol is burnt out, and re-dry obtains the modified alta-mud.
The modification infusorial earth is made up of following methods:Diatomite is added into 2 times of heavy deionized waters, citric acid is added and adjusts
PH to 4 is saved, ball milling stands 28 minutes after 22 minutes, added after sodium acid carbonate regulation PH to 11, ball milling is placed in after 25 minutes
Temperature is increased to 400 DEG C in calcining furnace, after calcining 3 hours, and taking-up is cooled to room temperature and obtains the modification infusorial earth.
The preparation method of heavy metal absorbent prepared by described utilization bog moss, comprises the following steps:
Step 1: after bog moss is dried, crushing 100 mesh sieve, bog moss powder is obtained, is divided into 2 parts etc. weight, its
Middle a bog moss powder is placed in sintering in 250 DEG C of sintering furnace after being mixed with modified alta-mud, modification infusorial earth cold after 3 hours
But obtain powders A and be well mixed with another bog moss powder to obtain powder B;
Step 2: being heated to after sesbania gum, silica gel are mixed with propolis after molten condition, stir 30 minutes, nitrogen is used afterwards
Gas cooling immediately after high-pressure nozzle spraying is scattered obtains particle C, and the pressure of its mesohigh is 180Mpa;
Step 3: after powder B, particle C, seawood meal, feather meal, citric acid, oligosaccharide and chitosan are mixed, adding
Isometric deionized water, after being uniformly mixed, is passed through carbon dioxide 20mg/L, the heavy metal absorbent is obtained after drying.
Experiment:Using embodiment 1-3 heavy metal absorbent, to the sewage sampling 3000L of certain sewage treatment plant, sewage contains
Cadmium ion 32.4mg/L, lead ion 40.2mg/L, hexavalent chromium 22.6mg/L, 3 groups are divided into by 3000L sewage sample
A, B, C, correspond to the heavy metal absorbent 300g for adding embodiment 1-3 respectively, and a huge sum of money is recovered by filtration after 2.5 hours in stir process
Category adsorbent, the sewage of test processes, cadmium ion ND, lead ion ND, hexavalent chromium ND, the heavy metal absorbent of recovery can be again
Recycling.
Although embodiment of the present invention is disclosed as above, it is not restricted in specification and embodiment listed
With it can be applied to various suitable the field of the invention completely, can be easily for those skilled in the art
Other modification is realized, therefore under the universal limited without departing substantially from claim and equivalency range, the present invention is not limited
In specific details and shown here as the embodiment with description.
Claims (5)
1. a kind of heavy metal absorbent prepared by utilization bog moss, it is characterised in that heavy metal prepared by the utilization bog moss
Adsorbent is mainly made up of following parts by weight material:65-85 parts of bog moss, 5-10 parts of modified alta-mud, modification infusorial earth 5-8
Part, 10-20 parts of seawood meal, 5-10 parts of feather meal, 5-10 parts of citric acid, 5-8 parts of oligosaccharide, 5-8 parts of chitosan, silica gel 20-30
Part, 5-10 parts of sesbania gum, 15-20 parts of propolis.
2. heavy metal absorbent prepared by utilization bog moss according to claim 1, it is characterised in that the utilization peat
Heavy metal absorbent prepared by moss is mainly made up of following parts by weight material:75 parts of bog moss, 8 parts of modified alta-mud, modified silicon
7 parts of diatomaceous earth, 15 parts of seawood meal, 8 parts of feather meal, 8 parts of citric acid, 7 parts of oligosaccharide, 6 parts of chitosan, 25 parts of silica gel, sesbania gum 8
Part, 17 parts of propolis.
3. heavy metal absorbent prepared by utilization bog moss according to claim 2, it is characterised in that the bentone
Soil is made up of following methods:Bentonite is added into 2 times of heavy deionized waters, added after sodium acid carbonate regulation PH to 11-12, plus
Enter 10-15% organic silicone oils, ball milling is placed in temperature in calcining furnace and is increased to 300-450 DEG C, calcine 1-4 hours after 20-30 minutes
Afterwards, take out and be cooled to room temperature, add isometric concentration for the ethanol of mass fraction 95%, ball milling ignition in 20-30 minutes is extremely
Ethanol is burnt out, and re-dry obtains the modified alta-mud.
4. heavy metal absorbent prepared by utilization bog moss according to claim 3, it is characterised in that the modified diatom
Soil is made up of following methods:Diatomite is added into 2 times of heavy deionized waters, citric acid regulation PH to 3-5, ball milling 20-30 is added
After minute, 20-30 minutes are stood, is added after sodium acid carbonate regulation PH to 11-12, ball milling is placed in calcining furnace after 20-30 minutes
Middle temperature is increased to 300-450 DEG C, after calcining 1-4 hours, and taking-up is cooled to room temperature and obtains the modification infusorial earth.
5. the preparation method of heavy metal absorbent prepared by any described utilization bog moss in a kind of 1-4 according to claim,
Characterized in that, the preparation method comprises the following steps:
Step 1: after bog moss is dried, crushing 100 mesh sieve, bog moss powder is obtained, is divided into 2 parts etc. weight, wherein one
Part bog moss powder was placed in 200-300 DEG C of sintering furnace sintering after 2-4 hours after being mixed with modified alta-mud, modification infusorial earth,
Cooling obtains powders A and is well mixed with another bog moss powder to obtain powder B;
Step 2: being heated to after sesbania gum, silica gel are mixed with propolis after molten condition, stir 30 minutes, it is rear using nitrogen warp
Cross cooling immediately after high-pressure nozzle spraying disperses and obtain particle C, the pressure of its mesohigh is 100-200Mpa;
Step 3: after powder B, particle c, seawood meal, feather meal, citric acid, oligosaccharide and chitosan are mixed, the body such as addition
Product deionized water, after being uniformly mixed, is passed through carbon dioxide 20mg/L, the heavy metal absorbent is obtained after drying.