CN107138373A - Strengthen wood-plastic board adhesive force process of surface treatment - Google Patents
Strengthen wood-plastic board adhesive force process of surface treatment Download PDFInfo
- Publication number
- CN107138373A CN107138373A CN201710235524.2A CN201710235524A CN107138373A CN 107138373 A CN107138373 A CN 107138373A CN 201710235524 A CN201710235524 A CN 201710235524A CN 107138373 A CN107138373 A CN 107138373A
- Authority
- CN
- China
- Prior art keywords
- adhesive force
- plastic board
- surface treatment
- wood
- force process
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Present invention enhancing wood-plastic board adhesive force process of surface treatment, is mainly prepared from the following materials in mass ratio by treatment fluid A：Water 5 10, hydrochloric acid 0.5 2, fixing glue 0.5 1, the invention overcome it is existing due to caused by many reasons such as base material is loose, priming paint penetration difference priming paint adhesive force it is low, improve wood moulding plate surface finish paint adhesive ability.
Description
Technical field
The present invention relates to paint field, more particularly to enhancing wood-plastic board adhesive force process of surface treatment.
Background technology
It can be combined together between priming paint and base material by the mode such as mechanical bond and physics suction effect, it is firm that it is combined
Degree is referred to as adhesive force, and mainly the polar group of the polar group of polymer and substrate surface interacts adhesive force in paint film
Formed by.But in actual applications, often because many reasons such as base material is loose, priming paint penetration difference cause priming paint adhesive force mistake
It is low, particularly during imitative brick etc. needs the special-effect surface of the U.S. line paper of frequent tear-off to be constructed, priming paint adhesive force
It is not good to easily cause avulsion in blocks, influence attractive in appearance and usability.
Therefore provide that a kind of adhesive force and closure to base material is good, torn with good anti-general saline alkali and anti-U.S. line paper
High-adhesion primer of de- property and preparation method thereof oneself turn into when business urgently.
The content of the invention
It is an object of the invention to provide enhancing wood-plastic board adhesive force process of surface treatment, solve the above problems, possess to base
The adhesive force and closure of material is good, it is anti-tear de- the advantages of.
The technical scheme that specifically uses of the present invention specifically,
Strengthen wood-plastic board adhesive force process of surface treatment, comprise the following steps：
1) board surface is cleaned up, then dried；
2) plank for handling step (1) well carries out even application 3-5 times using treatment fluid A, treatment fluid A in mass ratio by
Following raw material is prepared from：Water 5-10, hydrochloric acid 0.5-2, fixing glue 0.5-1；
3) plank for handling step (2) well cleans board surface using 1% urea water；
4) it is for clearance clean and after drying, then painted using finish paint.
Preferably, described fixing glue main component is acrylic resin,
Preferably, the described specific mass components for the treatment of fluid A are：Water 10, hydrochloric acid 1, fixing glue 0.8.
The present invention has advantages below：The processing method mainly carries out painting area science and engineering skill in wood-plastic board, due to wood
Mould plate surface micropore is trickle, and traditional priming paint is difficult to penetrate into.The adhesive force priming paint of the present invention selects priming paint, and its particle diameter is small, formation
Paint film penetration is strong, and base material can be penetrated into well, improves the micropore of the adhesive force and closed substrate with base material, and has after film forming
Good waterproof and anti-general saline and alkaline ability；Add adhesion promoter again simultaneously, it is used cooperatively with urea water, further
The adhesion between base material is improved, the storage stability and workability of the High-adhesion primer is improved, its reclaimed water can
Using common running water or other clean waters, to play a part of regulation viscosity, reduce cost, enhancing application property.
Embodiment
With reference to specific embodiment, the present invention is described in further detail, it is described be explanation of the invention and
It is not to limit.
Embodiment one
Strengthen wood-plastic board adhesive force process of surface treatment, comprise the following steps：
1) board surface is cleaned up, then dried；
2) plank for handling step (1) well carries out even application 3-5 times using treatment fluid A, treatment fluid A in mass ratio by
Following raw material is prepared from：Water 10, hydrochloric acid 1, fixing glue 0.8；
3) plank for handling step (2) well cleans board surface using 1% urea water；
4) it is for clearance clean and after drying, then painted using finish paint.
Preferably, described fixing glue main component is acrylic resin.
Embodiment two
Strengthen wood-plastic board adhesive force process of surface treatment, comprise the following steps：
1) board surface is cleaned up, then dried；
2) plank for handling step (1) well carries out even application 3-5 times using treatment fluid A, treatment fluid A in mass ratio by
Following raw material is prepared from：Water 5, hydrochloric acid 0.5, fixing glue 0.5；
3) plank for handling step (2) well cleans board surface using 1% urea water；
4) it is for clearance clean and after drying, then painted using finish paint.
Preferably, described fixing glue main component is acrylic resin.
Embodiment three
Strengthen wood-plastic board adhesive force process of surface treatment, comprise the following steps：
1) board surface is cleaned up, then dried；
2) plank for handling step (1) well carries out even application 3-5 times using treatment fluid A, treatment fluid A in mass ratio by
Following raw material is prepared from：Water 10, hydrochloric acid 2, fixing glue 1；
3) plank for handling step (2) well cleans board surface using 1% urea water；
4) it is for clearance clean and after drying, then painted using finish paint.
Preferably, described fixing glue main component is acrylic resin.
Claims (3)
1. strengthen wood-plastic board adhesive force process of surface treatment, it is characterised in that comprise the following steps：
1) board surface is cleaned up, then dried；
2) plank for handling step (1) well carries out even application 3-5 times using treatment fluid A, and treatment fluid A is in mass ratio by following
Raw material is prepared from：Water 5-10, hydrochloric acid 0.5-2, fixing glue 0.5-1；
3) plank for handling step (2) well cleans board surface using 1% urea water；
4) it is for clearance clean and after drying, then painted using finish paint.
2. enhancing wood-plastic board adhesive force process of surface treatment according to claim 1, its characteristic is, described fixation
Glue main component is acrylic resin.
3. according to the enhancing wood-plastic board adhesive force process of surface treatment described in claim 1, its characteristic is, described treatment fluid
The specific mass components of A are：Water 10, hydrochloric acid 1, fixing glue 0.8.