CN107117906A - A kind of tile grout and preparation method thereof - Google Patents
A kind of tile grout and preparation method thereof Download PDFInfo
- Publication number
- CN107117906A CN107117906A CN201710446176.3A CN201710446176A CN107117906A CN 107117906 A CN107117906 A CN 107117906A CN 201710446176 A CN201710446176 A CN 201710446176A CN 107117906 A CN107117906 A CN 107117906A
- Authority
- CN
- China
- Prior art keywords
- parts
- agent
- cellulose
- tackifier
- accumulation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of tile grout, include the raw material of following parts by weight：15~25 parts of glass bead, 16~20 parts of acrylate synthetic resin, 17~28 parts of white cement, useless 10~20 parts of porcelain powder, 8~16 parts of bentonite, 5~11 parts of aerosil, 2~3 parts of redispersible latex powder, 3~6 parts of barium sulfate, 1~2 part of ultra-violet absorber, 2.5~3.5 parts of lignin fibre, 0.5~1 part of cellulose, 0.3~0.7 part of initiator, 1~2 part of anti-crack water-proof agent, 0.06~1.3 part of anti-accumulation of salt in the surface soil agent, 2~4 parts of inorganic antiseptic, 2.7~3.8 parts of tackifier.The tile grout can not only thoroughly solve the problems, such as the accumulation of salt in the surface soil of gap filler, and easy construction, be unnecessary gap filler capable of washing with water, meanwhile, cold curing, resistant, scrubbing resistance, cost is low.
Description
Technical field
The invention belongs to building material field, and in particular to a kind of tile grout and preparation method thereof.
Background technology
With the development of society, ceramic tile has become one of material the most frequently used in building decoration.At present, ceramic tile and ceramic tile
Between the most frequently used packing material in gap be cement base tile grout.This kind of cement base tile grout is through using a period of time table
Face is very dirty, influences aesthetic.
For there are problems, once there is the skill using epoxy resin, curing agent and filler mixing filling in this area
Art scheme attempts thoroughly to solve problem above.But the epoxy resin and curing agent used in such a scheme are all no-solvent types, are made
It is easy to pollute ceramic tile surface during, clears up extremely difficult, easily leave a trace, meanwhile, construction appliance is also extremely difficult
Cleaning, causes construction inconvenience.
The content of the invention
The invention provides a kind of tile grout and preparation method thereof, the deficiency in above-mentioned background technology is solved, it is described
Tile grout can not only thoroughly solve the problems, such as the accumulation of salt in the surface soil of gap filler, and easy construction, be unnecessary joint filling capable of washing with water
Agent, meanwhile, cold curing, resistant, scrubbing resistance, cost is low.
In order to solve the problem of prior art is present, adopt the following technical scheme that：
A kind of tile grout, includes the raw material of following parts by weight：15~25 parts of glass bead, acrylate synthetic resin 16~
20 parts, it is 17~28 parts of white cement, useless 10~20 parts of porcelain powder, 8~16 parts of bentonite, 5~11 parts of aerosil, redispersible
2~3 parts of latex powder of property, 3~6 parts of barium sulfate, 1~2 part of ultra-violet absorber, 2.5~3.5 parts of lignin fibre, cellulose
0.5~1 part, 0.3~0.7 part of initiator, 1~2 part of anti-crack water-proof agent, 0.06~1.3 part of anti-accumulation of salt in the surface soil agent, inorganic antiseptic 2~4
Part, 2.7~3.8 parts of tackifier.
It is preferred that, the tile grout includes the raw material of following parts by weight：18~22 parts of glass bead, acrylate
17~18 parts of synthetic resin, 22~26 parts of white cement, useless 13~19 parts of porcelain powder, 12~15 parts of bentonite, aerosil 7~
9 parts, 2.2~2.8 parts of redispersible latex powder, 3.7~4.3 parts of barium sulfate, 1.2~1.7 parts of ultra-violet absorber, lignin
2.8~3.3 parts of fiber, 0.7~0.9 part of cellulose, 0.4~0.6 part of initiator, 1.2~1.8 parts of anti-crack water-proof agent, the anti-accumulation of salt in the surface soil
0.3~0.9 part of agent, 2.5~3.7 parts of inorganic antiseptic, 3.1~3.6 parts of tackifier.
It is preferred that, the tile grout includes the raw material of following parts by weight：20 parts of glass bead, acrylate synthesis
17.8 parts of resin, 24 parts of white cement, useless 15 parts of porcelain powder, 14 parts of bentonite, 8 parts of aerosil, redispersible latex powder
2.6 parts, 3.9 parts of barium sulfate, 1.4 parts of ultra-violet absorber, 3.2 parts of lignin fibre, 0.8 part of cellulose, 0.5 part of initiator,
1.3 parts of anti-crack water-proof agent, 0.7 part of anti-accumulation of salt in the surface soil agent, 2.8 parts of inorganic antiseptic, 3.4 parts of tackifier.
It is preferred that, described tackifier are anilinomethyl triethoxysilane.
It is preferred that, the cellulose is in hydroxyethyl cellulose, hydroxyethylmethylcellulose, hydroxypropyl methyl cellulose
It is at least one.
It is preferred that, the inorganic antiseptic makees antimicrobial component, inorganic antibacterial with hydroxy-apatite masonry carrier, silver, zinc and copper
The percentage by weight of each composition is in agent：Hydroxyapatite is that 93%, silver is that 1%, zinc is that 5%, copper is 1%.
A kind of method for preparing the tile grout, comprises the following steps：
（1）Glass bead, acrylate synthetic resin, white cement, useless porcelain powder, bentonite, gas phase dioxy are weighed by above-mentioned formula
SiClx, redispersible latex powder, barium sulfate, ultra-violet absorber, lignin fibre, cellulose, initiator, anti-cracking waterproof
Agent, anti-accumulation of salt in the surface soil agent, inorganic antiseptic, tackifier, it is standby；
（2）Acrylate synthetic resin is placed in kneader, redispersible latex powder, initiator, lignin fibre is added
And cellulose, 70~80 DEG C are heated to, mediates 20~40 minutes, obtains sizing material；
（3）First glass bead, white cement, useless porcelain powder, bentonite, aerosil and barium sulfate are well mixed, ball is placed in
Ball milling 2~3 hours in grinding machine, then be placed in high speed dispersor, sequentially add step（2）Obtained sizing material, ultra-violet absorber,
Anti-crack water-proof agent, anti-crack water-proof agent, anti-accumulation of salt in the surface soil agent, inorganic antiseptic, tackifier are scattered 2~3 hours at a high speed, and the ceramic tile is made
Gap filler.
It is preferred that, the step（3）The speed of high speed dispersion machine is 1000~1200r/min.
Compared with prior art, it has the advantages that the present invention：
Tile grout of the present invention can not only thoroughly solve the problems, such as the accumulation of salt in the surface soil of gap filler, and easy construction, use water
Unnecessary gap filler i.e. capable of washing, meanwhile, cold curing, resistant, scrubbing resistance is specific as follows：
（1）Tile grout of the present invention, is acted synergistically by a variety of powder compositions, effectively inhibits free calcium ion
Calcium carbonate is produced with the carbon dioxide exposure in air, so as to avoid accumulation of salt in the surface soil problem；Composition used can be using washing simultaneously
Remove, so as to avoid unnecessary gap filler pollution ceramic tile；Epoxy resin used and curing agent are i.e. curable at room temperature, and
And resistant scrubbing resistance；
（2）Tile grout of the present invention largely uses useless porcelain powder as raw material, can be comprehensively utilized resource,
Environmental protection and waste utilization, reduces cost；
（3）Gas phase is with the addition of in tile grout of the present invention for silica, aerosil can improve viscosity, prevented
Only gap filler shrinks in solidification, and can assign gap filler good rheological behavior, improves the tile grout
Performance.
Embodiment
With reference to specific embodiment, the present invention is expanded on further.These embodiments be merely to illustrate the present invention and without
In limitation the scope of the present invention.
Embodiment 1
The present embodiment is related to a kind of tile grout, includes the raw material of following parts by weight：15 parts of glass bead, acrylate synthesis
16 parts of resin, 17 parts of white cement, useless 10 parts of porcelain powder, 8 parts of bentonite, 5 parts of aerosil, 2 parts of redispersible latex powder,
3 parts of barium sulfate, 1 part of ultra-violet absorber, 2.5 parts of lignin fibre, 0.5 part of cellulose, 0.3 part of initiator, anti-crack water-proof agent
1 part, 0.06 part of anti-accumulation of salt in the surface soil agent, 2 parts of inorganic antiseptic, 2.7 parts of tackifier.
Wherein, described tackifier are anilinomethyl triethoxysilane.
Wherein, the cellulose is selected from hydroxyethyl cellulose.
Wherein, the inorganic antiseptic is with hydroxy-apatite masonry carrier, and silver, zinc and copper make antimicrobial component, inorganic antiseptic
In the percentage by weight of each composition be：Hydroxyapatite is that 93%, silver is that 1%, zinc is that 5%, copper is 1%.
A kind of method for preparing the tile grout, comprises the following steps：
（1）Glass bead, acrylate synthetic resin, white cement, useless porcelain powder, bentonite, gas phase dioxy are weighed by above-mentioned formula
SiClx, redispersible latex powder, barium sulfate, ultra-violet absorber, lignin fibre, cellulose, initiator, anti-cracking waterproof
Agent, anti-accumulation of salt in the surface soil agent, inorganic antiseptic, tackifier, it is standby；
（2）Acrylate synthetic resin is placed in kneader, redispersible latex powder, initiator, lignin fibre is added
And cellulose, 70 DEG C are heated to, mediates 20 minutes, obtains sizing material；
（3）First glass bead, white cement, useless porcelain powder, bentonite, aerosil and barium sulfate are well mixed, ball is placed in
Ball milling 2 hours in grinding machine, then be placed in high speed dispersor, sequentially add step（2）It is obtained sizing material, ultra-violet absorber, anti-
Split waterproofing agent, anti-crack water-proof agent, anti-accumulation of salt in the surface soil agent, inorganic antiseptic, tackifier scattered 2 hours at a high speed, the ceramic tile joint filling is made
Agent.
Wherein, the step（3）The speed of high speed dispersion machine is 1000r/min.
Embodiment 2
The present embodiment is related to a kind of tile grout, includes the raw material of following parts by weight：25 parts of glass bead, acrylate synthesis
20 parts of resin, 28 parts of white cement, useless 20 parts of porcelain powder, 16 parts of bentonite, 11 parts of aerosil, redispersible latex powder 3
Part, 6 parts of barium sulfate, 2 parts of ultra-violet absorber, 3.5 parts of lignin fibre, 1 part of cellulose, 0.7 part of initiator, anti-cracking waterproof
2 parts of agent, 1.3 parts of anti-accumulation of salt in the surface soil agent, 4 parts of inorganic antiseptic, 3.8 parts of tackifier.
Wherein, described tackifier are anilinomethyl triethoxysilane.
Wherein, the cellulose is selected from hydroxyethylmethylcellulose.
Wherein, the inorganic antiseptic is with hydroxy-apatite masonry carrier, and silver, zinc and copper make antimicrobial component, inorganic antiseptic
In the percentage by weight of each composition be：Hydroxyapatite is that 93%, silver is that 1%, zinc is that 5%, copper is 1%.
A kind of method for preparing the tile grout, comprises the following steps：
（1）Glass bead, acrylate synthetic resin, white cement, useless porcelain powder, bentonite, gas phase dioxy are weighed by above-mentioned formula
SiClx, redispersible latex powder, barium sulfate, ultra-violet absorber, lignin fibre, cellulose, initiator, anti-cracking waterproof
Agent, anti-accumulation of salt in the surface soil agent, inorganic antiseptic, tackifier, it is standby；
（2）Acrylate synthetic resin is placed in kneader, redispersible latex powder, initiator, lignin fibre is added
And cellulose, 80 DEG C are heated to, mediates 40 minutes, obtains sizing material；
（3）First glass bead, white cement, useless porcelain powder, bentonite, aerosil and barium sulfate are well mixed, ball is placed in
Ball milling 3 hours in grinding machine, then be placed in high speed dispersor, sequentially add step（2）It is obtained sizing material, ultra-violet absorber, anti-
Split waterproofing agent, anti-crack water-proof agent, anti-accumulation of salt in the surface soil agent, inorganic antiseptic, tackifier scattered 3 hours at a high speed, the ceramic tile joint filling is made
Agent.
Wherein, the step（3）The speed of high speed dispersion machine is 1200r/min.
Embodiment 3
The present embodiment is related to a kind of tile grout, includes the raw material of following parts by weight：18 parts of glass bead, acrylate synthesis
17 parts of resin, 22 parts of white cement, useless 13 parts of porcelain powder, 12 parts of bentonite, 7 parts of aerosil, redispersible latex powder 2.2
It is part, 3.7 parts of barium sulfate, 1.2 parts of ultra-violet absorber, 2.8 parts of lignin fibre, 0.7 part of cellulose, 0.4 part of initiator, anti-
Split 1.2 parts of waterproofing agent, 0.3 part of anti-accumulation of salt in the surface soil agent, 2.5 parts of inorganic antiseptic, 3.1 parts of tackifier.
Wherein, described tackifier are anilinomethyl triethoxysilane.
Wherein, the cellulose is selected from hydroxypropyl methyl cellulose.
Wherein, the inorganic antiseptic is with hydroxy-apatite masonry carrier, and silver, zinc and copper make antimicrobial component, inorganic antiseptic
In the percentage by weight of each composition be：Hydroxyapatite is that 93%, silver is that 1%, zinc is that 5%, copper is 1%.
A kind of method for preparing the tile grout, comprises the following steps：
（1）Glass bead, acrylate synthetic resin, white cement, useless porcelain powder, bentonite, gas phase dioxy are weighed by above-mentioned formula
SiClx, redispersible latex powder, barium sulfate, ultra-violet absorber, lignin fibre, cellulose, initiator, anti-cracking waterproof
Agent, anti-accumulation of salt in the surface soil agent, inorganic antiseptic, tackifier, it is standby；
（2）Acrylate synthetic resin is placed in kneader, redispersible latex powder, initiator, lignin fibre is added
And cellulose, 75 DEG C are heated to, mediates 30 minutes, obtains sizing material；
（3）First glass bead, white cement, useless porcelain powder, bentonite, aerosil and barium sulfate are well mixed, ball is placed in
Ball milling 2.5 hours in grinding machine, then be placed in high speed dispersor, sequentially add step（2）Obtained sizing material, ultra-violet absorber,
Anti-crack water-proof agent, anti-crack water-proof agent, anti-accumulation of salt in the surface soil agent, inorganic antiseptic, tackifier are scattered 2.5 hours at a high speed, and the ceramic tile is made
Gap filler.
Wherein, the step（3）The speed of high speed dispersion machine is 1100r/min.
Embodiment 4
The present embodiment is related to a kind of tile grout, includes the raw material of following parts by weight：22 parts of glass bead, acrylate synthesis
18 parts of resin, 26 parts of white cement, useless 19 parts of porcelain powder, 15 parts of bentonite, 9 parts of aerosil, redispersible latex powder 2.8
Part, 4.3 parts of barium sulfate, 1.7 parts of ultra-violet absorber, 3.3 parts of lignin fibre, 0.9 part of cellulose, 0.6 part of initiator, cracking resistance
1.8 parts of waterproofing agent, 0.9 part of anti-accumulation of salt in the surface soil agent, 3.7 parts of inorganic antiseptic, 3.6 parts of tackifier.
Wherein, described tackifier are anilinomethyl triethoxysilane.
Wherein, the cellulose is selected from hydroxyethyl cellulose and the mixture of hydroxyethylmethylcellulose.
Wherein, the inorganic antiseptic is with hydroxy-apatite masonry carrier, and silver, zinc and copper make antimicrobial component, inorganic antiseptic
In the percentage by weight of each composition be：Hydroxyapatite is that 93%, silver is that 1%, zinc is that 5%, copper is 1%.
A kind of method for preparing the tile grout, comprises the following steps：
（1）Glass bead, acrylate synthetic resin, white cement, useless porcelain powder, bentonite, gas phase dioxy are weighed by above-mentioned formula
SiClx, redispersible latex powder, barium sulfate, ultra-violet absorber, lignin fibre, cellulose, initiator, anti-cracking waterproof
Agent, anti-accumulation of salt in the surface soil agent, inorganic antiseptic, tackifier, it is standby；
（2）Acrylate synthetic resin is placed in kneader, redispersible latex powder, initiator, lignin fibre is added
And cellulose, 72 DEG C are heated to, mediates 25 minutes, obtains sizing material；
（3）First glass bead, white cement, useless porcelain powder, bentonite, aerosil and barium sulfate are well mixed, ball is placed in
Ball milling 2.2 hours in grinding machine, then be placed in high speed dispersor, sequentially add step（2）Obtained sizing material, ultra-violet absorber,
Anti-crack water-proof agent, anti-crack water-proof agent, anti-accumulation of salt in the surface soil agent, inorganic antiseptic, tackifier are scattered 2.3 hours at a high speed, and the ceramic tile is made
Gap filler.
Wherein, the step（3）The speed of high speed dispersion machine is 1050r/min.
Embodiment 5
The present embodiment is related to a kind of tile grout, includes the raw material of following parts by weight：20 parts of glass bead, acrylate synthesis
17.8 parts of resin, 24 parts of white cement, useless 15 parts of porcelain powder, 14 parts of bentonite, 8 parts of aerosil, redispersible latex powder
2.6 parts, 3.9 parts of barium sulfate, 1.4 parts of ultra-violet absorber, 3.2 parts of lignin fibre, 0.8 part of cellulose, 0.5 part of initiator,
1.3 parts of anti-crack water-proof agent, 0.7 part of anti-accumulation of salt in the surface soil agent, 2.8 parts of inorganic antiseptic, 3.4 parts of tackifier.
Wherein, described tackifier are anilinomethyl triethoxysilane.
Wherein, the cellulose is selected from hydroxyethylmethylcellulose, the mixture of hydroxypropyl methyl cellulose.
Wherein, the inorganic antiseptic is with hydroxy-apatite masonry carrier, and silver, zinc and copper make antimicrobial component, inorganic antiseptic
In the percentage by weight of each composition be：Hydroxyapatite is that 93%, silver is that 1%, zinc is that 5%, copper is 1%.
A kind of method for preparing the tile grout, comprises the following steps：
（1）Glass bead, acrylate synthetic resin, white cement, useless porcelain powder, bentonite, gas phase dioxy are weighed by above-mentioned formula
SiClx, redispersible latex powder, barium sulfate, ultra-violet absorber, lignin fibre, cellulose, initiator, anti-cracking waterproof
Agent, anti-accumulation of salt in the surface soil agent, inorganic antiseptic, tackifier, it is standby；
（2）Acrylate synthetic resin is placed in kneader, redispersible latex powder, initiator, lignin fibre is added
And cellulose, 78 DEG C are heated to, mediates 35 minutes, obtains sizing material；
（3）First glass bead, white cement, useless porcelain powder, bentonite, aerosil and barium sulfate are well mixed, ball is placed in
Ball milling 2.5 hours in grinding machine, then be placed in high speed dispersor, sequentially add step（2）Obtained sizing material, ultra-violet absorber,
Anti-crack water-proof agent, anti-crack water-proof agent, anti-accumulation of salt in the surface soil agent, inorganic antiseptic, tackifier are scattered 2.8 hours at a high speed, and the ceramic tile is made
Gap filler.
Wherein, the step（3）The speed of high speed dispersion machine is 1150r/min..
The specific embodiment of the present invention is described above.It is to be appreciated that the invention is not limited in above-mentioned
Particular implementation, those skilled in the art can make various deformations or amendments within the scope of the claims, this not shadow
Ring the substantive content of the present invention.
Claims (8)
1. a kind of tile grout, it is characterised in that include the raw material of following parts by weight：15~25 parts of glass bead, acrylic acid
16~20 parts of Lipase absobed resin, 17~28 parts of white cement, useless 10~20 parts of porcelain powder, 8~16 parts of bentonite, aerosil 5
~11 parts, 2~3 parts of redispersible latex powder, 3~6 parts of barium sulfate, 1~2 part of ultra-violet absorber, lignin fibre 2.5
~3.5 parts, 0.5~1 part of cellulose, 0.3~0.7 part of initiator, 1~2 part of anti-crack water-proof agent, 0.06~1.3 part of anti-accumulation of salt in the surface soil agent,
2~4 parts of inorganic antiseptic, 2.7~3.8 parts of tackifier.
2. tile grout according to claim 1, it is characterised in that include the raw material of following parts by weight：Glass bead
18~22 parts, 17~18 parts of acrylate synthetic resin, 22~26 parts of white cement, useless 13~19 parts of porcelain powder, bentonite 12~15
Part, 7~9 parts of aerosil, 2.2~2.8 parts of redispersible latex powder, 3.7~4.3 parts of barium sulfate, ultraviolet radiation absorption
1.2~1.7 parts of agent, 2.8~3.3 parts of lignin fibre, 0.7~0.9 part of cellulose, 0.4~0.6 part of initiator, anti-cracking waterproof
1.2~1.8 parts of agent, 0.3~0.9 part of anti-accumulation of salt in the surface soil agent, 2.5~3.7 parts of inorganic antiseptic, 3.1~3.6 parts of tackifier.
3. tile grout according to claim 1, it is characterised in that include the raw material of following parts by weight：Glass bead
20 parts, 17.8 parts of acrylate synthetic resin, 24 parts of white cement, useless 15 parts of porcelain powder, 14 parts of bentonite, 8 parts of aerosil,
2.6 parts of redispersible latex powder, 3.9 parts of barium sulfate, 1.4 parts of ultra-violet absorber, 3.2 parts of lignin fibre, cellulose
0.8 part, 0.5 part of initiator, 1.3 parts of anti-crack water-proof agent, 0.7 part of anti-accumulation of salt in the surface soil agent, 2.8 parts of inorganic antiseptic, 3.4 parts of tackifier.
4. tile grout according to claim 1, it is characterised in that described tackifier are anilinomethyl triethoxy
Silane.
5. tile grout according to claim 1, it is characterised in that the cellulose is selected from hydroxyethyl cellulose, hydroxyl
At least one of ethylmethylcellulose, hydroxypropyl methyl cellulose.
6. tile grout according to claim 1, it is characterised in that the inorganic antiseptic is carried with hydroxy-apatite masonry
Body, the percentage by weight that silver, zinc and copper make each composition in antimicrobial component, inorganic antiseptic is：Hydroxyapatite is that 93%, silver is
1%th, zinc is that 5%, copper is 1%.
7. a kind of method for preparing any one of claim 1~6 tile grout, it is characterised in that comprise the following steps：
（1）Glass bead, acrylate synthetic resin, white cement, useless porcelain powder, bentonite, gas phase dioxy are weighed by above-mentioned formula
SiClx, redispersible latex powder, barium sulfate, ultra-violet absorber, lignin fibre, cellulose, initiator, anti-cracking waterproof
Agent, anti-accumulation of salt in the surface soil agent, inorganic antiseptic, tackifier, it is standby；
（2）Acrylate synthetic resin is placed in kneader, redispersible latex powder, initiator, lignin fibre is added
And cellulose, 70~80 DEG C are heated to, mediates 20~40 minutes, obtains sizing material；
（3）First glass bead, white cement, useless porcelain powder, bentonite, aerosil and barium sulfate are well mixed, ball is placed in
Ball milling 2~3 hours in grinding machine, then be placed in high speed dispersor, sequentially add step（2）Obtained sizing material, ultra-violet absorber,
Anti-crack water-proof agent, anti-crack water-proof agent, anti-accumulation of salt in the surface soil agent, inorganic antiseptic, tackifier are scattered 2~3 hours at a high speed, and the ceramic tile is made
Gap filler.
8. preparation method according to claim 7, it is characterised in that the step（3）The speed of high speed dispersion machine is
1000~1200r/min.