CN107099177A - A kind of water-repellent paint - Google Patents

A kind of water-repellent paint Download PDF

Info

Publication number
CN107099177A
CN107099177A CN201710489610.6A CN201710489610A CN107099177A CN 107099177 A CN107099177 A CN 107099177A CN 201710489610 A CN201710489610 A CN 201710489610A CN 107099177 A CN107099177 A CN 107099177A
Authority
CN
China
Prior art keywords
parts
water
paraffin
repellent paint
weight
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201710489610.6A
Other languages
Chinese (zh)
Inventor
车国宝
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201710489610.6A priority Critical patent/CN107099177A/en
Publication of CN107099177A publication Critical patent/CN107099177A/en
Pending legal-status Critical Current

Abstract

A kind of water-repellent paint, it is characterized in that, its parts by weight is made up of following components, 12 parts of polyvinyl alcohol, 8 parts of calcined kaolin, vulcanize 5 parts of silica gel, 8 parts of sodium metasilicate, 15 parts of acrylic acid, 6 parts of sodium hydroxide, 10 parts of potassium chlorate, 3 parts of polyurethane, 2 parts of polyureas, 5 parts of hydrophobic nano-silica, 3 parts of hydrophobicity paraffin, 30 parts of water, with good shock resistance fatigue effect, the present invention can be used as extreme weather prone areas external wall waterproof materials'use, with good mobility, it can penetrate among the interior layer gap of material, make the water resistance of material better.

Description

A kind of water-repellent paint
Technical field
The invention belongs to field of material technology, more particularly to a kind of water-repellent paint.
Background technology
Water-repellent paint is mainly used in water-impervious.Water-repellent paint in the market simple agitation is added water using emulsion mostly and Into after the water-repellent paint is coated on ground, the film of formation was both opaque, and film is very thin, is unfavorable for water-repellent paint and plays The effect of water-impervious, in addition, the material therefor of existing water-repellent paint often polarises, it is impossible to meet use ring changeable now Border, therefore a kind of pollution-free, applied widely, high response type water-repellent paint exploitation is necessary.
The content of the invention
To solve the deficiencies in the prior art, have it is an object of the invention to provide one kind, production technology simplicity is pollution-free, The water-repellent paint of applied widely, high response type.
In order to realize above-mentioned target, the present invention is adopted the following technical scheme that:
A kind of water-repellent paint, it is characterised in that its parts by weight is made up of following components, 10 ~ 15 parts of polyvinyl alcohol, calcined kaolin 8 ~ 12 parts, 5 ~ 10 parts of silica gel of vulcanization, 5 ~ 10 parts of sodium metasilicate, 15 ~ 20 parts of acrylic acid, 6 ~ 8 parts of sodium hydroxide, 9 ~ 12 parts of potassium chlorate, 3 ~ 5 parts of polyurethane, 2 ~ 3 parts of polyureas, 5 ~ 10 parts of hydrophobic nano-silica, 3 ~ 5 parts of hydrophobicity paraffin, 30 ~ 45 parts of water.
As a preference of the present invention, calcination kleit preparation method is as follows:Kaolin starting material is taken to be calcined, calcining temperature Degree is 4.2 DEG C/min from 500 DEG C of linear temperature increases to 750 DEG C of heating rates, is then calcined again at 750 DEG C 1 hour, the mistake of calcining Oxygen concentration in journey in combustion chamber is maintained at 50% state, after the completion of calcining under vacuum conditions, is discharged after natural cooling, Kaolin is finally stirred into the powder that particle mean size is less than 350 nanometers.
As a preference of the present invention, the stir speed (S.S.) of the mixer is 400r/min, mixing time is 6 hours.
As a preference of the present invention, the preparation method of the hydrophobicity paraffin is as follows:The paraffin of 1 parts by weight is taken to be added to 8 Among the acetone of parts by weight, it is heated to 55 DEG C and stirs 45min using mixing speed as 200r/min stir speed (S.S.), form paraffin Solution, the stir speed (S.S.) that then 3 parts of deionized water is added among paraffin solution and using mixing speed as 600r/min is stirred Mix 30min.
As present invention further optimization, parts by weight are made up of following components, 12 parts of polyvinyl alcohol, calcined kaolin 8 Part, 5 parts of silica gel of vulcanization, 8 parts of sodium metasilicate, 15 parts of acrylic acid, 6 parts of sodium hydroxide, 10 parts of potassium chlorate, 3 parts of polyurethane, 2 parts of polyureas, 5 parts of hydrophobic nano-silica, 3 parts of hydrophobicity paraffin, 30 parts of water.
Beneficial effect:
(1)With good shock resistance fatigue effect, extreme weather prone areas external wall waterproof materials'use can be used as;
(2)It with good mobility, can penetrate among the interior layer gap of material, make the water resistance of material better.
Embodiment
Make specific introduce to the present invention below in conjunction with specific embodiment.
A kind of water-repellent paint, it is characterised in that its parts by weight is made up of following components, 10 ~ 15 parts of polyvinyl alcohol, calcining is high 8 ~ 12 parts of ridge soil, vulcanizes 5 ~ 10 parts of silica gel, 5 ~ 10 parts of sodium metasilicate, 15 ~ 20 parts of acrylic acid, 6 ~ 8 parts of sodium hydroxide, potassium chlorate 9 ~ 12 Part, 3 ~ 5 parts of polyurethane, 2 ~ 3 parts of polyureas, 5 ~ 10 parts of hydrophobic nano-silica, 3 ~ 5 parts of hydrophobicity paraffin, 30 ~ 45 parts of water.
Calcination kleit preparation method is as follows:Kaolin starting material is taken to be calcined, calcining heat is from 500 DEG C of linear temperature increases It is 4.2 DEG C/min to 750 DEG C of heating rates, is then calcined again at 750 DEG C 1 hour, the oxygen during calcining in combustion chamber Gas concentration is maintained at 50% state, after the completion of calcining under vacuum conditions, discharges, finally stirs kaolin after natural cooling Into the powder that particle mean size is less than 350 nanometers.
The stir speed (S.S.) of mixer is 400r/min in the present embodiment, and mixing time is 6 hours.
The preparation method of hydrophobicity paraffin is as follows:Take the paraffin of 1 parts by weight to be added among the acetone of 8 parts by weight, heat Stir 45min as 200r/min stir speed (S.S.) to 55 DEG C and using mixing speed, form paraffin solution, then by 3 parts go from Sub- water is added among paraffin solution and stirs 30min using mixing speed as 600r/min stir speed (S.S.).
Hydrophobic nano-silica is known to those skilled in the art, and it has very strong hydrophobicity.Hydrophobicity is received The preparation method of rice silica is beneficial to well known to technical staff for this, preparation side of the present invention to hydrophobic nano-silica Method is not particularly limited, can be with hydrophobic nano-silica preparation method known to those skilled in the art, the present invention Preferably supercritical drying prepares hydrophobic nano-silica, i.e., first by tetraethyl orthosilicate, absolute ethyl alcohol, formamide, Deionized water, hydrochloric acid(1mol/L)Mix, reacted 30 minutes under rapid mixing conditions, solution is by mixing by certain mol ratio It is turbid to be changed into limpid transparent;Then with the pH value of appropriate weak aqua ammonia (0.05mol/L) regulation solution to about 5~6, and quickly Stirring is allowed to well mixed;Mixed liquor is fallen into people into beaker again, sealing is rearmounted to make its gelation at room temperature, adds anhydrous second Alcohol carries out ageing 24 hours;One dimethyldichlorosilane of surface modifier/hexamethylene is added, at room temperature reaction a period of time, Make its hydroxyl reaction with the aeroge surface after aging, substituted hydroxy group;Displaced again with absolute ethyl alcohol remaining in product Solvent;Finally it is placed in supercritical CO 2 extraction device, 10~20MPa, 30 DEG C are dried and obtain product.
In the present embodiment, parts by weight are made up of following components, 12 parts of polyvinyl alcohol, 8 parts of calcined kaolin, vulcanize silica gel 5 Part, 8 parts of sodium metasilicate, 15 parts of acrylic acid, 6 parts of sodium hydroxide, 10 parts of potassium chlorate, 3 parts of polyurethane, 2 parts of polyureas, hydrophobic nano two 5 parts of silica, 3 parts of hydrophobicity paraffin, 30 parts of water.

Claims (5)

1. a kind of water-repellent paint, it is characterised in that its parts by weight is made up of following components, 10 ~ 15 parts of polyvinyl alcohol, calcine kaolinite 8 ~ 12 parts of soil, vulcanizes 5 ~ 10 parts of silica gel, 5 ~ 10 parts of sodium metasilicate, 15 ~ 20 parts of acrylic acid, 6 ~ 8 parts of sodium hydroxide, potassium chlorate 9 ~ 12 Part, 3 ~ 5 parts of polyurethane, 2 ~ 3 parts of polyureas, 5 ~ 10 parts of hydrophobic nano-silica, 3 ~ 5 parts of hydrophobicity paraffin, 30 ~ 45 parts of water.
2. a kind of water-repellent paint according to claim 1, it is characterised in that calcination kleit preparation method is as follows:Take Kaolin starting material is calcined, and calcining heat is 4.2 DEG C/min, Ran Hou from 500 DEG C of linear temperature increases to 750 DEG C of heating rates Calcined again at 750 DEG C 1 hour, the oxygen concentration during calcining in combustion chamber is maintained at 50% state, after the completion of calcining Under vacuum environment, discharged after natural cooling, kaolin is finally stirred into the powder that particle mean size is less than 350 nanometers.
3. a kind of water-repellent paint according to claim 2, it is characterised in that the stir speed (S.S.) of the mixer is 400r/ Min, mixing time is 6 ~ 8 hours.
4. a kind of water-repellent paint according to claim 1, it is characterised in that the preparation method of the hydrophobicity paraffin is such as Under:Take the paraffin of 1 parts by weight to be added among the acetone of 8 parts by weight, be heated to 55 DEG C and using mixing speed as 200r/min's Stir speed (S.S.) stirs 45min, forms paraffin solution, and then 3 parts of deionized water is added among paraffin solution and to stir Speed stirs 30min for 600r/min stir speed (S.S.).
5. a kind of method of producing waterproof coating material according to claim 1, it is characterised in that parts by weight have following components group Into 12 parts of polyvinyl alcohol, 8 parts of calcined kaolin vulcanizes 5 parts of silica gel, 8 parts of sodium metasilicate, 15 parts of acrylic acid, 6 parts of sodium hydroxide, chlorine Sour 10 parts of potassium, 3 parts of polyurethane, 2 parts of polyureas, 5 parts of hydrophobic nano-silica, 3 parts of hydrophobicity paraffin, 30 parts of water.
CN201710489610.6A 2017-06-24 2017-06-24 A kind of water-repellent paint Pending CN107099177A (en)