CN107097551A - A kind of environmental friendly heat transfer printing carbon tape and preparation method thereof - Google Patents

A kind of environmental friendly heat transfer printing carbon tape and preparation method thereof Download PDF

Info

Publication number
CN107097551A
CN107097551A CN201710306608.0A CN201710306608A CN107097551A CN 107097551 A CN107097551 A CN 107097551A CN 201710306608 A CN201710306608 A CN 201710306608A CN 107097551 A CN107097551 A CN 107097551A
Authority
CN
China
Prior art keywords
layer
tape base
water
release layer
tape
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201710306608.0A
Other languages
Chinese (zh)
Inventor
郑言
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Peng Code New Materials (anhui) Co Ltd
Original Assignee
Peng Code New Materials (anhui) Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Peng Code New Materials (anhui) Co Ltd filed Critical Peng Code New Materials (anhui) Co Ltd
Priority to CN201710306608.0A priority Critical patent/CN107097551A/en
Publication of CN107097551A publication Critical patent/CN107097551A/en
Pending legal-status Critical Current

Abstract

The invention discloses a kind of environmental friendly heat transfer printing carbon tape and preparation method thereof, including tape base, it is coated in the refractory layer of tape base side, is coated in the release layer of tape base opposite side and the ink layer being coated on the outside of release layer, the refractory layer is made up of the raw material below according to mass fraction：Water 40 44%, polyester resin 20 26%, polyimide resin 16 24%；The release layer is made up of the raw material below according to mass fraction：Water 62 70%, acrylic resin 12 15%, emulsifiable polyethylene wax 3 6%, emulsification polypropylene wax 5 8%；The ink layer is made up of the raw material below according to mass fraction：Water 45 50%, polyester resin 12 17%, note alkene phenol resin 5 8%, carbon black 6 8%, auxiliary agent 1 2%.

Description

A kind of environmental friendly heat transfer printing carbon tape and preparation method thereof
Technical field
The present invention relates to heat transfer printing carbon tape technical field, more particularly to a kind of environmental friendly heat transfer printing carbon tape and its preparation side Method.
Background technology
Heat transfer colour ribbon of the prior art is solvent-based system, during coating is dried, a large amount of organic solvents Volatilization, both improves production cost, causes significant wastage, it is often more important that the volatilization of the organic solvent such as substantial amounts of toluene, butanone Pole fire hazardous, poisonous organic solvent is evaporate into the environment of printing ink to manufacture and carbon ribbon production, causes operating environment severe, Workers ' health is damaged, air environmental pollution is caused, does not meet environmental requirement, therefore, a kind of it is proposed that environmental friendly heat transfer printing carbon Band and preparation method thereof.
The content of the invention
To solve the defect of prior art, the invention discloses a kind of environmental friendly heat transfer printing carbon tape and preparation method thereof And preparation method thereof.
The invention discloses a kind of environmental friendly heat transfer printing carbon tape, including tape base, the refractory layer for being coated in tape base side, coating In the release layer and the ink layer that is coated on the outside of release layer of tape base opposite side, the refractory layer is by below according to mass fraction Raw material composition：Water 40-44%, polyester resin 20-26%, polyimide resin 16-24%；The release layer is by below according to matter Measure the raw material composition of fraction：Water 62-70%, acrylic resin 12-15%, emulsifiable polyethylene wax 3-6%, emulsification polypropylene wax 5- 8%；The ink layer is made up of the raw material below according to mass fraction：Water 45-50%, polyester resin 12-17%, note alkene phenol resin 5-8%, carbon black 6-8%, auxiliary agent 1-2%.
It is preferred that, the material of the tape base is degradable fiber membrane, and the thickness of tape base is 6-8 μm.
A kind of preparation method of environmental friendly heat transfer printing carbon tape, its preparation method is as follows：
（1）Weigh in water, emulsifiable polyethylene wax, emulsification polypropylene wax, acrylic resin, input shearing equipment, shearing equipment liter Temperature is to 65-70 DEG C, under 2500-3000 revs/min of rotating speed, stirring mixing decentralized processing 0.3-0.5h, then slow cooling is extremely 26-30 DEG C, release layer mixed solution is obtained, it is standby；
（2）Carbon black is weighed, after crushing, 900-1000 mesh sieves is crossed, obtains powdered carbon black；
（3）Water, polyester resin, note alkene phenol resin, auxiliary agent are weighed, is added in mixed solvent, input shearing dispersing apparatus, Under 2000-2500 revs/min of rotating speed, decentralized processing 2-3h obtains ink layer mixed liquor, standby；
（4）Weigh in water, polyester resin, polyimide resin, input shearing equipment, decentralized processing 2-3h obtains refractory layer and applied Covering liquid, it is standby；
（5）Refractory layer coating liquid is coated uniformly on by tape base front using coating machine, after drying, forms heat-resisting in tape base front Layer；
（6）Release layer coating liquid is coated uniformly on by the tape base back side using coating machine, after drying, forms release at the tape base back side Layer；
（7）In the uniform coating oil layer of ink coating liquid of release layer surface, after drying, in release layer surface formation ink layer.
Beneficial effect is：The environmental friendly heat transfer printing carbon tape of the present invention uses tape base for fiber membrane, and itself can be certainly So degraded, does not result in environmental pollution, dissolves organic using aqueous solvent in the refractory layer, release layer, ink layer for preparing carbon ribbon Dicyandiamide solution, instead of the use of the toxic solvents such as toluene, butanone, is conducive to environmental protection, it is ensured that operating personnel is healthy.
Embodiment
Embodiment 1
A kind of environmental friendly heat transfer printing carbon tape, including tape base, be coated in the refractory layer of tape base side, be coated in tape base opposite side from Type layer and the ink layer being coated on the outside of release layer, the refractory layer are made up of the raw material below according to mass fraction：Water 40%th, polyester resin 20%, polyimide resin 16%；The release layer is made up of the raw material below according to mass fraction：Water 62%th, acrylic resin 12%, emulsifiable polyethylene wax 3%, emulsification polypropylene wax 5%；The ink layer is by below according to mass fraction Raw material composition：Water 45%, polyester resin 12%, note alkene phenol resin 5%, carbon black 6%, auxiliary agent 1%.
It is preferred that, the material of the tape base is degradable fiber membrane, and the thickness of tape base is 6 μm.
A kind of preparation method of environmental friendly heat transfer printing carbon tape, its preparation method is as follows：
（1）Weigh in water, emulsifiable polyethylene wax, emulsification polypropylene wax, acrylic resin, input shearing equipment, shearing equipment liter Temperature is to 65 DEG C, under 2500 revs/min of rotating speed, stirring mixing decentralized processing 0.3h, then slow cooling is to 26 DEG C, obtains release Layer mixed solution, it is standby；
（2）Carbon black is weighed, after crushing, 900 mesh sieves is crossed, obtains powdered carbon black；
（3）Water, polyester resin, note alkene phenol resin, auxiliary agent are weighed, is added in mixed solvent, input shearing dispersing apparatus, 2000 Rev/min rotating speed under, decentralized processing 2h, obtain ink layer mixed liquor, it is standby；
（4）Weigh in water, polyester resin, polyimide resin, input shearing equipment, decentralized processing 2h obtains refractory layer coating Liquid, it is standby；
（5）Refractory layer coating liquid is coated uniformly on by tape base front using coating machine, after drying, forms heat-resisting in tape base front Layer；
（6）Release layer coating liquid is coated uniformly on by the tape base back side using coating machine, after drying, forms release at the tape base back side Layer；
（7）In the uniform coating oil layer of ink coating liquid of release layer surface, after drying, in release layer surface formation ink layer.
Embodiment 2
A kind of environmental friendly heat transfer printing carbon tape, including tape base, be coated in the refractory layer of tape base side, be coated in tape base opposite side from Type layer and the ink layer being coated on the outside of release layer, the refractory layer are made up of the raw material below according to mass fraction：Water 42%th, polyester resin 23%, polyimide resin 20%；The release layer is made up of the raw material below according to mass fraction：Water 66%th, acrylic resin 13.5%, emulsifiable polyethylene wax 4.5%, emulsification polypropylene wax 6.5%；The ink layer is by below according to matter Measure the raw material composition of fraction：Water 47.5%, polyester resin 14.5%, note alkene phenol resin 6.5%, carbon black 7%, auxiliary agent 1.5%.
It is preferred that, the material of the tape base is degradable fiber membrane, and the thickness of tape base is 7 μm.
A kind of preparation method of environmental friendly heat transfer printing carbon tape, its preparation method is as follows：
（1）Weigh in water, emulsifiable polyethylene wax, emulsification polypropylene wax, acrylic resin, input shearing equipment, shearing equipment liter Temperature is to 67 DEG C, under 2750 revs/min of rotating speed, stirring mixing decentralized processing 0.4h, then slow cooling is to 28 DEG C, obtains release Layer mixed solution, it is standby；
（2）Carbon black is weighed, after crushing, 950 mesh sieves is crossed, obtains powdered carbon black；
（3）Water, polyester resin, note alkene phenol resin, auxiliary agent are weighed, is added in mixed solvent, input shearing dispersing apparatus, 2250 Rev/min rotating speed under, decentralized processing 2.5h, obtain ink layer mixed liquor, it is standby；
（4）Weigh in water, polyester resin, polyimide resin, input shearing equipment, decentralized processing 2.5h obtains refractory layer and applied Covering liquid, it is standby；
（5）Refractory layer coating liquid is coated uniformly on by tape base front using coating machine, after drying, forms heat-resisting in tape base front Layer；
（6）Release layer coating liquid is coated uniformly on by the tape base back side using coating machine, after drying, forms release at the tape base back side Layer；
（7）In the uniform coating oil layer of ink coating liquid of release layer surface, after drying, in release layer surface formation ink layer.
Embodiment 3
A kind of environmental friendly heat transfer printing carbon tape, including tape base, be coated in the refractory layer of tape base side, be coated in tape base opposite side from Type layer and the ink layer being coated on the outside of release layer, the refractory layer are made up of the raw material below according to mass fraction：Water 44%th, polyester resin 26%, polyimide resin 24%；The release layer is made up of the raw material below according to mass fraction：Water 70%th, acrylic resin 15%, emulsifiable polyethylene wax 6%, emulsification polypropylene wax 8%；The ink layer is by below according to mass fraction Raw material composition：Water 50%, polyester resin 17%, note alkene phenol resin 8%, carbon black 8%, auxiliary agent 2%.
It is preferred that, the material of the tape base is degradable fiber membrane, and the thickness of tape base is 8 μm.
A kind of preparation method of environmental friendly heat transfer printing carbon tape, its preparation method is as follows：
（1）Weigh in water, emulsifiable polyethylene wax, emulsification polypropylene wax, acrylic resin, input shearing equipment, shearing equipment liter Temperature is to 70 DEG C, under 3000 revs/min of rotating speed, stirring mixing decentralized processing 0.5h, then slow cooling is to 30 DEG C, obtains release Layer mixed solution, it is standby；
（2）Carbon black is weighed, after crushing, 1000 mesh sieves is crossed, obtains powdered carbon black；
（3）Water, polyester resin, note alkene phenol resin, auxiliary agent are weighed, is added in mixed solvent, input shearing dispersing apparatus, 2500 Rev/min rotating speed under, decentralized processing 3h, obtain ink layer mixed liquor, it is standby；
（4）Weigh in water, polyester resin, polyimide resin, input shearing equipment, decentralized processing 3h obtains refractory layer coating Liquid, it is standby；
（5）Refractory layer coating liquid is coated uniformly on by tape base front using coating machine, after drying, forms heat-resisting in tape base front Layer；
（6）Release layer coating liquid is coated uniformly on by the tape base back side using coating machine, after drying, forms release at the tape base back side Layer；
（7）In the uniform coating oil layer of ink coating liquid of release layer surface, after drying, in release layer surface formation ink layer.
Finally it should be noted that：Above example only not limits technology described in the invention to illustrate the present invention Scheme；Therefore, although this specification with reference to each above-mentioned embodiment to present invention has been detailed description, this Field it is to be appreciated by one skilled in the art that still can be modified to the present invention or equivalent substitution；And all do not depart from this The technical scheme of the spirit and scope of invention and its improvement, it all should cover in scope of the presently claimed invention.

Claims (3)

1. a kind of environmental friendly heat transfer printing carbon tape, it is characterised in that：Including tape base, it is coated in the refractory layer of tape base side, is coated in The release layer of tape base opposite side and the ink layer being coated on the outside of release layer, the refractory layer is by below according to mass fraction Raw material is constituted：Water 40-44%, polyester resin 20-26%, polyimide resin 16-24%；The release layer is by below according to quality The raw material composition of fraction：Water 62-70%, acrylic resin 12-15%, emulsifiable polyethylene wax 3-6%, emulsification polypropylene wax 5-8%； The ink layer is made up of the raw material below according to mass fraction：Water 45-50%, polyester resin 12-17%, note alkene phenol resin 5- 8%th, carbon black 6-8%, auxiliary agent 1-2%.
2. a kind of printing label surface water resistance heat transfer printing carbon tape according to claim 1, it is characterised in that：The tape base Material be degradable fiber membrane, and tape base thickness be 6-8 μm.
3. a kind of preparation method of environmental friendly heat transfer printing carbon tape, its preparation method is as follows：
（1）Weigh in water, emulsifiable polyethylene wax, emulsification polypropylene wax, acrylic resin, input shearing equipment, shearing equipment liter Temperature is to 65-70 DEG C, under 2500-3000 revs/min of rotating speed, stirring mixing decentralized processing 0.3-0.5h, then slow cooling is extremely 26-30 DEG C, release layer mixed solution is obtained, it is standby；
（2）Carbon black is weighed, after crushing, 900-1000 mesh sieves is crossed, obtains powdered carbon black；
（3）Water, polyester resin, note alkene phenol resin, auxiliary agent are weighed, is added in mixed solvent, input shearing dispersing apparatus, Under 2000-2500 revs/min of rotating speed, decentralized processing 2-3h obtains ink layer mixed liquor, standby；
（4）Weigh in water, polyester resin, polyimide resin, input shearing equipment, decentralized processing 2-3h obtains refractory layer and applied Covering liquid, it is standby；
（5）Refractory layer coating liquid is coated uniformly on by tape base front using coating machine, after drying, forms heat-resisting in tape base front Layer；
（6）Release layer coating liquid is coated uniformly on by the tape base back side using coating machine, after drying, forms release at the tape base back side Layer；
（7）In the uniform coating oil layer of ink coating liquid of release layer surface, after drying, in release layer surface formation ink layer.
CN201710306608.0A 2017-05-04 2017-05-04 A kind of environmental friendly heat transfer printing carbon tape and preparation method thereof Pending CN107097551A (en)