CN104387857A - Environment-friendly nano paint and preparation method thereof - Google Patents
Environment-friendly nano paint and preparation method thereof Download PDFInfo
- Publication number
- CN104387857A CN104387857A CN201410621257.9A CN201410621257A CN104387857A CN 104387857 A CN104387857 A CN 104387857A CN 201410621257 A CN201410621257 A CN 201410621257A CN 104387857 A CN104387857 A CN 104387857A
- Authority
- CN
- China
- Prior art keywords
- parts
- paint
- raw material
- environment
- defoamer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides an environment-friendly nano paint, relating to the technical field of paint preparation. The environment-friendly nano paint is prepared from the following raw materials in parts by weight: 280-300 parts of water, 4-6 parts of dispersing agent, 0.5-1.5 parts of defoaming agent, 95-105 parts of titanium white, 90-100 parts of mineral, 190-200 parts of porous powder quartz, 280-300 parts of styrene-acrylic emulsion, 5-15 parts of color paste, 4-8 parts of hydroxyethyl cellulose and 10-20 parts of film-forming assistant. The production method has the advantages of convenient and simple preparation process, environmental protection, no pollution, accessible raw materials and low equipment investment, and is convenient for operation; and the prepared nano paint has the advantages of high purity, favorable use effect and high safety and reliability.
Description
Technical field
The present invention relates to technical field of paint preparation, be specifically related to a kind of environment protective nano-paint and preparation method thereof.
Background technology
Nanometer product is with after high-tech implication, it must match with corresponding nanotechnology, after nano level material is added simply, it is nanometer product that the product that performance does not significantly improve is not really, someone says, nano paint is called nano composite dope is more suitable, the one of coating inherently matrix material, therefore, be not that the coating that with the addition of nano material just can be referred to as nano paint, nano paint not only will put on display the paint of " insipidness ", show the advanced technologies of non-toxic coatings, also will put on display high in technological content nano paint.This high-tech nano paint is not only nontoxic, a kind of material can also be slowly released, objectionable impurities such as degraded indoor formaldehyde, dimethylbenzene etc., the nano paint existed on the market is at present in the preparation of reality, it is allotted and method all relatively tradition, proportioning is unreasonable, and preparation technology is also relatively loaded down with trivial details, can not meet the requirement of throughput rate.
Summary of the invention
It is high that technical problem to be solved by this invention is to provide a kind of purity, simple environment protective nano-paint of preparation technology and preparation method thereof.
Technical problem to be solved by this invention realizes by the following technical solutions:
A kind of environment protective nano-paint, is characterized in that: the raw material composition comprising following weight part,
Water 280-300 part, dispersion agent 4-6 part, defoamer 0.5-1.5 part, titanium dioxide 95-105 part, mineral substance 90-100 part, periporate quartz 190-200 part, benzene emulsion 280-300 part, mill base 5-15 part, Natvosol 4-8 part, film coalescence aid 10-20 part.
Preferred weight part of each raw material is: 195 parts, 290 parts, water, dispersion agent 5 parts, defoamer 1 part, titanium dioxide 100 parts, 95 parts, mineral substance, periporate quartz, benzene emulsion 290 parts, mill base 10 parts, Natvosol 6 parts, film coalescence aid 15 parts.
Described dispersion agent is stearylamide, and described defoamer is silicone oil, and described mineral substance is calcite.
Another object of the present invention prepares the method for environment protective nano-paint in the present invention, it is characterized in that: comprise the following steps:
A, select one with the reactor of agitator, the mixing of water, dispersion agent and defoamer is dropped into wherein, under the rotating speed of 3000r/min, stirs.
B, after step a stirs, feed liquid to 35 ~ 45 DEG C of heating, then add wherein by the titanium dioxide in raw material, mineral substance and periporate quartz, Keep agitation, until internal particle dissolves completely.
C, until step b dissolve after, the benzene emulsion in raw material, mill base, Natvosol and film coalescence aid are all added wherein, after stirring, cooling, filter, encapsulation after be desired product.
The invention has the beneficial effects as follows: the present invention is simply easy to prepare, environment friendly and pollution-free, raw material is easy to get, and facility investment is few, and purity is high, convenient operation, and the nano paint result of use of preparation is good, safe and reliable.
Embodiment
The technique means realized to make the present invention, creation characteristic, reaching object and effect is easy to understand, below in conjunction with specific embodiment, setting forth the present invention further.
Embodiment 1
A kind of environment protective nano-paint, comprises the raw material composition of following weight part,
Water 280kg, stearylamide 4kg, silicone oil 0.5kg, titanium dioxide 95kg, calcite 90kg, periporate quartz 190kg, benzene emulsion 280kg, mill base 5kg, Natvosol 4kg, film coalescence aid 10kg.
Another object of the present invention prepares the method for environment protective nano-paint in the present invention, comprises the following steps:
A, select one with the reactor of agitator, the mixing of water, stearylamide and silicone oil is dropped into wherein, under the rotating speed of 3000r/min, stirs.
B, after step a stirs, feed liquid to 35 ~ 45 DEG C of heating, then add wherein by the titanium dioxide in raw material, calcite and periporate quartz, Keep agitation, until internal particle dissolves completely.
C, until step b dissolve after, the benzene emulsion in raw material, mill base, Natvosol and film coalescence aid are all added wherein, after stirring, cooling, filter, encapsulation after be desired product.
Embodiment 2
A kind of environment protective nano-paint, comprises the raw material composition of following weight part,
Water 290kg, stearylamide 5kg, silicone oil 1kg, titanium dioxide 100kg, calcite 95kg, periporate quartz 195kg, benzene emulsion 290kg, mill base 10kg, Natvosol 6kg, film coalescence aid 15kg.
Another object of the present invention prepares the method for environment protective nano-paint in the present invention, comprises the following steps:
A, select one with the reactor of agitator, the mixing of water, stearylamide and silicone oil is dropped into wherein, under the rotating speed of 3000r/min, stirs.
B, after step a stirs, feed liquid to 35 ~ 45 DEG C of heating, then add wherein by the titanium dioxide in raw material, calcite and periporate quartz, Keep agitation, until internal particle dissolves completely.
C, until step b dissolve after, the benzene emulsion in raw material, mill base, Natvosol and film coalescence aid are all added wherein, after stirring, cooling, filter, encapsulation after be desired product.
More than show and describe ultimate principle of the present invention and principal character and advantage of the present invention.The technician of the industry should understand; the present invention is not restricted to the described embodiments; what describe in above-described embodiment and specification sheets just illustrates principle of the present invention; without departing from the spirit and scope of the present invention; the present invention also has various changes and modifications, and these changes and improvements all fall in the claimed scope of the invention.Application claims protection domain is defined by appending claims and equivalent thereof.
Claims (4)
1. an environment protective nano-paint, is characterized in that: the raw material composition comprising following weight part,
Water 280-300 part, dispersion agent 4-6 part, defoamer 0.5-1.5 part, titanium dioxide 95-105 part, mineral substance 90-100 part, periporate quartz 190-200 part, benzene emulsion 280-300 part, mill base 5-15 part, Natvosol 4-8 part, film coalescence aid 10-20 part.
2. a kind of environment protective nano-paint according to claim 1, is characterized in that: preferred weight part of each raw material is: 195 parts, 290 parts, water, dispersion agent 5 parts, defoamer 1 part, titanium dioxide 100 parts, 95 parts, mineral substance, periporate quartz, benzene emulsion 290 parts, mill base 10 parts, Natvosol 6 parts, film coalescence aid 15 parts.
3. a kind of environment protective nano-paint according to claim 1, is characterized in that: described dispersion agent is stearylamide, and described defoamer is silicone oil, and described mineral substance is calcite.
4. the method for a kind of environment protective nano-paint of preparation described in claim 1 or 2, is characterized in that, comprise the following steps:
A, select one with the reactor of agitator, the mixing of water, dispersion agent and defoamer is dropped into wherein, under the rotating speed of 3000r/min, stirs.
B, after step a stirs, feed liquid to 35 ~ 45 DEG C of heating, then add wherein by the titanium dioxide in raw material, mineral substance and periporate quartz, Keep agitation, until internal particle dissolves completely.
C, until step b dissolve after, the benzene emulsion in raw material, mill base, Natvosol and film coalescence aid are all added wherein, after stirring, cooling, filter, encapsulation after be desired product.