CN107083663A - 耐刮耐高温挂烫机喷头 - Google Patents
耐刮耐高温挂烫机喷头 Download PDFInfo
- Publication number
- CN107083663A CN107083663A CN201710209128.2A CN201710209128A CN107083663A CN 107083663 A CN107083663 A CN 107083663A CN 201710209128 A CN201710209128 A CN 201710209128A CN 107083663 A CN107083663 A CN 107083663A
- Authority
- CN
- China
- Prior art keywords
- scratch resistance
- parts
- high temperature
- ironing machine
- burner cap
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种耐刮耐高温挂烫机喷头，包括：喷头主体、防水耐高温保护涂层和耐刮隔热保护涂层，防水耐高温保护涂料包括以下重量份的原料：40‑100份重量份的环氧树脂、30‑80份重量份的聚苯醚、2‑30份重量份的纳米氧化铝空心球、5‑40份重量份的聚脲、1‑20份重量份的硅烷偶联剂、5‑40份重量份的第一相容剂、2‑20份重量份的第一分散剂、10‑50份重量份的第一溶剂、2‑40份重量份的加工助剂。本发明的耐刮耐高温挂烫机喷头，其防水和耐高温性能优越，能防止喷头内部的水蒸气腐蚀喷头主体，延长喷头的使用寿命；在喷头主体外壁上涂覆有耐刮隔热保护涂层，能防止对手持该喷头的使用者造成烫伤。
Description
技术领域
本发明涉及挂烫机设备领域，尤其是一种耐刮耐高温挂烫机喷头。
背景技术
挂烫机也叫挂式熨斗、立式烫斗，是能够对挂着衣服和布料进行烫熨的机器，挂烫机由蒸汽发生器、蒸汽软管和位于蒸汽软管前端的喷头组成。通电后蒸汽发生器将水蒸发产生蒸汽，蒸汽经蒸汽软管从喷头喷出，用户拿着喷头对衣物进行烫熨。由于喷头内的蒸汽温度很高，持续使用时，内部蒸汽的高温易传至喷头外壁使外壁发热烫手，不利于操作者使用；另外，现在的喷头内壁防水性能较差，内部的蒸汽易浸透至喷头内，而腐蚀损坏喷头，既影响喷头的美观，又会降低喷头的使用寿命；且现在的喷头外壁抗刮擦性能差、机械强度不够，表面以损坏或产生刮痕，极不美观，且使用寿命短。
发明内容
本发明所要解决的技术问题在于针对上述现有技术中的不足，提供一种耐刮耐高温挂烫机喷头。
为解决上述技术问题，本发明采用的技术方案是：一种耐刮耐高温挂烫机喷头，包括：喷头主体、涂覆在所述喷头主体内壁和外壁上的防水耐高温保护涂层和涂覆于所述喷头主体外壁上的防水耐高温保护涂层上的耐刮隔热保护涂层；所述防水耐高温保护涂层通过刷涂防水耐高温保护涂料后，再经干燥制得；所述耐刮隔热保护涂层通过刷涂耐刮隔热保护涂料后，再经干燥制得；
所述防水耐高温保护涂料包括以下重量份的原料：
优选的是，所述耐刮隔热保护涂料包括以下重量份的原料：
优选的是，所述抗氧剂为二苯胺、对苯二胺、二氢喹啉、双十二碳醇酯、硫代二丙酸双酯、三辛酯、三癸酯中的一种或多种的混合物。
优选的是，所述第一相容剂为环状酸酐型相容剂、丙烯酸型相容剂、酰亚胺型相容剂、异氰酸酯型相容剂中的一种。
优选的是，所述第二相容剂均为环状酸酐型相容剂、丙烯酸型相容剂、酰亚胺型相容剂、异氰酸酯型相容剂中的一种。
优选的是，所述第一分散剂和第二分散剂均为硬脂酰胺、乙烯基双硬脂酰胺、三硬脂酸甘油酯、硬脂酸钡、乙烯－丙烯酸共聚物、聚乙烯蜡、聚乙二醇中的一种或多种的混合物。
优选的是，所述硅烷偶联剂为氨基丙基三乙氧基硅烷
优选的是，所述加工助剂包括润滑剂、固化剂、稳定剂。
优选的是，所述防水耐高温保护涂层的厚度为1-20mm。
优选的是，所述耐刮隔热保护涂层的厚度为0.5-10mm。
本发明的有益效果：本发明的耐刮耐高温挂烫机喷头在喷头主体内壁和外壁上均设置有防水耐高温保护涂层，能显著提高喷头主体内壁的防水和耐高温性能，能防止喷头内部的水蒸气腐蚀喷头主体，避免喷头内部的高温水蒸气对喷头主体造成损害，能延长喷头的使用寿命；在喷头主体外壁上的防水耐高温保护涂层上还涂覆有耐刮隔热保护涂层，能隔绝喷头内部高温蒸汽向外传导的热量，防止对手持该喷头的使用者造成烫伤；还能提高喷头外壁的耐刮擦性能和机械强度，防止能避免喷头在使用过程中因磕碰而损坏或是在喷头表面产生刮痕而影响喷头的美观，另外还能提高喷头主体表面的光滑度和光亮度，使喷头主体更为美观。
附图说明
图1为本发明的耐刮耐高温挂烫机喷头的结构示意图；
图2为本发明的喷头主体的喷头壁厚度方向的剖视图。
附图标记说明：
1—喷头主体；2—防水耐高温保护涂层；3—耐刮隔热保护涂层；4—喷孔。
具体实施方式
下面结合附图对本发明做进一步的详细说明，以令本领域技术人员参照说明书文字能够据以实施。
应当理解，本文所使用的诸如“具有”、“包含”以及“包括”术语并不配出一个或多个其它元件或其组合的存在或添加。
本实施例的一种耐刮耐高温挂烫机喷头，包括：喷头主体1、涂覆在喷头主体1内壁和外壁上的防水耐高温保护涂层2和涂覆于喷头主体1外壁上的防水耐高温保护涂层2上的耐刮隔热保护涂层3。所述防水耐高温保护涂层通过刷涂防水耐高温保护涂料后，再经干燥制得；所述耐刮隔热保护涂层通过刷涂耐刮隔热保护涂料后，再经干燥制得。
其中，喷头主体1内部中空，使用时喷头主体1与挂烫机相连，喷头主体1内部充满高温蒸汽，高温蒸汽从喷头主体1上设置的喷孔4喷出，对衣服进行熨烫。
防水耐高温保护涂料2包括以下重量份的原料：
其中，环氧树脂具有较高的机械强度和防水性能；聚苯醚具有较好的耐高温性能，其耐温温度能达到110℃左右，且具有高抗冲击韧性；纳米氧化铝空心球可又工业氧化铝制得，其能显著提高材料的耐高温性能；聚脲的添加能有效提高该防水耐高温保护涂层2的防水性能，防止挂烫机喷头内部的水蒸气对喷头主体1造成腐蚀。通过加环氧树脂、聚苯醚、纳米氧化铝空心球、聚脲及上述其他材料按比例复配制得的防水耐高温保护涂层2，其不仅具有很好的防水性能，防止喷头内部的水蒸气腐蚀喷头主体1，同时还具有很强的耐高温性能，能避免喷头内部的高温水蒸气对喷头主体1造成损害，能延长喷头的使用寿命。
耐刮隔热保护涂料3包括以下重量份的原料：
其中，聚烯烃弹性体具有很高的抗冲击性能；超细玻璃棉具有体质轻、导热系数低、热绝缘性能好、耐腐蚀、耐热的突出优点；纳米二氧化硅气凝胶能显著提高材料的隔热性能和抗拉及抗压强度，能提高喷头的强度和隔热性能；聚四氟乙烯能增强材料的光滑度和抗冲击性能；玻璃微珠即能增强材料的润滑性、增强喷头外壁表面的光滑度，又能增强材料的机械强度、提高喷头外壁的耐刮擦性能；滑石粉能增强喷头外壁表面的光滑度和光亮度，使喷头更加美观；芥酸酰胺能进一步提高材料的耐刮性能；纳米氧化锆粉能显著提高材料的机械强度，增强上述耐刮隔热保护涂层3的刚度，能提高耐刮隔热保护涂层3对喷头的保护效果。通过将聚烯烃弹性体、超细玻璃棉、纳米二氧化硅气凝胶、聚四氟乙烯、玻璃微珠、滑石粉、芥酸酰胺、纳米氧化锆粉和上述其他材料复配使用制得该耐刮隔热保护涂层3，其具有极好的隔热性能，能隔绝喷头内部高温蒸汽向外传导的热量，防止对手持该喷头的使用者造成烫伤；另外其还具有极高的耐刮擦性能，能避免喷头在使用过程中因磕碰而损坏或是在喷头表面产生刮痕而影响喷头的美观，且该耐刮隔热保护涂层3还具有很高的表面光滑度和光亮度，能提高喷头的美观效果。
其中，抗氧剂为二苯胺、对苯二胺、二氢喹啉、双十二碳醇酯、硫代二丙酸双酯、三辛酯、三癸酯中的一种或多种的混合物。第一溶剂、第二溶剂均可选用常用溶剂。第一相容剂为环状酸酐型相容剂、丙烯酸型相容剂、酰亚胺型相容剂、异氰酸酯型相容剂中的一种。第二相容剂均为环状酸酐型相容剂、丙烯酸型相容剂、酰亚胺型相容剂、异氰酸酯型相容剂中的一种。第一分散剂和第二分散剂均为硬脂酰胺、乙烯基双硬脂酰胺、三硬脂酸甘油酯、硬脂酸钡、乙烯－丙烯酸共聚物、聚乙烯蜡、聚乙二醇中的一种或多种的混合物。硅烷偶联剂为氨基丙基三乙氧基硅烷。加工助剂包括润滑剂、固化剂、稳定剂。防水耐高温保护涂层2的厚度为1-20mm。耐刮隔热保护涂层3的厚度为0.5-10mm。
以下给出本发明的耐刮耐高温挂烫机喷头的防水耐高温保护涂层的制备方法，其包括以下步骤：
1)将环氧树脂、聚苯醚、聚脲、第一溶剂置于密炼机中混炼20min，；
2)依次加入纳米氧化铝空心球、硅烷偶联剂、第一相容剂、第一分散剂和润滑剂，加热至温度为75℃后，混炼20min；
3)依次加入固化剂、稳定剂继续升温至85℃后，混炼30min后得到防水耐高温保护涂料；
4)将步骤3)得到的防水耐高温保护涂料涂覆于挂烫机喷头的外壁上，得到防水耐高温保护涂层。
以下再给出本发明的耐刮耐高温挂烫机喷头的耐刮隔热保护涂层的制备方法，其包括以下步骤：
1)将聚烯烃弹性体、超细玻璃棉、纳米二氧化硅气凝胶、聚四氟乙烯、第二溶剂置于密炼机中混炼30min，；
2)依次加入玻璃微珠、纳米氧化锆粉、第二相容剂，加热至温度为75℃后，混炼20min；
3)依次加入滑石粉、芥酸酰胺继续升温至85℃后，混炼15min；
4)依次加入第二分散剂、抗氧剂，保持稳定为65℃，混炼25min后得到耐刮隔热保护涂料；
5)将步骤4)得到的耐刮隔热保护涂料涂覆于挂烫机喷头外壁的防水耐高温保护涂层上，得到耐刮隔热保护涂层。
以下给出实施例，用以对本发明的具有防尘吸振性能的吸尘器外壳进行说明，但是本发明的技术方案并不限于此。
实施例一
防水耐高温保护涂料包括以下重量份的原料：
耐刮隔热保护涂料包括以下重量份的原料：
其中，抗氧剂为二苯胺、对苯二胺、二氢喹啉、双十二碳醇酯、硫代二丙酸双酯、三辛酯、三癸酯中的一种或多种的混合物。第一溶剂、第二溶剂均可选用常用溶剂。第一相容剂为环状酸酐型相容剂、丙烯酸型相容剂、酰亚胺型相容剂、异氰酸酯型相容剂中的一种。第二相容剂均为环状酸酐型相容剂、丙烯酸型相容剂、酰亚胺型相容剂、异氰酸酯型相容剂中的一种。第一分散剂和第二分散剂均为硬脂酰胺、乙烯基双硬脂酰胺、三硬脂酸甘油酯、硬脂酸钡、乙烯－丙烯酸共聚物、聚乙烯蜡、聚乙二醇中的一种或多种的混合物。硅烷偶联剂为氨基丙基三乙氧基硅烷。加工助剂包括润滑剂、固化剂、稳定剂。防水耐高温保护涂层的厚度为10mm。耐刮隔热保护涂层的厚度为8mm。将得到的防水耐高温保护涂层和耐刮隔热保护涂层设置于挂烫机喷头上，从而得到耐刮耐高温挂烫机喷头。
实施例二
防水耐高温保护涂料包括以下重量份的原料：
耐刮隔热保护涂料包括以下重量份的原料：
其中，抗氧剂为二苯胺、对苯二胺、二氢喹啉、双十二碳醇酯、硫代二丙酸双酯、三辛酯、三癸酯中的一种或多种的混合物。第一溶剂、第二溶剂均可选用常用溶剂。第一相容剂为环状酸酐型相容剂、丙烯酸型相容剂、酰亚胺型相容剂、异氰酸酯型相容剂中的一种。第二相容剂均为环状酸酐型相容剂、丙烯酸型相容剂、酰亚胺型相容剂、异氰酸酯型相容剂中的一种。第一分散剂和第二分散剂均为硬脂酰胺、乙烯基双硬脂酰胺、三硬脂酸甘油酯、硬脂酸钡、乙烯－丙烯酸共聚物、聚乙烯蜡、聚乙二醇中的一种或多种的混合物。硅烷偶联剂为氨基丙基三乙氧基硅烷。加工助剂包括润滑剂、固化剂、稳定剂。防水耐高温保护涂层的厚度为12mm。耐刮隔热保护涂层的厚度为8mm。将得到的防水耐高温保护涂层和耐刮隔热保护涂层设置于挂烫机喷头上，从而得到耐刮耐高温挂烫机喷头。
实施例三
防水耐高温保护涂料包括以下重量份的原料：
耐刮隔热保护涂料包括以下重量份的原料：
其中，抗氧剂为二苯胺、对苯二胺、二氢喹啉、双十二碳醇酯、硫代二丙酸双酯、三辛酯、三癸酯中的一种或多种的混合物。第一溶剂、第二溶剂均可选用常用溶剂。第一相容剂为环状酸酐型相容剂、丙烯酸型相容剂、酰亚胺型相容剂、异氰酸酯型相容剂中的一种。第二相容剂均为环状酸酐型相容剂、丙烯酸型相容剂、酰亚胺型相容剂、异氰酸酯型相容剂中的一种。第一分散剂和第二分散剂均为硬脂酰胺、乙烯基双硬脂酰胺、三硬脂酸甘油酯、硬脂酸钡、乙烯－丙烯酸共聚物、聚乙烯蜡、聚乙二醇中的一种或多种的混合物。硅烷偶联剂为氨基丙基三乙氧基硅烷。加工助剂包括润滑剂、固化剂、稳定剂。防水耐高温保护涂层的厚度为13mm。耐刮隔热保护涂层的厚度为9mm。将得到的防水耐高温保护涂层和耐刮隔热保护涂层设置于挂烫机喷头上，从而得到耐刮耐高温挂烫机喷头。
实施例四
防水耐高温保护涂料包括以下重量份的原料：
耐刮隔热保护涂料包括以下重量份的原料：
其中，抗氧剂为二苯胺、对苯二胺、二氢喹啉、双十二碳醇酯、硫代二丙酸双酯、三辛酯、三癸酯中的一种或多种的混合物。第一溶剂、第二溶剂均可选用常用溶剂。第一相容剂为环状酸酐型相容剂、丙烯酸型相容剂、酰亚胺型相容剂、异氰酸酯型相容剂中的一种。第二相容剂均为环状酸酐型相容剂、丙烯酸型相容剂、酰亚胺型相容剂、异氰酸酯型相容剂中的一种。第一分散剂和第二分散剂均为硬脂酰胺、乙烯基双硬脂酰胺、三硬脂酸甘油酯、硬脂酸钡、乙烯－丙烯酸共聚物、聚乙烯蜡、聚乙二醇中的一种或多种的混合物。硅烷偶联剂为氨基丙基三乙氧基硅烷。加工助剂包括润滑剂、固化剂、稳定剂。防水耐高温保护涂层的厚度为12mm。耐刮隔热保护涂层的厚度为10mm。将得到的防水耐高温保护涂层和耐刮隔热保护涂层设置于挂烫机喷头上，从而得到耐刮耐高温挂烫机喷头。
实施例五
防水耐高温保护涂料包括以下重量份的原料：
耐刮隔热保护涂料包括以下重量份的原料：
其中，抗氧剂为二苯胺、对苯二胺、二氢喹啉、双十二碳醇酯、硫代二丙酸双酯、三辛酯、三癸酯中的一种或多种的混合物。第一溶剂、第二溶剂均可选用常用溶剂。第一相容剂为环状酸酐型相容剂、丙烯酸型相容剂、酰亚胺型相容剂、异氰酸酯型相容剂中的一种。第二相容剂均为环状酸酐型相容剂、丙烯酸型相容剂、酰亚胺型相容剂、异氰酸酯型相容剂中的一种。第一分散剂和第二分散剂均为硬脂酰胺、乙烯基双硬脂酰胺、三硬脂酸甘油酯、硬脂酸钡、乙烯－丙烯酸共聚物、聚乙烯蜡、聚乙二醇中的一种或多种的混合物。硅烷偶联剂为氨基丙基三乙氧基硅烷。加工助剂包括润滑剂、固化剂、稳定剂。防水耐高温保护涂层的厚度为14mm。耐刮隔热保护涂层的厚度为7mm。将得到的防水耐高温保护涂层和耐刮隔热保护涂层设置于挂烫机喷头上，从而得到耐刮耐高温挂烫机喷头。
对上述5个实施例得到的耐刮耐高温挂烫机喷头的外壁进行性能测试，从以下几个方面对耐刮耐高温挂烫机喷头的外壁进行测试：外观、铅笔硬度、耐磨性、耐候性、耐酸性、耐冷热循环性、耐碱性。外观的测试方法：目视挂烫机喷头的表面是否平整均一；铅笔硬度的测试方法：在同一水平面使用各种硬度的铅笔芯磨平后与被测物成45°角，用500g力使其形成300mm，查看有无刮痕和剥落；耐酸性的测试方法：在浓度为5％盐酸液进浸泡24h观察挂烫机喷头的外壁的状态，待恢复2h后做划格试验；耐碱性的测试方法：在浓度为5％氢氧化钠溶液内浸泡24h，观察挂烫机喷头的外壁的状态，待恢复2h后做划格试验；耐磨性(RCA)的测试方法：固定负荷175g/cm2，指标为100次不露底；耐冷热循环性的测试方法：采用温度与湿度控制箱对样品进行温度循环测试，从-40℃×2h升至室温，然后再升至65℃×2h，再降至室温，上述过程循环10次，然后测定外观以及附着力；耐候性的测试方法：采用温度湿度控制箱调节温度60℃、相对湿度95％，48h后测定外观以及附着力。测试结果如下表1所示：
表1
对上述5个实施例的耐刮耐高温挂烫机喷头进行使用情况测试，选用常见市售挂烫机喷头作为对比例，将5个实施例的喷头和对比例的喷头装设在相同型号、相同批次的挂烫机上进行测试，测试结果为：连续使用10分钟后，5个实施例的喷头的外壁的温度均小于40℃，对比例的喷头的外壁的温度为50℃；与对比例的喷头相比，实施例一、实施例二、实施例三、实施例四、实施例五的喷头的使用寿命分别延长了30％、34％、35％、33％、32％。
在本发明的描述中，需要理解的是，术语“中心”、“纵向”、“横向”、“长度”、“宽度”、“厚度”、“上”、“下”、“前”、“后”、“左”、“右”、“竖直”、“水平”、“顶”、“底”“内”、“外”、“顺时针”、“逆时针”、“轴向”、“径向”、“周向”等指示的方位或位置关系为基于附图所示的方位或位置关系，仅是为了便于描述本发明和简化描述，而不是指示或暗示所指的装置或元件必须具有特定的方位、以特定的方位构造和操作，因此不能理解为对本发明的限制。
尽管本发明的实施方案已公开如上，但其并不仅仅限于说明书和实施方式中所列运用。它完全可以被适用于各种适合本发明的领域。对于熟悉本领域的人员而言，可容易地实现另外的修改。因此在不背离权利要求及等同范围所限定的一般概念下，本发明并不限于特定的细节和这里示出与描述的图例。
Claims (10)
1.一种耐刮耐高温挂烫机喷头，其特征在于，包括：喷头主体、涂覆在所述喷头主体内壁和外壁上的防水耐高温保护涂层和涂覆于所述喷头主体外壁上的防水耐高温保护涂层上的耐刮隔热保护涂层，所述防水耐高温保护涂层通过刷涂防水耐高温保护涂料后，再经干燥制得；所述耐刮隔热保护涂层通过刷涂耐刮隔热保护涂料后，再经干燥制得；
所述防水耐高温保护涂料包括以下重量份的原料：
2.根据权利要求1所述的耐刮耐高温挂烫机喷头，其特征在于，所述耐刮隔热保护涂料包括以下重量份的原料：
3.根据权利要求2所述的耐刮耐高温挂烫机喷头，其特征在于，所述抗氧剂为二苯胺、对苯二胺、二氢喹啉、双十二碳醇酯、硫代二丙酸双酯、三辛酯、三癸酯中的一种或多种的混合物。
4.根据权利要求1所述的耐刮耐高温挂烫机喷头，其特征在于，所述第一相容剂为环状酸酐型相容剂、丙烯酸型相容剂、酰亚胺型相容剂、异氰酸酯型相容剂中的一种。
5.根据权利要求2所述的耐刮耐高温挂烫机喷头，其特征在于，所述第二相容剂均为环状酸酐型相容剂、丙烯酸型相容剂、酰亚胺型相容剂、异氰酸酯型相容剂中的一种。
6.根据权利要求2所述的耐刮耐高温挂烫机喷头，其特征在于，所述第一分散剂和第二分散剂均为硬脂酰胺、乙烯基双硬脂酰胺、三硬脂酸甘油酯、硬脂酸钡、乙烯－丙烯酸共聚物、聚乙烯蜡、聚乙二醇中的一种或多种的混合物。
7.根据权利要求1所述的耐刮耐高温挂烫机喷头，其特征在于，所述硅烷偶联剂为氨基丙基三乙氧基硅烷。
8.根据权利要求1所述的耐刮耐高温挂烫机喷头，其特征在于，所述加工助剂包括润滑剂、固化剂、稳定剂。
9.根据权利要求1所述的耐刮耐高温挂烫机喷头，其特征在于，所述防水耐高温保护涂层的厚度为1-20mm。
10.根据权利要求1所述的耐刮耐高温挂烫机喷头，其特征在于，所述耐刮隔热保护涂层的厚度为0.5-10mm。