CN107056192A - 一种以水生植物改良的混凝土 - Google Patents

一种以水生植物改良的混凝土 Download PDF

Info

Publication number
CN107056192A
CN107056192A CN201710377014.9A CN201710377014A CN107056192A CN 107056192 A CN107056192 A CN 107056192A CN 201710377014 A CN201710377014 A CN 201710377014A CN 107056192 A CN107056192 A CN 107056192A
Authority
CN
China
Prior art keywords
water plant
improved
concrete
parts
cement
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201710377014.9A
Other languages
English (en)
Inventor
盛家方
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Soup Was Building Materials (suzhou) Co Ltd Jianhua
Original Assignee
Soup Was Building Materials (suzhou) Co Ltd Jianhua
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Soup Was Building Materials (suzhou) Co Ltd Jianhua filed Critical Soup Was Building Materials (suzhou) Co Ltd Jianhua
Priority to CN201710377014.9A priority Critical patent/CN107056192A/zh
Publication of CN107056192A publication Critical patent/CN107056192A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种以水生植物改良的混凝土，包括以质量份数计量的以下原料:碎石料50‑400份，水泥100‑160份，黄沙50‑80份，黏土20‑30份，硅藻土5‑20份，玻璃纤维5‑10份，聚氨酯颗粒10‑20份等。本发明的结构强度好，韧性好，耐候性好，不易开裂，韧性好，抗震性能优异，性能稳定。

Description

一种以水生植物改良的混凝土
技术领域
本发明涉及建筑建材领域，尤其涉及一种以水生植物改良的混凝土。
背景技术
混凝土，是指由胶凝材料将骨料胶结成整体的工程复合材料的统称。通常讲的混凝土一词是指用水泥作胶凝材料，砂、石作骨料；与水按一定比例配合，经搅拌而得的水泥混凝土，也称普通混凝土，它广泛应用于土木工程。混凝土因其优良的物理力学性能在土木工程领域得到了广泛应用，是目前使用量最大的一种建筑材料。现有的混凝土存在耐候性能差，易开裂，内部孔隙结构多，抗震性能弱。
发明内容
为解决上述技术问题，本发明提供了一种以水生植物改良的混凝土，针对现有技术中的不足，采用水生植物浆液与聚氨酯颗粒结合的新型混凝土配方，解决了现有的混凝土存在耐候性能差，易开裂，内部孔隙结构多，抗震性能弱的问题。
为达到上述目的，本发明的技术方案如下：一种以水生植物改良的混凝土，包括以质量份数计量的以下原料:
作为本发明的一种优选方案，所述偶联剂为硅烷偶联剂。
作为本发明的一种优选方案，所述水泥为硅酸盐水泥或磷酸盐水泥。
作为本发明的一种优选方案，所述水生植物浆液由水葫芦通过粉碎搅拌后制成。
作为本发明的一种优选方案，混凝土原料中还包括香樟木粉，所述香樟木粉由香樟木粉碎而成，粒径小于600目。
作为本发明的一种优选方案，所述聚氨酯颗粒的粒径小于1.5mm。
通过上述技术方案，本发明技术方案的有益效果是：本发明的结构强度好，韧性好，耐候性好，不易开裂，韧性好，抗震性能优异，性能稳定。本发明采用聚氨酯颗粒作为填充剂，可能有效修补混凝土内的孔隙，提高混凝土的减震抗震性能，聚氨酯颗粒吸水后，易发生微膨胀，提高各组分之间结合的紧密度，减小和补偿混凝土收缩，防止混凝土出现开裂。而聚氨酯与碎石料、水泥、黄沙等结合度差，在混凝土中加入黏土，同时配合水生植物浆液，水生植物浆液具有很好的保水性，能够使黏土保持很好的胶粘性，可以有效增强混凝土的凝结强度。而水生植物浆液中的植物纤维和玻璃纤维可以有效增强混凝土的抗折强度和韧性，同时防止混凝土出现开裂。而硅藻土也有助于修复混凝土中的孔隙，进一步提高混凝土的强度。香樟木粉能够提高混凝土的防虫、驱虫能力，同时能够提高混凝土的抗寒保温性能。
具体实施方式
下面将结合本发明实施例，对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本发明一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有作出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。
实施例1
一种以水生植物改良的混凝土，包括以质量份数计量的以下原料:
其中，所述偶联剂为硅烷偶联剂。所述水泥为硅酸盐水泥。所述水生植物浆液由水葫芦通过粉碎搅拌后制成。所述聚氨酯颗粒的粒径小于1.5mm。
实施例2
一种以水生植物改良的混凝土，包括以质量份数计量的以下原料:
实施例3
一种以水生植物改良的混凝土，包括以质量份数计量的以下原料:
其中，所述偶联剂为硅烷偶联剂。所述水泥为磷酸盐水泥。所述水生植物浆液由水葫芦通过粉碎搅拌后制成。所述聚氨酯颗粒的粒径小于1.5mm。所述香樟木粉由香樟木粉碎而成，粒径小于600目。
通过上述具体实施例，本发明的有益效果是：本发明的结构强度好，韧性好，耐候性好，不易开裂，韧性好，抗震性能优异，性能稳定。
对所公开的实施例的上述说明，使本领域专业技术人员能够实现或使用本发明。对这些实施例的多种修改对本领域的专业技术人员来说将是显而易见的，本文中所定义的一般原理可以在不脱离本发明的精神或范围的情况下，在其它实施例中实现。因此，本发明将不会被限制于本文所示的这些实施例，而是要符合与本文所公开的原理和新颖特点相一致的最宽的范围。

Claims (6)

1.一种以水生植物改良的混凝土，其特征在于，包括以质量份数计量的以下原料:
2.根据权利要求1所述的以水生植物改良的混凝土，其特征在于，所述偶联剂为硅烷偶联剂。
3.根据权利要求2所述的以水生植物改良的混凝土，其特征在于，所述水泥为硅酸盐水泥或磷酸盐水泥。
4.根据权利要求3所述的以水生植物改良的混凝土，其特征在于，所述水生植物浆液由水葫芦通过粉碎搅拌后制成。
5.根据权利要求4所述的以水生植物改良的混凝土，其特征在于，还包括香樟木粉，所述香樟木粉由香樟木粉碎而成，粒径小于600目。
6.根据权利要求5所述的以水生植物改良的混凝土，其特征在于，所述聚氨酯颗粒的粒径小于1.5mm。
CN201710377014.9A 2017-05-25 2017-05-25 一种以水生植物改良的混凝土 Pending CN107056192A (zh)