CN107048573A - A kind of sweat absorbing deodorant slippers and its preparation technology - Google Patents
A kind of sweat absorbing deodorant slippers and its preparation technology Download PDFInfo
- Publication number
- CN107048573A CN107048573A CN201710409348.XA CN201710409348A CN107048573A CN 107048573 A CN107048573 A CN 107048573A CN 201710409348 A CN201710409348 A CN 201710409348A CN 107048573 A CN107048573 A CN 107048573A
- Authority
- CN
- China
- Prior art keywords
- parts
- plastic cement
- shoe body
- slippers
- cement shoe
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention proposes a kind of sweat absorbing deodorant slippers and its preparation technology, including plastic cement shoe body and fiber liner, the plastic cement shoe body includes sole and vamp, sole upper surface and the vamp lower surface is fitted with the fiber liner by VELCRO, the plastic cement shoe body is modified polyurethane material, the fiber liner is modified blend fibre cloth, slippers of the present invention use double-layer structure, by VELCRO by plastic cement shoe body and fiber liner can tearing fit, cleaning replacement is convenient, compared to disposable slippers, safety and environmental protection, cost can effectively be reduced, in addition, it is comfortably soft by plastic cement shoe body made from rational formula combination, obdurability is good, antibacterial is wear-resisting, with condensating fiber liner absorbing sweat, deodorization, sterilization, good permeability, improve comprehensive quality.
Description
Technical field
The present invention relates to slippers preparing technical field, and in particular to a kind of sweat absorbing deodorant slippers and its preparation technology.
Background technology
At present, the disposable slippers used are based primarily upon cost consideration, so selection is less expensive, from structure,
Basic vamp non-woven fabrics including slipper bottom (foam bottom) and above passes through manual lock seaming from layer and non-woven fabrics upper of a shoe after allowing
The mode of cloth, is stitched together, just at present, and the production also without automatic assembly line occurs.And above-mentioned disposably drag
Footwear skidproof effect when bathroom is used is poor, easily slips, it is impossible to effectively ensure the personal safety of user, and then once
Property slippers increase bottom surface functional layer demand.In addition, people easily produce pin sweat, particularly summer during dress, it is different
Taste is larger, is also easy to breed bacteria, has had a strong impact on and has worn quality.
The content of the invention
For above-mentioned problem, the present invention proposes a kind of sweat absorbing deodorant slippers and its preparation technology, using two layers
Structure, by VELCRO by plastic cement shoe body and fiber liner can tearing fit, cleaning replacement is convenient, compared to disposable slippers,
Safety and environmental protection, can effectively reduce cost.It is good, anti-by the comfortable soft, obdurability of plastic cement shoe body made from rational formula combination
Bacterium is wear-resisting, and with condensating fiber liner absorbing sweat, deodorization, sterilization, good permeability improves comprehensive quality.
In order to realize above-mentioned purpose, the present invention uses following technical scheme:
A kind of sweat absorbing deodorant slippers, including plastic cement shoe body and fiber liner, the plastic cement shoe body include sole and vamp, institute
State sole upper surface and vamp lower surface and the fiber liner is fitted with by VELCRO, the plastic cement shoe body is modified poly- ammonia
Ester material, the fiber liner is modified blend fibre cloth.
It is preferred that, the plastic cement shoe body includes following mass fraction component:80-90 parts of polyurethane resin, nano diatomite
10-35 parts, 1-6 parts of nano titanium oxide, 0.5-2 parts of hydrazine, 2-5 parts of microcrystalline cellulose, 1-4 parts of silane coupler, emulsifying agent
0.5-1.5 parts, 2-6 parts of methyl vinyl silicon oil, 0-35 parts of pigment.
It is preferred that, the plastic shoes preparation step is as follows:
1) nano titanium oxide, nano diatomite are blended, then add appropriate distilled water thereto, then by hydrazine,
Microcrystalline cellulose is added thereto, 50 DEG C of oscillation treatment 50-80min, freeze-drying, is ground to particle diameter less than 30nm, is obtained powder standby
With;
2) by polyurethane resin, powder add batch mixer in, stirring mixing 20-25min, then again by silane coupler,
Methyl vinyl silicon oil is added thereto, and is warming up to 80 DEG C, and stirring mixing 10-15min, obtains compound in an inert atmosphere;
3) feed the mixture into and mediate 3-5min in kneader under the conditions of 45 DEG C, leftover materials are then added thereto liter
Temperature continues to mediate 20-40min, discharges and deliver in kneading machine, knead 8-10min, extrude pulling-on piece, punching obtains piece to 65-70 DEG C
Material, it is then die-filling;
4) by mould heating plasticizing, it is stripped after cooling and shaping, sole and vamp is then cut to obtain on request, and carry out perforating
Assembling.
It is preferred that, step 1) in the addition of distilled water be 2-3 times of nano titanium oxide and nano diatomite gross mass.
It is preferred that, step 2) in inert atmosphere be specially condition of nitrogen gas, nitrogen filling speed is 0.2-0.4L/min.
It is preferred that, step 4) in heating plasticizing be specially 160-165 DEG C of plasticization temperature, plasticizing pressure 4.5-4.7MPa, modeling
The change time is 15-18min.
It is preferred that, the modified blend fibre cloth includes following percentage composition component:Bamboo-carbon fibre 15-30%, marine alga are fine
Tie up 10-20%, nano titanium oxide 3-9%, turkey red oil 5-7%, caryophyllus oil 2-3%, cotton fiber surplus.
Due to using above-mentioned technical scheme, the beneficial effects of the invention are as follows:Slippers of the present invention use double-layer structure, pass through
VELCRO by plastic cement shoe body and fiber liner can tearing fit, cleaning replacement is convenient, compared to disposable slippers, safety and environmental protection,
Cost can effectively be reduced.By the way that plastic cement shoe body made from rational formula combination is comfortable soft, obdurability is good, antibacterial is wear-resisting, match somebody with somebody
Condensating fiber liner absorbing sweat, deodorization, sterilization, good permeability improve comprehensive quality.
Polyurethane material and modified blend fibre cloth of the invention by rational modification, collective effect is effectively carried
The comfort level and obdurability of high slippers, with excellent absorbing sweat, deodorization, anti-microbial property, the network structure type bamboo of high adsorption
Carbon fibe, alginate fibre coordinate nano titanium oxide, turkey red oil and caryophyllus oil, further increase antibacterial effect, and with clear
Effect that is fragrant, calming the nerves, massage.Sole uses porous substrate with vamp, coordinates the antibacterial material of filling doping to show after modification
The effect time limit for improving antibacterial efficacy and the efficiency for adsorbing taste removal are write, it is practical.
Embodiment
To make the purpose, technical scheme and advantage of the embodiment of the present invention clearer, below in conjunction with the embodiment of the present invention,
Technical scheme in the embodiment of the present invention is clearly and completely described.Based on embodiments of the invention, the common skill in this area
The every other embodiment that art personnel are obtained under the premise of creative work is not made, belongs to the model that the present invention is protected
Enclose.
A kind of sweat absorbing deodorant slippers, including plastic cement shoe body and fiber liner, the plastic cement shoe body include sole and vamp, institute
State sole upper surface and vamp lower surface and the fiber liner is fitted with by VELCRO, the plastic cement shoe body is modified poly- ammonia
Ester material, the fiber liner is modified blend fibre cloth.
Embodiment 1:
The plastic cement shoe body includes following mass fraction component:85 parts of polyurethane resin, part, nanometer two of nano diatomite 15
4 parts of titanium oxide, 0.5 part of hydrazine, 4 parts of microcrystalline cellulose, 3 parts of silane coupler, 1.2 parts of emulsifying agent, methyl vinyl silicon oil 4
Part, 20 parts of pigment.
The plastic shoes preparation step is as follows:
1) nano titanium oxide, nano diatomite are blended, the distilled water of both 2 times of gross masses are then added thereto,
Hydrazine, microcrystalline cellulose are added thereto again, 50 DEG C of oscillation treatment 60min, are freeze-dried, be ground to particle diameter less than 30nm, obtain
Powder is standby;
2) polyurethane resin, powder are added in batch mixer, stirring mixing 20min, then again by silane coupler, methyl
Vinyl silicone oil is added thereto, and is warming up to 80 DEG C, and stirring mixing 10min, obtains compound in 0.2L/min nitrogen atmosphere;
3) feed the mixture into and mediate 3-5min in kneader under the conditions of 45 DEG C, leftover materials are then added thereto liter
Temperature continues to mediate 20min, discharges and deliver in kneading machine, knead 8-10min, extrude pulling-on piece, punching obtains sheet stock, so to 65 DEG C
It is die-filling afterwards;
4) by mould heating plasticizing, specific 160 DEG C of plasticization temperature, plasticizing pressure 4.6MPa, fusion time is 15min, cold
But it is stripped after shaping, sole and vamp is then cut to obtain on request, and carry out perforating assembling.
The modified blend fibre cloth includes following percentage composition component:Bamboo-carbon fibre 15%, alginate fibre 15%, nanometer
Titanium dioxide 8%, turkey red oil 5%, caryophyllus oil 2%, cotton fiber surplus.
Embodiment 2:
The plastic cement shoe body includes following mass fraction component:80 parts of polyurethane resin, part, nanometer two of nano diatomite 25
5 parts of titanium oxide, 1.5 parts of hydrazine, 3 parts of microcrystalline cellulose, 2 parts of silane coupler, 1.5 parts of emulsifying agent, methyl vinyl silicon oil 3
Part, 25 parts of pigment.
The plastic shoes preparation step is as follows:
1) nano titanium oxide, nano diatomite are blended, the distilled water of both 3 times of gross masses are then added thereto,
Hydrazine, microcrystalline cellulose are added thereto again, 50 DEG C of oscillation treatment 70min, are freeze-dried, be ground to particle diameter less than 30nm, obtain
Powder is standby;
2) polyurethane resin, powder are added in batch mixer, stirring mixing 25min, then again by silane coupler, methyl
Vinyl silicone oil is added thereto, and is warming up to 80 DEG C, and stirring mixing 15min, obtains compound in 0.3L/min nitrogen atmosphere;
3) feed the mixture into and mediate 3-5min in kneader under the conditions of 45 DEG C, leftover materials are then added thereto liter
Temperature continues to mediate 30min, discharges and deliver in kneading machine, knead 8-10min, extrude pulling-on piece, punching obtains sheet stock, so to 70 DEG C
It is die-filling afterwards;
4) by mould heating plasticizing, specific 165 DEG C of plasticization temperature, plasticizing pressure 4.5MPa, fusion time is 18min, cold
But it is stripped after shaping, sole and vamp is then cut to obtain on request, and carry out perforating assembling.
The modified blend fibre cloth includes following percentage composition component:Bamboo-carbon fibre 20%, alginate fibre 20%, nanometer
Titanium dioxide 6%, turkey red oil 6%, caryophyllus oil 3%, cotton fiber surplus.
Embodiment 3:
The plastic cement shoe body includes following mass fraction component:86 parts of polyurethane resin, part, nanometer two of nano diatomite 30
1 part of titanium oxide, 1.5 parts of hydrazine, 2 parts of microcrystalline cellulose, 1 part of silane coupler, 1 part of emulsifying agent, 2 parts of methyl vinyl silicon oil,
35 parts of pigment.
The plastic shoes preparation step is as follows:
1) nano titanium oxide, nano diatomite are blended, the distilled water of both 2 times of gross masses are then added thereto,
Hydrazine, microcrystalline cellulose are added thereto again, 50 DEG C of oscillation treatment 80min, are freeze-dried, be ground to particle diameter less than 30nm, obtain
Powder is standby;
2) polyurethane resin, powder are added in batch mixer, stirring mixing 25min, then again by silane coupler, methyl
Vinyl silicone oil is added thereto, and is warming up to 80 DEG C, and stirring mixing 15min, obtains compound in 0.25L/min nitrogen atmosphere;
3) feed the mixture into and mediate 3-5min in kneader under the conditions of 45 DEG C, leftover materials are then added thereto liter
Temperature continues to mediate 35min, discharges and deliver in kneading machine, knead 8-10min, extrude pulling-on piece, punching obtains sheet stock, so to 70 DEG C
It is die-filling afterwards;
4) by mould heating plasticizing, specific 165 DEG C of plasticization temperature, plasticizing pressure 4.7MPa, fusion time is 18min, cold
But it is stripped after shaping, sole and vamp is then cut to obtain on request, and carry out perforating assembling.
The modified blend fibre cloth includes following percentage composition component:Bamboo-carbon fibre 25%, alginate fibre 20%, nanometer
Titanium dioxide 4%, turkey red oil 5%, caryophyllus oil 2%, cotton fiber surplus.
Embodiment 4:
The plastic cement shoe body includes following mass fraction component:85 parts of polyurethane resin, part, nanometer two of nano diatomite 10
6 parts of titanium oxide, 2 parts of hydrazine, 3 parts of microcrystalline cellulose, 4 parts of silane coupler, 0.8 part of emulsifying agent, 5 parts of methyl vinyl silicon oil,
30 parts of pigment.
The plastic shoes preparation step is as follows:
1) nano titanium oxide, nano diatomite are blended, the distilled water of both 3 times of gross masses are then added thereto,
Hydrazine, microcrystalline cellulose are added thereto again, 50 DEG C of oscillation treatment 50min, are freeze-dried, be ground to particle diameter less than 30nm, obtain
Powder is standby;
2) polyurethane resin, powder are added in batch mixer, stirring mixing 25min, then again by silane coupler, methyl
Vinyl silicone oil is added thereto, and is warming up to 80 DEG C, and stirring mixing 15min, obtains compound in 0.4L/min nitrogen atmosphere;
3) feed the mixture into and mediate 3-5min in kneader under the conditions of 45 DEG C, leftover materials are then added thereto liter
Temperature continues to mediate 40min, discharges and deliver in kneading machine, knead 8-10min, extrude pulling-on piece, punching obtains sheet stock, so to 70 DEG C
It is die-filling afterwards;
4) by mould heating plasticizing, specific 160 DEG C of plasticization temperature, plasticizing pressure 4.6MPa, fusion time is 18min, cold
But it is stripped after shaping, sole and vamp is then cut to obtain on request, and carry out perforating assembling.
The modified blend fibre cloth includes following percentage composition component:Bamboo-carbon fibre 30%, alginate fibre 15%, nanometer
Titanium dioxide 3%, turkey red oil 7%, caryophyllus oil 2%, cotton fiber surplus.
Embodiment 5:
The plastic cement shoe body includes following mass fraction component:90 parts of polyurethane resin, part, nanometer two of nano diatomite 25
4 parts of titanium oxide, 1 part of hydrazine, 4 parts of microcrystalline cellulose, 3 parts of silane coupler, 0.5 part of emulsifying agent, 6 parts of methyl vinyl silicon oil,
0 part of pigment.
The plastic shoes preparation step is as follows:
1) nano titanium oxide, nano diatomite are blended, the distilled water of both 2 times of gross masses are then added thereto,
Hydrazine, microcrystalline cellulose are added thereto again, 50 DEG C of oscillation treatment 60min, are freeze-dried, be ground to particle diameter less than 30nm, obtain
Powder is standby;
2) polyurethane resin, powder are added in batch mixer, stirring mixing 20min, then again by silane coupler, methyl
Vinyl silicone oil is added thereto, and is warming up to 80 DEG C, and stirring mixing 10min, obtains compound in 0.3L/min nitrogen atmosphere;
3) feed the mixture into and mediate 3-5min in kneader under the conditions of 45 DEG C, leftover materials are then added thereto liter
Temperature continues to mediate 25min, discharges and deliver in kneading machine, knead 8-10min, extrude pulling-on piece, punching obtains sheet stock, so to 65 DEG C
It is die-filling afterwards;
4) by mould heating plasticizing, specific 165 DEG C of plasticization temperature, plasticizing pressure 4.5MPa, fusion time is 13min, cold
But it is stripped after shaping, sole and vamp is then cut to obtain on request, and carry out perforating assembling.
The modified blend fibre cloth includes following percentage composition component:Bamboo-carbon fibre 25%, alginate fibre 10%, nanometer
Titanium dioxide 9%, turkey red oil 6%, caryophyllus oil 3%, cotton fiber surplus.
Embodiment 6:
The plastic cement shoe body includes following mass fraction component:85 parts of polyurethane resin, part, nanometer two of nano diatomite 35
5 parts of titanium oxide, 1.5 parts of hydrazine, 5 parts of microcrystalline cellulose, 2 parts of silane coupler, 1 part of emulsifying agent, 4 parts of methyl vinyl silicon oil,
0 part of pigment.
The plastic shoes preparation step is as follows:
1) nano titanium oxide, nano diatomite are blended, the distilled water of both 2 times of gross masses are then added thereto,
Hydrazine, microcrystalline cellulose are added thereto again, 50 DEG C of oscillation treatment 70min, are freeze-dried, be ground to particle diameter less than 30nm, obtain
Powder is standby;
2) polyurethane resin, powder are added in batch mixer, stirring mixing 20min, then again by silane coupler, methyl
Vinyl silicone oil is added thereto, and is warming up to 80 DEG C, and stirring mixing 10min, obtains compound in 0.25L/min nitrogen atmosphere;
3) feed the mixture into and mediate 3-5min in kneader under the conditions of 45 DEG C, leftover materials are then added thereto liter
Temperature continues to mediate 30min, discharges and deliver in kneading machine, knead 8-10min, extrude pulling-on piece, punching obtains sheet stock, so to 70 DEG C
It is die-filling afterwards;
4) by mould heating plasticizing, specific 160 DEG C of plasticization temperature, plasticizing pressure 4.7MPa, fusion time is 15min, cold
But it is stripped after shaping, sole and vamp is then cut to obtain on request, and carry out perforating assembling.
The modified blend fibre cloth includes following percentage composition component:Bamboo-carbon fibre 15%, alginate fibre 15%, nanometer
Titanium dioxide 8%, turkey red oil 5%, caryophyllus oil 3%, cotton fiber surplus.
The above embodiments are merely illustrative of the technical solutions of the present invention, rather than its limitations;Although with reference to the foregoing embodiments
The present invention is described in detail, it will be understood by those within the art that:It still can be to foregoing each implementation
Technical scheme described in example is modified, or carries out equivalent substitution to which part technical characteristic;And these modification or
Replace, the essence of appropriate technical solution is departed from the spirit and scope of various embodiments of the present invention technical scheme.
Claims (7)
1. a kind of sweat absorbing deodorant slippers, it is characterised in that:Including plastic cement shoe body and fiber liner, the plastic cement shoe body includes sole
And vamp, sole upper surface and the vamp lower surface is fitted with the fiber liner, the plastic cement shoe body by VELCRO
For modified polyurethane material, the fiber liner is modified blend fibre cloth.
2. sweat absorbing deodorant slippers according to claim 1, it is characterised in that the plastic cement shoe body includes following mass fraction
Component:80-90 parts of polyurethane resin, 10-35 parts of nano diatomite, 1-6 parts of nano titanium oxide, 0.5-2 parts of hydrazine, crystallite are fine
Tie up 2-5 parts of element, 1-4 parts of silane coupler, 0.5-1.5 parts of emulsifying agent, 2-6 parts of methyl vinyl silicon oil, 0-35 parts of pigment.
3. sweat absorbing deodorant slippers according to claim 2, it is characterised in that the plastic shoes preparation step is as follows:
1) nano titanium oxide, nano diatomite are blended, then add appropriate distilled water thereto, then by hydrazine, crystallite
Cellulose is added thereto, 50 DEG C of oscillation treatment 50-80min, freeze-drying, is ground to particle diameter less than 30nm, is obtained powder standby;
2) polyurethane resin, powder are added in batch mixer, stirring mixing 20-25min, then again by silane coupler, methyl
Vinyl silicone oil is added thereto, and is warming up to 80 DEG C, and stirring mixing 10-15min, obtains compound in an inert atmosphere;
3) feed the mixture into and mediate 3-5min in kneader under the conditions of 45 DEG C, then leftover materials are added thereto and are warming up to
65-70 DEG C, continue to mediate 20-40min, discharge and deliver in kneading machine, knead 8-10min, extrude pulling-on piece, punching obtains sheet stock,
Then it is die-filling;
4) by mould heating plasticizing, it is stripped after cooling and shaping, sole and vamp is then cut to obtain on request, and carry out perforating assembling
.
4. sweat absorbing deodorant slippers according to claim 3, it is characterised in that:Step 1) in distilled water addition be nanometer
2-3 times of titanium dioxide and nano diatomite gross mass.
5. sweat absorbing deodorant slippers according to claim 3, it is characterised in that:Step 2) in inert atmosphere be specially nitrogen bar
Part, nitrogen filling speed is 0.2-0.4L/min.
6. sweat absorbing deodorant slippers according to claim 3, it is characterised in that:Step 4) in heating plasticizing be specially plasticizing temperature
160-165 DEG C of degree, plasticizing pressure 4.5-4.7MPa, fusion time is 15-18min.
7. sweat absorbing deodorant slippers according to claim 1, it is characterised in that:The modified blend fibre cloth includes following hundred
Divide content component:Bamboo-carbon fibre 15-30%, alginate fibre 10-20%, nano titanium oxide 3-9%, turkey red oil 5-7%, cloves
Oily 2-3%, cotton fiber surplus.