CN107034699B - A kind of imitative reactive adhesive and pigment printing technique - Google Patents
A kind of imitative reactive adhesive and pigment printing technique Download PDFInfo
- Publication number
- CN107034699B CN107034699B CN201611090797.4A CN201611090797A CN107034699B CN 107034699 B CN107034699 B CN 107034699B CN 201611090797 A CN201611090797 A CN 201611090797A CN 107034699 B CN107034699 B CN 107034699B
- Authority
- CN
- China
- Prior art keywords
- parts
- imitative reactive
- fabric
- imitative
- adhesive
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
A kind of imitative reactive adhesive and pigment printing technique, belong to pigment printing technical field.Adhesive is characterized in that: weight is grouped into: 4.5 ~ 6 parts of trioctyl lemon acid, 3 ~ 4.5 parts of lac resin, 0.5 ~ 1 part of starch, 3.7 ~ 5.5 parts of octyl phenol polyoxyethylene ether, 1.5 ~ 2 parts of dibutyl phthalate, 2 ~ 3 parts of butyl methacrylate, 1.5 ~ 2.5 parts of isopropanol, hydroxymethyl acrylamide 1 ~ 2,0.3 ~ 0.5 part of sodium bicarbonate.Printing technology is characterized in that: 18 ~ 27 parts of imitative reactive adhesives being made into slurry by weight, 0.5 ~ 3 part of pigment is added, moisturizing is made into 100 parts of mill base, and after printing on the fabric respectively by flower stencil, drying is baked and banked up with earth, decatize, washed to obtain the final product.The feel of Printing made from this technique has reached the feel that traditional handicraft softening agent just has, and dry and wet fastness of rubbing is held at higher grade.
Description
Technical field
A kind of imitative reactive adhesive and pigment printing technique, belong to pigment printing technical field.
Background technique
Pigment printing is with coating direct printing, which is generally termed dry prints, to be different from wet prints (or dye
Expect stamp).Coating is different from dyestuff, it is to fiber without substantivity.It cannot be combined with fiber, it, which is that one kind is insoluble, has
Color powder is mostly organic synthesis object, but also organic/inorganic substance.Its principle of " coloring " on fiber can be generated by means of a kind of
The synthetic resin of strong film anchors at the surface of fiber, therefore the fabric of its peering various fiber can stamp.
Pigment printing simple process, low in cost, effect is intuitive, is the first choice of many Printings.But conventional coating
But there is following defects for Printing: 1, feel is poor;2, color fastness is poor.In view of disadvantage mentioned above, pigment printing is fitted always
For more low-grade product.After softening agent is added in the formula of pigment printing technique, feel can be made to improve, but fabric simultaneously
Dry and wet rub fastness, all declined, and increase production cost.There is pigment printing product as reactive dye print
The same feel and washable ability are spent, is the target of dyeing effort always.
Summary of the invention
The technical problem to be solved by the present invention is overcoming the deficiencies of the prior art and provide, a kind of feel is submissive, good color fastness
Imitative reactive adhesive and pigment printing technique.
The technical solution adopted by the present invention to solve the technical problems is: the imitative reactive adhesive, it is characterised in that: weight
Part composition are as follows: 4.5 ~ 6 parts of trioctyl lemon acid, 3 ~ 4.5 parts of lac resin, 0.5 ~ 1 part of starch, octyl phenol polyoxyethylene ether 3.7 ~
5.5 parts, 1.5 ~ 2 parts of dibutyl phthalate, 2 ~ 3 parts of butyl methacrylate, 1.5 ~ 2.5 parts of isopropanol, methylol propylene
1 ~ 2 part of amide, 0.3 ~ 0.5 part of sodium bicarbonate.
Preferably, the parts by weight composition of adhesive are as follows: 5 ~ 5.5 parts of trioctyl lemon acid, 4 parts of lac resin, starch 0.7
Part, 4 ~ 5 parts of octyl phenol polyoxyethylene ether, 1.7 parts of dibutyl phthalate, 2.5 parts of butyl methacrylate, 2 parts of isopropanol,
1.5 parts of hydroxymethyl acrylamide, 0.4 part of sodium bicarbonate.Preferred adhesive formula keeps each component cooperation of the present invention the most proper,
The feel and dry and wet that Printing is made are rubbed the optimum state that fastness all reaches of the invention.
A kind of imitative reactive coating printing technology using above-mentioned adhesive, it is characterised in that: imitative by 18 ~ 27 parts by weight
Reactive adhesive is made into slurry, and 0.5 ~ 3 part of pigment is added, and moisturizing is made into 100 parts of mill base, prints on the fabric respectively by flower stencil
After system, drying is baked and banked up with earth, decatize, is washed to obtain the final product.
Pigment printing technique of the invention provides a kind of adhesive that mill base is prepared together with pigment, opens in this adhesive
The invasive starch for having used specific quantity, sodium bicarbonate, lac resin and trioctyl lemon acid carrys out the bonding of adjusting coating stamp
The performance of agent, so that the feel of Printing made from this technique has reached the feel that traditional handicraft softening agent just has, and
Dry and wet fastness of rubbing is held at higher grade.
The drying is that fabric dries 25 min ~ 30min in the environment of 60 DEG C ~ 80 DEG C.Through print prepared by the present invention
The drying of flower prod advanced specific degrees before baking and banking up with earth, can better ensure that color fastness.
It is described bake and bank up with earth as stamp after fabric be transferred on the forming machine that temperature is 127 DEG C ~ 135 DEG C bake 4min ~
7min.It suitably bakes and banks up with earth technique and is to maintain the feel of the obtained Printing of the present invention and the crucial means of comparison of color fastness, this
Invention is preferably baked and banked up with earth under technique, and the property retention of feel and color fastness is in optimum state.
The steam temperature is 103 DEG C ~ 105 DEG C, and the time is 20 min ~ 30min.
The washing is first to wash 10 min ~ 15min with the cleaning solution of 2g/L;Again with the soaping agent of 3g/L 92 DEG C ~
96 DEG C of 15 min that soap ~ 20min;Finally with clear water in 55 DEG C ~ 60 DEG C cleaning 10 min ~ 15min.Through felicity condition of the present invention
Decatize and washing after further improve the color fastness of product.
Compared with prior art, beneficial effect possessed by a kind of imitative reactive adhesive of the invention and pigment printing technique
Be: pigment printing technique of the invention provides a kind of adhesive that mill base is prepared together with pigment, initiative in this adhesive
The starch for having used specific quantity, sodium bicarbonate, lac resin and trioctyl lemon acid carry out adjusting coating stamp adhesive
Performance, so that the feel of Printing made from this technique has reached the feel that traditional handicraft softening agent just has, and dry and wet
Fastness of rubbing is held at higher grade.It, can be with using fabric color fastness of the invention in the identical situation of binder dosage
High fastness adhesive compares favourably, and is significantly better than using traditional binders stamp.And fabric feeling is significantly better than conventional adhesive.
In the identical situation of binder dosage, feel effect identical as use traditional binders and high fastness adhesive addition softening agent
Fruit, the dry and wet of fabric rub fastness increase.
Specific embodiment
The present invention will be further described combined with specific embodiments below, and wherein embodiment 1 is most preferred embodiment.
Embodiment 1
1) parts by weights forms are as follows: and 5 parts of trioctyl lemon acid, 4 parts of lac resin, 0.7 part of starch, octylphenol polyethylene ethylene oxide
5 parts of ether, 1.7 parts of dibutyl phthalate, 2.5 parts of butyl methacrylate, 2 parts of isopropanol, hydroxymethyl acrylamide 1.5
Part, 0.4 part of modulating adhesive of sodium bicarbonate;
2) 22.8 parts of adhesives are made into slurry by weight, 2 parts of pigment is added, moisturizing is made into 100 parts of mill base;
3) it is printed on the fabric respectively by flower stencil;
4) fabric dries 27min in the environment of 67 DEG C ~ 70 DEG C;
5) fabric is transferred on the forming machine that temperature is 130 DEG C and bakes 5min;
6) temperature is decatize 25min under conditions of 104 DEG C;
7) 12min is washed with the cleaning solution of 2g/L;Again with the soaping agent of 3g/L in 94 DEG C of 18min that soap;Finally use clear water
56 DEG C of cleaning 12min to obtain the final product.
Embodiment 2
1) parts by weights forms are as follows: and 5.5 parts of trioctyl lemon acid, 4 parts of lac resin, 0.7 part of starch, octyl phenol polyoxy second
4 parts of alkene ether, 1.7 parts of dibutyl phthalate, 2.5 parts of butyl methacrylate, 2 parts of isopropanol, hydroxymethyl acrylamide 1.5
Part, 0.4 part of modulating adhesive of sodium bicarbonate;
2) 22.3 parts of adhesives are made into slurry by weight, 2 parts of pigment is added, moisturizing is made into 100 parts of mill base;
3) it is printed on the fabric respectively by flower stencil;
4) fabric dries 27min in the environment of 75 DEG C;
5) fabric is transferred on the forming machine that temperature is 132 DEG C and bakes 5min;
6) temperature is decatize 24min under conditions of 104 DEG C;
7) 12min is washed with the cleaning solution of 2g/L;Again with the soaping agent of 3g/L in 95 DEG C of 17min that soap;Finally use clear water
55 DEG C of cleaning 13min to obtain the final product.
Embodiment 3
1) parts by weights forms are as follows: and 5.7 parts of trioctyl lemon acid, 3.5 parts of lac resin, 0.6 part of starch, octyl phenol polyoxy
3.8 parts of vinethene, 1.8 parts of dibutyl phthalate, 2.4 parts of butyl methacrylate, 1.7 parts of isopropanol, methylol propylene
1.4 parts of amide, 0.4 part of modulating adhesive of sodium bicarbonate;
2) 22 parts of adhesives are made into slurry by weight, 1.5 parts of pigment is added, moisturizing is made into 100 parts of mill base;
3) it is printed on the fabric respectively by flower stencil;
4) fabric dries 29min in the environment of 65 DEG C;
5) fabric is transferred on the forming machine that temperature is 128 DEG C and bakes 6min;
6) temperature is decatize 27min under conditions of 104 DEG C;
7) 11min is washed with the cleaning solution of 2g/L;Again with the soaping agent of 3g/L in 94 DEG C of 18min that soap;Finally use clear water
58 DEG C of cleaning 11min to obtain the final product.
Embodiment 4
1) parts by weights forms are as follows: and 6 parts of trioctyl lemon acid, 4.5 parts of lac resin, 1 part of starch, octylphenol polyethylene ethylene oxide
5.5 parts of ether, 2 parts of dibutyl phthalate, 3 parts of butyl methacrylate, 2.5 parts of isopropanol, 2 parts of hydroxymethyl acrylamide,
0.5 part of modulating adhesive of sodium bicarbonate;
2) 27 parts of adhesives are made into slurry by weight, 0.5 part of pigment is added, moisturizing is made into 100 parts of mill base;
3) it is printed on the fabric respectively by flower stencil;
4) fabric dries 30min in the environment of 60 DEG C;
5) fabric is transferred on the forming machine that temperature is 135 DEG C and bakes 4min;
6) temperature is decatize 30min under conditions of 103 DEG C;
7) 10 min are washed with the cleaning solution of 2g/L;It is soaped again at 96 DEG C 15 min with the soaping agent of 3g/L;Finally with clear
Water 60 DEG C of 10 min of cleaning to obtain the final product.
Embodiment 5
1) parts by weights forms are as follows: and 4.5 parts of trioctyl lemon acid, 3 parts of lac resin, 0.5 part of starch, octyl phenol polyoxy second
3.7 parts of alkene ether, 1.5 parts of dibutyl phthalate, 2 parts of butyl methacrylate, 1.5 parts of isopropanol, hydroxymethyl acrylamide 1
Part, 0.3 part of modulating adhesive of sodium bicarbonate;
2) 18 parts of adhesives are made into slurry by weight, 3 parts of pigment is added, moisturizing is made into 100 parts of mill base;
3) it is printed on the fabric respectively by flower stencil;
4) fabric dries 25 min in the environment of 80 DEG C;
5) fabric is transferred on the forming machine that temperature is 127 DEG C and bakes 7min;
6) temperature is 20 min of decatize under conditions of 105 DEG C;
7) 15min is washed with the cleaning solution of 2g/L;Again with the soaping agent of 3g/L in 92 DEG C of 20min that soap;Finally use clear water
55 DEG C of cleaning 15min to obtain the final product.
Comparative example 1
1) parts by weights forms are as follows: and 5 parts of trioctyl lemon acid, 4 parts of lac resin, 5 parts of octyl phenol polyoxyethylene ether, adjacent benzene
1.7 parts of dibutyl carboxylic acid, 2.5 parts of butyl methacrylate, 2 parts of isopropanol, 1.5 parts of modulation bondings of hydroxymethyl acrylamide
Agent;
2) 22.8 parts of adhesives are made into slurry by weight, 2 parts of pigment is added, moisturizing is made into 100 parts of mill base;
3) it is printed on the fabric respectively by flower stencil;
4) fabric dries 27min in the environment of 67 DEG C ~ 70 DEG C;
5) fabric is transferred on the forming machine that temperature is 130 DEG C and bakes 5min;
6) temperature is decatize 25min under conditions of 104 DEG C;
7) 12min is washed with the cleaning solution of 2g/L;Again with the soaping agent of 3g/L in 94 DEG C of 18min that soap;Finally use clear water
56 DEG C of cleaning 12min to obtain the final product.
Comparative example 2
1) parts by weights forms are as follows: and 5 parts of trioctyl lemon acid, 5 parts of octyl phenol polyoxyethylene ether, dibutyl phthalate
1.7 parts, 2.5 parts of butyl methacrylate, 2 parts of isopropanol, 1.5 parts of hydroxymethyl acrylamide, 0.4 part of modulation bonding of sodium bicarbonate
Agent;
2) 22.8 parts of adhesives are made into slurry by weight, 2 parts of pigment is added, moisturizing is made into 100 parts of mill base;
3) it is printed on the fabric respectively by flower stencil;
4) fabric dries 27min in the environment of 67 DEG C ~ 70 DEG C;
5) fabric is transferred on the forming machine that temperature is 130 DEG C and bakes 5min;
6) temperature is decatize 25min under conditions of 104 DEG C;
7) 12min is washed with the cleaning solution of 2g/L;Again with the soaping agent of 3g/L in 94 DEG C of 18min that soap;Finally use clear water
56 DEG C of cleaning 12min to obtain the final product.
Comparative example 3
1) parts by weights forms are as follows: and 5 parts of dimethylaminoethyl acrylate, 1.5 parts of citric acid, dibutyl phthalate
1.7 parts, 2.5 parts of butyl methacrylate, 2 parts of isopropanol, 1.5 parts of modulating adhesives of hydroxymethyl acrylamide;
2) 22.8 parts of adhesives are made into slurry by weight, 2 parts of pigment is added, moisturizing is made into 100 parts of mill base;
3) it is printed on the fabric respectively by flower stencil;
4) fabric dries 27min in the environment of 67 DEG C ~ 70 DEG C;
5) fabric is transferred on the forming machine that temperature is 130 DEG C and bakes 5min;
6) temperature is decatize 25min under conditions of 104 DEG C;
7) 12min is washed with the cleaning solution of 2g/L;Again with the soaping agent of 3g/L in 94 DEG C of 18min that soap;Finally use clear water
56 DEG C of cleaning 12min to obtain the final product.
The performance test results of each embodiment and comparative example of table one
。
Illustrate: this experiment dry and wet rub fastness result using Wenzhou have an area of Instrument Ltd. Y-571B type crock fastness detect
Instrument detection, and feel test is to touch that evaluation is good and bad, and from Pyatyi is divided into soft firmly, 1 grade is most hard by hand, 5 grades are most soft.
The above described is only a preferred embodiment of the present invention, being not that the invention has other forms of limitations, appoint
What those skilled in the art changed or be modified as possibly also with the technology contents of the disclosure above equivalent variations etc.
Imitate embodiment.But without departing from the technical solutions of the present invention, according to the technical essence of the invention to above embodiments institute
Any simple modification, equivalent variations and the remodeling made, still fall within the protection scope of technical solution of the present invention.
Claims (7)
1. a kind of imitative reactive adhesive, it is characterised in that: parts by weight composition are as follows: 4.5 ~ 6 parts of trioctyl lemon acid, lac resin 3 ~
4.5 parts, 0.5 ~ 1 part of starch, 3.7 ~ 5.5 parts of octyl phenol polyoxyethylene ether, 1.5 ~ 2 parts of dibutyl phthalate, metering system
2 ~ 3 parts of acid butyl ester, 1.5 ~ 2.5 parts of isopropanol, 1 ~ 2 part of hydroxymethyl acrylamide, 0.3 ~ 0.5 part of sodium bicarbonate.
2. a kind of imitative reactive adhesive according to claim 1, it is characterised in that: parts by weight composition are as follows: citric acid three is pungent
5 ~ 5.5 parts of ester, 4 parts of lac resin, 0.7 part of starch, 4 ~ 5 parts of octyl phenol polyoxyethylene ether, 1.7 parts of dibutyl phthalate,
2.5 parts of butyl methacrylate, 2 parts of isopropanol, 1.5 parts of hydroxymethyl acrylamide, 0.4 part of sodium bicarbonate.
3. a kind of imitative reactive coating printing technology using 2 described adhesive of claims 1 or 2, it is characterised in that: by weight
18 ~ 27 parts of imitative reactive adhesives are made into slurry, 0.5 ~ 3 part of pigment is added, moisturizing is made into 100 parts of mill base, by flower stencil point
After not printing on the fabric, drying is baked and banked up with earth, decatize, is washed to obtain the final product.
4. a kind of imitative reactive coating printing technology according to claim 3, it is characterised in that: the drying is that fabric exists
25 min ~ 30min is dried in the environment of 60 DEG C ~ 80 DEG C.
5. a kind of imitative reactive coating printing technology according to claim 3, it is characterised in that: described bakes and banks up with earth as after stamp
Fabric to be transferred to temperature be to bake 4min ~ 7min on 127 DEG C ~ 135 DEG C of forming machine.
6. a kind of imitative reactive coating printing technology according to claim 3, it is characterised in that: the steam temperature is
103 DEG C ~ 105 DEG C, the time is 20 min ~ 30min.
7. a kind of imitative reactive coating printing technology according to claim 3, it is characterised in that: the washing is first to use
The cleaning solution of 2g/L washs 10 min ~ 15min;Again with the soaping agent of 3g/L in 92 DEG C ~ 96 DEG C 15 min that soap ~ 20min;Most
Afterwards with clear water in 55 DEG C ~ 60 DEG C cleaning 10 min ~ 15min.