CN107034699A - A kind of imitative reactive adhesive and pigment printing technique - Google Patents
A kind of imitative reactive adhesive and pigment printing technique Download PDFInfo
- Publication number
- CN107034699A CN107034699A CN201611090797.4A CN201611090797A CN107034699A CN 107034699 A CN107034699 A CN 107034699A CN 201611090797 A CN201611090797 A CN 201611090797A CN 107034699 A CN107034699 A CN 107034699A
- Authority
- CN
- China
- Prior art keywords
- parts
- fabric
- imitative reactive
- adhesive
- weight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
A kind of imitative reactive adhesive and pigment printing technique, belong to pigment printing technical field.Adhesive is characterised by：Weight is grouped into：4.5 ~ 6 parts of trioctyl lemon acid, 3 ~ 4.5 parts of lac resin, 0.5 ~ 1 part of starch, 3.7 ~ 5.5 parts of OPEO, 1.5 ~ 2 parts of dibutyl phthalate, 2 ~ 3 parts of butyl methacrylate, 1.5 ~ 2.5 parts of isopropanol, NMA 1 ~ 2,0.3 ~ 0.5 part of sodium acid carbonate.Printing technology is characterised by：18 ~ 27 parts of imitative reactive adhesives are made into slurry by weight, 0.5 ~ 3 part of pigment is added, moisturizing is made into 100 parts of mill base, after being printed respectively on fabric by flower stencil, drying, bake and bank up with earth, decatize, washing are produced.The feel of Printing made from this technique has reached the feel that traditional handicraft softening agent just has, and dry and wet fastness of rubbing is held at higher grade.
Description
Technical field
A kind of imitative reactive adhesive and pigment printing technique, belong to pigment printing technical field.
Background technology
Pigment printing is to use coating direct printing, and the technique is generally termed dry prints, to be different from wet prints（Or dye
Expect stamp）.Coating is different from dyestuff, and it is to fiber without substantivity.It can not be combined with fiber, it, which is that one kind is insoluble, has
Color powder, is mostly organic synthesis thing, but also organic/inorganic substance.Its principle of " coloring " on fiber can be generated by means of one kind
The synthetic resin of strong film, anchors at the surface of fiber, therefore the fabric of its peering various fiber can stamp.
Pigment printing technique is easy, with low cost, and effect is directly perceived, is the first choice of many Printings.But conventional coating
Printing but has following defect：1st, feel is poor；2nd, color fastness is poor.In view of disadvantage mentioned above, pigment printing is fitted always
For more low-grade product.Added in the formula of pigment printing technique after softening agent, feel can be improved, but fabric simultaneously
Dry and wet rub fastness, all declined, and add production cost.Pigment printing product how is set to have as reactive dye print
The same feel and washable ability is spent, is the target of dyeing effort always.
The content of the invention
The technical problem to be solved in the present invention is：Overcoming the deficiencies in the prior art, there is provided a kind of feel is submissive, good color fastness
Imitative reactive adhesive and pigment printing technique.
The technical solution adopted for the present invention to solve the technical problems is：The imitative reactive adhesive, it is characterised in that：Weight
Part constitutes：4.5 ~ 6 parts of trioctyl lemon acid, 3 ~ 4.5 parts of lac resin, 0.5 ~ 1 part of starch, OPEO 3.7 ~
5.5 parts, 1.5 ~ 2 parts of dibutyl phthalate, 2 ~ 3 parts of butyl methacrylate, 1.5 ~ 2.5 parts of isopropanol, methylol propylene
1 ~ 2 part of acid amides, 0.3 ~ 0.5 part of sodium acid carbonate.
It is preferred that, the parts by weight composition of adhesive is：5 ~ 5.5 parts of trioctyl lemon acid, 4 parts of lac resin, starch 0.7
Part, 4 ~ 5 parts of OPEO, 1.7 parts of dibutyl phthalate, 2.5 parts of butyl methacrylate, 2 parts of isopropanol,
1.5 parts of NMA, 0.4 part of sodium acid carbonate.It is preferred that adhesive formula to coordinate each component of the present invention the most proper,
Be made Printing feel and dry and wet rub fastness all reach the present invention optimum state.
A kind of imitative reactive coating printing technology using above-mentioned adhesive, it is characterised in that：It is imitative by 18 ~ 27 parts by weight
Reactive adhesive is made into slurry, adds 0.5 ~ 3 part of pigment, and moisturizing is made into 100 parts of mill base, is printed respectively on fabric by flower stencil
After system, drying, bake and bank up with earth, decatize, washing are produced.
The pigment printing technique of the present invention is provided to be opened in a kind of adhesive that mill base is prepared together with pigment, this adhesive
The invasive starch, sodium acid carbonate, lac resin and the trioctyl lemon acid that have used specified quantitative carrys out the bonding of adjusting coating stamp
The performance of agent so that the feel of Printing made from this technique has reached the feel that traditional handicraft softening agent just has, and
Dry and wet fastness of rubbing is held at higher grade.
Described drying is that fabric dries 25 min ~ 30min in the environment of 60 DEG C ~ 80 DEG C.The print prepared through the present invention
The drying of flower prod advanced specific degrees before baking and banking up with earth, can better ensure that color fastness.
It is described bake and bank up with earth as stamp after fabric be transferred on the forming machine that temperature is 127 DEG C ~ 135 DEG C bake 4min ~
7min.It is suitable to bake and bank up with earth the crucial means of comparison that technique is to maintain the feel and color fastness of the obtained Printing of the present invention, this
The preferred of invention is baked and banked up with earth under technique, and the property retention of feel and color fastness is in optimum state.
Described steam temperature is 103 DEG C ~ 105 DEG C, and the time is 20 min ~ 30min.
Described washing is first to wash 10 min ~ 15min with 2g/L cleaning solution；Again with 3g/L soaping agent 92 DEG C ~
96 DEG C of 15 min that soap ~ 20min；Finally 10 min ~ 15min is cleaned with clear water at 55 DEG C ~ 60 DEG C.Through felicity condition of the present invention
Decatize and washing after further improve the color fastness of product.
Compared with prior art, a kind of imitative reactive adhesive and pigment printing technique of the invention is had the advantage that
It is：The pigment printing technique of the present invention provides initiative in a kind of adhesive that mill base is prepared together with pigment, this adhesive
The starch, sodium acid carbonate, lac resin and the trioctyl lemon acid that have used specified quantitative carry out adjusting coating stamp adhesive
Performance so that the feel of Printing made from this technique has reached the feel that traditional handicraft softening agent just has, and dry and wet
Fastness of rubbing is held at higher grade., can be with using the fabric color fastness of the present invention in the case of binder dosage identical
High fastness adhesive compares favourably, and is significantly better than and uses traditional binders stamp.And fabric feeling is significantly better than conventional adhesive.
In the case of binder dosage identical, softening agent is identical to imitate feel with using traditional binders and high fastness adhesive to add
Really, the dry and wet of fabric rub fastness increase.
Embodiment
With reference to specific embodiment, the present invention will be further described, and wherein embodiment 1 is most preferred embodiment.
Embodiment 1
1）It is grouped into by weight：5 parts of trioctyl lemon acid, 4 parts of lac resin, 0.7 part of starch, OPEO 5
Part, 1.7 parts of dibutyl phthalate, 2.5 parts of butyl methacrylate, 2 parts of isopropanol, 1.5 parts of NMA, carbon
Sour 0.4 part of modulating adhesive of hydrogen sodium；
2）22.8 parts of adhesives are made into slurry by weight, 2 parts of pigment is added, moisturizing is made into 100 parts of mill base；
3）Printed respectively on fabric by flower stencil；
4）Fabric dries 27min in the environment of 67 DEG C ~ 70 DEG C；
5）Fabric is transferred on the forming machine that temperature is 130 DEG C and bakes 5min；
6）Temperature is decatize 25min under conditions of 104 DEG C；
7）12min is washed with 2g/L cleaning solution；Again with 3g/L soaping agent in 94 DEG C of 18min that soap；Finally with clear water 56
DEG C cleaning 12min produce.
Embodiment 2
1）It is grouped into by weight：5.5 parts of trioctyl lemon acid, 4 parts of lac resin, 0.7 part of starch, OPEO
4 parts, 1.7 parts of dibutyl phthalate, 2.5 parts of butyl methacrylate, 2 parts of isopropanol, 1.5 parts of NMA,
0.4 part of modulating adhesive of sodium acid carbonate；
2）22.3 parts of adhesives are made into slurry by weight, 2 parts of pigment is added, moisturizing is made into 100 parts of mill base；
3）Printed respectively on fabric by flower stencil；
4）Fabric dries 27min in the environment of 75 DEG C；
5）Fabric is transferred on the forming machine that temperature is 132 DEG C and bakes 5min；
6）Temperature is decatize 24min under conditions of 104 DEG C；
7）12min is washed with 2g/L cleaning solution；Again with 3g/L soaping agent in 95 DEG C of 17min that soap；Finally with clear water 55
DEG C cleaning 13min produce.
Embodiment 3
1）It is grouped into by weight：5.7 parts of trioctyl lemon acid, 3.5 parts of lac resin, 0.6 part of starch, octyl phenol polyoxyethylene
3.8 parts of ether, 1.8 parts of dibutyl phthalate, 2.4 parts of butyl methacrylate, 1.7 parts of isopropanol, NMA
1.4 parts, 0.4 part of modulating adhesive of sodium acid carbonate；
2）22 parts of adhesives are made into slurry by weight, 1.5 parts of pigment is added, moisturizing is made into 100 parts of mill base；
3）Printed respectively on fabric by flower stencil；
4）Fabric dries 29min in the environment of 65 DEG C；
5）Fabric is transferred on the forming machine that temperature is 128 DEG C and bakes 6min；
6）Temperature is decatize 27min under conditions of 104 DEG C；
7）11min is washed with 2g/L cleaning solution；Again with 3g/L soaping agent in 94 DEG C of 18min that soap；Finally with clear water 58
DEG C cleaning 11min produce.
Embodiment 4
1）It is grouped into by weight：6 parts of trioctyl lemon acid, 4.5 parts of lac resin, 1 part of starch, OPEO
5.5 parts, 2 parts of dibutyl phthalate, 3 parts of butyl methacrylate, 2.5 parts of isopropanol, 2 parts of NMA, carbon
Sour 0.5 part of modulating adhesive of hydrogen sodium；
2）27 parts of adhesives are made into slurry by weight, 0.5 part of pigment is added, moisturizing is made into 100 parts of mill base；
3）Printed respectively on fabric by flower stencil；
4）Fabric dries 30min in the environment of 60 DEG C；
5）Fabric is transferred on the forming machine that temperature is 135 DEG C and bakes 4min；
6）Temperature is decatize 30min under conditions of 103 DEG C；
7）10 min are washed with 2g/L cleaning solution；Soaped again with 3g/L soaping agent at 96 DEG C 15 min；Finally existed with clear water
60 DEG C of 10 min of cleaning are produced.
Embodiment 5
1）It is grouped into by weight：4.5 parts of trioctyl lemon acid, 3 parts of lac resin, 0.5 part of starch, OPEO
3.7 parts, 1.5 parts of dibutyl phthalate, 2 parts of butyl methacrylate, 1.5 parts of isopropanol, 1 part of NMA,
0.3 part of modulating adhesive of sodium acid carbonate；
2）18 parts of adhesives are made into slurry by weight, 3 parts of pigment is added, moisturizing is made into 100 parts of mill base；
3）Printed respectively on fabric by flower stencil；
4）Fabric dries 25 min in the environment of 80 DEG C；
5）Fabric is transferred on the forming machine that temperature is 127 DEG C and bakes 7min；
6）Temperature is the min of decatize 20 under conditions of 105 DEG C；
7）15min is washed with 2g/L cleaning solution；Again with 3g/L soaping agent in 92 DEG C of 20min that soap；Finally with clear water 55
DEG C cleaning 15min produce.
Comparative example 1
1）It is grouped into by weight：5 parts of trioctyl lemon acid, 4 parts of lac resin, 5 parts of OPEO, O-phthalic
1.7 parts of dibutyl phthalate, 2.5 parts of butyl methacrylate, 2 parts of isopropanol, 1.5 parts of modulating adhesives of NMA；
2）22.8 parts of adhesives are made into slurry by weight, 2 parts of pigment is added, moisturizing is made into 100 parts of mill base；
3）Printed respectively on fabric by flower stencil；
4）Fabric dries 27min in the environment of 67 DEG C ~ 70 DEG C；
5）Fabric is transferred on the forming machine that temperature is 130 DEG C and bakes 5min；
6）Temperature is decatize 25min under conditions of 104 DEG C；
7）12min is washed with 2g/L cleaning solution；Again with 3g/L soaping agent in 94 DEG C of 18min that soap；Finally with clear water 56
DEG C cleaning 12min produce.
Comparative example 2
1）It is grouped into by weight：5 parts of trioctyl lemon acid, 5 parts of OPEO, dibutyl phthalate 1.7
Part, 2.5 parts of butyl methacrylate, 2 parts of isopropanol, 1.5 parts of NMA, 0.4 part of modulating adhesive of sodium acid carbonate；
2）22.8 parts of adhesives are made into slurry by weight, 2 parts of pigment is added, moisturizing is made into 100 parts of mill base；
3）Printed respectively on fabric by flower stencil；
4）Fabric dries 27min in the environment of 67 DEG C ~ 70 DEG C；
5）Fabric is transferred on the forming machine that temperature is 130 DEG C and bakes 5min；
6）Temperature is decatize 25min under conditions of 104 DEG C；
7）12min is washed with 2g/L cleaning solution；Again with 3g/L soaping agent in 94 DEG C of 18min that soap；Finally with clear water 56
DEG C cleaning 12min produce.
Comparative example 3
1）It is grouped into by weight：5 parts of dimethylaminoethyl acrylate, 1.5 parts of citric acid, dibutyl phthalate 1.7
Part, 2.5 parts of butyl methacrylate, 2 parts of isopropanol, 1.5 parts of modulating adhesives of NMA；
2）22.8 parts of adhesives are made into slurry by weight, 2 parts of pigment is added, moisturizing is made into 100 parts of mill base；
3）Printed respectively on fabric by flower stencil；
4）Fabric dries 27min in the environment of 67 DEG C ~ 70 DEG C；
5）Fabric is transferred on the forming machine that temperature is 130 DEG C and bakes 5min；
6）Temperature is decatize 25min under conditions of 104 DEG C；
7）12min is washed with 2g/L cleaning solution；Again with 3g/L soaping agent in 94 DEG C of 18min that soap；Finally with clear water 56
DEG C cleaning 12min produce.
The performance test results of each embodiment of table one and comparative example
。
Explanation：This experiment dry and wet rub fastness result using Wenzhou have an area of Instrument Ltd. Y-571B types crock fastness detect
Instrument is detected, and feel test is to touch to evaluate good and bad by hand, and from Pyatyi is divided into soft firmly, 1 grade most hard, and 5 grades most soft.
The above described is only a preferred embodiment of the present invention, being not the limitation for making other forms to the present invention, appoint
What those skilled in the art changed or be modified as possibly also with the technology contents of the disclosure above equivalent variations etc.
Imitate embodiment.But it is every without departing from technical solution of the present invention content, the technical spirit according to the present invention is to above example institute
Any simple modification, equivalent variations and the remodeling made, still fall within the protection domain of technical solution of the present invention.
Claims (7)
1. a kind of imitative reactive adhesive, it is characterised in that：Parts by weight are constituted：4.5 ~ 6 parts of trioctyl lemon acid, lac resin 3 ~
4.5 parts, 0.5 ~ 1 part of starch, 3.7 ~ 5.5 parts of OPEO, 1.5 ~ 2 parts of dibutyl phthalate, metering system
2 ~ 3 parts of acid butyl ester, 1.5 ~ 2.5 parts of isopropanol, 1 ~ 2 part of NMA, 0.3 ~ 0.5 part of sodium acid carbonate.
2. a kind of imitative reactive adhesive according to claim 1, it is characterised in that：Parts by weight are constituted：Citric acid three is pungent
5 ~ 5.5 parts of ester, 4 parts of lac resin, 0.7 part of starch, 4 ~ 5 parts of OPEO, 1.7 parts of dibutyl phthalate,
2.5 parts of butyl methacrylate, 2 parts of isopropanol, 1.5 parts of NMA, 0.4 part of sodium acid carbonate.
3. a kind of imitative reactive coating printing technology of the described adhesive of utilization claim 1 or 2, it is characterised in that：By weight
18 ~ 27 parts of imitative reactive adhesives are made into slurry, 0.5 ~ 3 part of pigment is added, moisturizing is made into 100 parts of mill base, by flower stencil point
After not printed on fabric, drying, bake and bank up with earth, decatize, washing are produced.
4. a kind of imitative reactive coating printing technology according to claim 3, it is characterised in that：Described drying is that fabric exists
25 min ~ 30min is dried in the environment of 60 DEG C ~ 80 DEG C.
5. a kind of imitative reactive coating printing technology according to claim 3, it is characterised in that：Described bakes and banks up with earth as after stamp
Fabric to be transferred to temperature be to bake 4min ~ 7min on 127 DEG C ~ 135 DEG C of forming machine.
6. a kind of imitative reactive coating printing technology according to claim 3, it is characterised in that：Described steam temperature is
103 DEG C ~ 105 DEG C, the time is 20 min ~ 30min.
7. a kind of imitative reactive coating printing technology according to claim 3, it is characterised in that：Described washing is first to use
2g/L cleaning solution washing 10 min ~ 15min；Again with 3g/L soaping agent in 92 DEG C ~ 96 DEG C 15 min that soap ~ 20min；Most
Afterwards 10 min ~ 15min is cleaned with clear water at 55 DEG C ~ 60 DEG C.