CN107033991A - A kind of bell metal cold heading technique lubricant compositions - Google Patents
A kind of bell metal cold heading technique lubricant compositions Download PDFInfo
- Publication number
- CN107033991A CN107033991A CN201610963534.3A CN201610963534A CN107033991A CN 107033991 A CN107033991 A CN 107033991A CN 201610963534 A CN201610963534 A CN 201610963534A CN 107033991 A CN107033991 A CN 107033991A
- Authority
- CN
- China
- Prior art keywords
- lubricant compositions
- cold heading
- metal cold
- heading technique
- bell metal
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of bell metal cold heading technique lubricant compositions, using oily based on HVI400 base oils, coordinate a variety of compound additives.Including:Antioxidant, metal deactivator, oiliness improver, friction improver, extreme pressure agent, antiwear additive, antirust agent, anti-foaming agent, oxidation and corrosion inhibitor, tackifier, dispersant etc..The composition of the present invention has good carrying wear resistence, Squeezing ground, low temperature flow diffusivity, lubricity, cooling; film strength is big, oil film thickness keeps stable; free from extraneous odour, do not stimulate skin; finish is improved, part to be processed surface not corrosion and oxidation is protected, power consumption is reduced; good anti-foaming property, resistance to emulsion, thermal oxide are qualitative, shear resistant is good; the generation of sediment and paint film is reduced, molding part easy cleaning extends die life.
Description
Technical field
A kind of bell metal cold heading technique lubricant compositions of the present invention belong to metal working process field of lubricant.
Background technology
Bronze is that metal smelts alloy earliest in history, and the alloy of tin or lead is added in fine copper (red metal), there is special
Importance and historic significance.Bronze is the name that modern gives, and ancient times bronze is that yellow is partially red, and after being embedded in soil color because
Oxidation and it is steel gray, be referred to as bronze.Compared with fine copper (red metal), bronze intensity height and fusing point low (25% tin smelting bronze, fusing point
800 DEG C will be reduced to.The fusing point of fine copper (red metal) is 1083 DEG C).Bronze casting is good, and wear-resisting and chemical property is stable.
Cold-heading processing is the forging method shaped at normal temperatures to metal bar material jumping-up (being often gathering stock) using mould.
Cold-heading is another form of upsetting.More metal mold becomes theoretical, applies certain pressure to metal stock at normal temperatures,
It is allowed to be deformed in die cavity.Shaped by defined shape and size.Cold heading technique is widely used in middle finding and various
The standard component of type.
Cold heading technique is mainly characterized by no machining, and stock utilization is high, and utilization rate is up to 80~90%, and metal material
Stream line will not be cut off, therefore product intensity is higher than machining or casting part strength, be given birth in certain batch
Under the conditions of production, cold-heading processing cost is more much lower than other processing costs, it is adaptable to it is generally necessary to cutting members and fastener etc.
The Product processing of symmetrical shape.Dimensional accuracy, weight accuracy and mechanical property of product etc. are attained by higher requirement.
The content of the invention
There is good carrying wear resistence, Squeezing ground, low temperature flow the technical problem to be solved in the present invention is to provide a kind of
Diffusivity, lubricity, cooling, film strength is big, oil film thickness keeps stable, free from extraneous odour, does not stimulate skin, improves bright and clean
Degree, protect part to be processed surface not corrosion and oxidation, reduction power consumption, and good anti-foaming property, resistance to emulsion, thermal oxide are fixed
Property it is good, reduce the generation of sediment and paint film, the bell metal cold heading technique lubricant compositions of molding part easy cleaning.
The present invention solves above-mentioned technical problem by following technical solution:
A kind of bell metal cold heading technique lubricant compositions, using oily based on HVI400 base oils, coordinate a variety of
Compound additive, its each mass percent composition composition:
The mass percent summation of above each component is 100%.
Antioxidant is that the copper naphthenate and 50% dinonyldiphenylamine T558 of mass ratio 50% are combined;
Metal deactivator is that the benzotriazole derivative T551 and 50% of mass ratio 50% thiadiazole is combined.
Oiliness improver is soybean oil;
Friction improver is alkyl phosphite.
Extreme pressure agent is boronation phosphate T3011;
Antiwear additive is chlorinated paraffin T301.
Antirust agent is that the BTA T706 and 50% of mass ratio 50% alkenyl succinic acid sheep ester T747 is combined;
Anti-foaming agent is methyl-silicone oil T901.
Oxidation and corrosion inhibitor is fatty diglycollic amide phosphate;
Tackifier are ethylene-propylene copolymer T612A.
Dispersant is high molecular weight polyisobutylene base succimide T164B.
The advantage of the invention is that:The good carrying wear resistence of composition of the present invention, Squeezing ground (not plucking, pull, have
The service life of effect extension punch die), low temperature flow diffusivity, lubricity, cooling, film strength is big, oil film thickness keeps steady
It is fixed, free from extraneous odour, do not stimulate skin;Finish is improved, part to be processed surface not corrosion and oxidation is protected, power consumption is reduced,
Low temperature flow is good, and good anti-foaming property, resistance to emulsion, thermal oxide are qualitative good, reduces the generation of sediment and paint film, molding part
Easy cleaning.
Embodiment
Embodiment 1:
Following each component is pressed into the mediation of row mass percent to form:
Component | Mass percentage content |
HVI400 base oils | Surplus |
The copper naphthenate of mass ratio 50% and 50% dinonyldiphenylamine (T558) are compound | 0.2% |
The benzotriazole derivative (T551) of mass ratio 50% and 50% thiadiazole are compound | 0.15% |
Soybean oil | 4.0% |
Alkyl phosphite | 2.0% |
Boronation phosphate (T3011) | 3.5% |
Chlorinated paraffin (T301) | 3.5% |
The BTA (T706) of mass ratio 50% and 50% alkenyl succinic acid sheep ester (T747) are compound | 0.2% |
Methyl-silicone oil (T901) | 30ppm |
Fatty diglycollic amide phosphate | 0.7% |
Ethylene-propylene copolymer (T612A) | 4.0% |
High molecular weight polyisobutylene base succimide (T164B) | 3.0% |
Above each component mass percentage content summation is 100%.
Embodiment 2:
Following each component is pressed into the mediation of row mass percent to form:
Component | Mass percentage content |
HVI400 base oils | Surplus |
The copper naphthenate of mass ratio 50% and 50% dinonyldiphenylamine (T558) are compound | 0.15% |
The benzotriazole derivative (T551) of mass ratio 50% and 50% thiadiazole are compound | 0.1% |
Soybean oil | 3.5% |
Alkyl phosphite | 2.0% |
Boronation phosphate (T3011) | 3.0% |
Chlorinated paraffin (T301) | 3.0% |
The BTA (T706) of mass ratio 50% and 50% alkenyl succinic acid sheep ester (T747) are compound | 0.1% |
Methyl-silicone oil (T901) | 35ppm |
Fatty diglycollic amide phosphate | 0.8% |
Ethylene-propylene copolymer (T612A) | 3.0% |
High molecular weight polyisobutylene base succimide (T164B) | 3.5% |
Above each component mass percentage content summation is 100%.
Embodiment 3:
Following each component is pressed into the mediation of row mass percent to form:
Component | Mass percentage content |
HVI400 base oils | Surplus |
The copper naphthenate of mass ratio 50% and 50% dinonyldiphenylamine (T558) are compound | 0.1% |
The benzotriazole derivative (T551) of mass ratio 50% and 50% thiadiazole are compound | 0.2% |
Soybean oil | 5.0% |
Alkyl phosphite | 2.0% |
Boronation phosphate (T3011) | 2.0% |
Chlorinated paraffin (T301) | 3.0% |
The BTA (T706) of mass ratio 50% and 50% alkenyl succinic acid sheep ester (T747) it is combined | 0.15% |
Methyl-silicone oil (T901) | 30ppm |
Fatty diglycollic amide phosphate | 0.9% |
Ethylene-propylene copolymer (T612A) | 5.0% |
High molecular weight polyisobutylene base succimide (T164B) | 3.0% |
Above each component mass percentage content summation is 100%.
The main physical and chemical index of the product of embodiment 1:
The main physical and chemical index of the product of embodiment 2:
The main physical and chemical index of the product of embodiment 3:
Claims (7)
1. a kind of bell metal cold heading technique lubricant compositions, it is characterised in that:Using oil based on HVI400 base oils,
Coordinate a variety of compound additives, its each mass percent composition composition:
The mass percent summation of above each component is 100%.
2. a kind of bell metal cold heading technique lubricant compositions as claimed in claim 1, it is characterised in that antioxidant is matter
The copper naphthenate and 50% dinonyldiphenylamine T558 measured than 50% are compound;Metal deactivator is the benzotriazole of mass ratio 50%
Derivative T551 and 50% thiadiazole is combined.
3. a kind of bell metal cold heading technique lubricant compositions as claimed in claim 1, it is characterised in that oiliness improver is big
Soya-bean oil;Friction improver is alkyl phosphite.
4. a kind of bell metal cold heading technique lubricant compositions as claimed in claim 1, it is characterised in that extreme pressure agent is boron
Change phosphate T3011;Antiwear additive is chlorinated paraffin T301.
5. a kind of bell metal cold heading technique lubricant compositions as claimed in claim 1, it is characterised in that antirust agent is matter
The alkenyl succinic acid sheep ester T747 for measuring the BTA T706 and 50% than 50% is combined;Anti-foaming agent is methyl-silicone oil T901.
6. a kind of bell metal cold heading technique lubricant compositions as claimed in claim 1, it is characterised in that oxidation and corrosion inhibitor
It is fatty diglycollic amide phosphate;Tackifier are ethylene-propylene copolymer T612A.
7. a kind of bell metal cold heading technique lubricant compositions as claimed in claim 1, it is characterised in that dispersant is high
Molec weight polyisobutylene base succimide T164B.