CN107022240A - The aqueous anilox roll inking of high adhesion force - Google Patents
The aqueous anilox roll inking of high adhesion force Download PDFInfo
- Publication number
- CN107022240A CN107022240A CN201710079477.7A CN201710079477A CN107022240A CN 107022240 A CN107022240 A CN 107022240A CN 201710079477 A CN201710079477 A CN 201710079477A CN 107022240 A CN107022240 A CN 107022240A
- Authority
- CN
- China
- Prior art keywords
- parts
- agent
- aqueous
- emulsion
- anilox roll
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of aqueous anilox roll inking of high adhesion force, it includes the component of following parts by weight：26~35 parts of acrylic emulsion A, 20~29 parts of acrylic emulsion B, 15~24 parts of Polyurethane emulsion, 0.5~3 part of wetting agent, 0.5~3 part of defoamer, 0.5~3 part of levelling agent, 0.5~3 part of wax powder, 10~20 parts of pigment, 0.5~4 part of dispersant, 0.5~3 part of scratch resistance agent, 0.5~3 part of thickener, 0.5~4 part of pH adjusting agent；Wherein acrylic emulsion A is that Shanghai is that Shanghai court multiplies the acrylic emulsions of industry TR 824 towards the acrylic emulsions of industry TR 803, acrylic emulsion B is multiplied.This water-based ink has pollution-free, environmentally friendly reliable, and solvent is aqueous low, ink noresidue on packaging material, non-toxic, easily reclaims, the advantages of cheap, and the hardness of film that ink of the invention is obtained through anilox roll is high, and adhesive force is strong, and printing levelability is good.
Description
Technical field
The invention belongs to ink area, tool manikin is related to a kind of aqueous anilox roll inking of high adhesion force and its preparation
Method.
Background technology
Gravure ink is a kind of coloured colloid of stabilization, and dispersion be able to will be coated on appropriate mode of printing
On appropriate material, make it that character pattern and color is presented and ceased there is provided line and attraction.
With the progress and development of society, the raising of national life level, class requirement of the society to plastic flexible package is got over
Come higher, demand is increasing, the kind and style of flexible package are increasingly various, and usage amount also increasingly increases, current domestic modeling
Expect the printing 95% of paper flexible package above is by the way of intaglio printing, plastics, paper gravure printing ink contain substantial amounts of
Organic solvent（Account for 50%）, the low boiling such as toluene, ethyl acetate, butanone, high volatilization contain aromatic hydrocarbon, not only poisonous but also inflammable, no
But the residual of organic solvent is easily produced in packaging, and is also the primary pollution source of intaglio printing environmental pollution.Therefore
The production of the gravure inks such as Plastics in China, paper is by regulation systems such as fire service law, labor safety method, the law of food safety
About.Printing packaging manufacturing industry is also faced with environmental protection cry continuous surging and Environmental protective policy, the law of food safety
Deng increasingly severe multiple pincer attack.Therefore it is extremely urgent green base gravure ink that is aqueous low and meeting environmental requirement to be developed again.
The content of the invention
The purpose of the present invention is that there is provided a kind of aqueous anilox roll inking and its preparation side on the basis of existing technology
Method.
The purpose of the present invention can be reached by following measures：
A kind of aqueous anilox roll inking of high adhesion force, it includes the component of following parts by weight：26~35 parts of acrylic emulsion A,
20~29 parts of acrylic emulsion B, 15~24 parts of Polyurethane emulsion, 0.5~3 part of wetting agent, 0.5~3 part of defoamer, levelling agent
0.5~3 part, 0.5~3 part of wax powder, 10~20 parts of pigment, 0.5~4 part of dispersant, 0.5~3 part of scratch resistance agent, thickener 0.5~3
Part, 0.5~4 part of pH adjusting agent；Wherein acrylic emulsion A is that Shanghai court multiplies industry TR-803 acrylic emulsions, acrylic emulsion B
For Shanghai, court multiplies industry TR-824 acrylic emulsions.
In a kind of preferred scheme, aqueous anilox roll inking includes the component of following parts by weight：Acrylic emulsion A 27
~33 parts, 22~27 parts of acrylic emulsion B, 17~23 parts of Polyurethane emulsion, 0.5~2 part of wetting agent, 0.5~2 part of defoamer,
0.5~2 part of levelling agent, 0.5~2 part of wax powder, 12~18 parts of pigment, 1~4 part of dispersant, 0.5~2 part of scratch resistance agent, thickener
0.5~2 part, 1~4 part of pH adjusting agent.
In another preferred scheme, aqueous anilox roll inking includes the component of following parts by weight：Acrylic emulsion A
28~32 parts, 23~27 parts of acrylic emulsion B, 18~22 parts of Polyurethane emulsion, 0.5~2 part of wetting agent, defoamer 0.5~2
Part, 0.5~2 part of levelling agent, 0.5~2 part of wax powder, 13~17 parts of pigment, 1~3 part of dispersant, 0.5~2 part of scratch resistance agent, thickening
0.5~2 part of agent, 1~3 part of pH adjusting agent.
In a kind of more preferably scheme, aqueous anilox roll inking includes the component of following parts by weight：Acrylic emulsion A
30 parts, 25 parts of acrylic emulsion B, 20 parts of Polyurethane emulsion, 1 part of wetting agent, 1 part of defoamer, 1 part of levelling agent, 1 part of wax powder, face
15 parts of material, 2 parts of dispersant, 1 part of scratch resistance agent, 1 part of thickener, 2 parts of pH adjusting agent.
Polyurethane emulsion in the present invention is selected from connection solidification and learns Polyurethane emulsion, this fertile chemical Polyurethane emulsion, Hubei wound
Prosperous CX-9129G Polyurethanes emulsion, Dongguan HTC HD566 Polyurethanes emulsion or super great chemical industry F-11C Polyurethane emulsions.
Wetting agent in the present invention is selected from Bi Ke chemistry BYK347, Bi Ke chemistry BYK346, Shanghai and wins Supreme Being Tego Do-75;
KL245、Tego Do-75;KL500、Tego Do-75;The KL 270 or modest chemical W469 of moral.
Defoamer in the present invention is selected from Shanghai and wins Supreme Being Tego k3;830、Tego k3;822、Tego k3;482nd, moral is modest
Chemical W-0506, Shanghai sea ease SD670, Bi Ke chemistry BYK-085 or Bi Ke chemistry BYK-071.
Dispersant in the present invention is selected from EFKA4560 or the dispersants of SN 5040.
Levelling agent in the present invention is selected from BYK333, BYK361, Glide 432, Flow 300 or the levellings of Efka 3600
Agent.
Scratch resistance agent in the present invention is selected from BYK378, BYK300 or BYK306.
Thickener in the present invention surpass/is opened up selected from Tao Shi thickeners TT-935, ROHM AND HAAS ACRYSOL ASE-60 or Shen
Good SC-01 thickeners.
Pigment in the present invention is selected from red pigment, yellow uitramarine, blue pigment or black pigment.
A kind of preparation method of above-mentioned aqueous anilox roll inking：First by acrylic emulsion A, acrylic emulsion B and polyamine
After the mixing of ester emulsion, wax powder and pigment are added, high-speed stirred is uniform, is ground to behind fineness≤10 μm, continuously adds after being stirred
Wetting agent, defoamer, levelling agent, dispersant, scratch resistance agent and thickener, are eventually adding pH adjusting agent and adjust pH value to 7~9.
In printing process, the transmission and ink amount control of aqueous anilox roll inking are undertaken by anilox roll, therefore
Need to select anilox roll according to product requirement, to obtain preferable print distinctness and resolving power.
The present invention can make under the cooperation of other components aqueous anilox roll by the mutual synergies of three kinds of emulsions
The printing levelability of inking, adhesive force, hardness, viscosity, it is low it is aqueous etc. reach preferably effect simultaneously, experiment is found, is removed
Any emulsion or emulsion consumption is then unable to reach Expected Results not in scope of the presently claimed invention.
Beneficial effects of the present invention：10 μm of the fineness ﹤ of the aqueous anilox roll inking of the present invention, solid content is 45 ± 5%,
Viscosity：25 DEG C apply 4 glasss 50-65 seconds or 25-35 seconds, pH value 7-9.This water-based ink has pollution-free, environmentally friendly reliable, aqueous solvent
Property low, ink noresidue on packaging material, it is non-toxic, easily reclaim, the advantages of cheap, ink of the invention is through anilox roll
Obtained hardness of film is high, and adhesive force is strong, and printing levelability is good.
Embodiment
Present disclosure is described further with reference to embodiments.But protection scope of the present invention is not limited to following
Each embodiment.
The preparation method of each example ink is：After first acrylic emulsion A, acrylic emulsion B and Polyurethane emulsion are mixed,
Add wax powder and pigment, high-speed stirred is uniform, is ground to after being stirred behind fineness≤10 μm, continuously add wetting agent, defoamer,
Levelling agent, dispersant, scratch resistance agent and thickener, are eventually adding pH adjusting agent and adjust pH value to 7~9.
Embodiment 1
The parts by weight of aqueous anilox roll inking are constituted：Shanghai multiplies towards 30 parts of industry TR-803 acrylic emulsions, Shanghai court is multiplied
25 parts of industry TR-824 acrylic emulsions, 20 parts of Dongguan HTC HD566 Polyurethanes emulsion, 1 part of BYK346 wetting agents, W-0506
1 part of defoamer, 1 part of 300 levelling agents of Flow, 1 part of wax powder, 15 parts of pigment, 2 parts of EFKA4560 dispersants, BYK378 scratch resistance agents 1
Part, open up good 1 part of SC-01 thickeners, 2 parts of pH adjusting agent.
Embodiment 2
The parts by weight of aqueous anilox roll inking are constituted：Shanghai multiplies towards 30 parts of industry TR-803 acrylic emulsions, Shanghai court is multiplied
25 parts of industry TR-824 acrylic emulsions, 20 parts of Dongguan HTC HD566 Polyurethanes emulsion, 1 part of BYK346 wetting agents, Hai Yi
1 part of SD670 defoamers, 1 part of 432 levelling agents of Glide, 1 part of wax powder, 15 parts of pigment, 2 parts of EFKA4560 dispersants, BYK378 resists
Scrape 1 part of agent, 1 part of ACRYSOL ASE-60 thickeners, 2 parts of pH adjusting agent.
Embodiment 3
The parts by weight of aqueous anilox roll inking are constituted：Shanghai multiplies towards 30 parts of industry TR-803 acrylic emulsions, Shanghai court is multiplied
25 parts of industry TR-824 acrylic emulsions, super great 20 parts of chemical industry F-11C Polyurethanes emulsion, 1 part of BYK347 wetting agents, BYK-
085 1 part of defoamer, 1 part of BYK361 levelling agents, 1 part of wax powder, 15 parts of pigment, 2 parts of 504 dispersants of SN, BYK300 scratch resistance agents 1
Part, 1 part of Tao Shi TT-935 thickeners, 2 parts of pH adjusting agent.
Embodiment 4
The parts by weight of aqueous anilox roll inking are constituted：Shanghai multiplies towards 30 parts of industry TR-803 acrylic emulsions, Shanghai court is multiplied
25 parts of industry TR-824 acrylic emulsions, super great 20 parts of chemical industry F-11C Polyurethanes emulsion, 1 part of BYK347 wetting agents, BYK-
071 1 part of defoamer, 1 part of BYK333 levelling agents, 1 part of wax powder, 15 parts of pigment, 2 parts of 504 dispersants of SN, BYK306 scratch resistance agents 1
Part, 1 part of Tao Shi TT-935 thickeners, 2 parts of pH adjusting agent.
Comparative example 1
Shanghai in embodiment 1 is removed towards industry TR-803 acrylic emulsions are multiplied, and Shanghai court is multiplied into industry TR-824 propylene
The consumption of yogurt liquid is changed to 55 parts, other be the same as Examples 1.
Comparative example 2
Shanghai in embodiment 1 is removed towards industry TR-824 acrylic emulsions are multiplied, and Shanghai court is multiplied into industry TR-803 propylene
The consumption of yogurt liquid is changed to 55 parts, other be the same as Examples 1.
Comparative example 3
Shanghai in embodiment 1 is changed to 40 towards the consumption for multiplying industry TR-803 acrylic emulsions, and Shanghai court is multiplied into industry TR-
The consumption of 824 acrylic emulsions is changed to 15 parts, other be the same as Examples 1.
Embodiment 5
10 μm of the fineness ﹤ of embodiment 1-4 aqueous anilox roll inking, solid content is 45 ± 5%, viscosity：25 DEG C apply 4 glasss
50-65 seconds or 25-35 seconds, pH value 7-9.
By the ink obtained by each example by anilox printing in substrate surface, dried after being completed for printing, obtain film, to applying
Film is tested.
The adhesive force of film is with reference to standard GB/T/T9286-1998《The lattice of drawing of paint and varnish paint film are tested》[enter
The stroke lattice tape pull method of row ten is tested, and test result is expressed as 0-5 grades, wherein 0 grade best, 5 grades worst.
The hardness of film is with reference to standard GB/T/T6739-1996《Hardness of film pencil determination method》It is measured, is divided into
Totally 13 grades of 6H to 6B, wherein 6H is most hard, and 6B is most soft.
Film is covered using this resin combination is printed on mylar film, and mylar film is placed under LED after drying
Look after, can't see LED light line good for 0 grade, it can be seen that LED light line is 1 grade poor.
Printing levelability uses visual observations, and smooth even is 0 grade good, and it is 1 grade to have rough or uneven situation.
The ink film that each example is obtained by more than further carries out performance test, as a result such as following table.
| Performance | Embodiment 1 | Embodiment 2 | Embodiment 3 | Embodiment 4 | Comparative example 1 | Comparative example 2 | Comparative example 3 |
| Hardness H | 4 | 3 | 3 | 3 | 1 | 1 | 2 |
| Adhesive force | 2 | 2 | 3 | 2 | 5 | 5 | 4 |
| Print levelability | 0 | 0 | 0 | 0 | 1 | 1 | 1 |
Claims (9)
1. a kind of aqueous anilox roll inking of high adhesion force, it is characterised in that it includes the component of following parts by weight：Propylene yogurt
26~35 parts of liquid A, 20~29 parts of acrylic emulsion B, 15~24 parts of Polyurethane emulsion, 0.5~3 part of wetting agent, defoamer 0.5
~3 parts, 0.5~3 part of levelling agent, 0.5~3 part of wax powder, 10~20 parts of pigment, 0.5~4 part of dispersant, 0.5~3 part of scratch resistance agent,
0.5~3 part of thickener, 0.5~4 part of pH adjusting agent；Wherein acrylic emulsion A is that Shanghai court multiplies industry TR-803 propylene yogurts
Liquid, acrylic emulsion B is that Shanghai court multiplies industry TR-824 acrylic emulsions.
2. aqueous anilox roll inking according to claim 1, it is characterised in that it includes the component of following parts by weight：Third
27~33 parts of olefin(e) acid latex A, 22~27 parts of acrylic emulsion B, 17~23 parts of Polyurethane emulsion, 0.5~2 part of wetting agent disappear
0.5~2 part of infusion, 0.5~2 part of levelling agent, 0.5~2 part of wax powder, 12~18 parts of pigment, 1~4 part of dispersant, scratch resistance agent 0.5
~2 parts, 0.5~2 part of thickener, 1~4 part of pH adjusting agent.
3. aqueous anilox roll inking according to claim 2, it is characterised in that it includes the component of following parts by weight：Third
28~32 parts of olefin(e) acid latex A, 23~27 parts of acrylic emulsion B, 18~22 parts of Polyurethane emulsion, 0.5~2 part of wetting agent disappear
0.5~2 part of infusion, 0.5~2 part of levelling agent, 0.5~2 part of wax powder, 13~17 parts of pigment, 1~3 part of dispersant, scratch resistance agent 0.5
~2 parts, 0.5~2 part of thickener, 1~3 part of pH adjusting agent.
4. aqueous anilox roll inking according to claim 3, it is characterised in that it includes the component of following parts by weight：Third
30 parts of olefin(e) acid latex A, 25 parts of acrylic emulsion B, 20 parts of Polyurethane emulsion, 1 part of wetting agent, 1 part of defoamer, 1 part of levelling agent,
1 part of wax powder, 15 parts of pigment, 2 parts of dispersant, 1 part of scratch resistance agent, 1 part of thickener, 2 parts of pH adjusting agent.
5. the aqueous anilox roll inking according to any one in Claims 1 to 4, it is characterised in that the Polyurethane breast
Liquid is selected from connection solidification and learns Polyurethane emulsion, this fertile chemical Polyurethane emulsion, Hubei to create prosperous CX-9129G Polyurethanes emulsion, Dongguan grand
Up to HD566 Polyurethanes emulsion or super great chemical industry F-11C Polyurethane emulsions.
6. the aqueous anilox roll inking according to any one in Claims 1 to 4, it is characterised in that the wetting agent choosing
Supreme Being Tego Do-75 are won from Bi Ke chemistry BYK347, Bi Ke chemistry BYK346, Shanghai;KL245、Tego Do-75;KL500、
Tego Do-75;The KL 270 or modest chemical W469 of moral；The defoamer is selected from Shanghai and wins Supreme Being Tego k3;830、Tego k3;
822、Tego k3;482nd, the modest chemical W-0506 of moral, Shanghai sea ease SD670, Bi Ke chemistry BYK-085 or Bi Ke chemistry BYK-
071；The dispersant is selected from EFKA4560 or the dispersants of SN 5040.
7. the aqueous anilox roll inking according to any one in Claims 1 to 4, it is characterised in that the levelling agent choosing
From BYK333, BYK361, Glide 432, Flow 300 or the levelling agents of Efka 3600；The scratch resistance agent be selected from BYK378,
BYK300 or BYK306.
8. the aqueous anilox roll inking according to any one in Claims 1 to 4, it is characterised in that the thickener choosing
Good SC-01 thickeners surpass/are opened up from Tao Shi thickeners TT-935, ROHM AND HAAS ACRYSOL ASE-60 or Shen；The pigment is selected from
Red pigment, yellow uitramarine, blue pigment or black pigment；The pH value of the ink is 7~9.
9. a kind of preparation method of the aqueous anilox roll inking of high adhesion force in Claims 1 to 4 described in any one, it is special
Levy after being first to mix acrylic emulsion A, acrylic emulsion B and Polyurethane emulsion, add wax powder and pigment, high-speed stirred
Uniformly, be ground to after being stirred behind fineness≤10 μm, continuously add wetting agent, defoamer, levelling agent, dispersant, scratch resistance agent and
Thickener, is eventually adding pH adjusting agent and adjusts pH value to 7~9.