CN106995680A - A kind of add-on type silica gel bonding agent for lighting tube plug - Google Patents

A kind of add-on type silica gel bonding agent for lighting tube plug Download PDF

Info

Publication number
CN106995680A
CN106995680A CN201710281397.XA CN201710281397A CN106995680A CN 106995680 A CN106995680 A CN 106995680A CN 201710281397 A CN201710281397 A CN 201710281397A CN 106995680 A CN106995680 A CN 106995680A
Authority
CN
China
Prior art keywords
silicone oil
bonding agent
silica gel
add
tube plug
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201710281397.XA
Other languages
Chinese (zh)
Inventor
蔡秀
潘斌俊
李彪
陈锦祥
周德宁
文德兴
钟寿增
蒙诚乐
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Zhongshan Dingli Electronics Material Co Ltd
Original Assignee
Zhongshan Dingli Electronics Material Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Zhongshan Dingli Electronics Material Co Ltd filed Critical Zhongshan Dingli Electronics Material Co Ltd
Priority to CN201710281397.XA priority Critical patent/CN106995680A/en
Publication of CN106995680A publication Critical patent/CN106995680A/en
Pending legal-status Critical Current

Abstract

The present invention provide a kind of add-on type silica gel bonding agent for lighting tube plug, by the material of following mass percentage content it is reacted after be made：Vinyl silicone oil (viscosity：10000~40000mpa.s) 10~30%, vinyl silicone oil (viscosity：1000~5000mpa.s) 10~25%, containing hydrogen silicone oil 1~3%, platinum catalyst 0.2%~2%, inhibitor 0.02~0.1%, tackifier 1~3% resist heavy powder 0.5~2%, precipitated calcium carbonate 50~75%.Wherein, inhibitor is alkynol, and tackifier are polar functionalities ester group and epoxy radicals, and it is silica to resist heavy powder.The beneficial effects of the present invention are curing rate is fast, significantly improves the production efficiency of fluorescent tube production, while reducing pollution of the harmful substance to human body and environment.

Description

A kind of add-on type silica gel bonding agent for lighting tube plug
Technical field
The present invention relates to a kind of silica gel bonding agent, particularly a kind of add-on type silica gel bonding agent for lighting tube plug.
Background technology
Currently on the market lighting tube plug (material of lighting tube plug is generally：Glass and PC or PVC plastic) it is viscous Connect agent and be mainly condensed type silica gel bonding agent, the bonding agent is present during use in many problems and shortcoming, such as raw material Containing organotin (heavy metal), there is very big harm to human body and environment, at room temperature curing rate slow (minimum 1 more than hour), Low production efficiency, and the pollutants such as the methanol or acidity of pollution air can be produced in the curing process.
The content of the invention
It is solid at room temperature to solve the above problems the invention provides a kind of add-on type silica gel bonding agent for lighting tube plug Change speed fast, methanol or acid contaminant will not be produced by being free of in product in organotin, solidification process.
The technical scheme that the present invention is provided is：A kind of add-on type silica gel bonding agent for lighting tube plug, by following quality It is made after the material of degree is reacted：
Wherein, inhibitor is alkynol, and tackifier are polar functionalities ester group and epoxy radicals, and it is silica to resist heavy powder.
The beneficial effects of the present invention are curing rate is fast, significantly improves the production efficiency of fluorescent tube production, while reducing has Pollution of the evil material to human body and environment.
Embodiment
Embodiment 1：
Embodiment 2：
Wherein, platinum catalyst concentration is 1500ppm, and inhibitor is alkynol, and tackifier are polar functionalities ester group and ring Epoxide, it is silica to resist heavy powder.
Embodiment 3：
Wherein, platinum catalyst concentration is 1500ppm, and inhibitor is alkynol, and tackifier are polar functionalities ester group and ring Epoxide, it is silica to resist heavy powder.
The add-on type silica gel bonding agent being made as stated above, is coated in the both sides of lighting tube plug, the material of lighting tube plug two After zoarium, then it is curable to toast 60~120s through 130 DEG C.
The present invention is explained in detail above in conjunction with embodiment, but the present invention is not limited to above-described embodiment.In ability , can also be on the basis of each composition effect basis mechanism is well understood that in the knowledge that domain those of ordinary skill possesses Do not depart from the premise of present inventive concept that various changes can be made, come under protection scope of the present invention.

Claims (1)

1. a kind of add-on type silica gel bonding agent for lighting tube plug, by the reacted rear system of the material of following mass percentage content Into：
Vinyl silicone oil（Viscosity：10000~40000mpa.s）10~30%
Vinyl silicone oil（Viscosity：1000~5000mpa.s）10~25%
Containing hydrogen silicone oil 1~3%
Platinum catalyst 0.2%~2%
Inhibitor 0.02~0.1%
Tackifier 1~3%
Anti- heavy powder 0.5~2%
Precipitated calcium carbonate 50~75%
Wherein, inhibitor is alkynol, and tackifier are polar functionalities ester group and epoxy radicals, and it is silica to resist heavy powder.
CN201710281397.XA 2017-04-26 2017-04-26 A kind of add-on type silica gel bonding agent for lighting tube plug Pending CN106995680A (en)