CN104479581A - Protective film with blue-light resistant function - Google Patents
Protective film with blue-light resistant function Download PDFInfo
- Publication number
- CN104479581A CN104479581A CN201410851558.0A CN201410851558A CN104479581A CN 104479581 A CN104479581 A CN 104479581A CN 201410851558 A CN201410851558 A CN 201410851558A CN 104479581 A CN104479581 A CN 104479581A
- Authority
- CN
- China
- Prior art keywords
- blue
- blue light
- transparent substrate
- layer
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a protective film with a blue-light resistant function. The protective film comprises a transparent substrate layer, wherein the upper surface and the lower surface of the transparent substrate layer are respectively coated with an anti-scraping coating and a blue-light resistant adhesive layer; the surface opposite to the blue-light resistant adhesive layer and the transparent substrate layer is coated with a release material layer; the blue-light resistant adhesive layer is prepared from the following components in parts by weight: 100 parts of acrylic ester adhesives, 0.075-0.1 part of an isocyanate curing agent, 10-20 parts of butanone, 2-5 parts of fluorescent powder, 0.2-0.5 part of hexamethylphosphoramide, 1-2 parts of benzoyl peroxide and 0.2-0.5 part of silicon oil. The protective film with the blue-light resistant function has the function of blue light resistance and has an adsorption and conversion function on blue purple high-energy short wave; 360-500 nm blue light waveband filtration rate reaches more than 90 percent, so that the health of the eyes can be protected well; the protective film has good adhesion performance on inorganic glass and organic plastic sheets.
Description
Technical field
The present invention relates to a kind of protective membrane with anti-blue light function, particularly a kind of OCA optical adhesive tape can for touch-screen with better adhesive property.
Background technology
In recent years, the development of touch-screen is very rapid, and along with growing with each passing day to multimedia information inquiry, people get more and more to the application of touch-screen.OCA optical adhesive tape due to possess water white transparency, transmitance more than 90%, consolidation strength is good, it is little to have cure shrinkage, do not produce the advantages such as xanthochromia, especially to ito glass and the advantage such as optical element is corrosion-free, so rely on its excellent process based prediction model, be widely used in touch-screen industry most.
Simultaneously along with the fast development of electronics technology, the requisite that the electronic product such as portable computer, TV has become people to live, people need the expensive time in the face of these electronic products every day, but include the very large blue light of human injury in the light that sends of the LED of these electronic products.Blue light refers to that wavelength is the high-energy light of 380nm ~ 480nm, it can penetrate lens and arrive retina, the epithelial cell of retinochrome is become feeble and die, photaesthesia cell is caused to lack nutrient, thus cause irreversible vision impairment, and blue light scattering probability when running into the fine particle in air is higher, easily produces dazzle, in addition blue light also can stimulate brain, suppress melatonin secretion and improve corticoid generation thus destroy hormone secretion balance directly affect sleep quality.
Therefore, develop a kind of anti-blue light optical adhesive tape, use it in electronic product, under the prerequisite with preferred optical performance, can also absorb blue light, this has very great meaning by the health of protection human body.
Summary of the invention
The invention provides a kind of protective membrane with anti-blue light function, this protective membrane with anti-blue light function had both had the effect of anti-blue light, royal purple high energy shortwave is had to the function of sorption enhanced, 360nm-500nm blue wave band filterability reaches more than 90%, better protects eye health; Also to unorganic glass and organic plastics sheet, there is better adhesive property.
For achieving the above object, the technical solution used in the present invention is: a kind of protective membrane with anti-blue light function, comprise a transparent substrate layer, the upper and lower surface of this transparent substrate layer is coated with anti-scratch coating, anti-blue light adhesive layer respectively, and described anti-blue light adhesive layer and the opposing surface of transparent substrate layer are covered with separated type material layer; Described anti-blue light adhesive layer is composed of the following components:
Acrylic ester sizing agent 100 parts,
Isocyanate curing agent 0.075 ~ 0.1 part,
Butanone 10 ~ 20 parts,
Ceria nanopowder: 2 ~ 5 parts, Er fluorescent material,
HMPA 0.2 ~ 0.5 part,
Benzoyl peroxide 1 ~ 2 part,
Silicone oil 0.2 ~ 0.5 part;
Described isocyanate curing agent model is Bayer L-75;
The weight average molecular weight range 200 ~ 8,000,000 of described acrylic acid series sizing agent, second-order transition temperature is-60 ~-30 DEG C;
Described transparent substrate layer thickness is 50 ~ 100 μm, transmittance > 98%, mist degree < 1.0%.
The technical scheme improved further in technique scheme is as follows:
1., in such scheme, the thickness of described anti-blue light coating is 0.5 ~ 3 μm.
2., in such scheme, described transparent substrate layer is film layer or layer of polypropylene foil or laminated polyester film.
Because technique scheme is used, the present invention compared with prior art has following advantages and effect:
The present invention has the protective membrane of anti-blue light function, and it had both had the effect of anti-blue light, royal purple high energy shortwave is had to the function of sorption enhanced, and 360nm-500nm blue wave band filterability reaches more than 90%, better protects eye health; Also to unorganic glass and organic plastics sheet, there is better adhesive property; Secondly, specific formula combination, solves liquid optical cement due to ceria nanopowder: Er fluorescent material adds and causes thickness wayward, and cure shrinkage easily produces the problem of bubble, thus effectively prevent the generation of bubble, touch display screen is better applied.
Accompanying drawing explanation
The protective membrane structural representation of accompanying drawing 1 anti-blue light function for the present invention has.
In above accompanying drawing: 1, transparent substrate layer; 2, anti-scratch coating; 3, anti-blue light adhesive layer; 4, separated type material layer.
Embodiment
Below in conjunction with drawings and Examples, the invention will be further described:
Embodiment 1 ~ 4: a kind of protective membrane with anti-blue light function, comprise a transparent substrate layer 1, the upper and lower surface of this transparent substrate layer 1 is coated with anti-scratch coating 2, anti-blue light adhesive layer 3 respectively, and described anti-blue light adhesive layer 3 surface opposing with transparent substrate layer 1 is covered with separated type material layer 4; Described anti-blue light adhesive layer 3 is composed of the following components:
The each ingredients weight parts content of described anti-blue light adhesive layer 3 is in table 1:
Table 1
Described isocyanate curing agent model is Bayer L-75;
The weight average molecular weight range 200 ~ 8,000,000 of described acrylic acid series sizing agent, second-order transition temperature is-60 ~-30 DEG C;
Described transparent substrate layer 1 thickness is 50 ~ 100 μm, transmittance > 98%, mist degree < 1.0%.
The thickness of above-mentioned anti-blue light coating is 0.5 μm or 2 μm or 1.5 μm or 3 μm.
Above-mentioned transparent substrate layer 1 embodiment 1 of stating is for film layer, and embodiment 2 is layer of polypropylene foil, and embodiment 3 is laminated polyester film, and embodiment 4 is film layer.
Adopt above-mentioned when having the protective membrane of anti-blue light function, it had both had the effect of anti-blue light, royal purple high energy shortwave was had to the function of sorption enhanced, and 360nm-500nm blue wave band filterability reaches more than 90%, better protects eye health; Also to unorganic glass and organic plastics sheet, there is better adhesive property; Secondly, specific formula combination, solves liquid optical cement due to ceria nanopowder: Er fluorescent material adds and causes thickness wayward, and cure shrinkage easily produces the problem of bubble, thus effectively prevent the generation of bubble, touch display screen is better applied.
Above-described embodiment, only for technical conceive of the present invention and feature are described, its object is to person skilled in the art can be understood content of the present invention and implement according to this, can not limit the scope of the invention with this.All equivalences done according to spirit of the present invention change or modify, and all should be encompassed within protection scope of the present invention.
Claims (3)
1. one kind has the protective membrane of anti-blue light function, it is characterized in that: comprise a transparent substrate layer (1), the upper and lower surface of this transparent substrate layer (1) is coated with anti-scratch coating (2), anti-blue light adhesive layer (3) respectively, and the surface that described anti-blue light adhesive layer (3) is opposing with transparent substrate layer (1) is covered with separated type material layer (4); Described anti-blue light adhesive layer (3) is composed of the following components:
Acrylic ester sizing agent 100 parts,
Isocyanate curing agent 0.075 ~ 0.1 part,
Butanone 10 ~ 20 parts,
Ceria nanopowder: 2 ~ 5 parts, Er fluorescent material,
HMPA 0.2 ~ 0.5 part,
Benzoyl peroxide 1 ~ 2 part,
Silicone oil 0.2 ~ 0.5 part;
Described isocyanate curing agent model is Bayer L-75;
The weight average molecular weight range 200 ~ 8,000,000 of described acrylic acid series sizing agent, second-order transition temperature is-60 ~-30 DEG C;
Described transparent substrate layer (1) thickness is 50 ~ 100 μm, transmittance > 98%, mist degree < 1.0%.
2. anti-blue light OCA optical adhesive tape according to claim 1, is characterized in that: the thickness of described anti-blue light adhesive layer (3) is 0.5 ~ 3 μm.
3. anti-blue light OCA optical adhesive tape according to claim 1, is characterized in that: described transparent substrate layer (1) is film layer or layer of polypropylene foil or laminated polyester film.